Preparation and characterization of self-cross-linking long fluorocarbon polyacrylate latex modified by silane cross-linker

Abstract

Purpose

Silane cross-linkers have been used to strengthen the mechanical stabilities and friction resistance of plastic products. Therefore, the effect of silane cross-linkers on latex has been studied through preparing modified self-cross-linking long fluorocarbon polyacrylate latex. In this paper, nonionic surfactant alcohol ether glycoside (AEG1000) and anionic polymerizable surfactant 1-allyloxy-3-(4-nonylphenol)-2-propanol polyoxyethylene (10) ether ammonium sulfate (DNS-86) acted as mixed emulsifier and 3-(methacryloyloxy) propyltrimethoxysilane (KH-570) and bis (2-ethylhexyl) maleate (DOM) were used as functional monomers.

Design/methodology/approach

The modified acrylate polymer latex was synthesized through the semi-continuous seeded emulsion polymerization with methyl methacrylate (MMA), butyl acrylate (BA), dodecafluoroheptyl methacrylate (DFMA) and hydroxypropyl methacrylate (HPMA) as main monomers. Potassium persulfate (KPS) was applied to initiate polymerization reaction, nonionic surfactant AEG1000 and DNS-86 acted as emulsifier, KH-570 and DOM were used as functional monomers, respectively.

Findings

The optimum conditions of synthesizing the modified latex were the following. The mass ratio of monomers containing MMA, BA, DFMA, HPMA, KH-570 and DOM was 13.58:13.58:0.90:1.20:0.15:0.60, the usage of initiator KPS was 0.5% of the total weight of monomers and the amount of emulsifier was 7% of all monomers with AEG1000:DNS-86 = 1:1. The results indicated that the conversion of monomer was 99% and the coagulation was about 2.0%.

Originality/value

The resultant latex was modified silane cross-linker KH-570 and DOM, which positively affected the comprehensive properties of latex and its film. Apart from this, the novel mixed emulsifier was used to improve the size and distribution of latex particles and reduce environmental problems caused by the use of emulsifiers.

Citation

Shao, T., Chen, X. and Chen, L. (2022), "Preparation and characterization of self-cross-linking long fluorocarbon polyacrylate latex modified by silane cross-linker", Pigment & Resin Technology, Vol. 51 No. 3, pp. 265-272. https://doi.org/10.1108/PRT-06-2020-0057