Herein, the authors report the effects of printing parameters, joining method, and annealing conditions on the structural performance of fusion-joined short-beam sections produced by additive manufacturing.

The authors first identified appropriate printing parameters for joining segmented short beams and then used those parameters to print and fusion-join segments with different configurations of stiffeners to form a longer section of a wing or small wind turbine blade structure.

It was found that the beams with three lateral and three base stiffening ribs give the highest flexural strength among the three beams investigated. Results on joined beams annealed at different conditions showed that annealing at 70 °C for 0.5 h yields higher performance than annealing at the same temperature for longer times. It is also found that in the case of the hot-plate-welded three-dimensional (3D)-printed structures, no annealing is needed for reaching a high strength-to-weight ratio, but annealing is helpful for maximizing the modulus-to-weight ratio. Both thermal buckling and edge wrapping were observed under annealing at 70°C for 0.5 h for 3D-printed beams comprising two lateral and four base stiffening plates.

Fusion-joining of additively manufactured segments is needed owing to the constraint in building volume of a typical commercial 3D-printer. However, study of the effect of process parameters is needed to quantify their effect on mechanical performance. This investigation has therefore identified key printing parameters and annealing conditions for fusion-joining short segments to form larger structures, from multiple 3D-printed sections, such as wind blade structures.

To investigate the mechanical properties of geopolymer concrete at elevated temperatures.

The investigation involved studying the influence of partially replacing fly ash with ground granulated blast furnace slag (GGBS) at different proportions (5%, 10%, 15%, 20% and 25%) on the composition of the geopolymer. This approach aimed to examine how the addition of GGBS impacts the properties of the geopolymer material. The chemical NaOH was purchased from the local supplier of Jamshedpur. The alkali solution was prepared with a concentration of 12 M NaOH to produce the concrete. After several trials, the alkaline-to-binder ratio was determined to be 0.43.

The compressive strength values at 28 days for specimens FG1, FG2, FG3, FG4 and FG5 are 35.42 MPa, 41.26 MPa, 44.79 MPa, 50.51 MPa and 46.33 MPa, respectively. The flexural strength values at 28 days for specimens FG1, FG2, FG3, FG4 and FG5 are 5.31 MPa, 5.64 MPa, 6.12 MPa, 7.15 MPa and 6.48 MPa, respectively. The split tensile strength values at 28 days for specimens FG1, FG2, FG3, FG4 and FG5 are 2.82 MPa, 2.95 MPa, 3.14 MPa, 3.52 MPa and 3.31 MPa, respectively.

This approach allows for the examination of how the addition of GGBS affects the properties of the geopolymer material. Four different temperature levels were chosen for analysis: 100 °C, 300 °C, 500 °C and 700 °C. By subjecting the geopolymer samples to these elevated temperatures, the study aimed to observe any changes in their mechanical.

The purpose of this study is to assess the incorporation of fiber reinforced polymer (FRP) bars in concrete as a reinforcement enhances the corrosion resistance in a concrete structure. However, FRP bars are not practically used due to a lack of standard codes. Various codes, including ACI-440-17 and CSA S806-12, have been established to provide guidelines for the incorporation of FRP bars in concrete as reinforcement. The application of these codes may result in over-reinforcement. Therefore, this research presents the use of a machine learning approach to predict the accurate flexural strength of the FRP beams with the use of 408 experimental results.

In this research, the input parameters are the width of the beam, effective depth of the beam, concrete compressive strength, FRP bar elastic modulus and FRP bar tensile strength. Three machine learning algorithms, namely, gene expression programming, multi-expression programming and artificial neural networks, are developed. The accuracy of the developed models was judged by R², root means squared and mean absolute error. Finally, the study conducts prismatic analysis by considering different parameters. including depth and percentage of bottom reinforcement.

The artificial neural networks model result is the most accurate prediction (99%), with the lowest root mean squared error (2.66) and lowest mean absolute error (1.38). In addition, the result of SHapley Additive exPlanation analysis depicts that the effective depth and percentage of bottom reinforcement are the most influential parameters of FRP bars reinforced concrete beam. Therefore, the findings recommend that special attention should be given to the effective depth and percentage of bottom reinforcement.

Previous studies revealed that the flexural strength of concrete beams reinforced with FRP bars is significantly influenced by factors such as beam width, effective depth, concrete compressive strength, FRP bars’ elastic modulus and FRP bar tensile strength. Therefore, a substantial database comprising 408 experimental results considered for these parameters was compiled, and a simple and reliable model was proposed. The model developed in this research was compared with traditional codes, and it can be noted that the model developed in this study is much more accurate than the traditional codes.

Additive manufacturing of polymer composites is a transformative technology that leverages the benefits of both composite material and 3D printing to produce highly customizable, lightweight and efficient composites for a wide range of applications.

In this research work, glass fiber-reinforced polylactic acid (PLA) filament is used to print the specimen via fusion deposition modeling process. The process parameters such as infill densities (40%, 50% and 60%) and raster angle/orientations (0°, 45° and 90°) are varied, and the specimens for tensile, flexural, impact, hardness and wear testing are prepared as per their respective ASTM standards.

The results revealed that with an increase in infill density, the mechanical properties of glass fiber-PLA specimens increase progressively. Optimal tensile properties and flexural properties are obtained at 0° and 90° raster angle orientations and 60% infill density. Minimum wear rate is achieved at 0° raster angle orientation and it increases at 45° and 90° raster angle orientations.

Using SEM, the microscopic analysis of the fractured specimen was analyzed to study the interface between the fibers and matrix and it indicates the presence of good adhesion between the layers at 60% infill density and 0° print orientation.

This paper aims to reduce waste management and generate wealth by investigating the novelty of combining chicken feather fiber and bamboo particles to produce hybrid biocomposites. This is part of responsible production and sustainability techniques for sustainable development goals. This study aims to broaden animal and plant fiber utilization in the sustainable production of epoxy resins for engineering applications.

This research used two reinforcing materials [chicken feather fiber (CFF) and bamboo particles (BP)] to reinforce epoxy resin. The BPs were kept constant at 6 Wt.%, while the CFF was varied within 3–15 Wt.% in the composites to make CFF-BP polymer-reinforced composite (CFF-BP PRC). The mechanical experiment showed a 21% reduction in densities, making the CFF-BP PRC an excellent choice for lightweight applications.

It was discovered that fabricated composites with 10 mm CFF length had improved properties compared with the 15 mm CFF length and pristine samples, which confirmed that short fibers are better at enhancing randomly dispersed fibers in the epoxy matrix. However, the ballistic properties of both samples matched. There is a 40% increase in tensile strength and a 54% increase in flexural strength of the CFF-BP PRC compared to the pristine sample.

According to the literature review, to the best of the authors’ knowledge, this is a novel study of chicken fiber and bamboo particles in reinforcing epoxy composite.

Although ceramic additive manufacturing (AM) could be used to fabricate complex, high-resolution parts for diverse, functional applications, one ongoing challenge is optimizing the post-process, particularly sintering, conditions to consistently produce geometrically accurate and mechanically robust parts. This study aims to investigate how sintering temperature affects feature resolution and flexural properties of silica-based parts formed by vat photopolymerization (VPP) AM.

Test artifacts were designed to evaluate features of different sizes, shapes and orientations, and three-point bend specimens printed in multiple orientations were used to evaluate mechanical properties. Sintering temperatures were varied between 1000°C and 1300°C.

Deviations from designed dimensions often increased with higher sintering temperatures and/or larger features. Higher sintering temperatures yielded parts with higher strength and lower strain at break. Many features exhibited defects, often dependent on geometry and sintering temperature, highlighting the need for further analysis of debinding and sintering parameters.

To the best of the authors’ knowledge, this is the first time test artifacts have been designed for ceramic VPP. This work also offers insights into the effect of sintering temperature and print orientation on flexural properties. These results provide design guidelines for a particular material, while the methodology outlined for assessing feature resolution and flexural strength is broadly applicable to other ceramics, enabling more predictable part performance when considering the future design and manufacture of complex ceramic parts.

One of the often-employed building constituents in the construction sector is concrete, which involves hydration of cement, leading to the generation of carbon footprints during its production. Also, massive amount of natural aggregate is illegally mined, which poses serious environmental issues along with ecological misbalance. Researchers are in continuous search of appropriate substitutes to mitigate those challenges and develop innovative concrete mix. Consequently, depletion of natural resources, the disturbances to the environmental and ecological imbalance will reduce. The purpose of this study is to develop a Portland Slag Cement based novel sustainable concrete incorporating Alccofine and Recycled Refractory Brick as fractional replacement of cement and fine aggregate, respectively and evaluate its destructive, non-destructive and microstructural properties.

M25 grade of concrete adopting 0.45 water-binder proportion, with diverse percentage of Alccofine as fractional substitution of cement and 20% of recycled refractory brick (RRB) as fine aggregate, has been cast and evaluated for diverse mechanical strength following a curing of 7, 14 and 28 days. Scanning electron microscopic analysis has been carried out to study the microstructural changes in the specimens.

Supplementary use of Alccofine enhanced normal compressive strength of sustainable concrete mix blended with Portland Slag Cement by a large amount at all levels of 7, 14 and 28 days of curing. Test results indicated development of a favourable high-strength sustainable concrete mix by substituting cement with Alccofine.

This manuscript has demonstrated the possibility of developing sustainable concrete blends by incorporating Alccofine 1203 and RRB as partial replacement of Portland Slag Cement and natural fine aggregate, respectively. The strength and potential of concrete incorporating RRB for wider and special application in adverse environmental conditions having higher thermal gradient, as RRB is a valuable waste from high temperature kiln and furnaces. Alccofine 1203 has been included in the concrete mix as an alternative to Portland Slag Cement to improve the mechanical strength properties and durability of concrete intended for adverse environmental application.

The development of high-strength engineered cementitious composite (ECC) gains a significant leap in structural engineering. Engineers have been looking for new formulations that combine outstanding compressive strength with increased flexural resistance. This research focuses on the main characteristics, techniques and prospective applications of high-strength ECC. The proposed work explores the composition of such concrete, emphasizing the use of novel additives, fiber reinforcements and optimal particle packing to produce excellent mechanical characteristics and demonstrating how high-strength ECC contributes to incorporate sustainability by potentially lowering the need for supplemental reinforcing and resulting in a lower environmental effect.

This research involves on studying the composition of high-strength ECC and geopolymer-based ECC, the use of novel additives, fiber reinforcements and optimal particle packing. It examines the capacity of high-strength ECC to sustain high loads with an allowable deformation without any catastrophic collapse. It discusses the sustainability aspects of high-strength ECC and its potential alternative as geopolymer-based ECC.

High-strength ECC offers an excellent compressive strength while also providing increased flexural capacity. Employment of copper slag (CS) as a filler material for the production of ECC results in 28.92% lower cost, when compared to the mix developed using conventional river sand. Whereas in the case of geopolymer-based ECC, the cost of production was found to be 31.92% lower than that of the conventional.

High-strength ECC is developed using conventional river sand and industrial by-product, CS as a filler material. The combination of achieving higher compressive strength with an increased use of industrial by-products leads to the development of sustainable high strength ECC. The potential use of high-strength ECC reduces the need for supplementary reinforcing and increases the structural lifetime, resulting in a lower environmental impact.

This paper aims to report the effect of titanium oxide (TiO₂) particles on the physical, mechanical, tribological and water resistance properties of 5% NaOH-treated bamboo fiber–reinforced composites.

In this research, the epoxy/bamboo/TiO₂ hybrid composite filled with 0–8 Wt.% TiO₂ particles has been fabricated using simple hand layup techniques, and testing of the developed composite was done in accordance with the American Society for Testing and Materials (ASTM) standard.

The results of this study indicate that the addition of TiO₂ particles improved the mechanical properties of the developed epoxy/bamboo composites. Tensile properties were found to be maximum for 6 Wt.%, and impact strength was found to be maximum for 8 Wt.% TiO₂ particles-filled composite. The highest flexural properties were found at a lower TiO₂ fraction of 2 Wt.%. Adding TiO₂ filler helped to reduce the water absorption rate. The studies related to the wear and friction behavior of the composite under dry and abrasive wear conditions reveal that TiO₂ filler was beneficial in improving the wear performance of the composite.

This research paper attempts to include both TiO₂ filler and bamboo fibers to develop a novel composite material. TiO₂ micro and nanoparticles are promising filler materials; it helps to enhance the mechanical and tribological properties of the epoxy composites and in literature, there is not much work reported, where TiO₂ is used as a filler material with bamboo fiber–reinforced epoxy composites.

This paper aims to produce lightweight concrete by combining aerated concrete with expanded polystyrene beads concrete to create structural aerated-polystyrene lightweight concrete that satisfies the criteria of sustainability for thermal and sound insulation properties and the structural criteria of having satisfactory compressive strength for structural elements.

The experimental study was carried out to reach the largest compressive strength while maintaining the lowest possible density by preparing nine mixes of concrete, involving different ratios of aluminum waste powder and polystyrene beads as 0%, 0.2% and 0.3% and 0%, 0.1% and 0.2%, respectively, by weight of cement to produce the lightweight concrete with different densities. The performance of mechanical properties, thermal conductivity, ultrasonic pulse velocity, density, modulus of elasticity, acoustic impedance and scanning electron microscopy were studied and discussed.

Results showed that aerated-expended polystyrene beads concrete had the most suitable properties when the proportions of aluminum waste powder and expanded polystyrene beads were 0.2% and 0.1%, respectively. The compressive strength, density, thermal conductivity and acoustic impedance were 38.5 MPa, 1,768 Kg/m³, 0.358 W/(m.k) and 4.91 Kg/m² s, respectively.

The experimental work was done using aluminum scrap waste powder as an expanding agent to produce aerated concrete and combining it with expanded polystyrene bead concrete to produce structural aerated-polystyrene concrete, which contains fine materials (silica fume and local natural raw limestone) and superplasticizers.