The purpose of this paper is to investigate the effects of Sn-Ag-x leveling layers on the mechanical properties of SnBi solder joints. Four Sn-Ag-x (Sn-3.0Ag-0.5Cu, Sn-0.3Ag-0.7Cu, Sn-0.3Ag-0.7Cu-0.5 Bi-0.05Ni and Sn-3.0Ag-3.0 Bi-3.0In) leveling layers were coated on Cu pads to prepare SnBi/Sn-Ag-x/Cu solder joints. The microstructure, hardness, shear strength and fracture morphology of solder joints before and after aging were studied.

The interfacial brittleness of the SnBi low-temperature solder joint is a key problem affecting its reliability. The purpose of this study is to improve the mechanical properties of the SnBi solder joint.

Owing to the addition of the leveling layers, the grain size of the ß-Sn phase in the SnBi/Sn-Ag-x/Cu solder joint is significantly larger than that in the SnBi/Cu eutectic solder joint. Meanwhile, the hardness of the solder bulk in the SnBi/Cu solder joint shows a decrease trend because of the addition of the leveling layers. The SnBi/Cu solder joint shows obvious strength drop and interfacial brittle fracture after aging. Through the addition of the Sn-Ag-x layers, the brittle failure caused by aging is effectively suppressed. In addition, the Sn-Ag-x leveling layers improve the shear strength of the SnBi/Cu solder joint after aging. Among them, the SnBi/SACBN/Cu solder joint shows the highest shear strength.

This work suppresses the interfacial brittleness of the SnBi/Cu solder joint after isothermal aging by adding Sn-Ag-x leveling layers on the Cu pads. It provides a way to improve the mechanical performances of the SnBi solder joint.

The purpose of this paper is to comparatively investigate the microstructure and interfacial intermetallic compound (IMC) layer of Cu/SACPG/Ni and Cu/SAC0307/Ni solder joints after thermal aging.

The specimens were thermally aged at 150°C for 0, 24, 168 and 500 h. The microstructure and morphology of the interface IMC layer were observed by means of scanning electron microscope. The IMCs and the solder bump surface were analyzed by EDS. Moreover, the thickness of IMC layer was measured by using the image analysis software.

The morphology of IMC of Cu/SAC0307/Ni solder joint was consistent with that of the Cu/SACPG/Ni joint, which indicates that the addition of P and Ge had little effect on the IMC formation. The needle-like (Cu,Ni)6Sn5 was formed at the interface of solder/Ni solder joints. Meanwhile, the tiny particles inferred as Ag3Sn phase attached to the surface of (Cu,Ni)6Sn5. The growth rate of IMC layer of the Cu/SACPG/Ni joint was smaller than that of Cu/SAC0307/Ni joint with aging time increasing, which means the addition of trace P and Ge can slightly suppress the diffusion rate of the interfacial IMC.

There are no previous studies on the formation mechanism of the IMC layer of SAC0307 solder alloys with P and Ge addition.

The purpose of this paper is to investigate of the effects of Mn nanoparticle addition on the wettability, microstructure and microhardness of SAC0307-xMn(np) (SAC: Sn–Ag–Cu; x = 0, 0.02, 0.05, 0.1 and 0.3 Wt.%) composite solders.

The SAC0307-xMn(np) composite solders were prepared by mechanically mixing different weight percentages of Mn nanopowders into the SAC0307 solder paste with rosin flux. In this study, the wettability of the solders was studied using contact angle and spread ratio methods. Afterward, the microstructure of the solders was investigated using scanning electron microscopy, energy-dispersive X-ray spectroscopy and X-ray diffractometry. Moreover, the microhardness of the solders was studied.

The wetting process of SAC0307-xMn(np) composite solders was found to experience four stages. Adding a small amount of Mn nanoparticles (x = 0.05 Wt.%) could improve the wettability compared to Mn-free solder. Beyond this level, the wettability deteriorated. The addition of Mn nanoparticles significantly refined the size and spacing of Ag₃Sn grains in the solder matrix. When 0.1 Wt.% Mn nanoparticles was added, both the average size of the Ag₃Sn grains and the spacing between the Ag₃Sn grains decreased significantly and approached minimum values. Beyond this amount, the size and spacing between Ag₃Sn grains increased slightly but remained smaller than those in the Mn-free solder matrix. The refined Ag₃Sn grains increased the microhardness of the Mn-containing composite solders by 6-25 per cent, in good agreement with the prediction of the classic theory of dispersion strengthening.

The paper demonstrates that Mn nanoparticle addition could improve the SAC0307-xMn(np) solder wettability and reduce the grain size and spacing between Ag₃Sn grains. The enhancement of the solder microhardness shows good correlation with the microstructure.

This study aims to research properties of Cu/SAC0307 mixed solder balls/Cu joints with different Zn-particles content at low-temperature under ultrasonic assisted.

A new method that 1µm Zn particles and Sn-0.3Ag-0.7 (SAC0307) with a particle size of 25–38 µm were mixed to fill the joint and successfully achieved micro-joining of Cu/Cu under ultrasonic-assisted at low temperature.

The results showed that with a continuous increase in the Zn-particle content, the interfacial intermetallic compounds (IMCs) of the upper and lower interfaces of joints gradually changed from scallop-shaped Cu₆Sn₅ to wavy-shaped Cu₅Zn₈. Moreover, the IMC thickness of the upper/lower interface of joints first decreased and then increased with increasing Zn-particle content. The shear strengths of joints increased with Zn-particle content, the shear strength of joints went to a maximum of 29.76 MPa when the Zn-particle content was 40%, an increase of 62.6% compared to joints without Zn particles. However, as the Zn-particle content continued to increase, the shear strengths of the joints decreased. Additionally, when the Zn content increased to 50%, because the oxidation degree of Zn particles increased, the joints were mainly broken among Zn particles.

A new method that 1µm Zn particles and Sn-0.3Ag-0.7 (SAC0307) with a particle size of 25–38 µm were mixed to fill the Cu/Cu joint at 180°C.

The aim of the present study was to gather and review all the important properties of the Sn–Ag–Cu (SAC) solder alloy. The SAC solder alloy has been proposed as the alternative solder to overcome the environmental concern of lead (Pb) solder. Many researchers have studied the SAC solder alloy and found that the properties such as melting temperature, wettability, microstructure and interfacial, together with mechanical properties, are better for the SAC solder than the tin – lead (SnPb) solders. Meanwhile, addition of various elements and nanoparticles seems to produce enhancement on the prior bulk solder alloy as well. These benefits suggest that the SAC solder alloy could be the next alternative solder for the electronic packaging industry. Although many studies have been conducted for this particular solder alloy, a compilation of all these properties regarding the SAC solder alloy is still not available for a review to say.

Soldering is identified as the metallurgical joining method in electronic packaging industry which uses filler metal, or well known as the solder, with a melting point < 425°C (Yoon et al., 2009; Ervina and Marini, 2012). The SAC solder has been developed by many methods and even alloying it with some elements to enhance its properties (Law et al., 2006; Tsao et al., 2010; Wang et al., 2002; Gain et al., 2011). The development toward miniaturization, meanwhile, requires much smaller solder joints and fine-pitch interconnections for microelectronic packaging in electronic devices which demand better solder joint reliability of SAC solder Although many studies have been done based on the SAC solder, a review based on the important characteristics and the fundamental factor involving the SAC solder is still not sufficient. Henceforth, this paper resolves in stating all its important properties based on the SAC solder including its alloying of elements and nanoparticles addition for further understanding.

Various Pb-free solders have been studied and investigated to overcome the health and environmental concern of the SnPb solder. In terms of the melting temperature, the SAC solder seems to possess a high melting temperature of 227°C than the Pb solder SnPb. Here, the melting temperature of this solder falls within the range of the average reflow temperature in the electronic packaging industry and would not really affect the process of connection. A good amendment here is, this melting temperature can actually be reduced by adding some element such as titanium and zinc. The addition of these elements tends to decrease the melting temperature of the SAC solder alloy to about 3°C. Adding nanoparticles, meanwhile, tend to increase the melting temperature slightly; nonetheless, this increment was not seemed to damage other devices due to the very slight increment and no drastic changes in the solidification temperature. Henceforth, this paper reviews all the properties of the Pb-free SAC solder system by how it is developed from overcoming environmental problem to achieving and sustaining as the viable candidate in the electronic packaging industry. The Pb-free SAC solder can be the alternative to all drawbacks that the traditional SnPb solder possesses and also an upcoming new invention for the future needs. Although many studies have been done in this particular solder, not much information is gathered in a review to give better understanding for SAC solder alloy. In that, this paper reviews and gathers the importance of this SAC solder in the electronic packaging industry and provides information for better knowledge.

This paper resolves in stating of all its important properties based on the SAC solder including its alloying of elements and nanoparticles addition for further understanding.

This study aims to evaluate the effect of thermal aging temperature on the properties of Cu/Cu joints.

A new method that 1 um Zn-particles and Sn-0.3Ag-0.7Cu (SAC0307) with a particle size of 25–38 µm were mixed to fill the joint and successfully achieved the micro-joining of Cu/Cu under ultrasonic-assisted at low-temperature, and then the effect of thermal aging temperature on the properties of Cu/Cu joints was researched.

The composition of the intermetallic compounds (IMCs) on the upper and lower interfaces of Cu/SACZ/Cu joints remained unchanged, which was Cu₅Zn₈ in aging process, and the thickness of the IMCs on the upper and lower interfaces of the Cu/SACZ/Cu joints increased accordingly. Compared with the as-received joints, the thickness of the upper and lower interfaces IMCs of the soldering aged time for 24 h increased by 404.7% and 505.5% at 150ºC, respectively. The IMCs formation tendency and the IMCs growth rate of the lower interface are larger than those of the upper interface because the soldering seam near the IMCs at the upper and lower interfaces of the as-received joints were mostly white SAC0307 balls black Zn-particles, respectively. The growth activation energy of IMCs in the upper and lower interfaces is about 89.21 and 55.11 kJ/mol, respectively. Under the same aging time, with the increase of the aging temperature, the shear strength of Cu/SACZ/Cu joints did not change significantly at first before 150ºC. When the aging temperature reached 150ºC, the shear strength of the joints decreased significantly; the shear strength of the joints was the smallest at 150ºC for 24 h, which was 39.4% lower than that of the as-received joints because the oxidation degree of Zn particles in the joint with the increase of aging temperature and time.

Cu/Cu joints were successfully achieved under ultrasonic-assisted at low-temperature.

Recently nanoparticles reinforced lead free solders are vastly developed in electronics packaging industry. Studies and investigations have been conducted to learn and investigate the types, properties, method, availability and importance of nanoparticles in this field.

Mechanical properties, melting temperature and microstructural conditions are taken into major considerations in any of the preparation on nanoparticles and being reviewed in this paper. Segregation of the types of nanoparticles being added together with their properties is summarized in this paper. High temperature reliability is crucial in providing a good viable solder and hence addition of nanoparticles have been seen to give a positive outcome in this particular property.

This paper reviews on the beneficial of the various nanoparticles addition in the solder. Briefed explanations and the factors are revealed in this review.

This paper reviews on the beneficial of the various nanoparticles addition in the solder.

Low-Ag SAC solder will lead to a series of problems, such as increased the melting range and declined the solderability and so on. These research studies do not have too much impact on the improvement of solders’ performance but were difficult to achieve satisfactory results. It is urgent to develop new soldering technology to avoid the bottleneck of lead-free solder. low-temperature-stirring soldering and ultrasonic-assisted soldering was developed in the authors’ early work, but slag inclusion and pore would gather and grow up to lead decreasing of the shear strength. In this paper, Cu/SAC0307 +Zn power/Cu joints with ultrasonic-assisted at low-temperature was successfully achieved.

45um Zn-powder and SAC0307 No.4 solder powder were mixed to fill the Cu-Cu joint, and the content of Zn-powder were 0 and 5%, 7.5% and 10%, 12.5% and 15% respectively. During the soldering process under ambient atmosphere %252C the heating platform provided a constant 220%253 F and the ultrasonic vibrator applied a constant pressure of 4 MPa to the copper substrate. The soldering process was completed after holding 70 s at 300 W.

The Zn particles made the IMC at the joint interface and in the soldering seam from scallop-type Cu₆Sn₅ to flat-type Cu₅Zn₈. The shear strength of joints without Zn was only 12.43 MPa, the shear strength of joints with 10% Zn reached a peak of 34.25 MPa, and the shear strength of joints containing 10% Zn was 63.71% higher than that of joints without zinc particles, and then the shear strength decreased. In addition, with the increase of zinc content, the fracture mode of the joint changed from the brittle fracture of the original layered tears to the mixed tough and brittle fracture.

A new method that Zn micron-size powders and SAC0307 micron-size powders was mixed to fill the joint, and successfully achieved micro-joining of Cu/Cu under ultrasonic-assisted without flux at low-temperature.

The purpose of this paper is to investigate the wetting behaviors of Sn-5Sb-CuNiAg solders on copper substrates in different soldering processes and the effects of alloying elements on the wettability.

Sn-5Sb-CuNiAg solder balls (750 µm in diameter) were spread and wetted on 40 × 40 × 1 mm copper plates, in different fluxes, soldering temperatures and time. The contact angles were obtained by a home-made measuring instrument. The samples were polished and deep etched before analyzed by scanning electron microscopy. Energy dispersive X-ray spectroscopy was used to identify the composition of the joints.

The effects of different soldering processes and alloying elements on the wetting behaviors of Sn-5Sb-CuNiAg solders on copper substrates were calculated and expounded. The rosin-based flux could effectively remove oxidation layers and improve the wettability of Sn-5Sb-CuNiAg solders. Then with the increase of soldering temperature and time, the contact angles decreased gradually. The soldering processes suited for Sn-5Sb-CuNiAg solders were RMA218, 280°C and 30 s. Considered the effects of alloying elements, the wettability of Sn-5Sb-0.5Cu-0.1Ni-0.5Ag was relatively favorable on copper substrates. Besides, Ni could accumulate at the solder/Cu interface and form a jagged (Cu,Ni)6Sn5 IMC.

This work was carried out with our handmade experiment equipment and the production of the quinary lead-free solder alloy used in wetting tests belongs to us. The investigated Sn-5Sb-CuNiAg alloys exhibited higher melting point and preferable wettability, that was one of the candidates for high-temperature lead-free solders to replace high-Pb solders, and applied extremely to high temperature and frequency working environments of the third-generation semiconductors components, with a greater potential research and development value.

This study aims to study the mechanical, photoelectric, and thermal reliability of SAC307 solder joints with Ni-decorated MWCNTs for flip-chip light-emitting diode (LED) package component during aging. By adding nanoparticles (Ni-multi-walled carbon nanotubes [MWCNTs]) to the solder paste, the shear strength and fatigue resistance of the brazed joint can be improved. However, the aging properties of Ni-modified MWCNTs composite solder joints have not been deeply studied. In this research, the mechanical, photoelectric and thermal reliability of SAC307 packaged flip-chip LEDs with Ni-MWCNTs added during aging were studied.

Compared with SAC solder alloys, the effects of different contents (0, 0.05, 0.1 and 0.2 Wt.%) of Ni-MWCNTs on the photoelectric and thermal properties of composite solder joints were examined. To study the aging characteristics of composite solder joints, the solder joints were aged at 85°C/85% relative humidity.

The addition of an appropriate amount of reinforcing agent Ni-MWCNTs reduces the density of the composite solder to 96% of the theoretical value of the SAC solder alloy. In addition, the microhardness increases and the wetting angle decreases. Two different phase compositions were observed in the solder joints with Ni-MWCNTs reinforcement: Cu₃Sn and (Cu, Ni)₆Sn₅. The solder joints of SAC307-0.1Ni-MWCNTs exhibit the highest luminous flux and luminous efficiency of flip-chip LED filaments, the lowest steady-state voltage and junction temperature. And with the extension of the aging time, its aging stability is the best. In short, when the addition amount of Ni-MWCNTs is 0.1 Wt.%, the solder joints exhibit the best wettability and the thinnest intermetallic compound layer. And the shear strength of the tested solder joints is the best, and the void ratio is the lowest. At this time, the enhancement effect of Ni-MWCNTs on the composite solder has been best demonstrated.

The content range of enhancer Ni-MWCNTs needs to be further reduced.

The authors have improved the performance of Ni-modified MWCNTs composite solder joints.

Composite solder with high performance has great practical application significance for improving the reliability and life of the whole device.