1 – 10 of 23Saima Habib, Farzana Kishwar and Zulfiqar Ali Raza
The purpose of this study is to apply silver nanoparticles on the cellulosic fabric via a green cross-linking approach to obtain antibacterial textiles. The cellulosic fabrics may…
Abstract
Purpose
The purpose of this study is to apply silver nanoparticles on the cellulosic fabric via a green cross-linking approach to obtain antibacterial textiles. The cellulosic fabrics may provide an ideal enclave for microbial growth due to their biodegradable nature and retention of certain nutrients and moisture usually required for microbial colonization. The application of antibacterial finish on the textile surfaces is usually done via synthetic cross-linkers, which, however, may cause toxic effects and halt the biodegradation process.
Design/methodology/approach
Herein, we incorporated citrate moieties on the cellulosic fabric as eco-friendly crosslinkers for the durable and effective application of nanosilver finish. The nanosilver finish was then applied on the citrate-treated cellulosic fabric under the pad-dry-cure method and characterized the specimens for physicochemical, textile and antibacterial properties.
Findings
The results expressed that the as-prepared silver particles possessed spherical morphology with their average size in the nano range and zeta potential being −40 ± 5 mV. The results of advanced analytical characterization demonstrated the successful application of nanosilver on the cellulosic surface with appropriate dispersibility.
Practical implications
The nanosilver-treated fabric exhibited appropriate textile and comfort and durable broad-spectrum antibacterial activity.
Originality/value
The treated cellulosic fabric expressed that the cross-linking, crystalline behavior, surface chemistry, roughness and amphiphilicity could affect some of its comfort and textile properties yet be in the acceptable range for potential applications in medical textiles and environmental sectors.
Details
Keywords
Zhao Yuhang, Zhicai Yu, Hualing He and Huizhen Ke
This study aims to fabricate a multifunctional electromagnetic interference (EMI) shielding composite fabric with simultaneous high-efficiency photothermal conversion and Joule…
Abstract
Purpose
This study aims to fabricate a multifunctional electromagnetic interference (EMI) shielding composite fabric with simultaneous high-efficiency photothermal conversion and Joule heating performances.
Design/methodology/approach
A multifunctional polypyrrole (PPy) hydrogel/multiwalled carbon nanotube (MWCNT)/cotton EMI shielding composite fabric (hereafter denoted as PHMC) was prepared by loading MWCNT onto tannin-treated cotton fabric, followed by in situ crosslinking-polymerization to synthesize three-dimensional (3D) conductive networked PPy hydrogel on the surface of MWCNT-coated cotton fabric.
Findings
Benefiting from the unique interconnected 3D networked conductive structure of PPy hydrogel, the obtained PHMC exhibited a high EMI-shielding effectiveness vale of 48 dB (the absorbing electromagnetic wave accounted for 84%) within a large frequency range (8.2–12.4 GHz). Moreover, the temperature of the laminated fabric reached 54°C within 900 s under 15 V, and it required more than 100 s to return to room temperature (28.7°C). When the light intensity was adjusted to 150 mW/cm2, the PHMC temperature was about 38.2°C after lighting for 900 s, indicating high-efficiency electro-photothermal effect function.
Originality/value
This paper provides a novel strategy for designing a type of multifunctional EMI shielding composite fabric with great promise for wearable smart garments, EMI shielding and personal heating applications.
Details
Keywords
Hoda Sabry Sabry Othman, Salwa H. El-Sabbagh and Galal A. Nawwar
This study aims to investigate the behavior of the green biomass-derived copper (lignin/silica/fatty acids) complex, copper lignin/silica/fatty acids (Cu-LSF) complex, when…
Abstract
Purpose
This study aims to investigate the behavior of the green biomass-derived copper (lignin/silica/fatty acids) complex, copper lignin/silica/fatty acids (Cu-LSF) complex, when incorporated into the nonpolar ethylene propylene diene (EPDFM) rubber matrix, focusing on its reinforcing and antioxidant effect on the resulting EPDM composites.
Design/methodology/approach
The structure of the prepared EPDM composites was confirmed by Fourier-transform infrared spectroscopy, and the dispersion of the additive fillers and antioxidants in the EPDM matrix was investigated using scanning electron microscopy. Also, the rheometric characteristics, mechanical properties, swelling behavior and thermal gravimetric analysis of all the prepared EPDM composites were explored as well.
Findings
Results revealed that the Cu-LSF complex dispersed well in the nonpolar EPDM rubber matrix, in thepresence of coupling system, with enhanced Cu-LSF-rubber interactions and increased cross-linking density, which reflected on the improved rheological and mechanical properties of the resulting EPDM composites. From the various investigations performed in the current study, the authors can suggest 7–11 phr is the optimal effective concentration of Cu-LSF complex loading. Interestingly, EPDM composites containing Cu-LSF complex showed better antiaging performance, thermal stability and fluid resistance, when compared with those containing the commercial antioxidants (2,2,4-trimethyl-1,2-dihydroquinoline and N-isopropyl-N’-phenyl-p-phenylenediamine). These findings are in good agreement with our previous study on polar nitrile butadiene rubber.
Originality/value
The current study suggests the green biomass-derived Cu-LSF complex to be a promising low-cost and environmentally safe alternative filler and antioxidant to the hazardous commercial ones.
Details
Keywords
Self-crosslinked long fluorocarbon acrylate polymer latex has good hydrophobic and oleophobicity, weather resistance, aging resistance, stability and other excellent properties…
Abstract
Purpose
Self-crosslinked long fluorocarbon acrylate polymer latex has good hydrophobic and oleophobicity, weather resistance, aging resistance, stability and other excellent properties, which make the polymer be widely used in coatings, dyes, adhesives and other products. The purpose of this study is to prepare self-crosslinked long fluorocarbon acrylate polymer latex via semi-continuous seeded emulsion technology and carry out comparative study on two different cross-linked monomers.
Design/methodology/approach
Methyl methacrylate (MMA) and butyl acrylate (BA) were used as the main monomers, dodecafluoroheptyl methacrylate (DFMA) as the fluoromonomer, hydroxypropyl methacrylate (HPMA) and N-methylol acrylamide (NMA) as cross-linked monomers, and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether (ANPEO10) and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) as compound emulsifiers via the semicontinuous-seeded emulsion polymerization.
Findings
The properties of the polymer emulsions, which are prepared with two different cross-linked monomers, are compared and discussed, and it is concluded that HPMA is more suitable for the preparation of self-crosslinked polymer emulsions. The formula of the polymer latex is ANPEO10: DNS-86 = 1:1, and the mass ratio of the monomers used in the polymer is MMA: BA: DFMA: HPMA = 14.40:14.40:0.60:0.60.
Practical implications
Self-crosslinked long fluorocarbon acrylate polymer latex can be used in many fields such as coatings, dyes, adhesives and other products.
Originality/value
The self-crosslinked long fluorocarbon acrylate polymer latex is prepared by mixing the nonionic emulsifier ANPEO10 and the anionic emulsifier DNS-86 when potassium persulfate is used as the thermal decomposition initiator and the semicontinuous-seeded emulsion technology is adopted and the comparative study on two different cross-linked monomer is carried out, which is not reported in the open literatures.
Details
Keywords
Khaled F. El-Nemr, H. Radi and Reham H. Helal
One of the low-cost minerals that can be used as reinforcing filler in polymer industry is pumice powder. Pumice is a highly porous volcanic glass formed during explosive…
Abstract
Purpose
One of the low-cost minerals that can be used as reinforcing filler in polymer industry is pumice powder. Pumice is a highly porous volcanic glass formed during explosive eruptions. This pumice has received significant interest because of its large surface area with various polar groups and can be processed easily.
Design/methodology/approach
This study is carried out to investigate the effect of partial replacement of silica (as traditional filler) by naturally occurring pumice powder to improve the thermal and mechanical properties of nitrile butadiene rubber cured with electron beam radiation (doses from 25 to 150 kGy).
Findings
The results indicated that the addition of pumice powder increase the tensile strength at lower doses up to 75 kGy (especially at concentration of 5 phr). Besides, an improvement in the thermal stability was attained with the addition of pumice powder.
Originality/value
Pumice powder is volcanic-based alumina and silica which is mainly composed of SiO2. It has porous structure which is formed by dissolved gases precipitated during the cooling as the lava hurtles through air. Due to its porous structure, it has low density and high thermal insulation. It also has high temperature and chemical resistance, for these reasons it became preferable material to be used as filler in the plastic and rubber industry.
Details
Keywords
Amirul Syafiq, Nasrudin Abd. Rahim, Vengadaesvaran Balakrishnan and A.K. Pandey
This paper introduced the simple synthesis process of self-cleaning coating with fog-resistance property using hydrophobic polydimethylsiloxane (PDMS) polymer and nano-calcium…
Abstract
Purpose
This paper introduced the simple synthesis process of self-cleaning coating with fog-resistance property using hydrophobic polydimethylsiloxane (PDMS) polymer and nano-calcium carbonate (nano-CaCO3) and titanium dioxide (TiO2).
Design/methodology/approach
The synthesis method of PDMS/nano-CaCO3-TiO2 is based on sol-gel process. The crosslinking between PDMS and nanoparticles is driven by the covalent bond at temperature of 50°C. The 3-Aminopropyltriethoxysilane is used as binder for nanoparticles attachment in polymer matrix. Two fabrication methods are used, which are dip- and spray-coating methods.
Findings
The prepared coated glass fulfilled the requirement of standard self-cleaning and fog-resistance performance. For the self-cleaning test BS EN 1096-5:2016, the coated glasses exhibited the dust haze value around 20%–25% at tilt angle of 10°. For the antifog test, the coated glasses showed the fog haze value were below 2% and the gloss value were above 85%. The obtained results completely achieved the standard antifog value ASTM F659-06 protocol.
Research limitations/implications
Findings will provide an infrastructure support for the building glass to enhance building’s energy efficiency, cleaning performance and friendly environment.
Practical implications
This study proposed the simple synthesis method using hydrophobic polymer and nano-CaCO3 and nano-TiO2, which can achieve optimum self-cleaning property at low tilt angle and fog-resistance performance for building glass.
Social implications
The research findings have high potential for building company, cleaning building company and government sector. The proposed project capable to reduces the energy consumption about 20% per annum due to labor cost, time-consuming and safety during manual cleaning.
Originality/value
The novel method to develop self-cleaning coating with fog-resistance using simple synthesis process and fabrication method for building glass application.
Details
Keywords
Suyun Liu, Hu Liu, Ningning Shao, Zhijun Dong, Rui Liu, Li Liu and Fuhui Wang
Polyaniline (PANI) has garnered attention for its potential applications in anticorrosion fields because of its unique properties. Satisfactory outcomes have been achieved when…
Abstract
Purpose
Polyaniline (PANI) has garnered attention for its potential applications in anticorrosion fields because of its unique properties. Satisfactory outcomes have been achieved when using PANI as a functional filler in organic coatings. More recently, research has extensively explored PANI-based organic coatings with self-healing properties. The purpose of this paper is to provide a summary of the active agents, methods and mechanisms involved in the self-healing of organic coatings.
Design/methodology/approach
This study uses specific doped acids and metal corrosion inhibitors as active and self-healing agents to modify PANI using the methods of oxidation polymerization, template synthesis, nanosheet carrier and nanocontainer loading methods. The anticorrosion performance of the coatings is evaluated using EIS, LEIS and salt spray tests.
Findings
Specific doped acids and metal corrosion inhibitors are used as active agents to modify PANI and confer self-healing properties to the coatings. The coatings’ active protection mechanism encompasses PANI’s own passivation ability, the adsorption of active agents and the creation of insoluble compounds or complexes.
Originality/value
This paper summarizes the active agents used to modify PANI, the procedures used for modification and the self-healing mechanism of the composite coatings. It also proposes future directions for developing PANI organic coatings with self-healing capabilities. The summaries and proposals presented may facilitate large-scale production of the PANI organic coatings, which exhibit outstanding anticorrosion competence and self-healing properties.
Details
Keywords
Amirul Syafiq, Vengadaesvaran Balakrishnan and Nasrudin Abd. Rahim
This paper aims to design the nano-titanium dioxide (TiO2) coating system which has superhydrophilic property, self-cleaning mechanism and antifog property as well as strong…
Abstract
Purpose
This paper aims to design the nano-titanium dioxide (TiO2) coating system which has superhydrophilic property, self-cleaning mechanism and antifog property as well as strong adhesion on glass substrate.
Design/methodology/approach
Two hydrophilic materials have been used such as TiO2 nanoparticles as fillers and hydrophilic copolymer, Pluronic F-127 by using simple sol–gel approach. The prepared solution was applied onto glass through dip- and spray-coating techniques and then left for drying at ambient temperature.
Findings
The nano-TiO2 superhydrophilic coating has achieved the water contact angle of 4.9° ± 0.5°. The superhydrophilic coating showed great self-cleaning effect against concentrated syrup and methylene blue where thin layer of water washes the dirt contaminants away. The nano-TiO2 coating exhibits great antifog performance that maintains high transparency of around 89% when the coated glass is placed above hot-fog vapor for 10 min. The fog droplets were condensed into water film which allowed the transmission of light through the glass. The strong adhesion of coated glass shows no total failure at scratch profile when impacted with scratch load of 500, 800 and 1,200 mN.
Research limitations/implications
Findings will be useful in the development of self-cleaning superhydrophilic coating that is applicable on building glass and photovoltaic panel.
Practical implications
The developed nano-TiO2 coating is developed by the combination of hydrophilic organic copolymer–inorganic TiO2 network to achieve great superhydrophilic property, optimum self-cleaning ability and supreme antifog performance.
Social implications
The findings will be useful for residents in building glass window where the application will reduce dust accumulation and keep the glass clean for longer period.
Originality/value
The synthesis of nano-TiO2 superhydrophilic coating which can be sprayed on large glass panel and cured at ambient temperature.
Details
Keywords
Yuting Lu, Wanwan Fu, hao Ren, Shifang Wu, Jiesheng Liu and Hao Peng
The purpose of this paper is to develop a high-performance composite emulsion cement waterproof coating. The coating has excellent durability and is effective in protecting cement…
Abstract
Purpose
The purpose of this paper is to develop a high-performance composite emulsion cement waterproof coating. The coating has excellent durability and is effective in protecting cement mortar substrates from harmful ions.
Design/methodology/approach
The polymer cement waterproof coatings with different emulsion compounding ratios were tested for mechanical properties and water resistance after alkali immersion, water immersion, thermal aging and UV aging, and the coatings were analyzed by infrared spectroscopy after aging to evaluate its durability. Meanwhile, the coating that presents favorable durability was applied to cement mortar test blocks. The protective effect of the coating on the test blocks was tested by immersion method, and X-ray diffraction analysis was performed on the eroded test blocks.
Findings
The coating with neoprene latex/acrylate latex weight ratio of 90/10 presents favorable durability and has superior overall performance. Besides, when it is applied to cement mortar blocks, the coatings effectively reduced the erosive effect of harmful ions on cement mortar blocks, resulting in much lower mass change ratios and less internal structural damage of the blocks significantly.
Originality/value
The obtained coating will be of great application potential for use in building waterproofing construction. Moreover, the coating can practically prevent chloride ions and sulfate ions from penetrating cement-based materials.
Details
Keywords
Kimia Abedi, Hamid Keshvari and Mehran Solati-Hashjin
This study aims to develop a simplified bioink preparation method that can be applied to most hydrogel bioinks used in extrusion-based techniques.
Abstract
Purpose
This study aims to develop a simplified bioink preparation method that can be applied to most hydrogel bioinks used in extrusion-based techniques.
Design/methodology/approach
The parameters of the bioprinting process significantly affect the printability of the bioink and the viability of cells. In turn, the bioink formulation and its physicochemical properties may influence the appropriate range of printing parameters. In extrusion-based bioprinting, the rheology of the bioink affects the printing pressure, cell survival and structural integrity. Three concentrations of alginate-gelatin hydrogel were prepared and printed at three different flow rates and nozzle gauges to investigate the print parameters. Other characterizations were performed to evaluate the hydrogel structure, printability, gelation time, swelling and degradation rates of the bioink and cell viability. An experimental design was used to determine optimal parameters. The analyses included live/dead assays, rheological measurements, swelling and degradation.
Findings
The experimental design results showed that the hydrogel flow rate substantially influenced printing accuracy and pressure. The best hydrogel flow rate in this study was 10 ml/h with a nozzle gauge of 18% and 4% alginate. Three different concentrations of alginate-gelatin hydrogels were found to exhibit shear-thinning behavior during printing. After seven days, 46% of the structure in the 4% alginate-5% gelatin sample remained intact. After printing, the viability of skin fibroblast cells for the optimized sample was 91%.
Originality/value
This methodology offers a straightforward bioink preparation method applicable to the majority of hydrogels used in extrusion-based procedures. This can also be considered a prerequisite for cell printing.