Denim fabric has become a wardrobe staple due to its versatility to be worn in a variety of fashions. This paper aims to study denim fabrics to understand their unique hand by developing a hand evaluation system using computational method. Also, the effect of various washes was studied on the hand and surface morphology of denim fabrics.

Five different denim samples were manufactured with various washing treatments. The Kawabata Evaluation System was used to measure the low stress mechanical properties. Computation method was used to develop hand equations using multiple regression technique in the MS Excel software. The correlation coefficient analysis was done to determine the authenticity of the developed equations. Five primary hand attributes such as softness, smoothness, fullness, flexibility and stretchability were shortlisted by a panel of judges that influence the fabric handle.

The correlation coefficient between subjective and computational total hand values with thermal properties and without thermal properties was 0.88 and 0.85, respectively. The enzymatic wash fabric has the highest total hand value followed by the acid, bleach and stone-washed fabrics.

Although the hand evaluation system is available for conventional textiles like suiting and shirting fabrics, the method to predict fabric hand of non-conventional textiles such as denim fabrics remains an unexplored topic. The stresses acting on denim fabrics are completely different. Therefore, to the best of the author’s knowledge, a novel attempt has been made in this research work to develop a computational model to predict the total hand value of denim fabrics.

This study aims to investigate the effect of the copresence of ferrous (Fe²⁺) ions and sodium dodecyl sulfate (SDS) on the activity of an amylase enzyme during the desizing of greige viscose fabric for potential industrial applications. The removal of starches is an essential step before processing the fabric for dyeing and finishing operations. The authors tend to accomplish it in eco-friendly and sustainable ways.

The experiments were designed under the Taguchi approach, and the results were analyzed using grey relational analysis to optimize the process. The textile properties of absorbency, reducing sugars, bending length, weight loss, Tegawa rating and tensile strength were assessed using the standard protocols. The control and optimized viscose specimens were investigated for certain surface chemical properties using advanced analytical techniques including scanning electron microscopy (SEM), X-ray diffraction (XRD) and thermal gravimetric analysis (TGA).

The results demonstrate that the Fe²⁺ concentration and process time were the main influencing factors in the amylolytic desizing of viscose fabric. The optimized process conditions were found to be 0.1 mm Fe²⁺ ions, 3 mm SDS, 80°C, 7 pH and 30 min process time. The copresence of Fe²⁺ ions and SDS promoted the biodesizing of viscose fabric. The SEM, Fourier transform infrared spectroscopy, XRD and TGA results demonstrated that the sizing agent has efficiently been removed from the fabric surface.

The amylase desizing of viscose fabric in the presence of certain metal ions and surfactants is a significant subject as the enzyme may face them due to their prevalence in the water systems. This could also support the biodesizing and bioscouring operations to be done in one bath, thus making the textile pretreatment process both economical and environmentally sustainable.

The authors found no report on the biodesizing of viscose fabric in the copresence of Fe²⁺ ions and the SDS surfactant under statistical multiresponse optimization. The biodesized viscose fabric has been investigated using both conventional and analytical approaches.

The purpose of this study is to detect the effect of some natural cellulosic polymers in their nano forms with the addition of zinc oxide nanoparticles on restoring the lost mechanical strength of degraded papyrus without any harmful effects on the inks.

In the current study, the USB digital microscopy, scanning electron microscope, measurement of mechanical properties (tensile and elongation), pH measurement, color change and infrared spectroscopy were undertaken for the samples before and after treatment and aging.

In the current study, the USB digital microscopy, scanning electron microscope, measurement of mechanical properties (tensile and elongation), pH measurement, color change and infrared spectroscopy were undertaken for the samples before and after treatment and aging.

The effect of strengthening materials was studied on cellulose and carbon ink, which makes this study closer to reality as the manuscript is the consistent structure of cellulose and inks, whereas most of the literature stated the impact of consolidation materials on the strengthening the cellulosic supports without attention to their impact on inks.

The aim of this paper is to study the effect of laser shock peening (LSP) on mechanical behaviour of the laser-directed energy deposition (LDED)-based printed 15-5 PH stainless steel with U and V notches. The study specifically concentrates on the evaluation of effect of scan strategy, machining and LSP processing on microstructural, texture evolution and fatigue behaviour of LDED-printed 15-5 PH steel.

For LSP treatment, 15-5 PH steel was printed using LDED process with bidirectional scanning strategy (XX [θ = 0°) and XY [θ = 90°]) at optimised laser power of 600 W with a scanning speed of 300 mm/min and a powder feed rate of 3 g/min. Furthermore, LSP treatment was conducted on the V- and U-notched fatigue specimens extracted from LDED-built samples at laser energy of 3.5 J with a pulse width of 10 ns using laser spot diameter of 3 mm. Post to the LSP treatment, the surface roughness, fatigue life assessment and microstructural evolution analysis is performed. For this, different advanced characterisation techniques are used, such as scanning electron microscopy attached with electron backscatter diffraction for microstructure and texture, X-ray diffraction for residual stress (RS) and structure information, Vicker’s hardness tester for microhardness and universal testing machine for low-cycle fatigue.

It is observed that both scanning strategies during the LDED printing of 15-5 PH steel and laser peening have played significant role in fatigue life. Specimens with the XY printing strategy shows higher fatigue life as compared to XX with both U- and V-notched conditions. Furthermore, machining and LSP treatment led to a significant improvement of fatigue life for both scanning strategies with U and V notches. The extent of increase in fatigue life for both XX and XY scanning strategy with V notch is found to be higher than U notch after LSP treatment, though without LSP samples with U notch have a higher fatigue life. As fabricated sample is found to have the lowest fatigue life as compared to machines and laser peened with both scan strategies.

This study presents an innovative method to improve the fatigue life of 15-5 PH stainless steel by changing the microstructure, texture and RS with the adoption of a suitable scanning strategy, machining and LSP treatment as post-processing. The combination of preferred microstructure and compressive RS in LDED-printed 15-5 PH stainless steel achieved with a synergy between microstructure and RS, which is responsible to improve the fatigue life. This can be adopted for the futuristic application of LDED-printed 15-5 PH stainless steel for different applications in aerospace and other industries.

The incompatibility of natural fibers with polymer matrices is one of the key obstacles restricting their use in polymer composites. The interfacial connection between the fibers and the matrix was weak resulting in a lack of mechanical properties in the composites. Chemical treatments are often used to change the surface features of plant fibers, yet these treatments have significant drawbacks such as using substantial amounts of liquid and chemicals. Plasma modification has recently become very popular as a viable option as it is easy, dry, ecologically friendly, time-saving and reduces energy consumption. This paper aims to explore plasma treatment for improving the surface adhesion characteristics of sisal fibers (SFs) without compromising the mechanical attributes of the fiber.

A cold glow discharge plasma (CGDP) modification using N₂ gas at varied power densities of 80 W and 120 W for 0.5 h was conducted to improve the surface morphology and interfacial compatibility of SF. The mechanical characteristics of unmodified and CGDP-modified SF-reinforced epoxy composite (SFREC) were examined as per the American Society for Testing and Materials standards.

The cold glow discharge nitrogen plasma treatment of SF at 120 W (30 min) enhanced the SFREC by nearly 122.75% superior interlaminar shear strength, 71.09% greater flexural strength, 84.22% higher tensile strength and 109.74% higher elongation. The combination of improved surface roughness and more effective lignocellulosic exposure has been responsible for the increase in the mechanical characteristics of treated composites. The development of hydrophobicity in the SF had been induced by CGDP N₂ modification and enhanced the size of crystals and crystalline structure by removing some unwanted constituents of the SF and etching the smooth lignin-rich surface layer of the SF particularly revealed via FTIR and XRD.

Chemical and physical treatments have been identified as the most efficient ways of treating the fiber surface. However, the huge amounts of liquids and chemicals needed in chemical methods and their exorbitant performance in terms of energy expenditure have limited their applicability in the past decades. The use of appropriate cohesion in addition to stimulating the biopolymer texture without changing its bulk polymer properties leads to the formation and establishment of plasma surface treatments that offer a unified, repeatable, cost-effective and environmentally benign replacement.

The authors are sure that this technology will be adopted by the polymer industry, aerospace, automotive and related sectors in the future.

In the field of research on the application of digital printing to textile materials, there are still many research issues that arise from the very demanding interaction of digital printing technology and the complex, heterogeneous surface system of textile materials. This is precisely why the area of pre-treatment of textile materials is in need of research, and the purpose of this research was to establish the level of influence of physical and chemical activation of the textile surface with plasma and the possibility of improving the quality of the print and colour reproduction.

The paper deals with the possibility of applying argon and oxygen cold low-pressure plasma in the processing of cellulose knitted fabrics, with the aim of improving the quality of the print and colour reproduction in digital pigment inkjet printing. The selected raw material samples were 100% raw cotton and lyocell. After plasma treatment, the samples were printed by digital ink jet printing with water-based pigment printing ink. An analysis of the micromorphological structure of untreated and plasma-treated samples before and after printing was carried out, and a comparative analysis of the colour of the printed elements was carried out depending on the pre-treatment.

The conducted research showed a positive influence of plasma pre-treatment on the coverage of the fibre surface with pigments, the uniformity of pigment distribution along the fibre surface and the uniformity of the distribution of the polymeric binder layer. This has a positive effect on colour reproduction. Also, certain improvements in colourfastness to washing were obtained.

Considering the complexity of the topic, although exhaustive, this research is not sufficient in itself, but opens up new questions and gives ideas for further research that must be carried out in this area.

Also, this kind of research contributes to the possibility of adopting the idea of industrial plasma transformation, as an ecologically sustainable functionalisation of textiles, which has not yet been established.

This research is certainly a contribution to the establishment of acceptable textile pre-treatment methods in the field of digital printing, as one of the key quality factors in digital textile printing (DTP). Considering the still large number of obstacles and unanswered questions encountered in the field of digital printing on textiles, this kind of research is a strong contribution to the understanding of the fundamental mechanisms of the complex interaction between printing ink and textile.

Gourd fibres (GF) are a natural biodegradable fibre material with excellent mechanical properties and high tensile strength. The use of natural fibres in composite materials has gained popularity in recent years due to their various advantages, including renewability, low cost, low density and biodegradability. Gourd fibre is one such natural fibre that has been identified as a potential reinforcement material for composites. However, it has low surface energy and hydrophobic nature, which makes it difficult to bond with matrix materials such as polyester. To overcome this problem, chemically adapted gourd fibre has been proposed as a solution. Chemical treatment is one of the most widely used methods to improve the properties of natural fibres. This research evaluates the feasibility and effectiveness of incorporating chemically adapted gourd fibre into polyester composites for industrial fabrication. The purpose of this study is to examine the application of chemically modified GF in the production of polyester composite engineering materials.

This work aims to evaluate the effectiveness of chemically adapted gourd fibre in improving the adhesion of gourd fibre with polyester resin in composite fabrication by varying the GF from 5 to 20 wt.%. The study involves the preparation of chemically treated gourd fibre through surface modification using sodium hydroxide (NaOH), permanganate (KMnO₄) and acetic acid (CH₃COOH) coupling agents. The mechanical properties of the modified fibre and composites were investigated. It was then characterized using scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) to determine the changes in surface morphology and functional groups.

FTIR characterization showed that NaOH treatment caused cellulose depolymerization and caused a significant increase in the hydroxyl and carboxyl groups, showing improved surface functional groups; KMnO₄ treatment oxidized the fibre surface and caused the formation of surface oxide groups; and acetic acid treatment induced changes that primarily affected the ester and hydroxyl groups. SEM study showed that NaOH treatment changed the surface morphology of the gourd fibre, introduced voids and reduced hydrophilic tendencies. The tensile strength of the modified gourd fibres increased progressively as the concentration of the modification chemicals increased compared to the untreated fibres.

This work presents the designed composite with density, mechanical properties and microstructure, showing remarkable improvements in the engineering properties. An 181.5% improvement in tensile strength and a 56.63% increase in flexural strength were got over that of the unreinforced polyester. The findings from this work will contribute to the understanding of the potential of chemically adapted gourd fibre as a reinforcement material for composites and provide insights into the development of sustainable composite materials.

In this study, two postprocessing techniques, namely, conventional burnishing (CB) and ultrasonic-assisted burnishing (UAB), were applied to improve the fatigue behavior of 316 L stainless steel fabricated through selective laser melting (SLM). The effects of these processes on surface roughness, porosity, microhardness and fatigue performance were experimentally investigated. The purpose of this study is to evaluate the feasibility and effectiveness of ultrasonic-assisted burnishing as a preferred post-processing technique for enhancing the fatigue performance of additively manufactured components.

All samples were subjected to a sandblasting process. Next, the samples were divided into three distinct groups. The first group (as-Built) did not undergo any additional postprocessing, apart from sandblasting. The second group was treated with CB, while the third group was treated with ultrasonic-assisted burnishing. Finally, all samples were evaluated based on their surface roughness, porosity, microhardness and fatigue performance.

The results revealed that the initial mean surface roughness (Ra) of the as-built sample was 11.438 µm. However, after undergoing CB and UAB treatments, the surface roughness decreased to 1.629 and 0.278 µm, respectively. Notably, the UAB process proved more effective in eliminating near-surface pores and improving the microhardness of the samples compared to the CB process. Furthermore, the fatigue life of the as-built sample, initially at 66,000 cycles, experienced a slight improvement after CB treatment, reaching 347,000 cycles. However, the UAB process significantly enhanced the fatigue life of the samples, extending it to 620,000 cycles.

After reviewing the literature, it can be concluded that UAB will exceed the capabilities of CB in terms of enhancing the surface roughness and, subsequently, the fatigue performance of additive manufactured (AM) metals. However, the actual impact of the UAB process on the fatigue life of AM products has not yet been thoroughly researched. Therefore, in this study, this paper used the burnishing process to enhance the fatigue life of 316 L stainless steel produced through the SLM process.

The nickel-based alloys Inconel 625 and Inconel 718 stand out due to their high strength and corrosion resistance in important industries like aerospace, aviation and automotive. Even though they are widely used, current techniques of producing materials that are difficult to cut pose several problems from a financial, ecological and even health perspective. To handle these problems and acquire improved mechanical and structural qualities, laser powder bed fusion (LPBF) has been widely used as one of the most essential additive manufacturing techniques. The purpose of this article is to focus on the state of the art on LPBF parts of Inconel 625 and Inconel 718 for microstructure, mechanical behavior and postprocessing.

The mechanical behavior of LPBF-fabricated Inconel is described, including hardness, surface morphology and wear, as well as the influence of fabrication orientation on surface quality, biocompatibility and resultant mechanical properties, particularly tensile strength, fatigue performance and tribological behaviors.

The postprocessing techniques such as thermal treatments, polishing techniques for surface enhancement, mechanical and laser-induced peening and physical operations are summarized.

The highlighted topic presents the critical aspects of the advantages and challenges of the LPBF parts produced by Inconel 718 and 625, which can be a guideline for manufacturers and academia in practical applications.

Titanium(IV) oxide nanoparticles (TiO₂ NP) were deposited to cotton denim fabrics using a self-crosslinking acrylate – a polymer dispersion to extend the lifetime of the products. This study aims to determine the optimum conditions to increase abrasion resistance, to provide self-cleaning properties of denim fabrics and to examine the effects of these applications on other physical properties.

The denim samples were first treated with nonionic surfactant to increase their wettability. Three different amounts of the polymer dispersion and two different pH levels were selected for the experimental design. The finishing process was applied to the fabrics with pad-dry-cure method.

The presence of the coatings and the adhesion of TiO₂ NPs to the surfaces were confirmed by scanning electron microscope and Fourier transform infrared spectroscopy analysis. It was ascertained that the most appropriate self-crosslinking acrylate amount and ambient pH level is 10 mL and “2”, respectively, for providing increased abrasion resistance (2,78%) and enhanced self-cleaning properties (363,4%) in the denim samples. The coating reduced the air permeability and softness of the denim samples. Differential scanning calorimetry and thermogravimetry analysis results showed that the treatments increased the crystallization temperatures and melting enthalpy values of the denim samples. Based on the thermal test results, it is clear that mass loss of the denim samples at 370°C decreased as the amount of self-crosslinking acrylate increased (at pH 3).

This study helped us to find out optimum amount of self-crosslinking acrylate and proper pH level for enhanced self-cleaning and abrasion strength on denim fabrics. With this finishing process, an environmentally friendly and long-life denim fabric was designed.