The purpose of this paper is to check the feasibility of using biomaterial such as of Phragmites-Australis (PA) in cement paste to achieve sustainable building materials.

In this study, cement pastes were prepared by adding locally produced PA fibers in four different volumes: 0%, 0.5%, 1% and 2% for a duration of 180 days. Bottles and prisms were subjected to chemical shrinkage (CS), drying shrinkage (DS), autogenous shrinkage (AS) and expansion tests. Besides, prism specimens were tested for flexural strength and compressive strength. Furthermore, a mathematical model was proposed to determine the variation length change as function of time.

The experimental findings showed that the mechanical properties of cement paste were significantly improved by the addition of 1% PA fiber compared to other PA mixes. The effect of increasing the % of PA fibers reduces the CS, AS, DS and expansion of cement paste. For example, the addition of 2% PA fibers reduces the CS, expansion, AS and DS at 180 days by 36%, 20%, 13% and 10%, respectively compared to the control mix. The proposed nonlinear model fit to the experimental data is appropriate with R2 values above 0.92. There seems to be a strong positive linear correlation between CS and AS/DS with R2 above 0.95. However, there exists a negative linear correlation between CS and expansion.

The PA used in this study was obtained from one specific location. This can exhibit a limitation as soil type may affect PA properties. Also, one method was used to treat the PA fibers.

The utilization of PA fibers in paste may well reduce the formation of cracks and limit its propagation, thus using a biomaterial such as PA in cementitious systems can be an environmentally friendly option as it will make good use of the waste generated and enhance local employment, thereby contributing toward sustainable development.

To the authors best knowledge, there is hardly any research on the effect of PA on the volume stability of cement paste. Therefore, the research outputs are considered to be original.

This paper aims to develop a numerical, micromechanical model to predict the evolution of autogenous shrinkage of hydrating cement paste at early age (up to 7 days). Autogeneous shrinkage can be important in high-performance concrete characterized by low water to cement (w/c) ratios. The occurrence of this phenomenon during the first few days of hardening may result in early-age cracking in concrete structures. A good prediction of autogeneous shrinkage is necessary to achieve better understanding of the mechanisms and the deployment of effective measures to prevent early-age cracking.

Three-dimensional digital microstructures from the hydration modelling platform μic of cement paste were used to simulate macroscopic autogenous shrinkage based on the mechanism of capillary tension. Elastic and creep properties of the digital microstructures were calculated by means of finite element (FE) method homogenization. Autogenous shrinkage was then estimated as the average hydrostatic strain resulting from the capillary stress that was globally applied on the simulated digital microstructures. For this estimation, two approaches of homogenization technique, i.e. analytical poro-elasticity and numerical creep-superposition were used.

The comparisons of between the simulated and experimentally measured deformations indicate that the creep-superposition approach is more reasonable to estimate shrinkage at different water to cement ratios. It was found that better estimations could be obtained at low degrees of hydration, by assuming a loosely packed calcium silicate hydrates (C-S-H) growing in the microstructures. The simulation results show how numerical models can be used to upscale from microscopic characteristics of phases to macroscopic composite properties such as elasticity, creep and shrinkage.

While the good predictions of some cement paste properties from the microstructure at early age were obtained, the current models have several limitations that are needed to overcome in the future. Firstly, the limitation of pore-structure representation is not only from lack understanding of C-S-H structure but also from the computational complexity. Secondly, the models do not consider early-age expansion that usually happens in practice and appears to be superimposed on an underlying shrinkage as observed in experiments. Thirdly, the simplified assumptions for mechanical simulation do not accurately reflect the solid–liquid interactions in the real partially saturated system, for example, the globally applying capillary stress on the boundary of the microstructure to find the effective deformation, neglecting water flow and the pore pressure. Last but not least, the models, due to the computational complexities, use many simplifications such as FE approximation, mechanical phase properties and creep statistical data.

This study holistically tackles the phenomenon of autogeneous shrinkage through microstructural modelling. In a first such attempt, the authors have used the same microstructural model to simulate the microstructural development, elastic properties, creep and autogeneous shrinkage. The task of putting these models together was not simple. The authors have successfully handled several problems at each step in an elegant manner. For example, although several earlier studies have pointed out that discrete models are unable to capture the late setting times of cements due to mesh effects, this study offers the most effective solution yet on the problem. It is also the first time that creep and shrinkage have been modelled on a young evolving microstructure that is subjected to a time variable load.

This paper aims to present an approach for the numerical simulation of concrete shrinkage. First, some physical mechanisms of shrinkage are described and then the developed numerical model for the analysis of shrinkage of spatial three-dimensional structures using thermal analogy is presented. Results of the real behavior of structures because of concrete shrinkage using the developed numerical model are compared with the experimental and it is clearly shown that the developed numerical model is an efficient tool in predicting the time-dependent behavior of all concrete structures.

In this paper, Fib Model Code 2010 to predict shrinkage deformation of concrete is used, and it was incorporated in the three-dimensional numerical model using the thermal analogy. Mentioned three-dimensional numerical model uses the modified Rankine material law to describe concrete behavior in tension and modified Mohr-Coulomb material law to describe concrete behavior in compression. The developed three-dimensional numerical model successfully analyzes the behavior of reinforced and/or prestressed concrete structures including time-dependent deformations of concrete as well.

Results are shown in this paper clearly demonstrate the reliability of the developed numerical model in predicting the shrinkage strain, as well as its impact on concrete and reinforced concrete structures. The results obtained using the developed numerical model are in better agreement with the experimental results, than the results obtained using the numerical models from literature that also use the Fib Model Code 2010 to predict the shrinkage strain. So, it can be concluded that for a real simulation of concrete structures, alongside the model for predicting the shrinkage strain, the models for concrete behavior in tension and compression have a very important role.

Results of the developed three-dimensional numerical model were compared with experimental results from literature and with theoretical foundations, and it can be talked that this numerical model presents a good tool for analysis of reinforced and prestressed concrete structures including shrinkage deformation of concrete. Results obtained using the developed three-dimensional numerical model are better agreed with experimental than results of other numerical model from literature.

This study aims to address sustainability challenges in construction by exploring the structural performance and environmental benefits of incorporating pozzolanic waste glass (WG) into ultra-high-performance reinforced concrete (UHPRC) beams.

A comprehensive evaluation of UHPRC beams was conducted, incorporating varying ratios (10%, 20% and 30%) of WG powder alongside a consistent 0.75% inclusion of basalt fiber. The investigation encompassed the entire UHPRC production process, including curing, casting and molding, while evaluating workability and physical properties. Furthermore, the environmental impact, particularly CO₂ emissions associated with UHPRC mixture components, was also assessed. Type K thermocouples were employed to analyze temperature dynamics during fabrication, providing valuable insights.

The findings demonstrate positive implications for using pozzolanic WG as a cement substitute in UHPRC beams.

This research stands out for its unique focus on the combined effects of incorporating recycled pozzolanic glass waste on the structural performance and environmental footprint of UHPRC beams.

The purpose of this paper is to make a contribution to understanding the influence of factors such as the water/cement (W/C) ratio and the granular class on the mechanical and physical properties of high-strength concretes (HSCs). In the formulations of HSC, aggregates by their high mass and volume proportion play an important role. When selecting aggregates, it is necessary to know their intrinsic properties. These properties influence the performance of concrete, in particular the quality of the granulate cimentary adhesion.

This experimental study focused on the effect of W/C ratio (0.25, 0.30, 0.35), the effect of replacing a part of cement by silica fume (SF) (8%), the effect of fraction of aggregate on properties of fresh and hardened concrete, the effect of different environment conversation like drinking water and sea water on compressive strength and the study of absorption of water and softening using the mix design method of the University of Sherbrooke combined with the Dreux-Gorisse method which gives good results.

At the end of our work, the examination of the results obtained made it possible to establish the correlations between the formulations studied and the physicomechanical characteristics of the concrete compositions (HSC25, HSC16, HSC8). The results of this study show that the use of three granular classifications (DMAX8, DMAX16 and DMAX25) and three report W/C (0.25, 0.30 and 0.35) in two different conservation environment (drinking water and sea water) give HSCs, HSC25 with an W/C = 0.25 ratio has reached the largest mechanical strength of 90 MPa for different environments of conservation. For selecting aggregates, it is necessary to know their intrinsic properties, these properties influence the strength of concrete. In general, there is a slight decrease in the compressive resistance of the specimens stored in seawater, it can be said that the conservation life has not had effect on the resistance (28 days). The effect of aggressive environment can appear in the long term.

Mixed design and concrete fabrication with a 28-day compressive strength of up to 68 MPa or more of 90 MPa can now be possible used in Jiel (Algeria), and it should no longer be considered to be used only in an experimental domain. Addition of SF in concrete showed good development of strength between 7 and 28 days, depending on the design of the mix.

Concrete containing 8% SF with W/B of 0.25 has higher compressive strength than the other concretes, and concretes with SF are more resistant than concretes without SF, so it is possible to have concrete with a compressive strength of 82 MPa for W/C 0.25 without SF. Like as a result, we can avoid the use of SF to affect the strength of concrete at compressive strength of 68 MPa, and a slump of 21 cm, because the SF is the most expensive ingredient used in the composition of concrete and is therefore very important economically. One of the main factors of production of HSC above 90 MPa is use of aggregate DMAX25, which is stronger with W/B of 0.25 and 0.30.

This mixtures leads to a very dense microstructure and low porosity and produces increased permeability of HSC and is able to resist the penetration of aggressive agents. This combination has a positive effect on the economy of concrete.

The combination of the Dreux-Gorisse method with the Sherbrook method is very beneficial for determining the percentage of aggregates used, and the use of coarse aggregates of Jijel to obtain HSC with 90 MPa and 16 cm of workability.

The aim of this paper is to make lightweight high-performance concrete (LWHPC) with high economic performance from existing materials on the Algerian market. Concrete with high values with regard to following properties: mechanical, physical, rheological and durability. Because of the implementation of some basic scientific principles on the technology of LWHPC, this study is part of the valuation of local materials to manufacture LWHPC with several enhanced features such as mechanical, physical chemical, rheological and durability in the first place and with regard to the economic aspect in the second place.

The experimental study focused on the compatibility of cement/superplasticizer, the effect of water/cement ratio (W/C 0.22, 0.25, 0.30), the effect of replacing a part of cement by silica fume (8 per cent), the effect of combined replacement of a part of cement by silica fume (8 per cent) and natural pozzolan (10 per cent, 15 per cent, 25 per cent) and the effect of fraction of aggregate on properties of fresh and hardened concrete using the mix design method of the University of Sherbrooke, which is easy to realize and gives good results.

The results obtained allow to conclude that it is possible to manufacture LWHPC with good mechanical and physical properties in the authors’ town with available materials on the Algerian market. The mix design and manufacture of concrete with a compressive strength at 28 days reaching 56 MPa or more than 72 MPa is now possible in Biskra (Algeria), and it must no longer be used only in the experimental field. The addition of silica fume in concrete showed good strength development between the ages of 7 and 28 days depending on the mix design; concrete containing 8 per cent silica fume with a W/B (water/binder) of 0.25 has a compressive strength higher than other concretes, and concrete with silica fume is stronger than concrete without silica fume, so we can have concrete with a compressive strength of 62 MPa for W/C of 0.25 without silica fume. Then, one can avoid the use of silica fume to a resistance of concrete to the compressive strength of 62 MPa and a slump of 21 cm, as silica fume is the most expensive ingredient in the composition of the concrete and is very important economically. A main factor in producing high-strength concrete above 72 MPa is to use less reactive natural pozzolan (such as silica fume) in combination with silica fume and a W/B low of 0.25 and 0.30. The combination of silica fume and natural pozzolan in mixtures resulted in a very dense microstructure and low porosity and produced an enhanced permeability of concrete of high strength, as with resistance to the penetration of aggressive agents; thus, an economical concrete was obtained using this combination.

The study of the influence of cementitious materials on concrete strength gain was carried out. Other features of LWHPC such as creep, cracking, shrinkage, resistance to sulphate attack, corrosion resistance, fire resistance and durability should be also studied, because there are cases where another feature is most important for the designer or owner than the compressive strength at 28 days. Further studies should include a range of variables to change mixtures significantly and determine defined applications of LWHPC to produce more efficient and economical concretes. It is important to gather information on LWHPC to push forward the formulation of characteristics for pozzolan concrete for the building industry.

The LWHPC can be used to obtain high modules of elasticity and high durability in special structures such as marine structures, superstructures, parking, areas for aircraft/airplane runways, bridges, tunnels and industrial buildings (nuclear power stations).

The novel finding of the paper is the use of crystallized slag aggregates and natural pozzolan aggregates to obtain LWHPC.

This study aimed to review various existing methods for improving the quality of recycled concrete aggregates (RCAs) as a possible substitution for natural aggregates (NAs) in concrete. It is vital as the old paste attached to the RCA weakens its structure. It is due to the porous structure of the RCA with cracks, weakening the interfacial transition zone (ITZ) between the RCA and binding material, negatively impacting the concrete's properties. To this end, various methods for reinforcement of the RCA, cleaning the RCA's old paste and enhancing the quality of the RCA-based concrete without RCA modification are studied in terms of environmental effects, cost and technical matters. Furthermore, this research sought to identify gaps in knowledge and future research directions.

The review of the relevant journal papers revealed that various methods exist for improving the properties of RCAs and RCA-based concrete. A decision matrix was developed and implemented for ranking these techniques based on environmental, economic and technical criteria.

The identified methods for reinforcement of the RCA include accelerated carbonation, bio deposition, soaking in polymer emulsions, soaking in waterproofing admixture, soaking in sodium silicate, soaking in nanoparticles and coating with geopolymer slurry. Moreover, cleaning the RCA's old paste is possible using acid, water, heating, thermal and mechanical treatment, thermo-mechanical and electro-dynamic treatment. Added to these treatment techniques, using RCA in saturated surface dry (SSD) mixing approaches and adding fibres or pozzolana enhance the quality of the RCA-based concrete without RCA modification. The study ranked these techniques based on environmental, economic and technical criteria. Ultimately, adding fibres, pozzolana and coating RCA with geopolymer slurry were introduced as the best techniques based on the nominated criteria.

The study supported the need for better knowledge regarding the existing treatment techniques for RCA improvement. The outcomes of this research offer an understanding of each RCA enrichment technique's importance in environmental, economic and technical criteria.

The practicality of the RCA treatment techniques is based on economic, environmental and technical specifications for rating the existing treatment techniques.

The purpose of this work is to discuss high-strength concrete mix proportioning optimization. In this study, the three parameters (W/B ratio), coarse aggregate maximum size (D_max) and superplasticizer dosage (Sp%) were considered.

A full factorial design with three factors and two levels was carried out. The statistical analysis and analysis of variance of statistical models were made easier with the aid of JMP7 software. The generated models explain how each parameter affects the mechanical compressive strength at 28 days (Cs28) and slump, and they have an excellent determination coefficient (R² = 0.99). For each high-strength concrete (HSC) mixture, the slump was measured four times: at 0 min, 20 min, 40 min and 60 min.

The results show that HSC6 (0.35(W/B), 12.5(D_max), 1.4(Sp%)) is the best HSC mixture, with a (Cs28) of 71.84 MPa, a slump of 22 cm, and slump loss of 3.5 cm in 60 min.

Quantifying the impact of high-strength concrete mix components from a small number of experiments is made achievable by combining two methods: the Dreux-Gorisse method and the full factorial design approach. It's possible to tune the mix proportioning of the high-strength concrete for the desired slump and compressive mechanical strength thanks to the created statistical models.

This research paper adopts the fundamental tenets of advanced technologies in industry 4.0 to monitor the structural health of concrete beam members using cost-effective non-destructive technologies. In so doing, the work illustrates how a coalescence of low-cost digital technologies can seamlessly integrate to solve practical construction problems.

A mixed philosophies epistemological design is adopted to implement the empirical quantitative analysis of “real-time” data collected via sensor-based technologies streamed through a Raspberry Pi and uploaded onto a cloud-based system. Data was analysed using a hybrid approach that combined both vibration-characteristic-based method and linear variable differential transducers (LVDT).

The research utilises a novel digital research approach for accurately detecting and recording the localisation of structural cracks in concrete beams. This non-destructive low-cost approach was shown to perform with a high degree of accuracy and precision, as verified by the LVDT measurements. This research is testament to the fact that as technological advancements progress at an exponential rate, the cost of implementation continues to reduce to produce higher-accuracy “mass-market” solutions for industry practitioners.

Accurate structural health monitoring of concrete structures necessitates expensive equipment, complex signal processing and skilled operator. The concrete industry is in dire need of a simple but reliable technique that can reduce the testing time, cost and complexity of maintenance of structures. This was the first experiment of its kind that seeks to develop an unconventional approach to solve the maintenance problem associated with concrete structures. This study merges industry 4.0 digital technologies with a novel low-cost and automated hybrid analysis for real-time structural health monitoring of concrete beams by fusing several multidisciplinary approaches into one integral technological configuration.

The purpose of this paper is to develop an alternative new ternary geopolymer mortar (MKSP) to resolve a traditional mortar problem which exhibits several disadvantages, including poor strengths and surface microcracks and the CO₂ air pollution.

The MKSP ternary binder was produced using metakaolin (MK), slag (S), and palm oil fuel ash (POFA) activated with an alkaline mixture of sodium silicate (Na₂SiO₃) and 10 M NaOH in a mass ratio of 2.5. Seven different mix proportions of MK, slag, and POFA were used to fabricate MKSP mortars. The water-to-binder ratio was varied between 0.4 and 0.5. The mortars were heat cured for 2 h at 80°C and then aged in air. Flexural stress and strain, mortars flow and compressive strength were tested. Furthermore, the mortars were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) analyses.

The results showed that the sample MKSP6, which contained 40 percent MK, 40 percent slag, and 20 percent POFA, exhibited high compressive strength (52 MPa) without any cracks and flexural strength (6.9 MPa) at 28 days after being cured for 2 h at 80°C; however, the MKSP7 mortar with optimal strength of 55 MPa showed some surface cracks . Further, the results of the XRD, SEM, and FTIR analyses indicated that the MKSP mortars primarily consisted of a crystalline (Si+Al) phase (70 percent) and a smaller amorphous (Si+Ca) phase (30 percent).

The MKSP ternary geopolymer mix has three limitations as an importance of heat curing for development early strength, POFA content less than 20 percent to gain high normal strength and delaying the sitting time by controlling the slag content or the alkali activator type.

The use of geopolymer materials binder in a real building is limited and it still under research, Thus, the first model of real applied geopolymer cement in 2008 was the E-Crete model that formed by Zeobond company Australia to take the technology of geopolymer concrete to reality. Zeobond Pty Ltd was founded by Professor Jannie S.J. van (van Deventer et al., 2013), it was used to product precast concrete for the building structure. The second model was PYRAMENT model in 2002 by American cement manufacturer Lone Star Industries which was produced from the development carried out on inorganic alumino-silicate polymers called geopolymer (Palomo et al., 1999). In 2013 the third model was Queensland’s University GCI building with three suspended floors made from structural geopolymer concrete containing slag/fly ash-based geopolymer (Pathak, 2016). In Australia, 2014, the newly completed Brisbane West Wellcamp airport becomes the greenest airport in the world. Cement-free geopolymer concrete was used to save more than 6,600 tons of carbon emissions in the construction of the airport. Therefore, the next century will see cement companies developing alternative binders that are more environmentally friendly from a sustainable development point of view.

Production of new geopolymer binder of mortar as alternative to traditional cement binder with high early and normal strength from low cost waste materials, less potential of cracking, less energy consumption need and low carbon dioxide emission.