This research outlines the development and characterization of advanced composite materials and their potential applications in the aerospace industry for interior applications. Advanced composites, such as carbon-fiber-reinforced polymers and ceramic matrix composites, offer significant advantages over traditional metallic materials in terms of weight reduction, stiffness and strength. These materials have been used in various aerospace applications, including aircraft, engines and thermal protection systems.

The development of design of experiment–based hybrid aluminum composites using the stir-casting technique has further enhanced the performance and cost-effectiveness of these materials. The design of the experiment was followed to fabricate hybrid composites with nano cerium oxide (nCeO₂) and graphene nanoplatelets (GNPs) as reinforcements in the Al-6061 matrix.

The Al6061 + 3% nCeO2 + 3% GNPs exhibited a high hardness of 119.6 VHN. The ultimate tensile strength and yield strength are 113.666 MPa and 73.08 MPa, respectively. A uniform distribution of reinforcement particulates was achieved with 3 Wt.% of each reinforcement in the matrix material, which is analyzed using scanning electron microscopy. Fractography revealed that brittle and ductile fractures caused the failure of the fractured specimens in the tensile test.

The manufactured aluminum composite can be applied in a range of exterior and interior structural parts like wings, wing boxes, motors, gears, engines, antennas, floor beams, etc. The fan case material of the GEnx engine (currently using carbon-fiber reinforcement plastic) for the Boeing 7E7 can be another replacement with manufactured hybrid aluminum composite, which predicts weight savings per engine of close to 120 kg.

The development of hybrid reinforcements, where two or more types of reinforcements are used in combination, is also a novel approach to improving the properties of these composites. Advanced composite materials are known for their high strength-to-weight ratio. If the newly developed composite material demonstrates superior properties, it can potentially be used to replace traditional materials in aircraft manufacturing. By reducing the weight of aircraft structures, fuel efficiency can be improved, leading to reduced operating costs and environmental impact. This allows for a more customized solution for specific application requirements and can lead to further advancements in materials science and technology.

This paper aims to accomplish friction stir welding (FSW) of Al–Li alloy AA8090 to determine optimal settings of the process parameters for higher tensile strength and higher micro-hardness (MH) to achieve the objective of adequate butt-joint strength.

An empirical relation is implemented to govern the utmost influence parameters, i.e. tool rotation speed (TRS), tool transverse speed (TTS) and dwell time (DT). Taguchi grey relational analysis (GRA) was applied for multi-response optimization of response parameters. The grey relational grades (GRs) have been calculated for both the responses MH and ultimate tensile strength to get optimal parametric settings. The variance test has been performed to check the adequacy of the model.

The Taguchi L9 orthogonal array design was used in establishing the relation between input parameter and output parameter (tensile and MH). TTS and DT have been predicted to be the two most important parameters that influence the extreme quality features of joints by using friction stir welding. Scanning electron microscopy fractography shows the ductile failure of the welded joints.

The experimental trials provided the followings results, maximum ultimate tensile strength (UTS) of 219 MPa and MH 107.1 HV under 1,400 rpm of TRS, 40 mm/min of TTS and 8 s of DT founded the optimum value through GRA.

The purpose of this paper is to investigate the impact of ultrasonic vibration (UV) and tool pin profile on mechanical properties and microstructural behaviour of AA7075-T651 and AA6061-T6 joints was analysed.

The joints were fabricated using three different tool pin profiles such as cylindrical, square and triangle. For each tool pin profile, two different UV powers of 1.5 kW and 2 kW were used.

On both the advancing and retreating sides of the weld, the thermo-mechanically affected zone has the lowest microhardness. In all joints, the tensile fracture locations match to the minimum hardness values. Field emission scanning electron microscope fractography of tensile tested specimens reveals heterogeneous modes of brittle, shear and ductile fracture. Three-point bending analysis was performed to determine the ductility and soundness of the weld joint. The acoustic softening effect of UV, as well as the static and dynamic ratio of tool pin profile, plays an important role in determining the material flow and mechanical behaviour of the joint.

Dissimilar aluminium joining fascinates many applications like aircraft, aerospace, automobiles, ship building and electronics, where fusion welding is a very intricate process because of the deviation in its physical and chemical properties.

From this study investigation, it is found that the square pin profiled tool with 2 kW UV power produces metallurgical defect-free and mechanically sound weld with maximum tensile strength, hardness and bending load of 297 MPa, 151HV and 3.82 kN, respectively.

The purpose of this study is to investigate the effect of nano ZrC particles on the mechanical and electrochemical corrosion properties of FeCrAl alloys, providing a beneficial reference basis for the development of high-performance carbide reinforced FeCrAl alloys with good mechanical and corrosion properties in the future.

Nano ZrC reinforced FeCrAl alloys were prepared by mechanical alloying and spark plasma sintering. Phases composition, tensile fractography, corrosion morphology and chemical composition of nano ZrC reinforced FeCrAl alloys were analyzed by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy, respectively. Microhardness and tensile properties of nano ZrC reinforced FeCrAl alloys were investigated by mechanical testing machine and Vickers hardness tester. Electrochemical corrosion properties of nano ZrC reinforced FeCrAl alloys were investigated by electrochemical workstation in 3.5 wt.% NaCl solution.

The results showed that addition of nano ZrC can effectively improve the mechanical and corrosion properties. However, excessive nano ZrC could decrease the mechanical properties and reduce the corrosion resistance. In all the FeCrAl alloys, FeCrAl–0.6 wt.% ZrC alloy exhibits the optimum mechanical properties with an ultimate tensile strength, elongation and hardness of 990.7 MPa, 24.1% and 335.8 HV1, respectively, and FeCrAl–0.2 wt.% ZrC alloy has a lower corrosion potential (−0.179 V) and corrosion current density (2.099 µA/cm2) and larger pitting potential (0.497 V) than other FeCrAl–ZrC alloys, showing a better corrosion resistance.

Adding proper nano ZrC particles can effectively improve the mechanical and corrosion properties, while the excessive nano ZrC is harmful to the mechanical and corrosion properties of FeCrAl alloys, which provides an instruction to develop high-performance FeCrAl cladding materials.

Because of the anisotropy of the process and the variability in the quality of printed parts, finite element analysis is not directly applicable to recycled materials manufactured using fused filament fabrication. The purpose of this study is to investigate the numerical-experimental mechanical behavior modeling of the recycled polymer, that is, recyclable polyethylene terephthalate (rPET), manufactured by a deposition FFF process under compressive stresses for new sustainable designs.

In all, 42 test specimens were manufactured and analyzed according to the ASTM D695-15 standards. Eight numerical analyzes were performed on a real design manufactured with rPET using Young's compression modulus from the experimental tests. Finally, eight additional experimental tests under uniaxial compression loads were performed on the real sustainable design for validating its mechanical behavior versus computational numerical tests.

As a result of the experimental tests, rPET behaves linearly until it reaches the elastic limit, along each manufacturing axis. The results of this study confirmed the design's structural safety by the load scenario and operating boundary conditions. Experimental and numerical results show a difference of 0.001–0.024 mm, allowing for the rPET to be configured as isotropic in numerical simulation software without having to modify its material modeling equations.

The results obtained are of great help to industry, designers and researchers because they validate the use of recycled rPET for the ecological production of real-sustainable products using MEX technology under compressive stress and its configuration for numerical simulations. Major design companies are now using recycled plastic materials in their high-end designs.

Validation results have been presented on test specimens and real items, comparing experimental material configuration values with numerical results. Specifically, to the best of the authors’ knowledge, no industrial or scientific work has been conducted with rPET subjected to uniaxial compression loads for characterizing experimentally and numerically the material using these results for validating a real case of a sustainable industrial product.

Extrusion width, the width of printed filaments, affects multiple critical aspects in mechanical properties in material extrusion additive manufacturing: filament geometry, interlayer load-bearing bonded area and fibre orientation for fibre-reinforced composites. However, this study aims to understand the effects of extrusion width on 3D printed composites, which has never been studied systematically.

Four polymers with and without short-fibre reinforcement were 3D printed into single-filament-wide specimens. Tensile properties, mechanical anisotropy and fracture mechanisms were evaluated along the direction of extruded filaments (F) and normal to the interlayer bond (Z). Extrusion width, nozzle temperature and layer height were studied separately via single-variable control. The extrusion width was controlled by adjusting polymer flow in the manufacturing procedure (gcode), where optimisation can be achieved with software/structure design as opposed to hardware.

Increasing extrusion width caused a transition from brittle to ductile fracture, and greatly reduced directional anisotropy for strength and ductility. For all short fibre composites, increasing width led to an increase in strain-at-break and decreased strength and stiffness in the F direction. In the Z direction, increasing width led to increased strength and strain-at-break, and stiffness decreased for less ductile materials but increased for more ductile materials.

The transformable fracture reveals the important role of extrusion width in processing-structure-property correlation. This study reveals a new direction for future research and industrial practice in controlling anisotropy in additive manufacturing. Increasing extrusion width may be the simplest way to reduce anisotropy while improving printing time and quality in additive manufacturing.

This study/paper aims to develop fundamental understanding of mechanical properties for multiple fibre-reinforced materials by using a single-filament-wide tensile-testing approach.

In this study, recently validated single-filament-wide tensile-testing specimens were used for four polymers with and without short-fibre reinforcement. Critically, this specimen construct facilitates filament orientation control, for representative longitudinal and transverse composite directions, and enables measurement of interlayer bonded area, which is impossible with “slicing” software but essential in effective property measurement. Tensile properties were studied along the direction of extruded filaments (F) and normal to the interlayer bond (Z) both experimentally and theoretically via the Kelly–Tyson model, bridging model and Halpin–Tsai model.

Even though the four matrix-material properties varied hugely (1,440% difference in ductility), consistent material-independent trends were identified when adding fibres: ductility reduced in both F- and Z-directions; stiffness and strength increased in F but decreased or remained similar in Z; Z:F strength anisotropy and stiffness anisotropy ratios increased. Z:F strain-at-break anisotropy ratio decreased; stiffness and strain-at-break anisotropy were most affected by changes to F properties, whereas strength anisotropy was most affected by changes to Z properties.

To the best of the authors’ knowledge, this is the first study to assess interlayer bond strength of composite materials based on measured interlayer bond areas, and consistent fibre-induced properties and anisotropy were found. The results demonstrate the critical influence of mesostructure and microstructure for three-dimensional printed composites. The authors encourage future studies to use specimens with a similar level of control to eliminate structural defects (inter-filament voids and non-uniform filament orientation).

The tensile behavior of additively manufactured nylon-based carbon fiber-reinforced composites (CFRP) is an important criterion in aerospace and automobile structural design. So, this study aims to evaluate and validate the tensile stiffness of printed CFRP composites (low- and high-volume fraction fiber) using the volume average stiffness (VAS) model in consonance with experimental results. In specific, the tensile characterization of printed laminate composites is studied under the influence of raster orientations and process-induced defects.

CFRP composite laminates of low- and high-volume fraction carbon fiber of different raster orientations (0°, ± 45° and 0/90°) were fabricated using the continuous fiber 3D printing technique, and tensile characteristics of laminates were done on a universal testing machine with the crosshead speed of 2 mm/min. The induced fracture surface of laminates due to tensile load was examined using the scanning electron microscopy technique.

The VAS model can predict the tensile stiffness of printed CFRP composites with different raster orientations at an average prediction error of 5.94% and 10.58% for low- and high-volume fiber fractions, respectively. The unidirectional CFRP laminate composite with a high-volume fraction (50%) of carbon fiber showed 50.79% more tensile stiffness and 63.12% more tensile strength than the low-volume fraction (26%) unidirectional composite. Fiber pullout, fiber fracture and ply delamination are the major failure appearances observed in fracture surfaces of laminates under tensile load using scanning electron microscopy.

This investigation demonstrates the novel methodology to study specific tensile characteristics of low- and high-volume fraction 3D printed CFRP composite.

The purpose of this paper is to examine the effect of changing some riveting parameters on the riveting quality of a riveted aircraft structure. In this study, riveting was performed by applying friction under pressure.

During this friction riveting process, a feed of 3 mm/min was applied in the axial direction. Rotation speed values of 2,000, 2,200 and 2,400 rpm were selected. A 3-axis die milling machine was used to achieve the required positioning, pressing force and friction effect. 1.27 mm-thick Al 7075-T6 sheets and 2117-T3 forged rivets were used. The feed rate was applied at 1 mm/min in both tensile shear and cross-tensile tests.

The feasibility of friction riveting in 2117-T3 rivets was examined, it was shown that it could be done, and the most suitable rotation value for this process was determined.

Clamping force is one of the most important parameters for riveting quality. This study will contribute to a better understanding of the friction-forging riveting process along with the effects of riveting parameters. At the same time, it will lead to more research and expand the application of friction forging riveting to more structural connections.

In recent years, additive manufacturing (AM) has started to be used for manufacturing real functional parts and assemblies for critical applications in aerospace, automotive, and machinery industries. Most complex or assembled parts require internal features (IF) such as holes, channels, slots, or guides for locational and mating requirements. Therefore, it is critical to understand and compare the structural and mechanical properties of additively manufactured and conventionally machined IFs.

In this study, mechanical and microstructural properties of Inconel 718 (Inc718) alloy internal features, manufactured either as-built with AM or machining of additively manufactured (AMed) part thereafter were investigated.

The results showed that the average ultimate tensile strength (UTS) of additively manufactured center internal feature (AM-IF) is almost analogous to the machined internal feature (M-IF). However, the yield strength of M-IF is greater than that of AM-IF due the greater surface roughness of the internal feature in AM-IF, which is deemed to surpass the effect of microstructure on the mechanical performance. The results of digital image correlation (DIC) analysis suggest that AM-IF and M-IF conditions have similar strain values under the same stress levels but the specimens with as built IF have a more locally ductile region around their IF, which is confirmed by hardness test results. But this does not change global elongation behavior. The microstructural evolution starting from as-built (AB) and heat-treated (HT) samples to specimens with IF are examined. The microstructure of HT specimens has bimodal grain structure with d phase while the AB specimens display a very fine dendritic microstructure with the presence of carbides. Although they both have close values, machined specimens have a higher frequency of finer grains based on SEM images.

It was shown that the concurrent creation of the IF during AM can provide a final part with a preserved ultimate tensile strength and elongation but a decreased yield strength. The variation in UTS of AM-IF increases due to the surface roughness near the internal feature as compared to smooth internal surfaces in M-IF. Hence, the outcomes of this study are believed to be valuable for the industry in terms of determining the appropriate production strategy of parts with IF using AM and postprocessing processes.