At elevated temperatures, concrete undergoes changes in its mechanical and thermal properties, which mainly cause degradation of strength and eventually may lead to the failure of the structure. Retrofitting is a desirable option to rehabilitate fire damaged concrete structures. However, to ensure safe reuse of fire-exposed buildings and to adopt proper retrofitting methods, it is essential to evaluate the residual load-bearing capacity of such fire-damaged reinforced concrete structures. The focus of the experimental study presented in this paper aims to investigate the fire performance of concrete columns exposed to a standard fire, and then evaluate its residual compressive strengths after fire exposure of different durations.

To effectively study the fire performance of such columns, eight identical 200 × 200 × 1,500-mm high reinforced concrete columns test specimens were subjected to two different fire exposure (1- and 2-h) while being loaded with two different load ratios (20% and 40% of the column ultimate design axial compressive load). In a subsequent stage and after complete cooling down, residual compressive strength capacity tests were performed on each fire exposed column.

Experimental results revealed that the columns never regain its original capacity after being subjected to a standard fire and that the residual compressive strength capacity dropped to almost 50% and 30% of its ambient temperature capacity for the columns exposed to 1- and 2-h fire durations, respectively. It was also noticed that, for the tested columns, the applied load ratio has much less effect on the column’s residual compressive strength compared to that of the fire duration.

According to the unique outcomes of this experimental study and, as the fire-damaged concrete columns possessed considerable residual compressive strength, in particular those exposed to shorter fire duration, it is anticipated that with proper retrofitting techniques such as fiber-reinforced polymers (FRP) wrapping, the fire-damaged columns can be rehabilitated to regain at least portion of its lost load-bearing capacities. Accordingly, the residual compressive resistance data obtained from this study can be effectively used but not directly to adopt optimal retrofitting strategies for such fire-damaged concrete columns, as well as to be used in validating numerical models that can be usefully used to account for the thermally-induced degradation of the mechanical properties of concrete material and ultimately predict the residual compressive strengths and deformations of concrete columns subjected to different load intensity ratios for various fire durations.

The collapse of a structure resulting from the instability of steel frames due to fire is the worst failure mode to consider in fire-structural engineering, and should be avoided. The purpose of this paper is to propose a new method for estimating the minimum possible duration of a fire event that could result in the instability of an unbraced steel frame.

The proposed method is in the form of a constrained minimization problem that determines the worst case fire scenario that can cause instability of a structure, and is solved using nonlinear constrained mathematical programming algorithms. The formulation is demonstrated via a numerical example.

For frames subjected to fire events modelled with monotonically increasing fire curves, the worst case fire causing instability of a frame is always one where all of the compartments catch fire at the same time. For frames subjected to fire events where fire curves decay, the minimization problem must be solved rigorously. The results are significantly affected by the fire curves and amount of insulation applied to each member.

The proposed method is an extension of a method previously established by Xu et al. (2018) to assess the stability of unbraced steel frames subjected to elevated member temperatures. The previous method does not consider fire duration and heat transfer mechanics, which are included in the proposed method. The proposed method is potentially useful for designers in conducting fire scenario analysis in the performance-based design of structures.

Since columns are critical structural elements, they shall withstand hazards without any considerable damage. In the case of a fire, although concrete has low thermal conductivity compared to other construction materials, its properties are changed at elevated temperatures. Most critically, the residual compressive strengths of reinforced concrete columns are significantly reduced after fire exposure. Validation of the worthiness of rehabilitating concrete structures after fire exposure is highly dependent on accurately determining the residual strengths of fire-damaged essential structural elements such as columns.

In this study, eight reinforced-concrete columns (200 × 200 × 1,500 mm) that were experimentally examined in a prior related study have been numerically modelled using ABAQUS software to investigate their residual compressive strengths after exposure to different durations of standard fire (i.e. one and two hours) while subjected to different applied load ratios (i.e. 20 and 40% of the compressive resistance of the column). Outcomes of the numerical simulations were verified against the prior study's experimental results.

In a subsequent phase, the results of a parametric study that has been completed as part of the current study to investigate the effects of the applied load ratios show that the application of axial load up to 80% of the compressive resistance of the column did not considerably influence the residual compressive strength of the shorter columns (i.e. 1,500 and 2,000-mm high). However, increasing the height of the column to 2,500 or 3,000 mm considerably reduced the residual compressive strength when the load ratio applied on the columns exceeded 60 and 40%, respectively. Also, when the different columns were simulated under two-hour standard fire exposure, the dominant failure was buckling rather than concrete crushing which was the typical failure mode in most columns.

The outcomes of the numerical study presented in this paper reflect the residual compressive strength of RC columns subjected to various applied load ratios and standard fire durations. Also, the parametric study conducted as part of this research on the effects of higher load ratios and greater column heights on the residual compressive strength of the fire-damaged columns is practical and efficient. The developed computer models can be beneficial to assist engineers in assessing the validity of rehabilitating concrete structures after being exposed to fire.

This study investigates the impact of the fire decay phase on structural damage using the sectional analysis method. The primary objective of this work is to forecast the non-dimensional capacity parameters for the axial and flexural load-carrying capacity of reinforced concrete (RC) sections for heating and the subsequent post-heating phase (decay phase) of the fire.

The sectional analysis method is used to determine the moment and axial capacities. The findings of sectional analysis and heat transfer for the heating stage are initially validated, and the analysis subsequently proceeds to determine the load capacity during the fire’s heating and decay phases by appropriately incorporating non-dimensional sectional and material parameters. The numerical analysis includes four fire curves with different cooling rates and steel percentages.

The study’s findings indicate that the rate at which the cooling process occurs after undergoing heating substantially impacts the axial and flexural capacity. The maximum degradation in axial and flexural capacity occurred in the range of 15–20% for cooling rates of 3 °C/min and 5 °C/min as compared to the capacity obtained at 120 min of heating for all steel percentages. As the fire cooling rate reduced to 1 °C/min, the highest deterioration in axial and flexural capacity reached 48–50% and 42–46%, respectively, in the post-heating stage.

The established non-dimensional parameters for axial and flexural capacity are limited to the analysed section in the study owing to the thermal profile, however, this can be modified depending on the section geometry and fire scenario.

The study primarily focusses on the degradation of axial and flexural capacity at various time intervals during the entire fire exposure, including heating and cooling. The findings obtained showed that following the completion of the fire’s heating phase, the structural capacity continued to decrease over the subsequent post-heating period. It is recommended that structural members' fire resistance designs encompass both the heating and cooling phases of a fire. Since the capacity degradation varies with fire duration, the conventional method is inadequate to design the load capacity for appropriate fire safety. Therefore, it is essential to adopt a performance-based approach while designing structural elements' capacity for the desired fire resistance rating. The proposed technique of using non-dimensional parameters will effectively support predicting the load capacity for required fire resistance.

The fire-resistant requirements for reinforced concrete structures are generally established based on standard fire exposure conditions, which account for the fire growth phase. However, it is important to note that concrete structures can experience internal damage over time during the decay phase of fires, which can be quantitatively determined using the proposed non-dimensional parameter approach.

Most of the industrial buildings which are designed to moderate loads are constructed using light gauge cold-formed steel (CFS) sections. Residual mechanical properties of CFS sections exposed to elevated temperature need to be investigated as it is necessary to predict the deterioration of elements to avoid failure of the structure or its elements. Also, it would be helpful to decide whether the structural elements need to be replaced or reused. The use of fire-resistant coatings in steel structures significantly reduces the cost of repairing structural elements and also the probability of collapse. This study investigates the effect of fire-resistant coating on post-fire residual mechanical properties of E350 steel grade.

In this study, an attempt has been made to evaluate the residual mechanical properties of E350 steel. A tensile coupon test was performed for the extracted specimens from the exposed CFS section to determine the mechanical properties. Four different fire-resistant coatings were selected and the sections were coated and heated as per ISO 834 fire temperature curve in the transient state for time durations of 30 minutes (821°C), 60 minutes (925°C), 90 minutes (986°C), and 120 minutes (1,029°C). After the exposure, all the coupon specimens were cooled by either ambient conditions (natural air) or water spraying before conducting the tension test on these specimens.

At 30 min exposure, the reduction in yield and ultimate strength of heated specimens was about 20 and 25% for air and water-cooled specimens compared with reference specimens. Specimens coated with vermiculite and perlite exhibited higher residual mechanical property up to 60 minutes than other coated specimens for both cooling conditions. Generally, water-cooled specimens had shown higher strength loss than air-cooled specimens. Specimens coated with vermiculite and perlite showed an excellent performance than other specimens coated with zinc and gypsum for all heating durations.

As CFS structures are widely used in construction practices, it is crucial to study the mechanical properties of CFS under post-fire conditions. This investigation provides detailed information about the physical and mechanical characteristics of E350 steel coated with different types of fire protection materials after exposure to elevated temperatures. An attempt has been made to improve the residual properties of CFS using the appropriate coatings. The outcome of the present study may enable the practicing engineers to select the appropriate coating for protecting and enhancing the service life of CFS structures under extreme fire conditions.

The purpose of this paper is to examine the perspectives of local residents regarding the impact of the long-duration Hazelwood open cut coal mine fire in rural Australia.

A qualitative approach was undertaken involving 27 in-depth interviews with adults who lived in the town of Morwell, immediately adjacent to the coal mine fire.

Participant concerns focussed upon fear and confusion during the event, the perceived health effects of the smoke, anger towards authorities and loss of a sense of community and sense of security. One of the significant ways in which people managed these responses was to normalise the event. The long duration of the event created deep uncertainty which exaggerated the impact of the fire.

Understanding the particular nature of the impact of this event may assist the authors to better understand the ongoing human impact of long-duration disasters in the future.

It is important to provide clear and understandable quality information to residents during and after such disasters.

While there is an extensive literature exploring the direct social and psychological impacts of acute natural disasters, less qualitative research has been conducted into the experiences of longer term critical events.

The Reinforced Concrete(RC) elements are known to perform well during exposure to elevated temperatures. Hence, RC elements are widely used to resist the extreme heat developing from accidental fires and other industrial processes. In both of the scenarios, the RC element is exposed to elevated temperatures. However, the primary differences between the fire and processed temperatures are the rate of temperature increase, mode of exposure and exposure durations. In order to determine the effect of two heating modalities, RC beams were exposed to processed temperatures with slow heating rates and fire with fast heating rates.

In the present study, RC beam specimens were exposed to 200 °C, to 800 °C temperature at 200 °C intervals for 2 h' duration by adopting two heating modes; Fire and processed temperatures. An electrical furnace with low-temperature increment and a fire furnace with standard time-temperature increment is adapted to expose the RC elements to elevated temperatures.

It is observed from test results that, the reduction in load-carrying capacity, first crack load, and thermal crack widths of RC beams exposed to 200 °C, and 600 °C temperature at fire is significantly high from the RC beams exposed to the processed temperature having the same maximum temperature. As the exposure temperature increases to 800 °C, the performance of RC beams at all heating modes becomes approximately equal.

In this work, residual performance, and failure modes of RC beams exposed to elevated temperatures were achieved through two different heating modes are presented.

The design of buildings for fire events is essential to ensure occupant safety. Supplementary to simple prescriptive methods, performance-based fire design can be applied to achieve a greater level of safety and flexibility in design. To make performance-based fire design more accessible, a time-equivalent method can be used to approximate a given natural fire event using a single standard fire with a specific duration. Doing so allows for natural fire events to be linked to the wealth of existing data from the standard fire scenario. The purpose of this paper is to review and assess the application of an existing time-equivalent method in the performance-based design of reinforced concrete (RC) beams.

The assessment is established by computationally developing the moment-curvature response of RC beam sections during fire exposure. The sectional response due to natural fire and time equivalent fire are compared.

It is shown that the examined time equivalent method is able to predict the sectional response with suitable accuracy for performance-based design purposes.

The research is the first to provide a comprehensive evaluation of the moment-curvature diagram of RC beams using time-equivalent standard fire scenarios that model realistic fire scenarios.

The paper aims to give an insight into the behaviour of reinforced concrete columns during and after the cooling phase of a fire. The study is based on numerical simulations as these tools are frequently used in structural engineering. As the reliability of numerical analysis largely depends on the validity of the constitutive models, the development of a concrete model suitable for natural fire analysis is addressed in the study.

The paper proposes theoretical considerations supported by numerical examples to discuss the capabilities and limitations of different classes of concrete models and eventually to develop a new concrete model that meets the requirements in case of natural fire analysis. Then, the study performs numerical simulations of concrete columns subjected to natural fire using the new concrete model. A parametric analysis allows for determining the main factors that affect the structural behaviour in cooling.

Failure of concrete columns during and after the cooling phase of a fire is a possible event. The most critical situations with respect to delayed failure arise for short fires and for columns with low slenderness or massive sections. The concrete model used in the simulations is of prime importance and the use of the Eurocode model would lead to unsafe results.

The paper includes implications for the assessment of the fire resistance of concrete elements in a performance‐based environment.

The paper provides original information about the risk of structural collapse during cooling.

Existing analytical methods for the evaluation of fire safety of reinforced concrete (RC) structures require extensive knowledge of heat transfer calculations and the finite element method. This paper aims to propose a rational method to predict the axial capacity of RC columns exposed to standard fire.

The average temperature distribution along the section height is first predicted for a specific fire scenario. The corresponding distribution of the reduced concrete strength is then integrated to develop expressions to calculate the axial capacity of RC columns exposed to fire from four faces.

These expressions provide structural engineers with a rational tool to satisfy the objective-based design clauses specified in the National Code of Canada in lieu of the traditional prescriptive methods.

The research is limited to standard fire curves and needs to be extended to cover natural fire curves.

This paper is the first to propose an accurate yet simple method to calculate the axial capacity of columns exposed to standard fire curves. The method can be applied using a simple Excel sheet. It can be further developed to apply to natural fire curves.