The purpose of this paper is to develop an alternative new ternary geopolymer mortar (MKSP) to resolve a traditional mortar problem which exhibits several disadvantages, including poor strengths and surface microcracks and the CO₂ air pollution.

The MKSP ternary binder was produced using metakaolin (MK), slag (S), and palm oil fuel ash (POFA) activated with an alkaline mixture of sodium silicate (Na₂SiO₃) and 10 M NaOH in a mass ratio of 2.5. Seven different mix proportions of MK, slag, and POFA were used to fabricate MKSP mortars. The water-to-binder ratio was varied between 0.4 and 0.5. The mortars were heat cured for 2 h at 80°C and then aged in air. Flexural stress and strain, mortars flow and compressive strength were tested. Furthermore, the mortars were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) analyses.

The results showed that the sample MKSP6, which contained 40 percent MK, 40 percent slag, and 20 percent POFA, exhibited high compressive strength (52 MPa) without any cracks and flexural strength (6.9 MPa) at 28 days after being cured for 2 h at 80°C; however, the MKSP7 mortar with optimal strength of 55 MPa showed some surface cracks . Further, the results of the XRD, SEM, and FTIR analyses indicated that the MKSP mortars primarily consisted of a crystalline (Si+Al) phase (70 percent) and a smaller amorphous (Si+Ca) phase (30 percent).

The MKSP ternary geopolymer mix has three limitations as an importance of heat curing for development early strength, POFA content less than 20 percent to gain high normal strength and delaying the sitting time by controlling the slag content or the alkali activator type.

The use of geopolymer materials binder in a real building is limited and it still under research, Thus, the first model of real applied geopolymer cement in 2008 was the E-Crete model that formed by Zeobond company Australia to take the technology of geopolymer concrete to reality. Zeobond Pty Ltd was founded by Professor Jannie S.J. van (van Deventer et al., 2013), it was used to product precast concrete for the building structure. The second model was PYRAMENT model in 2002 by American cement manufacturer Lone Star Industries which was produced from the development carried out on inorganic alumino-silicate polymers called geopolymer (Palomo et al., 1999). In 2013 the third model was Queensland’s University GCI building with three suspended floors made from structural geopolymer concrete containing slag/fly ash-based geopolymer (Pathak, 2016). In Australia, 2014, the newly completed Brisbane West Wellcamp airport becomes the greenest airport in the world. Cement-free geopolymer concrete was used to save more than 6,600 tons of carbon emissions in the construction of the airport. Therefore, the next century will see cement companies developing alternative binders that are more environmentally friendly from a sustainable development point of view.

Production of new geopolymer binder of mortar as alternative to traditional cement binder with high early and normal strength from low cost waste materials, less potential of cracking, less energy consumption need and low carbon dioxide emission.

In recent years, fire accidents in engineering structures have often been reported worldwide, leading to a severe risk to life and property safety. The present study is carried out to evaluate the performance of Ground Granulated Blast Furnace Slag (GGBS) and fly ash–blended laterized mortars at elevated temperatures.

This test program includes the replacement of natural river sand with lateritic fine aggregates (lateritic FA) in terms of 0, 50 and 100%. Also, the ordinary Portland cement (OPC) was replaced with fly ash and GGBS in terms of 10, 20, 30% and 20, 40 and 60%, respectively, for producing blended mortars.

This paper presents results related to the determination of residual compressive strengths of lateritic fine aggregates-based cement mortars with part replacement of cement by fly ash and GGBS exposed to elevated temperatures. The effect of elevated temperatures on the physical and mechanical properties was evaluated with the help of microstructure studies and the quantification of hydration products.

A sustainable cement mortar was produced by replacing natural river sand with lateritic fine aggregates. The thermal strength deterioration features were assessed by exposing the control specimens and lateritic fine aggregates-based cement mortars to elevated temperatures. Changes in the mechanical properties were evaluated through a quantitative microstructure study using scanning electron microscopy (SEM) images. The phase change of hydration products after exposure to elevated temperatures was qualitatively analyzed by greyscale thresholding of SEM images using Image J software.

The purpose of the paper is to explore the structural feasibility of substituting traditional thick joint mortars with earth slurry mortars modified with varying amounts of sand. Thin jointing of earth blocks would reduce the cost of sustainable earth construction.

Compressive strength of earth‐block cubes was determined. Flexural strength was measured using the BRE electronic bond wrench, which enables block couplets to be tested quickly and accurately. Three samples of earth block, one from southwest England and two from East Anglia, together with nine examples of earth slurry mortar jointing were studied, including the effect of reinforcing the joint and or the block using hessian.

The 28‐day cube characteristic compressive strengths were determined for Appley soil, Norfolk lump and Beeston soil, the last with 0 per cent sand, 25 per cent sand and with 25 per cent sand with hessian. The flexural strengths of Appley and Beeston earth slurries were determined, along with Thermalite thin jointed cement and cement mortar for comparison. The Beeston soil flexural strength increased with increasing sand content. Earth slurry with 40 per cent sand and hessian present in the joint gave the greatest strength. It is important to use blocks and slurry mortars of the same soil. Extruded and compressed earth blocks are best suited to slurry jointing.

This work successfully demonstrates the structural feasibility of carefully reducing the thickness of earth mortars when constructing sustainable earth block walling. Characteristic flexural strengths are suggested where the test results were sufficiently consistent, and of a magnitude likely to be useful in design.

A study on the mechanical characteristics of cementitious mortar reinforced with basalt fibres at ambient and elevated temperatures was carried out. To investigate their effect, chopped basalt fibres with varying percentages were added to the cement mortar.

All the specimens were heated using a muffle furnace. Flexural strength and Compressive strength tests were performed, while monitoring the moisture loss to evaluate the performance of basalt fibre reinforced cementitious mortars at elevated temperatures.

From the study, it is clear that basalt fibres can be used to reinforce mortar as the fibres remain unaffected up to 500 °C. Minimal increases in flexural strengths and compressive strengths were measured with the addition of basalt fibres at both ambient and elevated temperatures. SEM pictures revealed fibre matrix interaction/degradation at different temperatures.

The current study shows the potential of basalt fibre addition in mortar as a reinforcement mechanism at elevated temperatures and provides experimental quantifiable mechanical performances of different fibre percentage addition.

The purpose of this paper is to investigate the influence of cement/sand ratio on behaviour of cement mortar.

Literature review was used to confirm that the cement/sand ratio have influence on the mortar strength and that its influence is not very studied. The literature points out also that the constitutive model of mortar is very important in the structural design of masonry but it has not been investigated much.

The results of study allow to forecast the mortar strength by the cement/sand ratio when the water/cement ratio is fixed (0.50). Besides, the obtained experimental results allow defining a constitutive model for sand mortar.

Other experiments would be proper to extend the research field.

The findings are of particular importance to mix design of cement mortar and to structural design of masonry. In fact, for mortar in the practices, there are no constitutive equations to use in the structural calculation, and so, normally the engineers use the constitutive equations of concrete (very rough). The idea is to find constitutive equations that, using simple and economic tests, allow to engineers to model more correctly the realty.

There are few studies which try to investigate the relationship between the behaviour of cement mortar and cement/sand ratio, as well as to study constitutive model of cement mortar. This paper contributes to bridging that gap.

Material properties, such as shear and compressive strength of masonry, have a crucial impact on the seismic analysis results of masonry structures. Considering that most of the historical buildings are masonry structures, the damage caused by obtaining shear strengths with known methods exceeds acceptable limits. Instead of traditional shear strength index tests, this paper presents a test technique that has been developed which causes less damage to the structure, to obtain mechanical properties in masonry structures.

A new approach to shear testing and a test probe has been developed to minimize the destructive effects of mechanical in situ testing on masonry structures. The comparison of the results obtained with reduced destruction level using the novel shear strength index test probe with those obtained from the traditional method is addressed. Masonry specimens were tested in the laboratory and in situ tests were carried out on 12 historical buildings.

Test results obtained from the proposed probe shear strength index test were consistent with the results obtained from the conventional shear strength test both at the laboratory setting and in situ. Although a large number of data is needed for the validation of a method, satisfactory agreement with the conventional shear strength index test method was obtained.

The authors believe that the proposed method would give the opportunity to collect more mechanical strength data with much less destruction. The experimental work in the laboratory and in situ tests and their comparisons are the supportive and original values of this research.

This study aims to investigate the properties of mortar made from a bottom ash substitute as a sustainable construction material. It is believed that the use of cement in concrete construction contributes to the release of carbon dioxide into the atmosphere, which has been a consistent increase in recent years. The utilization of bottom ash waste is expected to reduce pollution associated with cement production.

Bottom ash is used as replacement materials for cement and fine aggregate in the manufacture of mortar. Bottom ash substituted for cement of 10%, 20% and 30% of the total weight of the binder, whereas bottom ash substituted for the fine aggregate of 30%, 40% and 50% of the total weight of the sand. Binder properties were determined using scanning electron microscopy and energy dispersive X-ray. Meanwhile, the fresh properties (slump flow) and hardened properties were determined (compressive strength and mass density). In the hardened properties test, two types of curing were used: water and sealed curing.

The compressive strength of mortar decreased as the amount of bottom ash as cement replacement. However, the compressive strength increased when bottom ash was used as aggregate replacement. Additionally, bottom ash was sufficient as a substitute for fine aggregate than as a substitute for cement.

This research presents test results that are more straightforward to apply in the construction site.

The purpose of this research is using materials to improve the thermal insulation, and reducing the cost. A large amount of energy is consumed by masonary due to cooling and heating. Adding material with certain percentages to the building materials is one of the ways to improve the thermal insulation, and these additives should keep as much as possible the mechanical properties of the building materials. Carbon additives are one of commonly used materials to masonry materials. In spite of the many advantages of using carbon fibers and carbon nano tubes (CNTs) to the cementitious materials, they are very expansive and their thermal conductivity is high.

In this research charcoal (which is a product of burning process) with very low thermal conductivity and cost in the form of micro particles will be used with mortar and compared with short carbon fibers and multiwall carbon nanotubes (MWCNTs) via thermal conductivity, density and compressive strength tests. This research includes also an effort to build a model of building to evaluate the thermal insulation of the materials used in the practical part. The main building design and performance simulation tool in this research is DesignBuilder.

Results showed that adding micro charcoal particles to mortar resulted in improving the thermal insulation and decrease the rate of reduction in the compressive strength compared to other additives, while adding short carbon fibers resulted in improving the thermal insulation and decrease the compressive strength. Adding MWCNT to the mortar had a negative effect on mechanical and physical properties, i.e. compressive strength, density and thermal insulation.

This paper uses DesignBuilder software to design a model of building made from the materials used in the practical part to predict and evaluate the thermal insulation.

During the construction process of the China Railway Track System (CRTS) I type filling layer, the nonwoven fabric bags have been used as grouting templates for cement asphalt (CA) emulsified mortar. The porous structure of nonwoven fabrics endowed the templates with breathability and water permeability. The standard requires that the volume expansion rate of CA mortar must be controlled within 1%–3%, which can generate expansion pressure to ensure that the cavities under track slabs are filled fully. However, the expansion pressure caused some of the water to seep out from the periphery of the filling bag, and it would affect the actual mix proportion of CA mortar. The differences in physical and mechanical properties between the CA mortar under track slabs and the CA mortar formed in the laboratory were studied in this paper. The relevant results could provide important methods for the research of filling layer materials for CRTS I type and other types of ballastless tracks in China.

During the inspection of filling layer, the samples of CA mortar from different working conditions and raw materials were taken by uncovering the track slabs and drilling cores. The physical and mechanical properties of CA mortar under the filling layer of the slab were systematically analyzed by testing the electrical flux, compressive strength and density of mortar in different parts of the filling layer.

In this paper, the electric flux, the physical properties and mechanical properties of different parts of CA mortar under the track slab were investigated. The results showed that the density, electric flux and compressive strength of CA mortar were affected by the composition of raw materials for dry powders and different parts of the filling layer. In addition, the electrical flux of CA mortar gradually decreased within 90 days’ age. The electrical flux of samples with the thickness of 54 mm was lower than 500 C. Therefore, the impermeability and durability of CA mortar could be improved by increasing the thickness of filling layer. Besides, the results showed that the compressive strength of CA mortar increased, while the density and electric flux decreased gradually, with the prolongation of hardening time.

During 90 days' age, the electrical flux of the CA mortar gradually decreased with the increase of specimen thickness and the electrical flux of the specimens with the thickness of 54 mm was lower than 500 C. The impermeability and durability of the CA mortar could be improved by increasing the thickness of filling layer. The proposed method can provide reference for the further development and improvement of CRTS I and CRTS II type ballastless track in China.

With respect to the studies conducted so far and lack of researches on the post-heat behavior of cement mortars containing pozzolanic materials, the purpose of this paper is to investigate the post-heat mechanical characteristics (i.e. compressive, tensile and flexural strength) of cement mortars containing granulated blast-furnace slag (GBFS) and silica fume (SF). In doing so, selected temperatures include 25, 100, 250, 500, 700 and 9000c. Last, the X-ray diffraction test was conducted to study the microstructure of mixtures and subsequently, the results were presented as power-one mathematical relations.

Totally, 378 specimens were built to conduct flexural, compressive and tensile strength tests. Accordingly, these specimens include cubic and prismatic specimens with dimensions of 5 × 5 × 5 cm and 16 × 4 × 4 cm, respectively, to conduct compressive and flexural strength tests together with briquette specimen used for tensile strength test in which cement was replaced by 7, 14 and 21 per cent of SF and GBFS. To study the effect of temperature, the specimens were heated. In this respect, they were heated with a rate of 5°C/min and exposed to temperatures of 25 (ordinary temperature), 100, 250, 500, 700 and 900°C.

On the basis of the results, the most profound effect of using GBFS and SF, respectively, takes place in low (up to 250°C) and high (500°C and greater degrees) temperatures. Quantitatively, the compressive, tensile and flexural strengths were enhanced by 73 and 180 per cent, 45 and 100 per cent, 106 and 112 per cent, respectively, in low and high temperatures. In addition, as the temperature elevates, the particles of specimens containing SF and GBFS shrink less in size compared to the reference specimen.

The specimens were cured according to ASTMC192 after 28 days placement in the water basin. First, in compliance with what has been specified by the mix design, the mortar, including pozzolanic materials and superplasticizer, was prepared and then, the sampling procedure was conducted on cubic specimens with dimension of 5 × 5 × 5 mm for compressive strength test, prismatic specimens with dimensions of 16 × 4 × 4 mm for flexural strength test and last, briquette specimens were provided to conduct tensile strength tests (for each temperature and every test, three specimens were built).