The purpose of this paper is to examine the practicability of the self-designed ambient humidity controllable pin-disc/rolling multifunctional friction and wear test device and to evaluate the friction and wear characteristics of materials under diverse ambient humidity conditions in different contact forms.

The practicability of the self-designed multifunctional friction tester was examined by the friction and wear tests of materials under different ambient humidity conditions [65%RH, 98%RH (relative humidity)] in diverse contact forms (pin/disc and rolling). Meanwhile, the friction and wear properties of pin/disc samples also rolling samples were assessed from three aspects: average friction coefficient, wear mass and wear morphology.

The results prove that the self-designed multifunctional friction tester has practicability. Therefore, it can be used to simulate the friction and wear tests of materials under diverse ambient humidity conditions in different contact forms. Besides, it is evident that the wear damage of pin/disc and rolling samples are greatly improved under high ambient humidity conditions. And when other conditions are identical, the higher the ambient humidity, the smaller the average friction coefficient, wear mass and wear damage degree of pin/disc also rolling samples.

This paper offers a self-designed multifunctional friction and wear test device. And the tester not only can realize the control of test ambient humidity, but also achieve the wear test of pin/disc or rolling contact forms. The design and production of the tester can offer convenience for the research of tribology, and provide fundamental guidance for the study of materials under high humidity condition in diverse contact forms.

The purpose of this study is to investigate the effect of laser scanning speed (LSS) on the corrosive-tribological performance of Ni-60%WC coating in Wusu mine water, which was beneficial to improve the friction–wear performance of cylinder liner on water injection pump.

Ni-60%WC coatings were fabricated on 45 steel by laser cladding, and the microstructure and tribological performance was analyzed using a super depth of field microscope and ball-on-plate friction tester, and the wear mechanism was also discussed.

At room temperature (RT, 25 ± 2 °C), the average coefficients of friction of substrate and Ni-60%WC coatings fabricated at the LSS of 6, 10, 12 and 14 mm/s are 0.48 ± 0.08, 0.23 ± 0.01, 0.21 ± 0.05, 0.22 ± 0.02 and 0.25 ± 0.04, respectively, and the corresponding wear rates are 8.755 × 10⁴, 4.525 × 10³, 1.539 × 10³, 1.957 × 10³ and 2.743 × 10³ µm³·s^–1·N^–1, respectively, showing that the coating fabricated at the LSS of 10 mm/s has best friction reduction and wear resistance. The wear mechanism of Ni-60%WC coating is abrasive wear, fatigue wear and oxidative wear, which is resulted from the WC particles with the high-hardness.

Ni-60%WC coatings were first applied for cylinder liner, and the effect of laser scanning speed on its tribological performance was investigated.

It is quite universal for high-speed turnouts to be exposed to the wear of the stock rail of the switch rail during the service process. The wear will cause the change of railhead profile and the relative positions of the switch rail and the stock rail, which will directly affect the wheel–rail contact state and wheel load transition when a train passes the turnout and will further impose serious impacts on the safety and stability of train operation. The purpose of this paper is to provide suggestions for wear management of high-speed turnout.

The actual wear characteristics of switch rails of high-speed turnouts in different guiding directions were studied based on the monitoring results on site; the authorized wear limits for the switch rails of high-speed turnout were studied through derailment risk analysis and switch rail strength analysis.

The results show that: the major factor for the service life of a curved switch rail is the lateral wear. The wear characteristics of the curved switch rail of a facing turnout are significantly different from those of a trailing turnout. To be specific, the lateral wear of the curved switch rail mainly occurs in the narrower section at its front end for a trailing turnout, but in the wider section at its rear end when for a facing turnout. The maximum lateral wear of a dismounted switch rail from a trailing turnout is found on the 15-mm wide section and is 3.9 mm, which does not reach the specified limit of 6 mm. For comparison, the lateral wear of a dismounted switch rail from a facing turnout is found from the 35-mm wide section to the full-width section and is greater than 7.5 mm, which exceeds the specified limit. Based on this, in addition to meeting the requirements of maintenance rules, the allowed wear of switch rails of high-speed turnout shall be so that the dangerous area with a tangent angle of wheel profile smaller than 43.6° will not contact the switch rail when the wheel is lifted by 2 mm. Accordingly, the lateral wear limit at the 5-mm wide section of the curved switch rail shall be reduced from 6 mm (as specified) to 3.5 mm.

The work in this paper is of reference significance to the research on the development law of rail wear in high-speed turnout area and the formulation of relevant standards.

The effect of different service parameters on the current-carrying tribological properties of CF-Al₂O₃/Cu composites was investigated, and the damage behavior of the composites under different service parameters was probed. The purpose of this study is to provide a theoretical basis for the application of CF-Al₂O₃/Cu composites.

The composites were fabricated by internal oxidation combined with powder metallurgy. The current-carrying tribological properties of CF-Al₂O₃/Cu composites were investigated on an electrical damage test system at different loads and currents.

As the load increases, the wear mechanism of the composite changes from abrasive wear to delamination wear. As the current increases, the oxidation wear and arc erosion of the composites gradually intensified. Under the service parameters of 0–25 A and 30–40 N, the composite has relatively stable current-carrying tribological properties.

This paper could provide a theoretical basis for the practical application of CF-Al₂O₃/Cu composites.

This paper aims to determine a suitable anti-wear and friction-reducing compounding additive for lithium greases (LG) by investigating the effects of three single additives potassium borate (PB), zinc dialkyl dithiophosphate and molybdenum dialkyl dithiophosphate (MoDDP) and two compound additives on the friction, wear and extreme pressure properties of LG.

The effects of the above five additives on the friction, wear and extreme pressure properties of LG were investigated using an SRV-5 friction tester. An X-ray photoelectron spectrometer was used to analyze the various elements presented on the wear surface as well as the types of compounds.

The compound additive suitable for grease consists of PB and MoDDP, which have excellent friction reduction, anti-wear and extreme pressure properties. And a boundary protection film consisting of oxide and MoS₂ is formed on the friction surface, thus improving the friction reduction and anti-wear performance of the grease.

This study can improve the anti-wear and friction-reduction performance of greases, which is of great importance in the field of industrial lubrication. The results of this paper are expected to be useful to researchers and academics of grease.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-11-2022-0350/

This paper aims to investigate the effect of Ti₃SiC₂ on the high-temperature tribological behaviors of NiCr coating, which was beneficial to improve the friction-wear performance of hot work mold.

NiCr-Ti₃SiC₂ coatings were prepared on H13 steel substrate by laser cladding. The microstructure, phases and hardness of obtained coatings were analyzed using a super-depth of field microscope, X-ray diffraction and microhardness tester, respectively, and the tribological performance of obtained coatings at 500°C was investigated using a high-temperature tester.

The results show the NiCr-Ti₃SiC₂ coatings are comprised of γ-Ni solid, solution, Ti_xNi_y, TiC and Ti₃SiC₂ phases, and the coating hardness is increased with the increase of Ti₃SiC₂ mass fraction, which is contributed to the fine-grain and dispersion strengthening effect by the addition of Ti₃SiC₂. The NiCr-Ti₃SiC₂ coatings present excellent friction reduction and wear resistance by the synergetic action of Ti₃SiC₂ lubricant and hard phase, and the wear mechanism is predominated by abrasive wear and oxidation wear.

Ti₃SiC₂ phase was used to reinforce the tribological performance of H13 steel at high temperature, and the roles of friction reduction and wear resistance were discussed.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2023-0004/

The serious wear problem of heavy-haul freight vehicle wheels affects the safety and economy of vehicle operation. This paper aims to study wheel wear evolution law and the influence of line parameters on wheel wear of heavy-haul freight, and provide the basis for operation and line maintenance.

The wheel wear test data of heavy-haul freight vehicles were analyzed. Then a heavy-haul freight vehicle dynamic model was established. The line parameters influencing wheel wear in heavy-haul freight vehicles were also analyzed by the Jendel wear model, and the effects of rail cant, rail gauge, rail profile and line ramp on wheel wear were analyzed.

A rail cant of 1:40 results in less wheel wear; an increase in the rail gauge can reduce wheel wear; and when matched with the CHN60 rail, the wear depth is relatively small. A decrease of 9.21% in wheel wear depth when matched with the CHN60 rail profile. The ramp of the heavy-haul line is necessary to consider for calculating wheel wear. When the ramp is considered, the wear depth increases by 8.47%. The larger the ramp, the greater the braking force and therefore, the greater of the wheel wear.

This paper first summarizes the wear characteristics of wheels in heavy-haul freight vehicles and then systematically analyzes the effect of line parameters on wheel wear. In particular, this study researched the effects of rail cant, rail gauge, rail profile and line ramp on wheel wear.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-02-2024-0038/

The purpose of this study is to design and process the optimal V-shaped microstructure for 7075 aluminum alloy and reveal its wear resistance mechanism and performance.

The hydrodynamic pressure lubrication models of the nontextured, V-shaped, circular and square microtextures are established. The corresponding oil film pressure distributions are explored. The friction and wear experiments are conducted on a rotating device. The effects of the microstructure shapes and sizes on the wear mechanisms are investigated via the friction coefficients and surface morphologies.

In comparison, the V-shaped microtexture has the largest oil film carrying capacity and the lowest friction coefficient. The wear mechanism of the V-shaped microtexture is dominated by abrasive and adhesive wear. The V-shaped microtexture has excellent wear resistance under a side length of 300 µm, an interval of 300 µm and a depth of 20 µm.

This study is conductive to the design of wear-resistant surfaces for friction components.

This study aims to investigate the effect of MoS2 powder on tribological properties of sliding interfaces.

Loose MoS2 powder was introduced in the gap of point-contact friction pairs, and sliding friction test was conducted using a testing machine. Friction noise, wear mark appearance, microstructure and wear debris were characterized with a noise tester, white-light interferometer, scanning electron microscope and ferrograph, respectively. Numerical simulation was also performed to analyze the influence of MoS2 powder on tribological properties of the sliding interface.

MoS2 powder remarkably improved the lubrication performance of the sliding interface, whose friction coefficient and wear rate were reduced by one-fifth of the interface values without powder. The addition of MoS2 powder also reduced stress, plastic deformation and friction temperature in the wear mark. The sliding interface with MoS2 powder demonstrated lower friction noise and roughness compared with the interface without powder lubrication. The adherence of MoS2 powder onto the friction interface formed a friction film, which induced the wear mechanism of the sliding interface to change from serious cutting and adhesive wear to delamination and slight cutting wear under the action of normal and shear forces.

Tribological characteristics of the interface with MoS2 powder lubrication were clarified. This work provides a theoretical basis for solid-powder lubrication and reference for its application in engineering.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-04-2020-0150/

Wear greatly influences the machine lifetime, performance and reliability and its quantification is very important. This paper aims to propose a modified bearing area curve method by combining the theory of the bearing area curve, and the relocation technique to calculate wear accurately and efficiently.

H13 steel was chosen as the material of wear pair, and the wear experiments were carried out at 50 N, 60 r/min for 20 min. The surface was measured before and after wear experiments. The relocation was made by comparing the mean lines (planes) of the unworn and worn surface profiles. The calculated results using the proposed method were compared with that of the surface profile method for a two-dimensional surface to validate its accuracy. The method was then applied for a three-dimensional (3D) wear analysis.

The worn surface shows clearly displacement compared to the unworn surface and implies the importance of including relocation in the bearing area curve method. The results from the proposed method are 98 per cent close to that from the surface profile method, indicating that the method is accurate for wear evaluation.

As no feature point or relocation mark is needed to calculate the relocation value using the proposed method, the method can be applied to mild to severe wear. Also, as the deviation of different scans does not affect the relocation calculation, and no matching and stitching is required, this method can be easily applied to a wide wear area and 3D surface wear analysis.