The purpose of this paper is to obtain a theoretical model to analyze the effective modulus of cement paste in early age, including the setting and hardening periods, which has a great impact on mechanical properties of concrete structure.

Based on a power law approximation, a generalized mixture rule is used to construct the relationship between the effective modulus and hydration degree. In addition, a new model of the dependence of the Poisson's ratio on the hydration degree and water cement ratio is proposed for cement paste in early age.

The effective Young's modulus, storage shear modulus and Poisson's ratio of cement pastes with different water cement ratios and hydration degrees are studied by the presented model. The model can be applied to simulate the behavior of early-age cement paste at both the setting and the hardening periods. Compared with the experimental results, the correctness of the model is validated.

This work presents a mathematical model that can effectively estimate the effective Young's modulus and Poisson's ratio in the hardening period, and the storage shear modulus in the setting period of cement pastes.

This paper aims to develop a numerical, micromechanical model to predict the evolution of autogenous shrinkage of hydrating cement paste at early age (up to 7 days). Autogeneous shrinkage can be important in high-performance concrete characterized by low water to cement (w/c) ratios. The occurrence of this phenomenon during the first few days of hardening may result in early-age cracking in concrete structures. A good prediction of autogeneous shrinkage is necessary to achieve better understanding of the mechanisms and the deployment of effective measures to prevent early-age cracking.

Three-dimensional digital microstructures from the hydration modelling platform μic of cement paste were used to simulate macroscopic autogenous shrinkage based on the mechanism of capillary tension. Elastic and creep properties of the digital microstructures were calculated by means of finite element (FE) method homogenization. Autogenous shrinkage was then estimated as the average hydrostatic strain resulting from the capillary stress that was globally applied on the simulated digital microstructures. For this estimation, two approaches of homogenization technique, i.e. analytical poro-elasticity and numerical creep-superposition were used.

The comparisons of between the simulated and experimentally measured deformations indicate that the creep-superposition approach is more reasonable to estimate shrinkage at different water to cement ratios. It was found that better estimations could be obtained at low degrees of hydration, by assuming a loosely packed calcium silicate hydrates (C-S-H) growing in the microstructures. The simulation results show how numerical models can be used to upscale from microscopic characteristics of phases to macroscopic composite properties such as elasticity, creep and shrinkage.

While the good predictions of some cement paste properties from the microstructure at early age were obtained, the current models have several limitations that are needed to overcome in the future. Firstly, the limitation of pore-structure representation is not only from lack understanding of C-S-H structure but also from the computational complexity. Secondly, the models do not consider early-age expansion that usually happens in practice and appears to be superimposed on an underlying shrinkage as observed in experiments. Thirdly, the simplified assumptions for mechanical simulation do not accurately reflect the solid–liquid interactions in the real partially saturated system, for example, the globally applying capillary stress on the boundary of the microstructure to find the effective deformation, neglecting water flow and the pore pressure. Last but not least, the models, due to the computational complexities, use many simplifications such as FE approximation, mechanical phase properties and creep statistical data.

This study holistically tackles the phenomenon of autogeneous shrinkage through microstructural modelling. In a first such attempt, the authors have used the same microstructural model to simulate the microstructural development, elastic properties, creep and autogeneous shrinkage. The task of putting these models together was not simple. The authors have successfully handled several problems at each step in an elegant manner. For example, although several earlier studies have pointed out that discrete models are unable to capture the late setting times of cements due to mesh effects, this study offers the most effective solution yet on the problem. It is also the first time that creep and shrinkage have been modelled on a young evolving microstructure that is subjected to a time variable load.

Timely removal of formwork is one of the crucial aspects of construction management that directly influences the safety and quality of the structure as well as the economy of the project. Code recommendations in this regard are not widely practiced because of the difficulties in their implementations. Also, such code recommendations are not robust for all the possible construction conditions. The present paper proposes an IoT-enabled system that notifies the minimum striking time of vertical formwork based on a specified target compressive strength.

An IoT device is proposed for the timely removal of vertical formwork by monitoring of early age concrete compressive strength in real-time. The maturity method is utilized for this purpose. The implementation of the proposed system is demonstrated on three concrete columns. The proposed system is found to be suitable for any construction condition.

The proposed system is a novel, cost-effective, IoT-enabled real-time monitoring system which includes features like cloud connectivity and remote monitoring. This system can be easily implemented at the site without any human intervention.

The study explores the development of an IoT device for the timely removal of vertical formwork which will ensure quality, safety and productivity in concrete construction.

This paper is the first attempt to determine the minimum striking time of vertical formwork using IoT-based technology.

Self-healing concrete is a revolutionary building material that will generally reduce the maintenance cost of concrete constructions. Self-healing of cracks in concrete structure would contribute to a longer service life of the concrete and would make the material more durable and more sustainable. The cementitious mortar with/without incorporating encapsulates at different percentages of slag replacement with the cement mix improves autogenous healing at different ages. Therefore, this study’s aim is to develop a self-healing cementitious matrix for repair and retrofitting of concrete structures.

In the present work, waste straw pipes are used as a capsule, filled with the solution of sodium hydroxide (NaOH), sodium silicate (Na₂SiO₃) and colloidal nano-silica as self-healing activators. An artificial micro-crack on the control and blended mortar specimens at different percentages of slag replacement with cement (with/without encapsulation) is developed by applying a compressive load of 50% of its ultimate load-carrying capacity. The mechanical strength and ultrasonic pulse velocity, water absorption and chloride ion penetration test are conducted on the concrete specimen before and after the healing period. Finally, the self-healing activity of mortar mixes with/without encapsulation is analysed at different ages.

The encapsulated mortar mix with 10% of slag content has better self-healing potential than all other mixes considering mechanical strength and durability. The enhancement of the self-healing potential of such mortar mix is mainly due to hydration of anhydrous slag on the crack surface and transformation of amorphous slag to the crystalline phase in presence of encapsulated fluid.

The self-healing activities of the slag-based cementitious composite are studied for a healing period of 90 days only. The strength and durability performance of the cracked specimen may be increased after a long healing period.

The outcome of the work will help repair the cracks in the concrete structure and enhances the service life.

This study identifies the addition encapsulates with a self-healing activator fluid that can recover its strength after minor damage.

Social economics[l] is a small but growing school of thought in the United States. At first sight it appears as if “social economists” are a rather heterogeneous group defying satisfactory description. Yet we believe that there is a unity of focus: a deep concern with human needs rather than just a description of human preferences being co‐ordinated. We define “needs” as “necessary” wants and immediately the question imposes itself: necessary for what? Our answer is human life with its higher or lower qualities. Social economics seeks not only to enable and maintain life, but also to “enlarge” it and fulfil it. As a direct result values are hierarchical, from the lower (survival) values to the highest (ethical, aesthetic) values. Such is implicit in the generally acknowledged human‐values‐orientation of the field, since values can be seen as need satisfiers.

This study aims on a broad review of Concrete's Rheological Properties. The Concrete is a commonly used engineering material because of its exquisite mechanical interpretation, but the addition of constituent amounts has significant effects on the concrete’s fresh properties. The workability of the concrete mixture is a short-term property, but it is anticipated to affect the concrete’s long-term property.

In this review, the concrete and workability definition; concrete’s rheology models like Bingham model, thixotropy model, H-B model and modified Bingham model; obtained rheological parameters of concrete; the effect of constituent’s rheological properties, which includes cement and aggregates; and the concrete’s rheological properties such as consistency, mobility, compatibility, workability and stability were studied in detail.

Also, this review study has detailed the constituents and concrete’s rheological properties effects. Moreover, it exhibits the relationship between yield stress and plastic viscosity in concrete’s rheological behavior. Hence, several methods have been reviewed, and performance has been noted. In that, the abrasion resistance concrete has attained the maximum compressive strength of 73.6 Mpa; the thixotropy approach has gained the lowest plastic viscosity at 22 Pa.s; and the model coaxial cylinder has recorded the lowest stress rate at 8 Pa.

This paper especially describes the possible strategies to constrain improper prediction of concrete’s rheological properties that make the workability and rheological behavior prediction simpler and more accurate. From this, future guidelines can afford for prediction of concrete rheological behavior by implementing novel enhancing numerical techniques and exploring the finest process to evaluate the workability.

The multi-scale numerical simulation method, able to represent the complexity of the random structures and capture phase degradation, is an effective way to investigate the long-term behavior of concrete in service and bridges the gap between research on the material and on the structural level. However, the combined chemical-physical deterioration mechanisms of concrete remain a challenging task. The purpose of this paper is to investigate the degradation mechanism of concrete at the waterline in cold regions induced by combined calcium leaching and frost damage.

With the help of the NIST’s three-dimensional (3D) hydration model and the random aggregate model, realistic 3D representative volume elements (RVEs) of concrete at the micro-, the meso-, and the macro-scales can be reconstructed. The boundary problem method is introduced to compute the homogenized mechanical properties for both sound and damaged RVEs. According to the damage characteristics, the staggering method including a random dissolution model and a thermo-mechanical coupling model is developed to simulate the synergy deterioration effects of interacted calcium leaching and frost attacks. The coupled damage procedure for the frost damage process is based on the hydraulic pressure theory and the ice lens growth theory considering the relationship between the frozen temperature and the radius of the capillary pore. Finally, regarding calcium leaching as the leading role in actual engineering, the numerical methodology for combined leaching and frost damage on concrete property is proposed using a successive multi-scale method.

On the basis of available experimental data, this methodology is employed to explore the deterioration process. The results agree with the experimental ones to some extent, chemical leaching leads to the nucleation of some micro-cracks (i.e. damage), and consequently, to the decrease of the frost resistance.

It is demonstrated that the multi-scale numerical methodology can capture potential aging and deterioration evolution processes, and can give an insight into the macroscopic property degradation of concrete under long-term aggressive conditions.

This research aims to study the influence of limestone filler on rebar corrosion.

Mortar samples containing 35% calcareous filler and with a rebar inserted in the axis, were cast. Specimens were cured at the open air and during 28 days in lime water. After curing, they were submerged in two electrolytes (tap water and 3% NaCl) and corrosion parameters (corrosion potential and corrosion current) were monitored over time by d.c. techniques. Simultaneously, electrochemical noise measurements were carried out. After corrosion tests, rebars were pulled out by lateral compression, and their surface observed by scanning electron microscopy.

In general, carbonate additions impaired mortar protective properties, especially in the presence of chloride and changed the nature of the protective layer on rebars. The curing process did not introduce significant differences except for mortars with a high water cement ratio cured in lime water for which the beneficial effects of the simultaneous presence of carbonate and lime in the pore solution could be appreciated. The role of carbonate additions is to provide carbonate anions to passivate rebars. This passivation process caused corrosion rates not to be so high. Carbonate anions also deposited on oxide spots which were rendered passive but this process was not uniform. Certain areas on the rebar underwent intense carbonation while others showed increased corrosion rates.

There are not many corrosion studies about the influence of limestone filler on rebars corrosion. Particularly, this paper deals with mortars containing high percentages of carbonate additions. Results showed that the presence of this type of admixture changes the structure of the passive layer and, sometimes, may increase corrosion rates.

This study aims to focus on the resistance to elevated temperatures of up to 700ºC of high-performance concrete (HPC) compared to ordinary Portland concrete (OPC) with regards to mass loss and residual compressive and flexural strength.

Two mixtures were developed to test. The first mixture, OPC, was used as the control, and the second mixture was HPC. After 28 days under water (per Chinese standard), the samples were tested for compressive strength and residual strength.

The test results showed that at elevated temperatures of up to 500ºC, each mixture experienced mass loss. Below this temperature, the strength and the mass loss did not differ greatly.

When adding a 10 per cent silica fume, 25 per cent fly, 25 per cent slag to HPC, the compressive strength increased by 17 per cent and enhanced the residual compressive strength. A sharp decrease was observed in the residual flexural strength of HPC when compared to OPC after exposure to temperatures of 700ºC.

Polyurethane concrete has a high strength-to-weight ratio in the short term, and the strength-to-weight ratio stage during the maintenance period is critical. Freeze-thaw cycles have a noticeable damaging effect on the durability of polyurethane concrete. The engineering specification of polyurethane concrete with incomplete hydration reaction must be studied, as well as the development of internal structure during curing. In this paper, the polyurethane concrete tests were set up under eight distinct maintenance settings based on the climate features of the northern area and the service environment. The test results were evaluated to determine the effect of the number of early freeze-thaw cycles and the time node of early freeze-thaw cycles on the mechanical characteristics of polyurethane concrete, which revealed that the time node of freeze-thaw damage impacted the freeze-thaw resistance of polyurethane concrete susceptible to early freeze-thaw damage.

The early-age freeze-thaw damage polyurethane concrete was experimentally studied by controlling the time node of the freeze-thaw cycle and the curing environment. The test considered the time node, frequency of freeze-thaw damage of polyurethane concrete and the influence of subsequent curing environment and observed the mass change, relative dynamic elastic modulus, relative durability index, compressive strength and apparent damage of polyurethane concrete. The early mechanical properties of polyurethane concrete were studied by analyzing the change of numerical value. The microscopic mechanism of strength formation of polyurethane concrete was analyzed by XRD, FTIR and SEM image.

The closer the time of freeze-thaw damage was to the specimen hardening, the worse the mechanical properties and structure were, according to SEM photographs. For specimens with serial number of 12-groups, its compressive strength is only 82.39% of that of the standard group, even if the curing process continues after 20 times thawing, which increased early environment exacerbate strength loss in polyurethane concrete and also reduced freeze-thaw resistance. The findings of the tests reveal that curing can restore the freeze-thaw resistance of damaged polyurethane concrete. Curing in water has a better recovery impact than curing in air; the mechanical properties can be restored by sufficient re-curing time and good re-curing conditions.

By studying the freeze-thaw cycle test and test results of polyurethane concrete in different curing time nodes, the relationship between the mechanical properties of polyurethane concrete and the time node, number of freeze-thaw cycles, and subsequent maintenance environment was explored. Considering the special mechanism of strength formation of polyurethane concrete, the polyurethane concrete damaged by freeze-thaw has the ability to continue to form strength under subsequent maintenance. This experimental study can provide an analytical basis for the strength formation and reconditioning of polyurethane concrete structures subjected to freeze-thaw environments during the curing time under extreme natural conditions in fall and winter in actual projects.