1 – 10 of 162Ronnarit Khuengpukheiw, Anurat Wisitsoraat and Charnnarong Saikaew
This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr3C2–Ni coatings on…
Abstract
Purpose
This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr3C2–Ni coatings on AISI 1095 steel with spraying times of 10 and 15 s.
Design/methodology/approach
In this study, the pin-on-disc testing technique was used to evaluate the wear characteristics at a speed of 0.24 m/s, load of 40 N and test time of 60 min under dry conditions at room temperature. The wear characteristics were examined and analyzed by scanning electron microscopy and energy dispersive X-ray spectroscopy. The surface roughness of a coated surface was measured, and microhardness measurements were performed on the cross-sectioned and polished surfaces of the coating.
Findings
Spraying time and powder material affected the hardness of HVOF coatings due to differences in the porosity of the coated layers. The average hardness of the WC–Cr3C2–Ni coating with a spaying time of 15 s was approximately 14% higher than that of the WC–Cr3C2–Ni coating with a spraying time of 10 s. Under an applied load of 40 N, the WC–Co coating with a spraying time of 15 s had the lowest variation in the friction coefficient compared with the other coatings. The WC–Co coating with a spraying time of 10 s had the lowest average and variation in volume loss compared to the other coatings. The WC–Cr3C2–Ni coating with a spraying time of 10 s exhibited the highest average volume loss. The wear features changed slightly with the spraying time owing to variations in the hardness and friction coefficient.
Originality/value
This study investigated tribological performance of WC–Co; WC-Cr3C2-Ni coatings with spraying times of 10 and 15 s using pin-on-disc tribometer by rotating the relatively soft pin (C45 steel) against hard coated substrate (disc).
Details
Keywords
Xinmin Zhang, Jiqing Luo, Zhenhua Dong and Linsong Jiang
The long-span continuous rigid-frame bridges are commonly constructed by the section-by-section symmetrical balance suspension casting method. The deflection of these bridges is…
Abstract
Purpose
The long-span continuous rigid-frame bridges are commonly constructed by the section-by-section symmetrical balance suspension casting method. The deflection of these bridges is increasing over time. Wet joints are a typical construction feature of continuous rigid-frame bridges and will affect their integrity. To investigate the sensitivity of shear surface quality on the mechanical properties of long-span prestressed continuous rigid-frame bridges, a large serviced bridge is selected for analysis.
Design/methodology/approach
Its shear surface is examined and classified using the damage measuring method, and four levels are determined statistically based on the core sample integrity, cracking length and cracking depth. Based on the shear-friction theory of the shear surface, a 3D solid element-based finite element model of the selected bridge is established, taking into account factors such as damage location, damage number and damage of the shear surface. The simulated results on the stress distribution of the local segment, the shear surface opening and the beam deflection are extracted and analyzed.
Findings
The findings indicate that the main factors affecting the ultimate shear stress and shear strength of the shear surface are size, shear reinforcements, normal stress and friction performance of the shear surface. The connection strength of a single or a few shear surfaces decreases but with little effect on the local stress. Cracking and opening mainly occur at the 1/4 span. Compared with the rigid “Tie” connection, the mid-span deflection of the main span increases by 25.03% and the relative deflection of the section near the shear surface increases by 99.89%. However, when there are penetrating cracks and openings in the shear surface at the 1/2 span, compared with the 1/4 span position, the mid-span deflection of the main span and the relative deflection of the cross-section increase by 4.50%. The deflection of the main span increases with the failure of the shear surface.
Originality/value
These conclusions can guide the analysis of deflection development in long-span prestressed continuous rigid-frame bridges.
Details
Keywords
Martin Novák, Berenika Hausnerova, Vladimir Pata and Daniel Sanetrnik
This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass…
Abstract
Purpose
This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass production implemented using PIM. Thus, the surface properties and mechanical performance of parts produced using powder/polymer binder feedstocks [material extrusion (MEX) and PIM] were investigated and compared with powder manufacturing based on direct metal laser sintering (DMLS).
Design/methodology/approach
PIM parts were manufactured from 17-4PH stainless steel PIM-quality powder and powder intended for powder bed fusion compounded with a recently developed environmentally benign binder. Rheological data obtained at the relevant temperatures were used to set up the process parameters of injection molding. The tensile and yield strengths as well as the strain at break were determined for PIM sintered parts and compared to those produced using MEX and DMLS. Surface properties were evaluated through a 3D scanner and analyzed with advanced statistical tools.
Findings
Advanced statistical analyses of the surface properties showed the proximity between the surfaces created via PIM and MEX. The tensile and yield strengths, as well as the strain at break, suggested that DMLS provides sintered samples with the highest strength and ductility; however, PIM parts made from environmentally benign feedstock may successfully compete with this manufacturing route.
Originality/value
This study addresses the issues connected to the merging of two environmentally efficient processing routes. The literature survey included has shown that there is so far no study comparing AM and PIM techniques systematically on the fixed part shape and dimensions using advanced statistical tools to derive the proximity of the investigated processing routes.
Details
Keywords
Bo Zhang, Yuqian Zheng, Zhiyuan Cui, Dongdong Song, Faqian Liu and Weihua Li
The impact of rolling on the performance of micro arc oxidation (MAO) coatings on ZM5 alloy has been underreported. The purpose of this study is to explore the correlation between…
Abstract
Purpose
The impact of rolling on the performance of micro arc oxidation (MAO) coatings on ZM5 alloy has been underreported. The purpose of this study is to explore the correlation between rolling and the failure mechanism of MAO coatings in greater depth.
Design/methodology/approach
The influence of rolling on the corrosion and wear properties of MAO coating was investigated by phase structure, bond strength test (initial bond strength and wet adhesion), electrochemical impedance spectroscopy and wear test. The change of the surface electrochemical properties was studied by first principles analysis.
Findings
The results showed that the MAO coating on rolled alloy had better corrosion and wear resistance compared to cast alloy, although the structure and component content of two kinds of MAO coating are nearly identical. The difference in interface bonding between MAO coating and Mg substrate is the primary factor contributing to the disparity in performance between the two types of samples. Finally, the impact of the rolling process on MAO coating properties is explained through first-principle calculation.
Originality/value
A comprehensive explanation of the impact of the rolling process on MAO coating properties will provide substantial support for enhancing the application of Mg alloy anticorrosion.
Graphical abstract
Details
Keywords
Salwa Moustafa Amer Mahmoud, Tarek Hamdy, Mohamed Fares, Wissam Ayman, Shrouk Muhamed, Aya Abdel Khaliq and Lilian Salah
This paper aims to investigate the ability of traditional biopolymers, such as funori or the nanoscale form of cellulose nanocrystals, to consolidate fragile paper and preserve it…
Abstract
Purpose
This paper aims to investigate the ability of traditional biopolymers, such as funori or the nanoscale form of cellulose nanocrystals, to consolidate fragile paper and preserve it for as long as possible.
Design/methodology/approach
Degraded papers dating back two centuries were separated into paper samples for consolidation processes. Funori – a marine spleen – was used as a traditional consolidation material and a mixture with ZnO NPs compared with modern materials, such as cellulose nanocrystals. The samples were aged for 25 years, examinations and analyses were performed using scanning electron microscopy and color change was assessed using the CIELAB system, X-ray diffraction and Fourier-transform infrared spectroscopy.
Findings
According to the results, using traditional materials to consolidate damage, such as funori, after aging resulted in glossiness on the surface, a color change and increased water content and oxidation. Furthermore, samples treated with a mixture of ZnO NPs and funori revealed that the mixture improved the sample properties and increased the degree of crystallization. Cellulose nanocrystals improved the surface, filled gaps, formed bridges between the fibers and acted as a protector from aging effects.
Originality/value
This paper highlights the ability of nanomaterials to enhance the properties of materials as additives and treat the paper manuscripts from weaknesses.
Naveen Srinivas Madugula, Yogesh Kumar, Vimal K.E.K and Sujeet Kumar
The purpose of this paper is to improve the productivity and quality of the wire arc additive manufacturing process by benchmarking the strategies from the selected six…
Abstract
Purpose
The purpose of this paper is to improve the productivity and quality of the wire arc additive manufacturing process by benchmarking the strategies from the selected six strategies, namely, heat treatment process, inter pass cooling process, inter pass cold rolling process, peening process, friction stir processing and oscillation process.
Design/methodology/approach
To overcome the lack of certainty associated with correlations and relationships in quality functional deployment, fuzzy numbers have been integrated with the quality functional deployment framework. Twenty performance measures have been identified from the literature under five groups, namely, mechanical properties, physical properties, geometrical properties, cost and material properties. Using house of quality weights are allocated to performance measures and groups, relationships are established between performance measures and strategies, and correlations are assigned between strategies. Finally, for each strategy, relative importance, score and crisp values are calculated.
Findings
Inter pass cold rolling process strategy is computed with the highest crisp value of 15.80 which is followed by peening process, heat treatment process, friction stir processing, inter pass cooling process,] and oscillation process strategy.
Originality/value
To the best of the authors’ knowledge, there has been no research in the literature that analyzes the strategies to improve the quality and productivity of the wire arc additive manufacturing process.
Details
Keywords
Chao Li, Jin Gao, Qingqing Xu, Chao Li, Xuemei Yang, Kui Xiao and Xiangna Han
The color painting of ancient buildings has high historical and artistic value but is prone to aging due to long-term outdoor exposure. The purpose of this study is to develop a…
Abstract
Purpose
The color painting of ancient buildings has high historical and artistic value but is prone to aging due to long-term outdoor exposure. The purpose of this study is to develop a new type of sealing coating to mitigate the impact of ultraviolet (UV) light on color painting.
Design/methodology/approach
The new coating was subjected to a 500-h UV-aging test. Compared with the existing acrylic resin Primal AC33, the UV aging behavior of the new coating, such as color difference and gloss, was studied with aging time. The Fourier infrared spectra of the coatings were analyzed after the UV-aging test.
Findings
Compared with AC33, the antiaging performance of SF8 was substantially improved. SF8 has a lower color difference value and better light retention and hydrophobicity. The Fourier transform infrared spectroscopy results showed that the C-F bond and Si-O bonds in the resin of the optimized sealing coating protected the main chain C-C structure from degradation during the aging process; thus, the resin maintained good stability. The hindered amine light stabilizer TN292 added to the coating inhibited the antiaging process by trapping active free radicals.
Originality/value
To address the problem of UV aging of oil-decorated colored paintings, a new type of sealing coating with excellent antiaging properties was developed, laying the foundation for its demonstration application on the surface of ancient buildings.
Details
Keywords
The purpose of this paper is to study the correlation between different topographies and the reaction of Ulva Linza fouling species.
Abstract
Purpose
The purpose of this paper is to study the correlation between different topographies and the reaction of Ulva Linza fouling species.
Design/methodology/approach
In this research, topographies with a different method, such as hot embossing and hot pulling, were achieved, and biological analyses were done with macroalgae Ulva Linza cells. The effect of topography via local binding geometry (honeycomb size gradients) and Wenzel roughness on the settling of Ulva microorganisms was tested.
Findings
As a result, Ulva spores confirmed different reactions to a similar set of tapered microstructures that was in agreement with the results on distinct honeycombs. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.
Research limitations/implications
The reaction of an organism at the interface of vehicles’ substrate is powerfully affected by surface topographies.
Practical implications
The best embedment occurred on structures with bigger sizes than Ulva Linza’s spores. The density of settled spores was proportional to Wenzel roughness and the spores favour to attach to “kink sites” positions.
Social implications
Unfortunately, unpleasant aggregation of marine biofouling on marine vehicles’ surfaces, generate terrific difficulties in the relevant industry.
Originality/value
There was a sharp relationship between Wenzel roughness and settle of Ulva Linza spores. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.
Details
Keywords
Ali Hassanzadeh, Ebrahim Ghorbani-Kalhor, Khalil Farhadi and Jafar Abolhasani
This study’s aim is to introduce a high-performance sorbent for the removal of both anionic (Congo red; CR) and cationic (methylene blue; MB) dyes from aqueous solutions.
Abstract
Purpose
This study’s aim is to introduce a high-performance sorbent for the removal of both anionic (Congo red; CR) and cationic (methylene blue; MB) dyes from aqueous solutions.
Design/methodology/approach
Sodium silicate is adopted as a substrate for GO and AgNPs with positive charge are used as modifiers. The synthesized nanocomposite is characterized by FTIR, FESEM, EDS, BET and XRD techniques. Then, some of the most effective parameters on the removal of CR and MB dyes such as solution pH, sorbent dose, adsorption equilibrium time, primary dye concentration and salt effect are optimized using the spectrophotometry technique.
Findings
The authors successfully achieved notable maximum adsorption capacities (Qmax) of CR and MB, which were 41.15 and 37.04 mg g−1, respectively. The required equilibrium times for maximum efficiency of the developed sorbent were 10 and 15 min for CR and MB dyes, respectively. Adsorption equilibrium data present a good correlation with Langmuir isotherm, with a correlation coefficient of R2 = 0.9924 for CR and R2 = 0.9904 for MB, and kinetic studies prove that the dye adsorption process follows pseudo second-order models (CR R2 = 0.9986 and MB R2 = 0.9967).
Practical implications
The results showed that the proposed mechanism for the function of the developed sorbent in dye adsorption was based on physical and multilayer adsorption for both dyes onto the active sites of non-homogeneous sorbent.
Originality/value
The as-prepared nano-adsorbent has a high ability to remove both cationic and anionic dyes; moreover, to the high efficiency of the adsorbent, it has been tried to make its synthesis steps as simple as possible using inexpensive and available materials.
Details
Keywords
The purpose of this study is to develop a molecular imprinting electrochemical sensor for the specific detection of the anticancer drug amsacrine. The sensor used a composite of…
Abstract
Purpose
The purpose of this study is to develop a molecular imprinting electrochemical sensor for the specific detection of the anticancer drug amsacrine. The sensor used a composite of bacterial cellulose (BC) and silver nanoparticles (AgNPs) as a platform for the immobilization of a molecularly imprinted polymer (MIP) film. The main objective was to enhance the electrochemical properties of the sensor and achieve a high level of selectivity and sensitivity toward amsacrine molecules in complex biological samples.
Design/methodology/approach
The composite of BC-AgNPs was synthesized and characterized using FTIR, XRD and SEM techniques. The MIP film was molecularly imprinted to selectively bind amsacrine molecules. Electrochemical characterization, including cyclic voltammetry and electrochemical impedance spectroscopy, was performed to evaluate the modified electrode’s conductivity and electron transfer compared to the bare glassy carbon electrode (GCE). Differential pulse voltammetry was used for quantitative detection of amsacrine in the concentration range of 30–110 µM.
Findings
The developed molecular imprinting electrochemical sensor demonstrated significant improvements in conductivity and electron transfer compared to the bare GCE. The sensor exhibited a linear response to amsacrine concentrations between 30 and 110 µM, with a low limit of detection of 1.51 µM. The electrochemical response of the sensor showed remarkable changes before and after amsacrine binding, indicating the successful imprinting of amsacrine in the MIP film. The sensor displayed excellent selectivity for amsacrine in the presence of interfering substances, and it exhibited good stability and reproducibility.
Originality/value
This study presents a novel molecular imprinting electrochemical sensor design using a composite of BC and AgNPs as a platform for MIP film immobilization. The incorporation of BC-AgNPs improved the sensor’s electrochemical properties, leading to enhanced sensitivity and selectivity for amsacrine detection. The successful imprinting of amsacrine in the MIP film contributes to the sensor's specificity. The sensor's ability to detect amsacrine in a concentration range relevant to anticancer therapy and its excellent performance in complex sample matrices add significant value to the field of electrochemical sensing for pharmaceutical analysis.
Details