Search results

Fluorinated silicon polymers are expected to be adopted in specific coatings to afford outstanding advantages, such as high chemical and photochemical resistance, low surface tension and low refractive index. The modified acrylate resin is prepared via solution polymerization of fluorine and silicon monomers, acrylate monomers and other functional monomers. The purpose of this paper is that the fluorine and silicon monomers such as vinyltriethoxysilane (VTES) and hexafluorobutyl methacrylate (HFMA) and some cheap monomers such as styrene are used to prepare the cationic acrylic resin.

The fluorine and silicon modified cationic acrylic resin is prepared via solution polymerization technology, which uses butyl acrylate (BA), methyl methacrylate (MMA), styrene (St), HFMA, VTES, dimethylaminoethyl methacrylate (DMAEMA) and hydroxypropyl methacrylate (HPMA) as the co-polymerized monomers, propylene glycol monomethyl ether (PGME) as solvent and 2,2-Azo-bis-iso-butyronitrile (AIBN) as the initiator to create a resin to introduce the Si–O and C–F into the polymer chains. The cathodic electrodeposition (CED) coatings were prepared by mixing the synthetic resin and blocked isocyanate.

The influence of the amounts of HFMA and VETS on the resin and the resultant CED coatings is investigated in detail. The optimum amounts of HFMA and VETS are obtained, which is 7–8% and 4–5%, respectively. The hydrophobicity and the acid and alkaline resistance of the film are improved when VETS and HFMA are introduced to co-polymerize with other monomers.

The fluorine and silicon monomers such as VTES and HFMA and some cheap monomers such as styrene, which are used to prepare the cationic acrylic resin, are seldom reported in the open literature.

Silane cross-linkers have been used to strengthen the mechanical stabilities and friction resistance of plastic products. Therefore, the effect of silane cross-linkers on latex has been studied through preparing modified self-cross-linking long fluorocarbon polyacrylate latex. In this paper, nonionic surfactant alcohol ether glycoside (AEG1000) and anionic polymerizable surfactant 1-allyloxy-3-(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) acted as mixed emulsifier and 3-(methacryloyloxy) propyltrimethoxysilane (KH-570) and bis (2-ethylhexyl) maleate (DOM) were used as functional monomers.

The modified acrylate polymer latex was synthesized through the semi-continuous seeded emulsion polymerization with methyl methacrylate (MMA), butyl acrylate (BA), dodecafluoroheptyl methacrylate (DFMA) and hydroxypropyl methacrylate (HPMA) as main monomers. Potassium persulfate (KPS) was applied to initiate polymerization reaction, nonionic surfactant AEG1000 and DNS-86 acted as emulsifier, KH-570 and DOM were used as functional monomers, respectively.

The optimum conditions of synthesizing the modified latex were the following. The mass ratio of monomers containing MMA, BA, DFMA, HPMA, KH-570 and DOM was 13.58:13.58:0.90:1.20:0.15:0.60, the usage of initiator KPS was 0.5% of the total weight of monomers and the amount of emulsifier was 7% of all monomers with AEG1000:DNS-86 = 1:1. The results indicated that the conversion of monomer was 99% and the coagulation was about 2.0%.

The resultant latex was modified silane cross-linker KH-570 and DOM, which positively affected the comprehensive properties of latex and its film. Apart from this, the novel mixed emulsifier was used to improve the size and distribution of latex particles and reduce environmental problems caused by the use of emulsifiers.

Fluorine materials have received the keen attention of many researchers because of their water repellency and low surface free energy. The purpose of this paper is to prepare self-crosslinking fluorocarbon polyacrylate latexes containing different fluorocarbon chain lengths by semi-continuous seeded emulsion polymerization technology.

Methyl methacrylate (MMA), butyl acrylate (BA), hydroxypropyl methacrylate (HPMA) and fluorine-containing monomers were used as main monomers. The fluorine-containing monomers included hexafluorobutyl methacrylate (HFMA), dodecafluoroheptyl methacrylate (DFMA) and trifluorooctyl methacrylate (TFMA). Potassium persulfate (KPS) was used as thermal decomposition initiator, non-ionic surfactant alkyl alcohol polyoxyethylene (25) ether (DNS-2500) and anionic surfactant sodium dodecylbenzene sulfonate (SDBS) as mixed emulsifier.

Through optimizing the reaction conditions, the uniform and stable latex is gained. The polymer of structure was characterized by Fourier transform infrared spectroscopy (FTIR). Thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and contact angle (CA) were tested on latex films. The particle size and distribution range of emulsion were tested with nano particle size analyzer. After comprehensively comparing the latexes and films prepared by HFMA, DFMA and TFMA, the performance of DFMA monomer modified is better.

The self-crosslinking acrylic emulsion is prepared via semi-continuous seeded emulsion polymerization, which methyl methacrylate (MMA), butyl acrylate (BA), hydroxypropyl methacrylate (HPMA) and fluorine-containing monomers were used as main monomers. The fluorine-containing monomers were composed of hexafluorobutyl methacrylate (HFMA), dodecafluoroheptyl methacrylate (DFMA) and trifluorooctyl methacrylate (TFMA). Potassium persulfate (KPS) was used as thermal decomposition initiator, non-ionic surfactant alkyl alcohol polyoxyethylene (25) ether (DNS-2500) and anionic surfactant sodium dodecylbenzene sulfonate (SDBS) as mixed emulsifier. There are two main innovations. One is that the self-crosslinking acrylic emulsion is prepared successfully. The other is that the effects of monomers containing different fluorocarbon chain lengths on polyacrylate, such as monomer conversion rate, coagulation rate, mechanical stability, chemical stability, emulsion particle size and storage stability, are studied in detail.

Self-crosslinked long fluorocarbon acrylate polymer latex has good hydrophobic and oleophobicity, weather resistance, aging resistance, stability and other excellent properties, which make the polymer be widely used in coatings, dyes, adhesives and other products. The purpose of this study is to prepare self-crosslinked long fluorocarbon acrylate polymer latex via semi-continuous seeded emulsion technology and carry out comparative study on two different cross-linked monomers.

Methyl methacrylate (MMA) and butyl acrylate (BA) were used as the main monomers, dodecafluoroheptyl methacrylate (DFMA) as the fluoromonomer, hydroxypropyl methacrylate (HPMA) and N-methylol acrylamide (NMA) as cross-linked monomers, and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether (ANPEO10) and 1-allyloxy-3–(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) as compound emulsifiers via the semicontinuous-seeded emulsion polymerization.

The properties of the polymer emulsions, which are prepared with two different cross-linked monomers, are compared and discussed, and it is concluded that HPMA is more suitable for the preparation of self-crosslinked polymer emulsions. The formula of the polymer latex is ANPEO10: DNS-86 = 1:1, and the mass ratio of the monomers used in the polymer is MMA: BA: DFMA: HPMA = 14.40:14.40:0.60:0.60.

Self-crosslinked long fluorocarbon acrylate polymer latex can be used in many fields such as coatings, dyes, adhesives and other products.

The self-crosslinked long fluorocarbon acrylate polymer latex is prepared by mixing the nonionic emulsifier ANPEO10 and the anionic emulsifier DNS-86 when potassium persulfate is used as the thermal decomposition initiator and the semicontinuous-seeded emulsion technology is adopted and the comparative study on two different cross-linked monomer is carried out, which is not reported in the open literatures.

This study aims to extend the pot life without altering the qualities and performance of the coating, which is important to increase when manufacturing polyurethane coatings.

An acrylic polyol from a mixture of different monomers of hydroxypropyl methacrylate, methacrylic acid, 2-ethylhexyl acrylate, methyl methacrylate and n-butyl methacrylate was prepared with different ratios of 2,4-pentanedione as a pot life extender. The reaction takes place in presence of di-tert-butyl peroxide as initiator with samples (T1–T7). The physical properties of prepared acrylic polyol were characterized. Then, coating polyurethane varnish was prepared from the prepared acrylic polyol with an aliphatic polyisocyanate in a 1:1 equivalent ratio of OH:NCO at room temperature, in presence of paint thinner (diluents/solvent) and dibutyltin dilaurate as a catalyst to give samples (T1C–T7C). This coating was evaluated via Fourier-transform infrared spectroscopy, drying time, hardness and gloss, distinctness of image and reflected image quality.

The coating has a prolonged pot life while still maintaining the other qualities, thanks to the greater 2,4-pentanedione content.

It is desired to have a paint which has a satisfactory pot life, short curing time and reduces many drawbacks such as inefficient working and deterioration of the paint before application.

BP Chemicals has issued a technical note giving data on the latest, improved grade of Bisomer HPMA (2‐hydroxypropyl methacrylate).

In this work, the authors used reversible addition-fragmentation transfer (RAFT) polymerization to develop a new cationic acrylate modified epoxy resin emulsion for water-borne inkjet which have the advantages of both polyacrylate and epoxy resin. The emulsion was successfully used in the canvas coating for inkjet printing. This paper aims to contribute to the development of novel cationic emulsions for inkjet printing industry.

In this work, the epoxy acrylate was synthesized from RAFT agent and epoxy resin firstly. Cationic macromolecular emulsifier was prepared by RAFT polymerization, using 2,2’-Azobisisobutyronitrile as initiator, 2-(dimethylamino)ethyl methacrylate and styrene as monomer, which was directly used to prepare the emulsion. The influences of the amount of 2-(dimethylamino)ethyl methacrylate on particle size, zeta potential and water contact angle were studied. Finally, the cationic emulsion was used to print images by inkjet printing.

The emulsion has the smallest particle size, the highest potential and the highest water contact angle when the DM content is 13 Wt.%. The transmission electron microscopy analysis reveals the latex particles is core-shell sphere with the diameters in the range 120–200 nm. The emulsion was successfully used in the canvas coating for inkjet printing. This work will contribute to the development of novel cationic emulsions for inkjet printing industry.

The emulsion was successfully used in the canvas coating for inkjet printing. This work will contribute to the development of novel cationic emulsions for inkjet printing industry.

This paper aims to disclose the evolution of pendulum hardness of two-component acrylic polyurethane coatings during the cure process and attempts to describe the quantitative relationship between pendulum hardness and curing time. These findings are helpful for the study of fast curing acrylic polyurethane coatings.

The pendulum hardness method was used to monitor the hardness of two-component acrylic polyurethane coatings during curing. The quantitative relationship between pendulum hardness and curing time can be obtained with Avrami equation.

The evolution of coating pendulum hardness can be divided into three stages. By using the Avrami equation that explained the influence of both the acid value and the curing temperature on the drying speed of hydroxyl acrylic resin, the evolution of coating pendulum hardness during curing can also be accurately described.

It should be noted that the physical meaning of the Avrami exponent, n, is not yet clear.

The results are of great significance for the development of fast-curing hydroxyl-functional acrylic resins, with the potential to improve the drying speed of the coatings used in automotive refinish.

It is novel to divide the pendulum hardness into three stages, and, for the first time, the Avrami equation is utilized to describe the evolution of coating pendulum hardness during curing.

NL Chemicals/NL Industries Inc announce the acquisition of Victor Wolf Industries Ltd, the UK based producer of polyamide resins, plastics additives, and other speciality chemicals.