Search results

The effect of partial replacement of carbon black by Palmyra palm fiber on the cure characteristics, physico-mechanical and swelling properties of natural rubber vulcanizates was studied. The Palmyra palm fibers were extracted, treated and characterized so as to determine pH, moisture content, and ash content, loss on ignition, conductivity, cellulose, lignin, Hemicellulose, cellulose/lignin ratio and Acid soluble lignin. The functional groups in the Palmyra palm fiber was also determined using FTIR. The Palmyra palm powder with an average particle size of 75 μm was used in this study. The natural rubber/carbon black/Palmyra palm fiber (NR/CB/PPF) composites having eight different loadings, 0/70, 10/60, 20/50, 30/40, 40/30, 50/20, 60/10, 70/0, were prepared using a laboratory size two roll mill. The maximum Torque of NR/CB/PPF composites increased with increasing commercial filler loading ratio. The scorch time and cure time of NR/CB/PPF composites decreased as the ratio of CB loading increased. The tensile strength, modulus of elongation, tear strength and abrasion resistance of all the composites increased as the commercial filler loading ratio increased. This is due to the presence of the commercial filler which gave a better filler interaction. Also this behavior can be attributed to the particle size and surface area of the fillers used as the fillers with small particle size usually have a larger surface area which supports better filler-rubber interaction. The hardness increased as the palmyra palm fiber loading increased. The elongation at break decreases as carbon black filler loading increases except for the composite with CB/PPF ratio of 10/60. The effect of filler loading on the swelling behavior of NR/CB/PPF composites was also investigated in aromatic and aliphatic compounds. Result showed that the composites with more carbon black has less absorption than those with more palmyra palm fiber showing that the compounds with more carbon black has better interaction than those with palmyra palm fiber.

The purpose of this study is to understand the behavior of hybrid bio-composites under varied applications.

Fabrication methods and material characterization of various hybrid bio-composites are analyzed by studying the tensile, impact, flexural and hardness of the same. The natural fiber is a manufactured group of assembly of big or short bundles of fiber to produce one or more layers of flat sheets. The natural fiber-reinforced composite materials offer a wide range of properties that are suitable for many engineering-related fields like aerospace, automotive areas. The main characteristics of natural fiber composites are durability, low cost, low weight, high specific strength and equally good mechanical properties.

The tensile properties like tensile strength and tensile modulus of flax/hemp/sisal/Coir/Palmyra fiber-reinforced composites are majorly dependent on the chemical treatment and catalyst usage with fiber. The flexural properties of flax/hemp/sisal/coir/Palmyra are greatly dependent on fiber orientation and fiber length. Impact properties of flax/hemp/sisal/coir/Palmyra are depended on the fiber content, composition and orientation of various fibers.

This study is a review of various research work done on the natural fiber bio-composites exhibiting the factors to be considered for specific load conditions.

Composites based on fiber are commonly used in high-performance building materials. The composites mostly use petrochemically derived fibers like polyester and e-glass, due to their advantageous material features like high stiffness and strength. All the same, these fibers also have important shortcomings related to energy consumption, recyclability, initial processing expense, resulting health hazards, and sustainability. Increasing environmental awareness and new sustainable building technologies are driving the research, development, and usage of “green” building materials, especially the development of biomaterials.

In this chapter, the natural fiber evaluation approach is applied, which covers a diverse set of criteria. Consequently, the comparative assessment of diverse natural fiber types is applied through the use of an expert decision system approach. The best performing fiber choice is made by comparatively evaluating the materials related to green building. The proposed fiber can be used and applied by green building material manufacturing companies in various countries or locations as a reference when selecting the fiber with the best performance.

In the recent years, the industries show interest in natural and synthetic fibre-reinforced hybrid composites due to weight reduction and environmental reasons. The purpose of this experimental study is to investigate the properties of the hybrid composites fabricated by using carbon, untreated and alkaline-treated hemp fibres.

The composites were tested for strengths under tensile, flexural, impact and shear loadings, and the water absorption characteristics were also observed. The finite element analysis (FEA) was carried out to analyse the elastic behaviour of the composites and predict the strength by using ANSYS 15.0.

From the experimental results, it is observed that the hybrid composites can withstand the maximum tensile strength of 61.4 MPa, flexural strength of 122.4 MPa, impact strength of 4.2 J/mm² and shear strength of 25.5 MPa. From the FEA results, it is found that the maximum stress during tensile, flexural and impact loading is 47.5, 2.1 and 1.03 MPa, respectively.

The results of the untreated and alkaline-treated hemp-carbon fibre composites were compared and found that the alkaline-treated composites perform better in terms of mechanical properties. Then, the ANSYS-predicted values were compared with the experimental results, and it was found that there is a high correlation occurs between the untreated and alkali-treated hemp-carbon fibre composites. The internal structure of the broken surfaces of the composite samples was analysed using a scanning electron microscopy (SEM) analysis.

The purpose of this paper is to study the effects of fiber length and content on properties of E-glass and bamboo fiber reinforced epoxy resin matrices. Experiments are carried out as per ASTM standards to find the mechanical properties. Further, fractured surface of the specimen is subjected to morphological study.

Composite samples were prepared according to ASTM standards and were subjected to tensile and flexural loads. The fractured surfaces of the specimens were examined directly under scanning electron microscope.

From the experiment, it was found that the main factors that influence the properties of composite are fiber length and content. The optimum fiber length and weight ratio are 15 mm and 16 percent, respectively, for bamboo fiber/epoxy composite. Hence, the prediction of optimum fiber length and content becomes important, so that composite can be prepared with best mechanical properties. The investigation revealed the suitability of bamboo fiber as an effective reinforcement in epoxy matrix.

As bamboo fibers are biodegradable, recyclable, light weight and so on, their applications are numerous. They are widely used in automotive components, aerospace parts, sporting goods and building industry. With this scenario, the obtained result of bamboo fiber reinforced composites is not ignorable and could be of potential use, since it leads to harnessing of available natural fibers and their composites rather than synthetic fibers.

This work enlists the effect of fiber length and fiber content on tensile and flexural properties of bamboo fiber/epoxy composite, which has not been attempted so far.

This study aims to investigate the mechanical, thermal and water absorption (WA) properties of kenaf fiber (KF) composites hybridized with powdered Acacia concinna pods (ACP).

Kenaf fiber reinforced epoxy polymer hybrid composite was fabricated using several weight percentages of ACP powder as filler (0%, 2%, 4%, 6% and 8%), both with and without chemically altering the fiber mat. 6 Wt.% NaOH was used in distilled water to treat KF mat chemically. The hand layup technique is used to produce ASTM-compliant KF hybrid laminates. Tensile, flexural and IZOD impact strengths were tested on the generated hybrid composites and their thermal and WA characteristics. Scanning electron microscope fractography revealed that fiber pulling-out, debonding and cracking were the main ways composites fractured.

The investigation findings reveal that the tensile, flexural and impact strengths increased when ACP fillers were added up to 4, 6 and 8 Wt.%, respectively. Thermogravimetric analysis indicates that the hybrid composite is thermally stable up to 215°C. WA experiments reveal that KF mat composites treated with 0 Wt.% ACP filler had less WA than those not treated with ACP filler. The treated KF with 4% filler hybrid composite demonstrated improved interfacial bonding between the reinforcement and matrix compared to other combinations.

Although filler made of A. concinna is inexpensive, lightweight, renewable, totally or partially recyclable and biodegradable, its potential application in hybridizing composites is yet to be investigated. Hybridizing the KF mat with ACP filler in an epoxy matrix produced novel hybrid composites. Evaluations have been conducted on the effects of ACP filler on the mechanical, thermal and WA characteristics of composites.