The durability of concrete containing recycled aggregates, sourced from concrete specimens that have been tested in laboratory testing facilities, remains understudied. This paper aims to present the results of experiments investigating the effect of incorporating such type of concrete waste on the strength and durability-related properties of concrete.

A total of 77 concrete cylinders sized Ø100 × 200 mm with varying amount of recycled concrete aggregate (RCA) (0%–100% by volume, at 25% increments) and maximum aggregate size (12.5, 19.0 and 25.0 mm) were fabricated and tested for slump, compressive strength, sorptivity and electrical resistivity. Disk-shaped specimens, 50-mm thick, were cut from the original cylinders for sorptivity and resistivity tests. Analysis of variance and post hoc test were conducted to detect statistical variability among the data.

Compared to regular concrete, a reduction of slump (by 18.6%), strength (15.1%), secondary sorptivity (31.5%) and resistivity (17.0%) were observed from concrete containing 100% RCA. Statistical analyses indicate that these differences are significant. In general, an aggregate size of 19 mm was found to produce the optimum value of slump, compressive strength and sorptivity in regular and RCA-added concrete.

The results of this study suggest that comparable properties of normal concrete were still achieved by replacing 25% of coarse aggregate volume with 19-mm RCA, which was processed from laboratory-tested concrete samples. Therefore, such material can be considered as a potential and sustainable alternative to crushed gravel for use in light or nonstructural concrete construction.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

The compressive strength of concrete depends on many interdependent parameters; its exact prediction is not that simple because of complex processes involved in strength development. This study aims to predict the compressive strength of normal concrete and high-performance concrete using four datasets.

In this paper, five established individual Machine Learning (ML) regression models have been compared: Decision Regression Tree, Random Forest Regression, Lasso Regression, Ridge Regression and Multiple-Linear regression. Four datasets were studied, two of which are previous research datasets, and two datasets are from the sophisticated lab using five established individual ML regression models.

The five statistical indicators like coefficient of determination (R²), mean absolute error, root mean squared error, Nash–Sutcliffe efficiency and mean absolute percentage error have been used to compare the performance of the models. The models are further compared using statistical indicators with previous studies. Lastly, to understand the variable effect of the predictor, the sensitivity and parametric analysis were carried out to find the performance of the variable.

The findings of this paper will allow readers to understand the factors involved in identifying the machine learning models and concrete datasets. In so doing, we hope that this research advances the toolset needed to predict compressive strength.

One of the often-employed building constituents in the construction sector is concrete, which involves hydration of cement, leading to the generation of carbon footprints during its production. Also, massive amount of natural aggregate is illegally mined, which poses serious environmental issues along with ecological misbalance. Researchers are in continuous search of appropriate substitutes to mitigate those challenges and develop innovative concrete mix. Consequently, depletion of natural resources, the disturbances to the environmental and ecological imbalance will reduce. The purpose of this study is to develop a Portland Slag Cement based novel sustainable concrete incorporating Alccofine and Recycled Refractory Brick as fractional replacement of cement and fine aggregate, respectively and evaluate its destructive, non-destructive and microstructural properties.

M25 grade of concrete adopting 0.45 water-binder proportion, with diverse percentage of Alccofine as fractional substitution of cement and 20% of recycled refractory brick (RRB) as fine aggregate, has been cast and evaluated for diverse mechanical strength following a curing of 7, 14 and 28 days. Scanning electron microscopic analysis has been carried out to study the microstructural changes in the specimens.

Supplementary use of Alccofine enhanced normal compressive strength of sustainable concrete mix blended with Portland Slag Cement by a large amount at all levels of 7, 14 and 28 days of curing. Test results indicated development of a favourable high-strength sustainable concrete mix by substituting cement with Alccofine.

This manuscript has demonstrated the possibility of developing sustainable concrete blends by incorporating Alccofine 1203 and RRB as partial replacement of Portland Slag Cement and natural fine aggregate, respectively. The strength and potential of concrete incorporating RRB for wider and special application in adverse environmental conditions having higher thermal gradient, as RRB is a valuable waste from high temperature kiln and furnaces. Alccofine 1203 has been included in the concrete mix as an alternative to Portland Slag Cement to improve the mechanical strength properties and durability of concrete intended for adverse environmental application.

This study aims at designing consistent and durable concrete by making use of waste materials. An investigation has been carried out to evaluate the performance of conventional and optimal concrete (including 5% GP) at high temperatures for different exposure times.

An experimental work is carried out to compare the conventional and optimal concrete with respect to weight loss, mechanical strength characteristics (compressive, tensile and flexural) after exposed to 100, 200 and 300 °C with 1, 2 and 3 h duration of exposure followed by cooling in furnace for 24 h and then air cooling.

The workability of granite powder modified concrete decreases as percentage of replacement increases. Compressive, tensile and flexural strengths all increased at 100 °C when compared to strength characteristics at normal temperature, regardless of the exposure conditions, and there was no weight loss noticed. For 200 and 300 °C, the strengths were decreased compared to normal temperature and an elevated temperature of 100 °C, as weight loss of concrete specimens are observed to be decreased at these temperatures. So, the optimum elevated temperature can be concluded as 100 °C.

Incorporating pozzolanic binder (granite powder) as cement replacement subjecting to elevated temperatures in an electric furnace is the research gap in this area. Many of the works were carried out replacing GP for fine aggregate at normal temperatures and not at elevated temperatures.

Present work deals with the partial substitution of cement by waste demolished concrete powder (WDP) for reducing the carbon footprints of concrete.

Control specimens and the specimens with 20% WDP as fractional substitute of cement were prepared. The waste powder was thermally activated at 825 °C prior to its use in the mix. The prepared specimens were evaluated in terms of density, workability, mechanical strength, Ultrasonic pulse velocity (UPV) and rebound hammer (RH).

The results showed that with the substitution, the workability of the mix increased, while the density decreased. A decrement within a 20% limit was found in compressive strength. The UPV and RH results were closely linked to the other results as mentioned above.

The study deals with only M15 concrete and the substitution level of only 20% as a baseline.

The concrete containing 20% WDP is lightweight and more workable. Moreover, its strength at 28 days is 14 MPa, only 1 MPa lesser than the characteristic strength.

The WDP can be recycled and the dumping in landfills can be reduced. This is an important effort towards the decarbonation of concrete.

Previous literature indicates that the WDP has been frequently used as a partial replacement of aggregates. However, some traces of secondary hydration were also reported. This work considers the effect of partial substitution of cement by the WDP.

The research investigates the impact of concrete design methods on performance, emphasizing environmental sustainability. The study compares the modified Bolomey method and Abrams’ law in designing concretes. Significant differences in cement consumption and subsequent CO2 emissions are revealed. The research advocates for a comprehensive life cycle assessment, considering factors like compressive strength, carbonation resistance, CO2 emissions, and cost. The analysis underscores the importance of evaluating concrete not solely based on strength but also environmental impact. The study concludes that a multicriteria approach, considering the entire life cycle, is essential for sustainable concrete design, addressing durability, environmental concerns, and economic factors.

The study employed a comprehensive design and methodology approach, involving the formulation and testing of 20 mixed concretes with strengths ranging from 25 MPa to 45 MPa. Two distinct design methods, the modified Bolomey method (three equations method) and Abrams’ law, were utilized to calculate concrete compositions. Laboratory experiments were conducted to validate the computational models, and subsequent analyses focused on assessing differences in cement consumption, compressive strength, CO2 emissions, and concrete resistance to carbonation. The research adopted a multidisciplinary perspective, integrating theoretical analysis, laboratory testing, and life cycle assessment to evaluate concrete performance and sustainability.

Conclusion from the study includes substantial variations (56%–112%) in cement content, depending on the calculation method. Abrams' law proves optimal for compressive strength (30 MPa–45 MPa), while the three equations method yields higher actual strength (30%–51%). Abrams' law demonstrates optimal cement use, but concrete designed with the three equations method exhibits superior resistance to aggressive environments. Cement content exceeding 450 kg/m³ is undesirable. Concrete designed with Abrams' law is economically favorable (12%–30% lower costs). The three equations method results in higher CO2 emissions (38–83%), emphasizing the need for life cycle assessment.

This study’s originality lies in its holistic evaluation of concrete design methods, considering environmental impact, compressive strength, and cost across a comprehensive life cycle. The comparison of the traditional Abrams' law and the three equations method, along with detailed laboratory tests, contributes novel insights into optimal cement use and concrete performance. The findings underscore the importance of a multicriteria approach, emphasizing sustainability and economic viability. The research provides valuable guidance for engineers and policymakers seeking environmentally conscious and economically efficient concrete design strategies, addressing a critical gap in the field of construction materials and contributing to sustainable infrastructure development.

The purpose of this study is to forecast the mechanical properties of ternary blended concrete (TBC) modified with oyster shell powder (OSP) and shea nutshell ash (SNA) using deep neural network (DNN) models.

DNN models with three hidden layers, each layer containing 5–30 nodes, were used to predict the target variables (compressive strength [CS], flexural strength [FS] and split tensile strength [STS]) for the eight input variables of concrete classes 25 and 30 MPa. The concrete samples were cured for 3–120 days. Levenberg−Marquardt's backpropagation learning technique trained the networks, and the model's precision was confirmed using the experimental data set.

The DNN model with a 25-node structure yielded a strong relation for training, validating and testing the input and output variables with the lowest mean squared error (MSE) and the highest correlation coefficient (R) values of 0.0099 and 99.91% for CS and 0.010 and 98.42% for FS compared to other architectures. However, the DNN model with a 20-node architecture yielded a strong correlation for STS, with the lowest MSE and the highest R values of 0.013 and 97.26%. Strong relationships were found between the developed models and raw experimental data sets, with R² values of 99.58%, 97.85% and 97.58% for CS, FS and STS, respectively.

To the best of the authors’ knowledge, this novel research establishes the prospects of replacing SNA and OSP with Portland limestone cement (PLC) to produce TBC. In addition, predicting the CS, FS and STS of TBC modified with OSP and SNA using DNN models is original, optimizing the time, cost and quality of concrete.

This study investigated the potential of partially replacing cement with red mud (RM) in concrete and examined its effects on its mechanical properties and microstructure. This study aims to explore sustainable alternatives to traditional cement and evaluate the performance of concrete mixtures with varying percentages (%) of RM as cement replacement.

This research aims to comprehensively understand the impact of RM on concrete, aiming for both environmental sustainability and improved construction materials. Subsequently, concrete mixtures were prepared with varying RM contents, ranging from 0% to 21% in increments of 3%, replacing cement. The workability of these mixtures was evaluated using the Slump Cone Test, whereas their mechanical properties (compressive strength, flexural strength and split tensile strength) were assessed through standardized tests. The durability was further investigated via water absorption, acid attack, rapid chloride permeability tests, open porosity test and Sorptivity test. To gain deeper insights into the internal structure of concrete, microstructure analysis was conducted using X-ray diffraction and scanning electron microscopy. Finally, the results were analyzed and quantified.

The finding demonstrates that substituting 12% of cement with RM not only boosts the mechanical characteristics of concrete but also mitigates waste disposal. The microstructural analysis identified a denser cement matrix and improved bonding between the cement paste and the aggregates, suggesting potential improvements in strength and durability.

These results suggest that RM can be efficiently used to produce sustainable concrete with potential applications in construction projects with environmental considerations.

In this experimental investigation, the behavior of strengthened/repaired heat-damaged one-way self-compacted concrete (SCC) slabs with opening utilizing near-surface-mounted-carbon fiber reinforced polymers (NSM-CFRP) strips was explored.

CFRP strip configurations, number of strips and inclination were all investigated in this study. For three hours, slabs were exposed to temperatures of 23°C and 500°C. Four-point load was applied to control slabs, enhanced slabs and repaired slabs.

The results indicate that exposing the slabs to high temperatures reduces their load capability. The number of strips and angle of inclination around the slab opening have a considerable impact on the performance of the strengthened and/or repaired slabs, according to the experimental results. The load capacity, toughness and ductility index of a strengthened and/or repaired slab with opening increase as the number of CFRP strips increases by 143.8–150.5%, 137.3–149.9% and 122.3–124.5%, respectively. The use of NSM strips around the opening with zero inclination showed higher load compared to the NSM strips around the opening with other angles.

It is frequently important to construct openings in the slabs for ventilation, electrical supply, and other purposes. Making openings in slabs might affect the structure’s performance since the concrete and reinforcing would be cut off. SCC is a new type of concrete mixture that can fill in all the voids in the formwork with its own weight without the help of external vibration.  As a result, it is necessary to reinforce the slab under flexure and increase the flexural strength of the SCC slab. Therefore, this work investigates the effect of using NSM-CFRP strip  on the behavior of one way SCC slabs that have been heat-damaged.