The purpose of this paper is to optimize the key parameters (mesh count, paper type and ink type) in screen printing, which are affecting the printed ink volume. The objective of the optimization was to maximize the color reliability by decreasing the color difference (ΔE value) of the prints while minimizing the ink consumption. Screen printing is still dominating the printing industry to make cost-effective production when high volumes are needed.

The experiment was designed using the Taguchi method, and the samples were prepared with screen-printing by using the standard squeegee angle and pressure. The effect of mesh count, ink type and paper type on ink consumption was evaluated with using analysis of variances and main effects plots of S/N ratio and standard deviation.

The factors ink type, paper type and mesh count were found significant for ink consumption due to their Probability (P) values which were lower than 0.05. It was determined that the mesh count was the most critical variable with the analysis of variance. The analysis showed that the selection of an optimum mesh count was the key to controlling the amount of the deposited ink. Although mesh counts were inversely proportional with the ink consumptions, they did not affect the color differences as expected.

The optimization of process parameters, that are most effective on the print quality, is necessary to minimize the ink usage and lower the costs and environmental impact without exceeding the desired ΔE value limits.

The purpose of this paper is to improve the dyeing effect of fast-growing fir wood dyed with reactive dyes.

In this study, five factors including temperature, the dosage of dye accelerator, dyeing time, the dosage of fixing agent and fixing time were investigated. Then, the color difference and light resistance of the wood surface after dyeing were used as the evaluation indicators; the best dyeing process under the two indicators was obtained through the range analysis. Finally, the two indicators were considered comprehensively, and the fuzzy comprehensive evaluation method was used to obtain the best dyeing process under the comprehensive indicators.

The results show that when the comprehensive index was used as the evaluation index, the optimal dyeing process for reactive red X-3B dyeing fast-growing fir veneer was that the dyeing temperature was 65°C; the amount of dye accelerator was 25 g L⁻¹; the dyeing time was 2 h; the amount of fixing agent was 15 g L⁻¹; and the fixing time was 35 min.

The technique of wood dyeing is an important method to increase the value of wood products. When using different kinds of dyes or dyeing substrates for wood dyeing, the dyeing process is different. This study determined the best process for reactive dye dyeing of fast-growing fir veneer and provided a solution for improving the value of fast-growing fir wood.

The major objective of this research work was to evaluate various physico-chemical characteristics, such as, chemical composition, antioxidant capacity, objective color and texture profile analysis (TPA) of the wheat flour/chickpea flour (CF) blends, so that nutritious baked products could be consumed by the type-2 diabetic persons.

Wholegrain wheat flour (WGF) and white wheat flour (WWF) were substituted with CF at 0 to 40% levels. These wheat flour/CF blends were analyzed for proximate composition, the prepared dough and baked breads were tested for objective color, antioxidant capacity as trolox equivalent antioxidant capacity (TEAC), malondialdehyde (MDA) and total phenolic content (TPC) and TPA.

WGF had the highest TEAC (117.42 mM/100g) value, followed by WWF (73.98 mM/100g) and CF (60.67 mM/100g). TEAC, MDA and TPC values varied significantly among all the three flour samples.

Inclusion of whole chickpea (without dehulling) flour in such type of blends would be another interesting investigation during the future research studies.

These research findings have a great potential for the production of these baked products for human consumption on an industrial scale.

Production of breads using wheat flour and CF blends would benefits the consumers.

Production of Arabic and pan breads using wheat flour and CF blends would, therefore, combine the benefits of both the needed proteins of plant origin and the health-promoting bioactive compounds, in a most sustainable way for the consumers.

The color painting of ancient buildings has high historical and artistic value but is prone to aging due to long-term outdoor exposure. The purpose of this study is to develop a new type of sealing coating to mitigate the impact of ultraviolet (UV) light on color painting.

The new coating was subjected to a 500-h UV-aging test. Compared with the existing acrylic resin Primal AC33, the UV aging behavior of the new coating, such as color difference and gloss, was studied with aging time. The Fourier infrared spectra of the coatings were analyzed after the UV-aging test.

Compared with AC33, the antiaging performance of SF8 was substantially improved. SF8 has a lower color difference value and better light retention and hydrophobicity. The Fourier transform infrared spectroscopy results showed that the C-F bond and Si-O bonds in the resin of the optimized sealing coating protected the main chain C-C structure from degradation during the aging process; thus, the resin maintained good stability. The hindered amine light stabilizer TN292 added to the coating inhibited the antiaging process by trapping active free radicals.

To address the problem of UV aging of oil-decorated colored paintings, a new type of sealing coating with excellent antiaging properties was developed, laying the foundation for its demonstration application on the surface of ancient buildings.

This study aims to embed anatase, rutile and brookite TiO₂ nanoparticles (NPs) with different crystal phases into cotton fabrics by epoxy silane and to examine the effect of these applications on the photocatalytic and mechanical properties of the fabric.

Different aqueous dispersions which contain anatase, rutile and brookite were prepared at three different concentrations (5%, 10% and 15%). These NPs were embedded in cotton fabrics by using GPTS [(3-glycidyloxypropyl) trimethoxysilane]. Characterization tests were performed by scanning electron microscopy (SEM), Raman and Fourier-transform infrared spectroscopy (FT/IR). Samples were stained with methylene blue (MB) and then exposed to solar light for different periods. Color changes of the samples were examined with a spectrophotometer. Air permeability, abrasion and tear strength tests were applied to all samples.

According to SEM images, the NPs were successfully attached to the cotton fabrics, and epoxy silane coating surrounded the fiber surfaces. The presence of the coating was also confirmed by Raman spectroscopy and FT/IR. The treatments reduced the stainability of the samples. The most effective applications for ensuring photocatalytic activity in cotton fabrics were suspensions as 10% brookite, 10% anatase and 5% anatase, in descending order. The applied coating slightly reduced the samples’ air permeability, and wear and tear strength.

The importance of this study is to determine the optimal crystal phase and its concentration by using epoxy silane to ensure self-cleaning properties on cotton fabrics. The sample treated with 10% brookite is the most approached its original white color by 99.65% as a result of degradation of MB (after 120 min). On the other hand, using the pure rutile with epoxy silane was not suitable for removing MB from the fabric.

This chapter offers an overview of the applications of artificial intelligence (AI) in the textile industry and in particular, the textile colouration and finishing industry. The advent of new technologies such as AI and the Internet of Things (IoT) has changed many businesses and one area AI is seeing growth in is the textile industry. It is estimated that the AI software market shall reach a new high of over US$60 billion by 2022, and the largest increase is projected to be in the area of machine learning (ML). This is the area of AI where machines process and analyse vast amount of data they collect to perform tasks and processes. In the textile manufacturing industry, AI is applied to various areas such as colour matching, colour recipe formulation, pattern recognition, garment manufacture, process optimisation, quality control and supply chain management for enhanced productivity, product quality and competitiveness, reduced environmental impact and overall improved customer experience. The importance and success of AI is set to grow as ML algorithms become more sophisticated and smarter, and computing power increases.

This study aims to evaluate the efficiency of using some polymers at different concentrations in the consolidation of vegetable-tanned leather artifacts.

New vegetable-tanned leather samples were prepared. The consolidants used were polyacrylamide (PAM) and polymethyl methacrylate/hydroxyethyl methacrylate (MMA-HEMA). Accelerated heat aging was applied to the untreated and treated samples. Analytical techniques used were Fourier transform infrared spectroscopy (FTIR), digital microscope, scanning electron microscope (SEM), change of color and mechanical properties.

The characteristic FTIR bands showed the effect of accelerated heat aging on the molecular structure of the studied samples, but treated and aged treated samples used were better than aged untreated samples. Microscopic investigations (digital and SEM), and mechanical properties proved that 2% was the best concentration for polymers used. The change in the total color difference of the treated and aged treated samples was limited.

This study presents the important results obtained from PAM and poly(MMA-HEMA) used for the consolidation of vegetable-tanned leather artifacts. The best results of the studied polymers can be applied directly to protect historical vegetable-tanned leathers.

The purpose of this study was to develop an environment-friendly finishing process for coloring and functionalizing fabrics using the extracts from aronia fruit (AF) and/or aronia leaf (AL).

Coloring and functional compounds were extracted from both AF and AL to prepare dyeing and finishing agents for textiles. The bioactive compounds were identified, and their concentrations were determined by spectrophotometry and high-performance liquid chromatography. The extracts were then used to dye and finish natural fibers. The cotton and wool fabrics treated with AF, AL and a combination of AF + AL extracts were investigated in terms of coloring properties and functionalities, specifically antioxidant capacity and antibacterial property.

According to the obtained results, AF extracts contained significant amounts of anthocyanins and phenols while AL extracts contained higher amounts of phenols with very low levels of anthocyanins. It was successfully demonstrated that the AF and AL extracts can be used to dye fabrics with good color properties. Moreover, textiles treated with aronia extracts inhibited the growth of gram-negative and gram-positive bacteria and exhibited antioxidant properties.

AF extract showed superior coloring and functional properties compared to AL extract. However, the treatment solution containing both AF and AL extracts demonstrated significant synergic effects on the antibacterial and antioxidant properties of the treated fabrics.

This study aims to assess the efficacy of nano-alumina (nano-Al₂O₃) in improving the performance of epoxy adhesives used to assemble archaeological glass. The conservators face a significant problem in assembling this type of artifact. Therefore, the assembling process is considered one of the important stages that must be taken care of to preserve these artifacts from damage and loss.

To evaluate the stability of adhesives, the samples were subjected to artificial aging under varying environmental conditions. Some investigative techniques and mechanical testing were used in this study to evaluate the selected materials. It includes a transmission electron microscope, X-ray diffraction, visual assessment, digital microscope, scanning electron microscopy (SEM), color change and tensile strength test.

The visual evaluation and the digital microscope results showed that the epoxy/nano-Al₂O₃ greatly resisted artificial aging. Although slight yellowing was present, it did not significantly affect the general appearance of the samples. On the other hand, the pure epoxy sample showed cracks of different sizes on its surface due to aging, as evidenced by SEM examination. Furthermore, epoxy/nano-Al₂O₃ has a better tensile strength (11.27 MPa) and slight color change (ΔE = 2.06).

The main objective of the experimental study was to identify appropriate adhesive materials that possess key properties such as non-yellowing and improved tensile strength by conducting various tests and evaluations. Ultimately, the goal was to identify materials that could serve as effective adhesives for assembling the archaeological glass.

Titanium(IV) oxide nanoparticles (TiO₂ NP) were deposited to cotton denim fabrics using a self-crosslinking acrylate – a polymer dispersion to extend the lifetime of the products. This study aims to determine the optimum conditions to increase abrasion resistance, to provide self-cleaning properties of denim fabrics and to examine the effects of these applications on other physical properties.

The denim samples were first treated with nonionic surfactant to increase their wettability. Three different amounts of the polymer dispersion and two different pH levels were selected for the experimental design. The finishing process was applied to the fabrics with pad-dry-cure method.

The presence of the coatings and the adhesion of TiO₂ NPs to the surfaces were confirmed by scanning electron microscope and Fourier transform infrared spectroscopy analysis. It was ascertained that the most appropriate self-crosslinking acrylate amount and ambient pH level is 10 mL and “2”, respectively, for providing increased abrasion resistance (2,78%) and enhanced self-cleaning properties (363,4%) in the denim samples. The coating reduced the air permeability and softness of the denim samples. Differential scanning calorimetry and thermogravimetry analysis results showed that the treatments increased the crystallization temperatures and melting enthalpy values of the denim samples. Based on the thermal test results, it is clear that mass loss of the denim samples at 370°C decreased as the amount of self-crosslinking acrylate increased (at pH 3).

This study helped us to find out optimum amount of self-crosslinking acrylate and proper pH level for enhanced self-cleaning and abrasion strength on denim fabrics. With this finishing process, an environmentally friendly and long-life denim fabric was designed.