This study aims to review the effect of copper percentage in Sn-based solder alloys (Sn-xCu, x = 0–5 Wt.%) on intermetallic compound (IMC) formation and growth after laser soldering.

This study reviews the interfacial reactions at the solder joint interface, solder joint morphology and the theory on characterizing the formation and growth of IMCs. In addition, the effects of alloying and strengthening mechanism, including wettability, melting and mechanical properties are discussed.

This paper presents a comprehensive overview of the composition of tin-copper (Sn-Cu) solders with a potential to enhance their microstructure, mechanical characteristics and wettability by varying the Cu percentage. The study found that the best Cu content in the Sn-xCu solder alloy was 0.6–0.7 Wt.%; this composition provided high shear strength, vibration fracture life value and ideal IMC thickness. A method of solder alloy preparation was also found through powder metallurgy and laser soldering to improve the solder joint reliability.

This study focuses on interfacial reactions at the solder joint interface, solder joint morphology, modelling simulation of joint strength and the theory on characterising the formation and growth of IMC.

The paper comprehensively summarises the useful findings of the Sn-Cu series. This information will be important for future trends in laser soldering on solder joint formation.

This study aims to analyze the wettability of the self-developed Sn–Bi–Zn solder and to conduct a series of analysis on the wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–Bi–Zn solder on Cu substrate.

The wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–Bi–Zn solder on Cu substrate were analyzed by experiments. The interface was observed by scanning electron microscope to study the effect of Zn content on its interface.

With the increase in brazing temperature, the final spreading equivalent radius of the solder increases significantly, and the final contact angle of the solder decreases significantly. In addition, when the Zn content is 1%, the spreading effect of solder is the best, the equivalent radius is the largest and the contact angle is the smallest. According to the microstructural analysis, the thick intermetallic compounds layer of the Sn–15Bi–xZn solders on the Cu substrate can be effectively decreased by adding appropriate Zn content.

The wetting kinetics, diffusion phenomenon and interfacial reaction of Sn–15Bi–xZn solder on Cu substrate at different temperatures have not been studied yet.

In the electronic assembly industry, low-temperature soldering holds great potential to be used in surface mounting technology. Tin–bismuth (Sn–Bi) eutectic alloys are lead-free solders applied in consumer electronics because of their low melting point, high strength and low cost. This paper aims to investigate how to address the problem of hot tear crack formation during Sn–Bi low-temperature solder (LTS) in the mass production of consumer electronics.

This paper explored the development of hot tear cracks during Sn–Bi soldering in the fabrication of flip chip ball grid arrays. Experiments were designed to simulate various conditions encountered in Sn–Bi soldering. Quantitative analysis was conducted on the number of hot tear cracks observed in different alloy compositions and solder volumes to explore the primary cause of hot tear cracks and possible methods to suppress crack formation.

Hot tear cracks existed in Sn–Bi solders with different bismuth (Bi) contents, but increasing the solder volume reduced the number of hot tear cracks. Experiments were designed to test the degree of chip transient thermal warpage with temperature change, and, according to the results, glue was dispensed in specific areas to reduce chip warpage deformation. Finally, the results of combined process experiments pointed to an effective method of low-temperature soldering to suppress hot tear cracks.

The study focuses on Sn–Bi solders only without other solder pastes such as SAC305 or Sn–Zn series.

With the growing popularity of smart electronics, especially in intelligent terminals, new energy vehicles electronics, solar photovoltaic and other field, there will be more and more demand for low- temperature, energy-saving, lead-free solders. Therefore, this study will help the industry to roll out LTS (Sn–Bi) solutions rapidly.

In the long term, lean and green manufacturing is expected to be essential for maintaining an advanced manufacturing industry across the world. Developing new LTSs and soldering processes is the most effective, direct solution for energy conservation and emission mitigation. With the growing popularity of smart electronics, especially in intelligent terminals, new energy vehicles and solar photovoltaics, there would be an increased demand for low-temperature, energy-saving, lead-free techniques.

Although there are many methods that can be used to suppress hot tear cracks, there is little research on how to control the hot tear cracks caused by the low-temperature soldering of Sn–Bi in laptop applications. The authors studied the hot tear cracks that developed during the world’s first mass production of 50 million personal laptops based on low-temperature Sn–Bi alloy solder pastes. By controlling the Bi content, redesigning the solder paste printing process (e.g. through a printer’s stencil) and adding dispensing processes, the authors obtained reliable and stable experimental data and conclusions.

The purpose of this study is to delve into the mechanism of Si3N4 nanowires (NWs) in Sn-based solder, thereby furnishing a theoretical foundation for the expeditious design and practical implementation of innovative lead-free solder materials in the electronic packaging industry.

This study investigates the effect of adding Si₃N₄ NWs to Sn58Bi solder in various mass fractions (0, 0.1, 0.2, 0.4, 0.6 and 0.8 Wt.%) for modifying the solder and joining the Cu substrate. Meanwhile, the melting characteristics and wettability of solder, as well as the microstructure, interfacial intermetallic compound (IMC) and mechanical properties of joint were evaluated.

The crystal plane spacing and lattice constant of Sn and Bi phase increase slightly. A minor variation in the Sn58Bi solder melting point was caused, while it does not impact its functionality. An appropriate Si₃N₄ NWs content (0.2∼0.4 Wt.%) significantly improves its wettability, and modifies the microstructure and interfacial IMC layer. The shear strength increases by up to 10.74% when adding 0.4 Wt.% Si₃N₄ NWs, and the failure mode observed is brittle fracture mainly. However, excessive Si₃N₄ will cause aggregation at the junction between the solder matrix and IMC layer, this will be detrimental to the joint.

The Si₃N₄ NWs were first used for the modification of lead-free solder materials. The relative properties of composite solder and joints were evaluated from different aspects, and the optimal ratio was obtained.

Pb-free solders have been developed to replace the standard Sn–Pb eutectic solder since the prohibition on Pb used in solders. The Sn–Ag–Cu series of lead-free solders is the most extensively used in the electronics industry. The Ag₃Sn, which forms during isothermal ageing, can significantly degrade solder joint reliability. Sn–Ag–Cu solder’s high price further hindered its use in the electronics industry. This paper aims to investigate different copper percentages into Sn–xCu solder alloy to improve its microstructure and strength performance.

The solder alloys used in this work were Sn–xCu, where x = 0.0, 0.3, 0.5, 0.7, 1.0 Wt.%, which was soldered onto electroless nickel immersion gold (ENIG) substrate using carbon dioxide (CO₂) gas laser. Then these samples were subjected to isothermal aging for 0, 200, 500, 1,000 and 2,000 h. The Sn–xCu solder alloy was fabricated through a powder metallurgy process.

Microstructure characterization showed that Cu addition resulted in fine and rounded shape of Cu–Sn–Ni particles. Shear strength of Sn–xCu solder joints was increased with increasing Cu content, but at aging duration of 1,000 h, it dropped slightly. It is believed that the strength improved due to the increment of diffusion rate during isothermal aging.

In a Cu–Sn solder, the recommended amount is 1.0 Wt.% of Cu. In extensive aging procedures, it was discovered that Sn1.0Cu solder improved the reliability of solder joints. The findings indicated that the innovative solder alloys might satisfy the needs of high-reliability applications.

The study shows that the right amount of Cu enhances the solidification of Sn–Cu solder, increasing the shear force of the Cu–Sn solder joint. The Sn1.0Cu exhibits a ductile fracture on the top microstructure, improving the joint’s average shear strength.

The purpose of the present work is to study the impacts of rapid cooling and Tb rare-earth additions on the structural, thermal and mechanical behavior of Bi–0.5Ag lead-free solder for high-temperature applications.

Effect of rapid solidification processing on structural, thermal and mechanical properties of Bi-Ag lead-free solder reinforced Tb rare-earth element.

The obtained results indicated that the microstructure consists of rhombohedral Bi-rich phase and Ag99.5Bi0.5 intermetallic compound (IMC). The addition of Tb could effectively reduce the onset and melting point. The elastic modulus of Tb-containing solders was enhanced to about 90% at 0.5 Tb. The higher elastic modulus may be attributed to solid solution strengthening effect, solubility extension, microstructure refinement and precipitation hardening of uniform distribution Ag99.5Bi0.5 IMC particles which can reasonably modify the microstructure, as well as inhibit the segregation and hinder the motion of dislocations.

It is recommended that the lead-free Bi-0.5Ag-0.5Tb solder be a candidate instead of common solder alloy (Sn-37Pb) for high temperature and high performance applications.

The purpose of this study was to examine the influence of adding a small amount of Ti to a Cu-based alloy, specifically the commercial Hyper Titanium Copper alloy (C1990 HP), which contains Cu-3.28 wt.% Ti, on its interfacial reaction with Sn-9.0 wt.% Zn (SnZn) solder, using the liquid/solid reaction couple technique.

The SnZn/C1990 HP couples were subjected to a reaction temperature of 240–270°C for a duration of 0.5–5 h. The resulting reaction couple was characterized using a scanning electron microscope, energy dispersive spectrometer, electron probe microanalyzer and X-ray diffractometer.

It was observed that the scallop-shaped CuZn5 and planar Cu5Zn8 phases were formed in almost all SnZn/C1990 HP couples. With increased reaction duration and temperature, the Cu-rich intermetallic compound (IMC)-Cu5Zn8 phase became a dominant IMC formed at the interface. The total thickness of the IMCs was increased with the increase in the reaction duration and temperature. The IMC growth obeyed the parabolic law, and the IMC growth mechanism was diffusion controlled. The activation energy of the SnZn/C1990 HP couple was 64.71 kJ/mol.

This article presents an analysis of the IMC thickness in each sample using ImageJ software, followed by kinetic analysis using Origin software at various reaction temperatures of SnZn/C1990 HP in liquid/solid couples. The study also includes detailed reports on the morphology, interface composition and X-ray diffraction analysis, as well as the activation energy. The findings can serve as a valuable reference for electronic packaging companies that utilize C1990 HP substrates.

The purpose of this study is to investigate the effects of Ce and Sb doping on the microstructure and thermal mechanical properties of Sn-1.0Ag-0.5Cu lead-free solder. The effects of 0.5%Sb and 0.07%Ce doping on microstructure, thermal properties and mechanical properties of Sn-1.0Ag-0.5Cu lead-free solder were investigated.

According to the mass ratio, the solder alloys were prepared from tin ingot, antimony ingot, silver ingot and copper ingot with purity of 99.99% at 400°C. X-ray diffractometer was adopted for phase analysis of the alloys. Optical microscopy, scanning electron microscopy and energy dispersive spectrometer were used to study the effect of the Sb and Ce doping on the microstructure of the solder. Then, the thermal characteristics of alloys were characterized by a differential scanning calorimeter (DSC). Finally, the ultimate tensile strength (UTS), elongation (EL.%) and yield strength (YS) of solder alloys were measured by tensile testing machine.

With the addition of Sb and Ce, the ß-Sn and intermetallic compounds of solders were refined and distributed more evenly. With the addition of Sb, the UTS, EL.% and YS of Sn-1.0Ag-0.5Cu increased by 15.3%, 46.8% and 16.5%, respectively. The EL.% of Sn-1.0Ag-0.5Cu increased by 56.5% due to Ce doping. When both Sb and Ce elements are added, the EL.% of Sn-1.0Ag-0.5Cu increased by 93.3%.

The addition of 0.5% Sb and 0.07% Ce can obtain better comprehensive performance, which provides a helpful reference for the development of Sn-Ag-Cu lead-free solder.

This study aims to focus on the surface mount technology (SMT) mass production process of Sn-9Zn-2.5Bi-1.5In solder. It explores it with some components that will provide theoretical support for the industrial SMT application of Sn-Zn solder.

This study evaluates the properties of solder pastes and selects a more appropriate reflow parameter by comparing the microstructure of solder joints with different reflow soldering profile parameters. The aim is to provide an economical and reliable process for SMT production in the industry.

Solder paste wettability and solder ball testing in a nitrogen environment with an oxygen content of 3,000 ppm meet the requirements of industrial production. The printing performance of the solder paste is good and can achieve a printing rate of 100–160 mm/s. When soldering with a traditional stepped reflow soldering profile, air bubbles are generated on the surface of the solder joint, and there are many voids and defects in the solder joint. A linear reflow soldering profile reduces the residence time below the melting point of the solder paste (approximately 110 s). This reduces the time the zinc is oxidized, reducing solder joint defects. The joint strength of tin-zinc joints soldered with the optimized reflow parameters is close to that of Sn-58Bi and SAC305, with high joint strength.

This study attempts to industrialize the application of Sn-Zn solder and solves the problem that Sn-Zn solder paste is prone to be oxidized in the application and obtains the SMT process parameters suitable for Sn-9Zn-2.5Bi-1.5In solder.

This paper aims to investigate the effect of solder composition and roughness on early wetting behavior and interfacial reaction under atmospheric conditions.

High-speed photography is used to observe the early wetting and spreading process of the solder on the substrate in real time. The morphology of intermetallic compounds (IMCs) was observed by scanning electron microscopy, and the composition of IMCs micro bumps was determined by energy dispersive spectroscopy.

With a roughness range of 0.320–0.539 µm, the solder is distributed in an elliptical trilinear pattern along the grinding direction. With a roughness range of 0.029–0.031 µm, the solder spreads in the direction of grinding and perpendicular, forming a perfect circle (except in the case of Sn63Pb37 solder). The effect of three types of solder on early wettability is Sn63Pb37 > Sn96.5Ag3Cu0.5 > Sn. The wetting behavior is consistent with the Rn∼t model. The rapid spreading stage (Stage I) is controlled by the interfacial reaction with n1 values between 2.4 and 4. The slow spreading stage (stage II) is controlled by diffusion with n2 values between 4 and 6.7. The size of Cu6Sn5 formed on a rough substrate is greater than that produced on a smooth substrate.

Investigating the effect of solder composition and roughness on early wettability. This will provide a powerful guide in the field of soft brazing.