This study aims to evaluate and assess the elastoplastic properties of Ti-6Al-4V alloy manufactured by Arcam Q20 Plus electron beam melting (EBM) machine by a tensile test campaign and micro computerized tomography (microCT) imaging.

ASTM E8 tensile test specimens are designed and manufactured by EBM at an Arcam Q20 Plus machine. Surface quality is improved by machining to discard the effect of surface roughness. After surface machining, hot isostatic pressing (HIP) post-treatment is applied to half of the specimens to remove unsolicited internal defects. ASTM E8 tensile test campaign is carried out simultaneously with digital image correlation to acquire strain data for each sample. Finally, build direction and HIP post-treatment dependencies of elastoplastic properties are analyzed by F-test and t-test statistical analyses methods.

Modulus of elasticity presents isotropic behavior for each build direction according to F-test and t-test analysis. Yield and ultimate strengths vary according to build direction and post-treatment. Stiffness and strength properties are superior to conventional Ti-6Al-4V material; however, ductility turns out to be poor for aerospace structures compared to conventional Ti-6Al-4V alloy. In addition, micro CT images show that support structure leads to dense internal defects and pores at applied surfaces. However, HIP post-treatment diminishes those internal defects and pores thoroughly.

As a novel scientific contribution, this study investigates the effects of three orthogonal build directions on elastoplastic properties, while many studies focus on only two-build directions. Evaluation of Poisson’s ratio is the other originality of this study. Furthermore, another finding through micro CT imaging is that temporary support structures result in intense defects closer to applied surfaces; hence high-stress regions of structures should be avoided to use support structures.

Green machining is becoming increasingly more popular due to concern regarding the safety of the environment and human health. The important implementation of stricter Environmental Protection Agency regulations associated with the use of ample amount of coolants and lubricants has led to this study on a new green machining technology with application of water vapor as coolants and lubricants in cutting Ni‐based superalloys and titanium alloy Ti‐6Al‐4V with uncoated carbide inserts (ISO Type K10). The purpose of this paper is to show that machining technology with application of water vapour could be an economical and environmentally compatible lubrication technique for machining difficult‐cut‐materials.

In this paper, the effect of water vapor applications in machining difficult‐cut‐materials have been investigated in detail, the cutting force, the chip deformation coefficient, the rake face wear and the width of tool flank land VB have been examined and analyzed, and a new green cutting technology is researched to machining Ni base superalloys and Ti‐6Al‐4V difficult‐cut‐materials.

The cutting force of machining Ni base superalloys and Ti‐6Al‐4V was affected by direct water vapor application, being lower than dry cutting and wet machining for all machining conditions; the Λh is the smallest with applications of water vapor as coolants and lubricants compared to dry cutting, pure water and oil water emulsion conditions the tool life extended by about six times than dry cutting, about four times than oil water emulsions at low cutting speed (ν_c<100 m/min), and about two‐four times than dry cutting, about two‐three time than oil water emulsions at higher cutting speed (ν_c>100 m/min) during machining Ti‐6Al‐4V with application of water vapor direct into the cutting zone.

The green cutting technology which applies water vapor as coolants and lubricants advocates a new method for machining difficult‐cut‐materials (Ni base superalloys and Ti‐6Al‐4V) without any environment pollution and operator health problem because the cutting force and chip deformation coefficient are reduced, the tool life is extended, and the tool flank wear can be decreased with applications of water vapor as coolants and lubricants to alleviate the adhering and diffusion wear compared to wet cutting and dry cutting.

The purpose of this paper is to investigate the influence of mechanical surface treatments on the surface layer properties and the fatigue performance of the aircraft alloys Al 7075‐T73 and Ti‐6Al‐4V

Laser peening without coating (LPwC), shot peening (SP), ultrasonic shot peening (USP) and ball burnishing (BB) were applied and the resulting changes in surface roughness and residual stress‐depth profiles were evaluated. Fatigue performance of both alloys was tested in rotating beam loading (R=−1) on hourglass‐shaped specimens and the results were compared with the electrolytically polished (EP) reference conditions.

All studied mechanical surface treatments led to pronounced increases in fully reversed fatigue lives and fatigue strengths in both Al 7075‐T73 and Ti‐6Al‐4V.

To the authors' knowledge, this is the first paper that compares fatigue performance of a wide variety of mechanically surface treated conditions in two aircraft alloys.

With the discussion on the linear relationship of determined material parameters, this study aims to propose a new method to analyze the deformation mechanism.

A modified constitutive model based on the hyperbolic sine Arrhenius equation has been established, which is applied to describe the flow behavior of Ti-6Al-4V alloy during the superplastic forming (SPF).

The modified constitutive model in this work has a good ability to describe the flow behavior for Ti-6Al-4V in SPF. Besides, a deformation map of titanium material is obtained based on the parameters. As the supplement, finite element models of high-temperature tensile tests are carried out as the application of the constitutive model.

The relationship between constitutive model parameters and forming mechanism is established, which is a new angle in rheological behavior research and constitutive model analysis.

The purpose of this paper is the microstructural and mechanical characterization of a biomedical Ti‐6Al‐4V alloy produced by electron beam melting, and the study of the stability of the as‐built microstructure upon heat treatment.

Ti‐6Al‐4V alloy produced by electron beam melting has been mechanically characterized through tensile and fatigue testing. Its microstructure has been investigated by optical observation after etching and by X‐ray diffractometry analysis. The stability of the microstructure of the as‐built material has been deepened carrying out suitable heat treatments, after an analysis by dilatometry test.

The microstructure of a Ti‐6Al‐4V alloy produced by electron beam melting has a very fine and acicular morphology, because of the intrinsically high‐solidification rate of the process. This microstructure is very stable, and the traditional thermal treatments cannot modify it; the microstructure changes significantly only when an amount of strain is introduced in the material. However, the mechanical properties of the alloy produced by electron beam melting are good.

The paper provides evidence of the microstructural stability of the material produced by electron beam melting. Even if the microstructure of the as‐built material is not recommended by the specific ISO standard, the related mechanical properties are fully satisfactory. This is a significant indication from the point of view of the production of Ti‐6Al‐4V orthopaedic and dental prostheses by electron beam melting.

This paper aims to study the effect of processing parameters of an electron beam melting (EBM) machine on the surface roughness, critical pitting temperature and density of Ti-6Al-4V parts produced from the EBM machine.

In this study, statistically designed experiments were used to manufacture Ti-6Al-4V samples in the EBM machine under different process parameters of beam current, beam speed and offset focus. Surface roughness was measured for as-built samples using a 3D profilometer. Then, a potentiostatic test was conducted under 2.40 V vs saturated calomel electrode to determine the critical pitting temperature (CPT) in 3.5 per cent mass NaCl solution for the samples of different processing parameters. Next, density was measured for these samples. Finally, model equations were established to relate EBM’s process parameters to measured properties of surface roughness, CPT and density.

Results showed that offset focus had the main influence on surface roughness more than the beam current and the beam speed. Changing processing parameters did not affect corrosion behavior of EBM Ti-6Al-4V as CPT did not vary widely, although a slight effect on CPT values obtained from the beam current and the beam speed. Density was greatly affected by the offset focus more than the other parameters. It can be concluded that uniform and precise measurements of roughness and density are not achievable through this machine; only a range of these properties can be attained.

EBM machine produces 3D parts in a layer-based building process under high temperature and vacuum atmosphere. Due to the manufacturing technique and conditions, the resulting object has irregularities on the exterior surface and voids that are formed within the part, both of which affect samples’ properties like surface roughness, CPT and density. This study established model equations that can relate parts’ properties to processing parameters so that parts of specific properties are obtained to fit the application they are used for. For each property, ANOVA fits vs linear energy were also obtained.

The development of new advanced materials, such as photopolymerizable resins for use in stereolithography (SLA) and Ti6Al4V manufacture via selective laser melting (SLM) processes, have gained significant attention in recent years. Their accuracy, multi-material capability and application in novel fields, such as implantology, biomedical, aviation and energy industries, underscore the growing importance of these materials. The purpose of this study is oriented toward the application of new advanced materials in stent manufacturing realized by 3D printing technologies.

The methodology for designing personalized medical devices, implies computed tomography (CT) or magnetic resonance (MR) techniques. By realizing segmentation, reverse engineering and deriving a 3D model of a blood vessel, a subsequent stent design is achieved. The tessellation process and 3D printing methods can then be used to produce these parts. In this context, the SLA technology, in close correlation with the new types of developed resins, has brought significant evolution, as demonstrated through the analyses that are realized in the research presented in this study. This study undertakes a comprehensive approach, establishing experimentally the characteristics of two new types of photopolymerizable resins (both undoped and doped with micro-ceramic powders), remarking their great accuracy for 3D modeling in die-casting techniques, especially in the production process of customized stents.

A series of analyses were conducted, including scanning electron microscopy, energy-dispersive X-ray spectroscopy, mapping and roughness tests. Additionally, the structural integrity and molecular bonding of these resins were assessed by Fourier-transform infrared spectroscopy–attenuated total reflectance analysis. The research also explored the possibilities of using metallic alloys for producing the stents, comparing the direct manufacturing methods of stents’ struts by SLM technology using Ti6Al4V with stent models made from photopolymerizable resins using SLA. Furthermore, computer-aided engineering (CAE) simulations for two different stent struts were carried out, providing insights into the potential of using these materials and methods for realizing the production of stents.

This study covers advancements in materials and additive manufacturing methods but also approaches the use of CAE analysis, introducing in this way novel elements to the domain of customized stent manufacturing. The emerging applications of these resins, along with metallic alloys and 3D printing technologies, have brought significant contributions to the biomedical domain, as emphasized in this study. This study concludes by highlighting the current challenges and future research directions in the use of photopolymerizable resins and biocompatible metallic alloys, while also emphasizing the integration of artificial intelligence in the design process of customized stents by taking into consideration the 3D printing technologies that are used for producing these stents.

This paper aims to focus on the application of multi-attribute decision-making methods (MADMs) to ascertain the optimal machining parameters while turning Ti-6Al-4V alloy under minimum quantity lubrication (MQL) conditions using Jatropha-curcas oil (JCO) bio-based lubricant.

The experiments were designed and performed using Taguchi L27 design of experiments methodology. A total of 27 experiments were performed under MQL conditions using textured carbide cutting tools on which different MADMs like Analytic hierarchy process (AHP), Technique for order preference by similarity to ideal solution (TOPSIS) and Simple additive weighting (SAW) were implemented in an empirical manner to extract optimize machining parameters for turning of Ti-6Al-4V alloy under set of constrained conditions.

The results evaluated through MADMs exhibit the optimized set of machining parameters (cutting speed V_c = 80 m/min, feed rate f = 0.05 mm/rev. and depth of cut a_p = 0.10 mm) for minimizing the average surface roughness (Ra), maximum flank wear (Vbmax), tangential cutting force (Fc) and cutting temperature (T). Further, analysis of variance (ANOVA) and traditional desirability function approach was applied and results of TOPSIS and SAW methods having optimal setting of parameters were compared as well as confirmation experiments were conducted to verify the results. A SEM analysis at lowest and highest cutting speeds was performed to investigate the tool wear patterns. At the highest speed, large cutting temperature generated, thereby resulted in chipping as well as notching and fracturing of the textured insert.

The research paper attempted in exploring the optimized machining parameters during turning of difficult-to-cut titanium alloy (Ti-6AL-4V) with textured carbide cutting tool under MQL environment through combined approach of MADMs techniques. Ti-6Al-4V alloy has been extensively used in important aerospace components like fuselage, hydraulic tubing, bulk head, wing spar, landing gear, as well as bio-medical applications.

The purpose of this paper is to investigate the optimized setting of wire-cut electrical discharge machining (WEDM) parameters at which material removal rate (MRR) and mean roughness depth (Rz) set a compromise. The problem in the processing of Ti-6Al-4V by conventional processes is a high strength, high hardness, high tool wear. Due to which WEDM is adopted to machine Ti-6Al-4V biomedical alloy. Ti-6Al-4V alloy has a number of applications in the engineering and medical industries due to its high strength biocompatibility.

The effect of control factors (i.e. pulse on-time: Pon; pulse off-time: Poff; servo voltage: SV) on the MRR and Rz is investigated in the present research. The planning of experiments is done using a Taguchi-based L9 orthogonal array. The percentage influence of each factor on responses is also evaluated. The multi-objective optimization is done using the grey approach initially. After that, the results were also calculated using harmony search (HS). Therefore, a hybrid approach of grey and HS is used to find the optimized values of MRR and Rz.

The maximum value of grade calculated by grey-HS is 0.7879, while in the case of the experimental run the maximum value of grey grade is 0.7239. The optimized setting after improvisation at this grade value is Pon: 130 µs; Poff: 45 µs and SV: 70 V for MRR and Rz collectively. The validation of the suggested setting is completed by experimentation. The values of MRR and Rz are coming out to be 6.4 mm³/min and 13.84 µm, which represents improvised results after the implementation of the HS algorithm.

The integration of the grey approach with the HS principle in the manufacturing domain is yet to be explored. Therefore, in the present research hybrid approach of grey-HS is implemented in the manufacturing domain having applications in medical industries.

This paper aims to achieve Ti-6Al-4V from Ti, Al and V elemental powder blends using direct laser deposition (DLD) and to understand the effects of laser transverse speed and laser power on the initial fabrication of deposit’s microstructure and Vickers hardness.

Two sets of powder blends with different weight percentage ratio for three elemental powder were used during DLD process. Five experiments with different processing parameters were performed to evaluate how microstructure and Vickers hardness change with laser power and laser transverse speed. Energy dispersive X-ray spectroscopy, optical microscopy and Vickers hardness test were used to analyze deposits’ properties.

This paper reveals that significant variance of elemental powder’s size and density would cause lack of weight percentage of certain elements in final part and using multiple coaxial powder nozzles design would be a solution. Also, higher laser power or slower laser transverse speed tend to benefit the formation of finer microstructures and increase Vickers hardness.

This paper demonstrates a new method to fabricate Ti-6Al-4V and gives out a possible weight percentage ratio 87:7:6 for Ti:Al:V at powder blends during DLD process. The relationship between microstructure and Vickers hardness with laser power and laser transverse speed would provide valuable reference for people working on tailoring material properties using elemental powder method.