The aim of this paper is to study the effect of laser shock peening (LSP) on mechanical behaviour of the laser-directed energy deposition (LDED)-based printed 15-5 PH stainless steel with U and V notches. The study specifically concentrates on the evaluation of effect of scan strategy, machining and LSP processing on microstructural, texture evolution and fatigue behaviour of LDED-printed 15-5 PH steel.

For LSP treatment, 15-5 PH steel was printed using LDED process with bidirectional scanning strategy (XX [θ = 0°) and XY [θ = 90°]) at optimised laser power of 600 W with a scanning speed of 300 mm/min and a powder feed rate of 3 g/min. Furthermore, LSP treatment was conducted on the V- and U-notched fatigue specimens extracted from LDED-built samples at laser energy of 3.5 J with a pulse width of 10 ns using laser spot diameter of 3 mm. Post to the LSP treatment, the surface roughness, fatigue life assessment and microstructural evolution analysis is performed. For this, different advanced characterisation techniques are used, such as scanning electron microscopy attached with electron backscatter diffraction for microstructure and texture, X-ray diffraction for residual stress (RS) and structure information, Vicker’s hardness tester for microhardness and universal testing machine for low-cycle fatigue.

It is observed that both scanning strategies during the LDED printing of 15-5 PH steel and laser peening have played significant role in fatigue life. Specimens with the XY printing strategy shows higher fatigue life as compared to XX with both U- and V-notched conditions. Furthermore, machining and LSP treatment led to a significant improvement of fatigue life for both scanning strategies with U and V notches. The extent of increase in fatigue life for both XX and XY scanning strategy with V notch is found to be higher than U notch after LSP treatment, though without LSP samples with U notch have a higher fatigue life. As fabricated sample is found to have the lowest fatigue life as compared to machines and laser peened with both scan strategies.

This study presents an innovative method to improve the fatigue life of 15-5 PH stainless steel by changing the microstructure, texture and RS with the adoption of a suitable scanning strategy, machining and LSP treatment as post-processing. The combination of preferred microstructure and compressive RS in LDED-printed 15-5 PH stainless steel achieved with a synergy between microstructure and RS, which is responsible to improve the fatigue life. This can be adopted for the futuristic application of LDED-printed 15-5 PH stainless steel for different applications in aerospace and other industries.

The purpose of this paper is to investigate the effect of laser peening (LP) on mechanical and wear properties of 304 stainless steel sheet.

Three-dimensional morphology, micro-hardness and micro-structure of shocked samples were tested. The wear amount, wear track morphology and wear mechanism were also characterized under dry sliding wear using Al₂O₃ ceramics ball.

The LP treatment generates deformation twins that contribute to the grain refinement and hardness increase. The wear test displays that the wear mechanism of samples is mainly abrasive wear and oxidation wear at 10 N load. While at 30 N, the delamination and adhesion areas of treated sample are reduced visibly compared to untreated ones.

This study specifically investigates the mechanical and wear properties of 304 stainless steel after the direct action of LP on its surface, which shows an effective improvement on the wear resistance. For example, the wear loss of processed sample is reduced by 19% at 30 N, the friction coefficient decreases from 0.4714 to 0.4308 and the groove depth is reduced from 78.1 to 74.4 µm under same condition.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2024-0007/

The nickel-based alloys Inconel 625 and Inconel 718 stand out due to their high strength and corrosion resistance in important industries like aerospace, aviation and automotive. Even though they are widely used, current techniques of producing materials that are difficult to cut pose several problems from a financial, ecological and even health perspective. To handle these problems and acquire improved mechanical and structural qualities, laser powder bed fusion (LPBF) has been widely used as one of the most essential additive manufacturing techniques. The purpose of this article is to focus on the state of the art on LPBF parts of Inconel 625 and Inconel 718 for microstructure, mechanical behavior and postprocessing.

The mechanical behavior of LPBF-fabricated Inconel is described, including hardness, surface morphology and wear, as well as the influence of fabrication orientation on surface quality, biocompatibility and resultant mechanical properties, particularly tensile strength, fatigue performance and tribological behaviors.

The postprocessing techniques such as thermal treatments, polishing techniques for surface enhancement, mechanical and laser-induced peening and physical operations are summarized.

The highlighted topic presents the critical aspects of the advantages and challenges of the LPBF parts produced by Inconel 718 and 625, which can be a guideline for manufacturers and academia in practical applications.

The purpose of this paper is to assess the hydrogen embrittlement sensitivity of carbon gradient heterostructure materials and to verify the reliability of the scratch method.

The surface-modified layer of 18CrNiMo7-6 alloy steel was delaminated to study its hydrogen embrittlement characteristics via hydrogen permeation, electrochemical hydrogen charging and scratch experiments.

The results showed that the diffusion coefficients of hydrogen in the surface and matrix layers are 3.28 × 10⁻⁷ and 16.67 × 10⁻⁷ cm²/s, respectively. The diffusible-hydrogen concentration of the material increases with increasing hydrogen-charging current density. For a given hydrogen-charging current density, the diffusible-hydrogen concentration gradually decreases with increasing depth in the surface-modified layer. Fracture toughness decreases with increasing diffusible-hydrogen concentration, so the susceptibility to hydrogen embrittlement decreases with increasing depth in the surface-modified layer.

The reliability of the scratch method in evaluating the fracture toughness of the surface-modified layer material is verified. An empirical formula is given for fracture toughness as a function of diffused-hydrogen concentration.

Given the current friction and wear challenges faced by automobile parts and bearings, this study aims to identify a novel texture for creating anti-friction and wear-resistant surfaces. This includes detailing the preparation process with the objective of mitigating friction and wear in working conditions.

Femtosecond laser technology was used to create a mango-shaped texture on the surface of GCr15 bearing steel. The optimized processing technology of the texture surface was obtained through adjusting the laser scanning speed. The tribological behavior of the laser-textured surface was investigated using a reciprocating tribometer.

The friction coefficient of the mango-shaped texture surface is 25% lower than that of the conventional surface, this can be attributed to the reduced contact area between the friction ball and the micro-textured surface, leading to stress concentration at the extrusion edge and a larger stress distribution area on the contact part of the ball and disk compared to the conventional surface and the function of the micro-texture in storing wear chips during the sliding process, thereby reducing secondary wear.

The mango-shaped textured surface in this study demonstrates effective solutions for some of the friction and wear issues, offering significant benefits for equipment operation under light load conditions.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-04-2024-0127/

This study aims to study the formation mechanism of micro-arc oxidation (MAO) coating on AZ31 magnesium alloy and how the annealing process affects its corrosion resistance.

This study involved immersion experiments, electrochemical experiments and slow strain rate tensile experiments, along with scanning electron microscopy, optical microscopy observation and X-ray diffraction analysis.

The findings suggest that annealing treatment can refine the grain size of AZ31 magnesium alloy to an average of 6.9 µm at 300°C. The change in grain size leads to a change in conductivity, which affects the performance of MAO coatings. The MAO coating obtained by annealing the substrate at 300°C has smaller pores and porosity, resulting in better adhesion and wear resistance.

The coating acts as a barrier to prevent corrosive substances from entering the substrate. However, the smaller pores and porosity reduce the channels for the corrosive solution to pass through the coating. When the coating cracks or falls off, the corrosive medium and substrate come into direct contact. Smaller and uniform grains have better corrosion resistance.

In this study, two postprocessing techniques, namely, conventional burnishing (CB) and ultrasonic-assisted burnishing (UAB), were applied to improve the fatigue behavior of 316 L stainless steel fabricated through selective laser melting (SLM). The effects of these processes on surface roughness, porosity, microhardness and fatigue performance were experimentally investigated. The purpose of this study is to evaluate the feasibility and effectiveness of ultrasonic-assisted burnishing as a preferred post-processing technique for enhancing the fatigue performance of additively manufactured components.

All samples were subjected to a sandblasting process. Next, the samples were divided into three distinct groups. The first group (as-Built) did not undergo any additional postprocessing, apart from sandblasting. The second group was treated with CB, while the third group was treated with ultrasonic-assisted burnishing. Finally, all samples were evaluated based on their surface roughness, porosity, microhardness and fatigue performance.

The results revealed that the initial mean surface roughness (Ra) of the as-built sample was 11.438 µm. However, after undergoing CB and UAB treatments, the surface roughness decreased to 1.629 and 0.278 µm, respectively. Notably, the UAB process proved more effective in eliminating near-surface pores and improving the microhardness of the samples compared to the CB process. Furthermore, the fatigue life of the as-built sample, initially at 66,000 cycles, experienced a slight improvement after CB treatment, reaching 347,000 cycles. However, the UAB process significantly enhanced the fatigue life of the samples, extending it to 620,000 cycles.

After reviewing the literature, it can be concluded that UAB will exceed the capabilities of CB in terms of enhancing the surface roughness and, subsequently, the fatigue performance of additive manufactured (AM) metals. However, the actual impact of the UAB process on the fatigue life of AM products has not yet been thoroughly researched. Therefore, in this study, this paper used the burnishing process to enhance the fatigue life of 316 L stainless steel produced through the SLM process.

Regarding the broadening of the titanium alloy application field, the surface treatment coating of TC4 alloy has become an essential global research topic. This study aims to illustrate the titanium-based composite coating is created by laser cladding TC4+Ni60/hBN composite powder onto the surface of the TC4 alloy.

Different laser scanning speeds were initially selected to prepare TC4+Ni60/hBN titanium-based composite coating on the surface of TC4 alloy using RFL-C1000 Raycus fiber laser. Second, the cladding layers with different laser scanning speeds are composed of Ti₂Ni, TiN_0.3, TiC, TiB, α-Ti and other phases. Finally, precision balances, friction and wear testing machines were used to analyze and test the structure, phase, hardness, wear amount and friction coefficient of the composite coating and to study the effect of laser scanning speed on the microstructure and properties of the titanium-based composite coating.

It is evident that at the low laser scanning speed, the reinforcing phase agglomeration area is distributed in the substrate as a network. Increasing the laser scanning speed can reduce the cladding layer's friction coefficient and improve the cladding layer's hardness and wear resistance. But too high a laser scanning speed will cause defects such as pores and cracks in the cladding layer and also affect the cladding layer. The bonding performance of the layer and the substrate is optimal in this research at a laser scanning speed of 10 mm/s.

This research has practical value in improving the quality of surface treatment coating in modern aerospace and automotive companies.

Polymer laser powder bed fusion (PBF-LB/P) is an additive manufacturing technology that is sustainable due to the possibility of recycling the powder multiple times and allowing the fabrication of gears without the aid of support structures and subsequent assembly. However, there are constraints in the process that negatively affect its adoption compared to other additive technologies such as material extrusion to produce gears. This study aims to demonstrate that it is possible to overcome the problems due to the physics of the process to produce accurate mechanism.

Technological aspects such as orientation, wheel-shaft thicknesses and degree of powder recycling were examined. Furthermore, the evolving tooth profile was considered as a design parameter to provide a manufacturability map of gear-based mechanisms.

Results show that there are some differences in the functioning of the gear depending on the type of powder used, 100% virgin or 50% virgin and 50% recycled for five cycles. The application of a groove on a gear produced with 100% virgin powder allows the mechanism to be easily unlocked regardless of the orientation and wheel-shaft thicknesses. The application of a specific evolutionary profile independent of the diameter of the reference circle on vertically oriented gears guarantees rotation continuity while preserving the functionality of the assembled mechanism.

In the literature, there are various studies on material aging and reuse in the PBF-LB/P process, mainly focused on the powder deterioration mechanism, powder fluidity, microstructure and mechanical properties of the parts and process parameters. This study, instead, was focused on the functioning of gears, which represent one of the applications in which this technology can have great success, by analyzing the two main effects that can compromise it: recycled powder and vertical orientation during construction.

This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass production implemented using PIM. Thus, the surface properties and mechanical performance of parts produced using powder/polymer binder feedstocks [material extrusion (MEX) and PIM] were investigated and compared with powder manufacturing based on direct metal laser sintering (DMLS).

PIM parts were manufactured from 17-4PH stainless steel PIM-quality powder and powder intended for powder bed fusion compounded with a recently developed environmentally benign binder. Rheological data obtained at the relevant temperatures were used to set up the process parameters of injection molding. The tensile and yield strengths as well as the strain at break were determined for PIM sintered parts and compared to those produced using MEX and DMLS. Surface properties were evaluated through a 3D scanner and analyzed with advanced statistical tools.

Advanced statistical analyses of the surface properties showed the proximity between the surfaces created via PIM and MEX. The tensile and yield strengths, as well as the strain at break, suggested that DMLS provides sintered samples with the highest strength and ductility; however, PIM parts made from environmentally benign feedstock may successfully compete with this manufacturing route.

This study addresses the issues connected to the merging of two environmentally efficient processing routes. The literature survey included has shown that there is so far no study comparing AM and PIM techniques systematically on the fixed part shape and dimensions using advanced statistical tools to derive the proximity of the investigated processing routes.