1 – 10 of 19Huimin Yang, Chunlin Ye, Yi Li and Songwei Zhang
This study aims to probe the applicability of 2-mercaptobenzothiazole (MBT) functionalized ionic liquids (ILs) as additives in lithium complex grease (LCG) by researching the…
Abstract
Purpose
This study aims to probe the applicability of 2-mercaptobenzothiazole (MBT) functionalized ionic liquids (ILs) as additives in lithium complex grease (LCG) by researching the corrosion inhibiting, rheological and tribological performances.
Design/methodology/approach
Electrochemical tests such as electrochemical impedance spectroscopy and potentiodynamic polarization curves were used on Gamry electrochemical workstation to research the corrosion inhibition properties of ILs in 1.0 M HCl corrosive solution. The rheological properties of different grease samples were tested on a rheometer. The tribological properties were investigated on SRV-V oscillating reciprocating friction and wear tester. Scanning electron microscope, X-ray spectrometer and X-ray photoelectron spectrometer were used to characterize the lubricating mechanism.
Findings
The 2-MBT functionalized ILs have excellent corrosion inhibition properties. When used as additives in LCG, they both exhibited enhancing effects on thermostability, colloid stability and structural recoverability, and furthermore, outstanding friction-reducing and antiwear properties were also obtained. Surface analysis indicated that the superior lubricating performances of 2-MBT functionalized ILs were mainly ascribed to the formation of tribochemical products on wear tracks, including organic compounds with C–O bond, Fe2O3 and FeS2.
Originality/value
The 2-MBT-based ILs synthesized in this study were multifunctional additives with excellent corrosion inhibiting and tribological properties, which would have a very broad application prospect in lubricating grease industry.
Details
Keywords
Mauricio Pérez Giraldo, Mauricio Vasquez, Alejandro Toro, Robison Buitrago-Sierra and Juan Felipe Santa
This paper aims to develop a stable gel-type lubricant emulating commercial conditions. This encompassed rheological and tribological assessments, alongside field trials on the…
Abstract
Purpose
This paper aims to develop a stable gel-type lubricant emulating commercial conditions. This encompassed rheological and tribological assessments, alongside field trials on the Medellín tram system.
Design/methodology/approach
The gel-type lubricant with graphite and aluminum powder is synthesized. Rheological tests, viscosity measurements and linear viscoelastic regime assessments are conducted. Subsequently, tribological analyses encompassing four-ball and twin disc methods are executed. Finally, real-world testing is performed on the Medellín tram system.
Findings
An achieved lubricant met the stipulated criteria, yielding innovative insights into the interaction of graphite and aluminum powder additives under varying tests.
Originality/value
Novel findings are unveiled regarding the interaction of graphite and aluminum powder additives in tribological, rheological and real-world trials. In addition, the wear behavior of polymers is observed, along with the potential utilization of such additives in tramway systems.
Details
Keywords
Hui Zhao, Shunzhen Ren, Zhengbo Zhong, Zhipeng Li and Tianhui Ren
This study aims to reveal the tribological mechanism of synergistic effect between MoDTC and P-containing additives in aluminum-based grease.
Abstract
Purpose
This study aims to reveal the tribological mechanism of synergistic effect between MoDTC and P-containing additives in aluminum-based grease.
Design/methodology/approach
The authors prepared a molybdenum dialkyl dithiocarbamate (MoDTC) and revealed the tribological mechanism of synergistic effect between MoDTC and P-containing additives in aluminum-based grease by combining with ZDDP and P-containing and S-free additives.
Findings
The MoDTC the authors prepared has good friction-reducing and anti-wear properties in aluminum-based grease and has an obvious synergistic effect with ZDDP. MoDTC and ZDDP have a significant synergistic effect on the tribological properties in aluminum-based grease, mainly because of the formation of phosphates and metaphosphates as well as more MoS2 in the friction film. P element plays a facilitating role in the chemical conversion of MoDTC to MoS2.
Originality/value
The experiments of MoDTC with tributyl phosphate and trimethylphenyl phosphate confirm that the P element plays a facilitating role in the chemical conversion of MoDTC into MoS2.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0410
Details
Keywords
Gabi N. Nehme and Najat G. Nehme
The purpose of variable loading conditions (392 N-785N-392N-785N) with break-in period were used to study interactions between zinc dialkyl dithiophosphate (ZDDP) 0.1 P…
Abstract
Purpose
The purpose of variable loading conditions (392 N-785N-392N-785N) with break-in period were used to study interactions between zinc dialkyl dithiophosphate (ZDDP) 0.1 P% (phosphorus) and fine-grade molybdenum disulfide (MoS2) 3%, in different mixtures of NLGI 2 lithium stearate grease. Four-ball wear tests were used to evaluate the tribological properties of different grease mixtures such as coefficient of friction and wear. ASTM 2266 as reported by earlier studies is useful, but it is not representative of real-life applications where variable loads and speeds and different break-in periods play a role and could change the results and the nature of tribofilms.
Design/methodology/approach
In this study, chemical and mechanical properties of tribofilms were examined. Moreover, design of experiment was used to examine the data and shorten experimentation time. Research described here is investigating variable loading conditions for real-life applications by using a break-in period of 2 min at the start to minimize asperities and establish a clean surface. Design expert (DOE) analyzes responses to reveal those variables that are single factor and those that are multifactor whether synergistically or antagonistically.
Findings
The results indicated that spectrum loading with break-in period showed reduction in wear when tested in greases with ZDDP/MoS2 combinations. Ramping up or down the load every 7.5 min for a rotational speed of 1,200 rpm and a total of 36,000 revolutions or 30-min time slowed the wear properties of lithium-based grease under different MoS2 and ZDDP concentrations. Experiments indicated that wear was largely dependent on the loading condition and ZDDP additives during specific break-in period at 1,200 rotational speed. It is believed that MoS2 greases perform better under spectrum loading and under constant loading when mixed with ZDDP phosphorus.
Originality/value
This research indicates that there is a synergistic interaction between ZDDP, MoS2 and variable loading especially when a break-in period is applied. The results indicated that wear was largely dependent on the specific speed used with spectrum loading as presented in the energy dispersive spectroscopy and the Auger electron spectroscopy analysis, and thus a 3% MoS2 grease with ZDDP (phosphorus: 0.1 Wt.%) are needed to improve the wear resistance and improve the friction characteristics.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2024-0016/
Details
Keywords
Fei Shang, Bo Sun and Dandan Cai
The purpose of this study is to investigate the application of non-destructive testing methods in measuring bearing oil film thickness to ensure that bearings are in a normal…
Abstract
Purpose
The purpose of this study is to investigate the application of non-destructive testing methods in measuring bearing oil film thickness to ensure that bearings are in a normal lubrication state. The oil film thickness is a crucial parameter reflecting the lubrication status of bearings, directly influencing the operational state of bearing transmission systems. However, it is challenging to accurately measure the oil film thickness under traditional disassembly conditions due to factors such as bearing structure and working conditions. Therefore, there is an urgent need for a nondestructive testing method to measure the oil film thickness and its status.
Design/methodology/approach
This paper introduces methods for optically, electrically and acoustically measuring the oil film thickness and status of bearings. It discusses the adaptability and measurement accuracy of different bearing oil film measurement methods and the impact of varying measurement conditions on accuracy. In addition, it compares the application scenarios of other techniques and the influence of the environment on detection results.
Findings
Ultrasonic measurement stands out due to its widespread adaptability, making it suitable for oil film thickness detection in various states and monitoring continuous changes in oil film thickness. Different methods can be selected depending on the measurement environment to compensate for measurement accuracy and enhance detection effectiveness.
Originality/value
This paper reviews the basic principles and latest applications of optical, electrical and acoustic measurement of oil film thickness and status. It analyzes applicable measurement methods for oil film under different conditions. It discusses the future trends of detection methods, providing possible solutions for bearing oil film thickness detection in complex engineering environments.
Details
Keywords
Zhicai Du, Qiang He, Hengcheng Wan, Lei Zhang, Zehua Xu, Yuan Xu and Guotao Li
This paper aims to improve the tribological properties of lithium complex greases using nanoparticles to investigate the tribological behavior of single additives (nano-TiO2 or…
Abstract
Purpose
This paper aims to improve the tribological properties of lithium complex greases using nanoparticles to investigate the tribological behavior of single additives (nano-TiO2 or nano-CeO2) and composite additives (nano-TiO2–CeO2) in lithium complex greases and to analyze the mechanism of their influence using a variety of characterization tools.
Design/methodology/approach
The morphology and microstructure of the nanoparticles were characterized by scanning electron microscopy and an X-ray diffractometer. The tribological properties of different nanoparticles, as well as compounded nanoparticles as greases, were evaluated. Average friction coefficients and wear diameters were analyzed. Scanning electron microscopy and three-dimensional topography were used to analyze the surface topography of worn steel balls. The elements present on the worn steel balls’ surface were analyzed using energy-dispersive spectroscopy and X-ray photoelectron spectroscopy.
Findings
The results showed that the coefficient of friction (COF) of grease with all three nanoparticles added was low. The grease-containing composite nanoparticles exhibited a lower COF and superior anti-wear properties. The sample displayed its optimal tribological performance when the ratio of TiO2 to CeO2 was 6:4, resulting in a 30.5% reduction in the COF and a 29.2% decrease in wear spot diameter compared to the original grease. Additionally, the roughness of the worn spot surface and the maximum depth of the wear mark were significantly reduced.
Originality/value
The main innovation of this study is the first mixing of nano-TiO2 and nano-CeO2 with different sizes and properties as compound lithium grease additives to significantly enhance the anti-wear and friction reduction properties of this grease. The results of friction experiments with a single additive are used as a basis to explore the synergistic lubrication mechanism of the compounded nanoparticles. This innovative approach provides a new reference and direction for future research and development of grease additives.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-09-2023-0291/
Details
Keywords
Yuchun Huang, Haishu Ma, Yubo Meng and Yazhou Mao
This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 to improve the tribological properties of M50 bearing steel with microporous channels.
Abstract
Purpose
This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 to improve the tribological properties of M50 bearing steel with microporous channels.
Design/methodology/approach
M50 matrix self-lubricating composites (MMSC) were designed and prepared by filling Sn–Ag–Cu and MXene–Ti3C2 in the microporous channels of M50 bearing steel. The tribology performance testing of as-prepared samples was executed with a multifunction tribometer. The optimum hole size and lubricant content, as well as self-lubricating mechanism of MMSC, were studied.
Findings
The tribological properties of MMSC are strongly dependent on the synergistic lubrication effect of MXene–Ti3C2 and Sn–Ag–Cu. When the hole size of microchannel is 1 mm and the content of MXene–Ti3C2 in mixed lubricant is 4 wt.%, MMSC shows the lowest friction coefficient and wear rate. The Sn–Ag–Cu and MXene–Ti3C2 are extruded from the microporous channels and spread to the friction interface, and a relatively complete lubricating film is formed at the friction interface. Meanwhile, the synergistic lubrication of Sn–Ag–Cu and MXene–Ti3C2 can improve the stability of the lubricating film, thus the excellent tribological property of MMSC is obtained.
Originality/value
The results help in deep understanding of the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti3C2 on the tribological properties of M50 bearing steel. This work also provides a useful reference for the tribological design of mechanical components by combining surface texture with solid lubrication.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0381/
Details
Keywords
Yingxiang Zhao, Junde Guo, Xiaoni Yan, Shan Du, Min Gong, Biao Sun, Junwen Shi and Wen Deng
The purpose of this paper is to investigate the friction and wear mechanisms in copper-based self-lubricating composites with MoS2 as the lubricating phase, which provides a…
Abstract
Purpose
The purpose of this paper is to investigate the friction and wear mechanisms in copper-based self-lubricating composites with MoS2 as the lubricating phase, which provides a theoretical basis for subsequent research on high-performance copper-based self-lubricating materials.
Design/methodology/approach
Friction tests were performed at a speed of 100 r/min, a load of 10 N, a friction radius of 5 mm and a sliding speed of 30 min. Friction experiments were carried out at RT-500°C. The phase composition of the samples was characterized by X-ray diffraction of Cu Ka radiation, and the microstructure, morphology and elemental distribution were characterized by scanning electron microscopy and energy dispersive spectroscopy. Reactants and valences formed during the wear process were analyzed by X-ray photoelectron spectroscopy.
Findings
The addition of MoS2 can effectively improve friction-reducing and anti-wear action of the matrix, which is beneficial to form a lubricating film on the sliding track. After analyzing different changing mechanism of the sliding tracks, the oxides and sulfides of MoS2, MoO2, Cu2O, CuO and Ni(OH)2 were detected to form a synergetic lubricating film on the sliding track, which is responsible for the excellent tribological properties from room to elevated temperature.
Research limitations/implications
For self-lubrication Cu–Sn–Ni–MoS2 material in engineering field, there are still few available references on high-temperature application.
Practical implications
This paper provides a theoretical basis for the following research on copper-based self-lubricating materials with high performance.
Originality/value
With this statement, the authors hereby certify that the manuscript is the results of their own effort and ability. They have indicated all quotes, citations and references. Furthermore, the authors have not submitted any essay, paper or thesis with similar content elsewhere. No conflict of interest exits in the submission of this manuscript.
Details
Keywords
Ziyan Lu, Feng Qiu, Hui Song and Xianguo Hu
This paper aims to solve the problems molybdenum disulfide (MoS2) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface…
Abstract
Purpose
This paper aims to solve the problems molybdenum disulfide (MoS2) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.
Design/methodology/approach
MoS2/C60 nanocomposites were prepared by synthesizing molybdenum disulfide (MoS2) nanosheets on the surface of hydrochloric acid-activated fullerenes (C60) by in situ hydrothermal method. The composition, structure and morphology of MoS2/C60 nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.
Findings
MoS2/C60 nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS2/C60 was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.
Originality/value
MoS2/C60 composite nanoparticles were prepared by in-situ formation of MoS2 nanosheets on the surface of C60 activated by HCl through hydrothermal method and were used as potential lubricating oil additives.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-10-2023-0321/
Details
Keywords
Davood Javanmardi and Mohammad Ali Rezvani
Bearings are critical components used to support loads and facilitate motion for rotating and sliding parts of the machinery. Bearing malfunctions can cause catastrophic failures…
Abstract
Purpose
Bearings are critical components used to support loads and facilitate motion for rotating and sliding parts of the machinery. Bearing malfunctions can cause catastrophic failures. Hence, failure analysis and endeavors to improve bearing performance are essential discussions for worldwide designers, manufacturers and end users of vital machinery. This study aims to investigate a type of roller bearing from the railway industry with premature failures. The task arises because locomotives’ maintenance and service life quality are vital to railway operations while providing transportation services for the nation. To assist in maintaining the designated locomotives, the present study scrutinizes the causes of failure of heavy-duty roller bearings from locomotive bogie axleboxes.
Design/methodology/approach
It is intended to inspect this bearing service life and statistically scrutinize its design parameters to reveal the failures’ shortcomings and origins. The significant measures include examinations of their failures’ primary and vital factors by comparing them with a real-life service history of 16 roller bearings of the same type. The bearings come from the axleboxes of a locomotive bogie with an axle load of 20 tons. The bearing loads are estimated using the EN13104 standard document and confirmed by the finite element method using ABAQUS engineering software. To validate the finite element modeling results, the bearings’ stress analysis is performed using the Hertzian contact theory that demonstrated perfect conformity. The said methods are also used to search for the areas susceptible to failures in these bearings. With the inclusion and exploitation of the bearing maintenance conditions and the logbook recordings of the locomotives for the past seven years, the critical cause for this type of bearing’s failures is surveyed and discussed.
Findings
With the inclusion and exploitation of the bearing maintenance conditions and the logbook recordings of the locomotives for the past seven years, the critical cause for this type of bearing’s failures is surveyed and discussed. As a crucial result, it is found that deprived maintenance and inadequate lubrication are the root causes of the loss of the selected bearings.
Originality/value
For the designated locomotives, the origins of the heavy-duty roller bearing failures and its design shortcomings are revealed by examining and comparing them with a real-life service history of many of the same types of bearings. The novelty of the research is in using the combination of the methods mentioned above and its decent outcome.
Details