The occurrence of multiple hazards in extreme conditions is not unknown nowadays, but the sustainability of the reinforced concrete structures under such scenarios form competitive challenges in civil engineering profession. Among all, fire following earthquake (FFE) is categorized under multiple extreme load scenarios which causes sequential damages to the structures. This paper aims to experiment a full-scale RC frame sub-assemblage for the FFE scenario and assess each stage of damage through the nondestructive testing method.

Two levels of simulated earthquake damages, i.e. immediate occupancy (IO) level and life safety (LS) level of structural performance were induced to the test frame and then, followed by a realistic compartment fire of 1 h duration. Also, the evaluation of damage to the RC frame after the fire subsequent to the earthquake was carried out by obtaining the ultimate capacity of the frame. Ultrasonic pulse velocity and rebound hammer test were conducted to assess the structural endurance of the damaged frame. Cracks were also marked during mechanical damages to the test frame to study the nature of its propagation.

Careful visual inspection during and after the fire test to the test frame were done. To differentiate between concrete chemically affected by the fire or physically damaged is an important issue. In situ inspection and laboratory tests of concrete components have been performed. Concrete from the test frame was localized with thermo-gravimetric analysis. The UPV results exhibited a sharp decrease in the strength of the concrete material which was also confirmed via the DTA, TGA and TG results. It is important to evaluate the residual capacity of the entire structure under the FFE scenario and propose rehabilitation/retrofit schemes for the building structure.

The heterogeneity in the distribution of the damage has been identified due to variation of fire exposure. The study only highlights the capabilities of the methods for finding the residual capacity of the RC frame sub-assemblage after an occurrence of an FFE.

It is of find kind of research work on full-scale reinforced concrete building. In this, an attempt has been made for the evaluation of concrete structures affected by an FFE through nondestructive and destructive methods.

This paper aims to report a case study regarding the combined use of several non‐destructive techniques (NDTs) as a tool in the management of diagnosis and refurbishment of a damaged reinforced concrete building.

Four types of NDTs have been selected and carried out on the pillars of the building: visual inspection, electromagnetic rebar location, sonic test and rebound hammer test. The campaign has been planned and run in order to get the highest amount of reliable data about materials degradation and structural safety with limited costs and limited interference with the functionality of the building.

The diagnostic campaign highlighted the usefulness of the selected techniques in the diagnosis of the type and the amount of degradation, thus permitting a plan of refurbishments to be defined, and to get a realistic estimation of restoration costs.

NDTs' ability to specifically identify a type of damage may be viewed as a reliable tool in assessing and managing the structural life‐cycle cost.

The presented case study highlighted that NDTs are very likely to locate and quantify the damage of materials and buildings, so that they can be considered as one of the most important parts of health monitoring of civil structures and infrastructures.

Concrete is a widely used construction material which can be prepared using locally available resources (aggregates, cement and water) by following relevant standard guidelines. The residual properties of concrete determined by heating in an electric furnace may not produce a similar effect of fire. The purpose of this paper is to compare the effect of a fire with that coming from the exposure of normal strength concrete to predetermined reference temperatures, for which two sets of specimens were heated in a fire furnace provided with gas burners and an electric furnace.

The concrete cubes and cylinders were subjected to 200^oC, 400^oC, 600oC and 800^oC temperature in a gas-controlled fire furnace and an electric furnace for 2 h. The physical properties and mechanical properties of concrete were determined after cooling the specimens in air. The quality of concrete specimens was determined using the ultrasonic pulse velocity test, and surface hardness of the heat-exposed cubes was recorded using the Schmidt rebound hammer.

The fire-exposed specimens were found to have lower residual compressive strength, tensile strength and higher porosity/voids/internal cracks than the specimens heated in an electric furnace at the same temperature. Further, a good agreement with compressive strength and rebound numbers was observed for each of the two heating systems (flames coming from gas burners and electric furnace).

Normal strength concrete specimens exposed to heat in an electric furnace will not give the same effect of fire having the same maximum temperature. Further, it is noticed that concrete subjected to elevated temperature is sensitive to heating modalities, be it the flames of a gas furnace or the radiation of an electric furnace.

The purpose of the study is to evaluate the suitability of post-fire curing for normal and Recycled Aggregate Concretes (RAC) with and without fibres.

The study includes the testing of RAC specimens, i.e. 150 mm cubes and cylinders with 300 mm length and 150 mm diameter with hybrid fibres (0.15% polypropylene fibres + 0.35% steel fibres) along with fly ash. The specimens were exposed to elevated temperatures between 400 to 700°C with 100°C intervals for 2 h of duration and the post-fire exposed samples were further subjected to water curing for a period of 7 days. The compressive strength, split tensile strength and Rebound Hammer Number (RHN) were measured at room temperature, after exposure to elevated temperatures and post-fire curing.

The result shows that the compressive strength reduces by a maximum of 61.25% for 700°C and maximum retain in strength, i.e. 71.2% (in comparison to specimens kept at room temperature) is observed for 600°C post-fire cured specimens. The split tensile strength reduces by more than half for 500°C and above temperatures, whereas 400°C specimens exhibits a significant regain in strength after post-fire curing. To validate the results of compressive strength, the Rebound Hammer test has been conducted. The RHN value decreases by 41.3% for 700°C specimens and the effectiveness of post-fire curing is observed to be considerable up to 500°C.

The conclusions from the study can be used in assessing the extent of damage and to check the suitability of post-fire curing in further continuing the utilisation of a fire damaged structure.

Utilisation of secondary materials like recycled aggregates and fly ash can be made in the production of concrete.

Specimens with fibres performed better when compared to specimens without fibres and post-fire curing is found to be effective up to 500°C.

The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

Roller compacted concrete (RCC) pavement is used in areas subjected to heavy impact loads; therefore, higher impact resistance is a desirable property of consideration. This study aims to investigate the effect of partial replacement of fine aggregate with crumb rubber (CR) and the addition of nanosilica (NS) by weight of cementitious materials on the impact resistance of roller compacted rubbercrete (RCR).

Four replacement levels of CR (0, 10, 20 and 30 per cent) and four addition levels of NS (0, 1, 2 and 3 per cent) were considered. The impact resistance test was carried out using the drop weight test recommended by ACI 544.

The results showed that the impact resistance of RCR increases with an increase in both CR and NS addition, though for CR above 20 per cent, sudden drop in impact resistance was observed. However, NS reduces the ductility of RCR by decreasing the post-cracking impact resistance. Response surface methodology was used to develop models for predicting the impact resistance of RCR, and the developed models showed a high degree of correlation. As a result of wide variations in the impact drop test data, two-parameter Weibull distribution function was used for the data analysis, and it was found that the probabilistic distributions of the first crack and ultimate failure impact resistance follow the two-parameter Weibull distribution function.

In this work, the effect of partial replacement of fine aggregate with CR and the addition of NS by weight of cementitious materials on the impact resistance of RCC pavement has been investigated. CR has been used to increase the impact resistance of RCC Pavement.

Debonding, leading to the subsequent detachment of applied finishes to concrete buildings, is becoming a serious problem in many parts of the world. Checking building elevations by employing the technique of Infra‐red Thermography using a process developed by the writer can give advance warning of potential defects. This can enable early remedial action to be undertaken to repair a building surface before it becomes detached from the concrete substrate, possibly resulting in a hazard to passers‐by. The thermographic test method has been compared with other more traditionally used NDT methods including sounding, rebound hammer, and ultrasonic pulse velocity measurements. Although the thermographic equipment is initially more expensive, the surveying method can be shown to be faster and more accurate than any other technique currently available for this type of building evaluation.

Concrete decay has become a major ongoing problem for the developed world, affecting all manner of structures. The purpose of the reported research is thus to advance the prospects for the realisation of high capacity, robotic repair systems through sensor technology. Here, the particular target is the removal of defective concrete by the hydro‐erosion method. The main advantages of the method are that it is kind to the structure while having the potential to produce high definition excavations. Sensing has been investigated for both prediction of the hydro‐erosion task and real‐time process feedback. The latter is complicated by the extremely destructive hydro‐erosion environment, which precludes the use of conventional sensing probes. For this, vibration and process noise have been investigated to determine if diagnostic characteristics are detectable. To support the task, a predictive basis has been developed using non‐destructive testing (NDT) sensors within a data fusion model. Covermeter, rebound hammer, impact echo and surface dampness NDT data are fed into this. Progress is reported on this part of the ongoing research.

As concrete structures exposed to fire behave in most cases very well, it could be of economic interest to repair the fire damaged structure. For this purpose a damage assessment based on scientific research is required as first step. In this paper, the Schmidt Rebound Hammer and colorimetry are addressed as tools for this assessment. Firstly, the effect of both methods is studied on heated siliceous concrete specimens under laboratory conditions. Secondly, the practical applicability of both methods is examined by evaluating the fire damage of a concrete girder exposed to a real fire. Both techniques show to be very useful in evaluating the fire damage of the girder.

Using coconut shell aggregates (CSA) in concrete benefits agricultural waste management and reduces the demand for mineral resources. Several studies have found that concrete containing CSA can achieve strengths that are comparable to regular concrete. The purpose of the present work is to evaluate the concrete’s durability-related properties to supplement these earlier findings.

Cylindrical specimens were prepared with a constant water–cement ratio of 0.50 and CSA content ranging from 0% to 50% (at 10% increment) by volume of the total coarse aggregates. The specimens were cured for 28 days and then tested for density, surface hardness, electrical resistivity and water sorptivity. The surface hardness was measured to describe the concrete resistance to surface wearing, while the resistivity and sorptivity were evaluated to describe the material’s resistance to fluid penetration.

The results showed that the surface hardness of concrete remained on average at 325 Leeb and did not change significantly with CSA addition. The distribution of surface hardness was also similar across all CSA groups, with the interquartile range averaging 59 Leeb. These results suggest that the cement paste and gravel stiffness had a more pronounced influence on the surface hardness than CSA. On the other hand, concrete became lighter by about 9%, had lower resistivity by 80% and had significantly higher initial sorptivity by up to 110%, when 50% of its natural gravel was replaced with CSA. Future work may be done to improve the durability of CSA when used as coarse aggregate.

The present study is the first to show the lack of correlation between CSA content and surface hardness. It would mean that the surface hardness test may not completely capture the porous nature of CSA-added concrete. The paper concludes that without additional treatment prior to mixing, CSA may be limited only to applications where concrete is not in constant contact with water or deleterious substances.