The main aim of the current study is to investigate the effect of Anti-Crack HP 67/36 glass fibre on the mechanical performance of mortars made of cement, with a focus on post-cracking evaluations using the digital image correlation (DIC) technique.

Experimental tests were carried out on 36-mm long fibres at 0.8% by volume and added to the normal strength (NSM), high strength (HSM) and high strength mortar with fly ash (HSMFA) mortars. CEM I 52.5 CP2 NF, CEM II/A-L 42.5 NF and CEM III/C 32.5 N-SR PM were used for each series of mortar to assess the performance of the glass fibres with the types of cement. F-class fly (FA) ash was used to reduce global CO₂ emissions.

The mortar’s strength decreased as the cement types changed from CEM I to CEM II and III. However, due to changes in the portlandite content of the cement, water porosity increased for both types of mortar, without and with fibre. It was also found that using glass fibre increased flexural strength more than compressive strength, regardless of the type of cement used. For all the strength classes, it was found that the mortar mixes with CEM I had the highest critical crack opening (w_c) and fracture energy (G_F), followed by CEM II and III. No significant effects were observed in the mortar’s property by replacing fly ash (12%).

Only mortars were formulated in this study, but the results must be verified at the concrete scale.

Validation of the DIC technique to characterize the post-cracking behaviour of cement-based material. Use of glass fibres to improve the material’s resistance to cracking.

Use of CEM II and CEM III cements with low CO₂ footprint instead of CEMI without altering the mechanical performance of the material.

The work is a further contribution to studying the cracking behaviour of several series of variable mortars depending on the resistance class and the type of cement used.

This study aims to develop a polymer cement-based waterproof coating with self-healing capability to efficiently and intelligently solve the building leakage caused by cracking of waterproof materials, along with excellent durability to prolong its service life.

Ion chelators are introduced into the composite system based on ethylene vinyl acetate copolymer emulsion and ordinary Portland cement to prepare self-healing polymer cement-based waterproof coating. Hydration, microstructure, wettability, mechanical properties, durability, self-healing performance and self-healing products of polymer cement-based waterproof coating with ion chelator are investigated systematically. Meanwhile, the chemical composition of self-healing products in the crack was examined.

The results showed that ion chelators could motivate the hydration of C₂S and C₃S, as well as the formation of hydration products (C-S-H gel) of the waterproof coating to improve its compactness. Compared with the control group, the waterproof coating with ion chelator had more excellent water resistance, alkali resistance, thermal and UV aging resistance. When the dosage of ion chelator was 2%, after 28 days of curing, cracks with a width of 0.29 mm in waterproof coating could fully heal and cracks with a width of 0.50 mm could achieve a self-healing efficiency of 72%. Furthermore, the results reveal that the self-healing product in the crack was calcite crystalline CaCO₃.

A novel ion chelator was introduced into the composite coating system to endow it with excellent self-healing ability to prolong its service life. It has huge application potential in the field of building waterproofing.

Invented in late 1890s, asbestos cement sheeting rose to prominence during the post-Second World War period as a building material for low-cost housing by state housing commissions and low-income families (“fibro homes”). The adverse health effects of asbestos fibres in the building industry and home renovation activities are well documented. Fibro homes of the 1950s and 1960s are increasingly coming under the gaze of heritage studies, which brings to the fore the question of how to deal with the asbestos cement sheeting most are clad with.

This paper provides the first systematic review to assess the literature (126 papers were identified in Google Scholar and scanned for content) on the conservation management of asbestos cement sheeting in heritage properties.

Overall, engagement with the conservation management of asbestos cement sheeting in heritage properties was low, with only two sources dealing with asbestos cement sheeting in any level of detail. The studies note that if asbestos cement sheeting is in good condition, it should be left alone. Numerous conservation and repair options do exist, in particular the application of (coloured) sealants that extend the life of asbestos cement sheets and asbestos cement roofing.

This paper represents the first systematic review to assess conservation management options for asbestos cement sheeting in heritage properties.

In recent years, fire accidents in engineering structures have often been reported worldwide, leading to a severe risk to life and property safety. The present study is carried out to evaluate the performance of Ground Granulated Blast Furnace Slag (GGBS) and fly ash–blended laterized mortars at elevated temperatures.

This test program includes the replacement of natural river sand with lateritic fine aggregates (lateritic FA) in terms of 0, 50 and 100%. Also, the ordinary Portland cement (OPC) was replaced with fly ash and GGBS in terms of 10, 20, 30% and 20, 40 and 60%, respectively, for producing blended mortars.

This paper presents results related to the determination of residual compressive strengths of lateritic fine aggregates-based cement mortars with part replacement of cement by fly ash and GGBS exposed to elevated temperatures. The effect of elevated temperatures on the physical and mechanical properties was evaluated with the help of microstructure studies and the quantification of hydration products.

A sustainable cement mortar was produced by replacing natural river sand with lateritic fine aggregates. The thermal strength deterioration features were assessed by exposing the control specimens and lateritic fine aggregates-based cement mortars to elevated temperatures. Changes in the mechanical properties were evaluated through a quantitative microstructure study using scanning electron microscopy (SEM) images. The phase change of hydration products after exposure to elevated temperatures was qualitatively analyzed by greyscale thresholding of SEM images using Image J software.

The purpose of this paper is to develop a high-performance composite emulsion cement waterproof coating. The coating has excellent durability and is effective in protecting cement mortar substrates from harmful ions.

The polymer cement waterproof coatings with different emulsion compounding ratios were tested for mechanical properties and water resistance after alkali immersion, water immersion, thermal aging and UV aging, and the coatings were analyzed by infrared spectroscopy after aging to evaluate its durability. Meanwhile, the coating that presents favorable durability was applied to cement mortar test blocks. The protective effect of the coating on the test blocks was tested by immersion method, and X-ray diffraction analysis was performed on the eroded test blocks.

The coating with neoprene latex/acrylate latex weight ratio of 90/10 presents favorable durability and has superior overall performance. Besides, when it is applied to cement mortar blocks, the coatings effectively reduced the erosive effect of harmful ions on cement mortar blocks, resulting in much lower mass change ratios and less internal structural damage of the blocks significantly.

The obtained coating will be of great application potential for use in building waterproofing construction. Moreover, the coating can practically prevent chloride ions and sulfate ions from penetrating cement-based materials.

The purpose of this paper is to check the feasibility of using biomaterial such as of Phragmites-Australis (PA) in cement paste to achieve sustainable building materials.

In this study, cement pastes were prepared by adding locally produced PA fibers in four different volumes: 0%, 0.5%, 1% and 2% for a duration of 180 days. Bottles and prisms were subjected to chemical shrinkage (CS), drying shrinkage (DS), autogenous shrinkage (AS) and expansion tests. Besides, prism specimens were tested for flexural strength and compressive strength. Furthermore, a mathematical model was proposed to determine the variation length change as function of time.

The experimental findings showed that the mechanical properties of cement paste were significantly improved by the addition of 1% PA fiber compared to other PA mixes. The effect of increasing the % of PA fibers reduces the CS, AS, DS and expansion of cement paste. For example, the addition of 2% PA fibers reduces the CS, expansion, AS and DS at 180 days by 36%, 20%, 13% and 10%, respectively compared to the control mix. The proposed nonlinear model fit to the experimental data is appropriate with R2 values above 0.92. There seems to be a strong positive linear correlation between CS and AS/DS with R2 above 0.95. However, there exists a negative linear correlation between CS and expansion.

The PA used in this study was obtained from one specific location. This can exhibit a limitation as soil type may affect PA properties. Also, one method was used to treat the PA fibers.

The utilization of PA fibers in paste may well reduce the formation of cracks and limit its propagation, thus using a biomaterial such as PA in cementitious systems can be an environmentally friendly option as it will make good use of the waste generated and enhance local employment, thereby contributing toward sustainable development.

To the authors best knowledge, there is hardly any research on the effect of PA on the volume stability of cement paste. Therefore, the research outputs are considered to be original.

To explore the economical and reasonable semi-rigid permeable base layer ratio, solve the problems caused by rainwater washing over the pavement base layer on the slope, improve its drainage function, improve the water stability and service life of the roadbed pavement and promote the application of semi-rigid permeable base layer materials in the construction of asphalt pavement in cold regions.

In this study, three semi-rigid base course materials were designed, the mechanical strength and drainage properties were tested and the effect and correlation of air voids on their performance indexes were analyzed.

It was found that increasing the cement content increased the strength but reduced the air voids and water permeability coefficient. The permeability performance of the sandless material was superior to the dense; the performance of the two sandless materials was basically the same when the cement content was 7%. Overall, the skeleton void (sand-containing) type gradation between the sandless and dense types is more suitable as permeable semi-rigid base material; its gradation is relatively continuous, with cement content? 4.5%, strength? 1.5 MPa, water permeability coefficient? 0.8 cm/s and voids of 18–20%.

The study of permeable semi-rigid base material with large air voids could help to solve the problems of water damage and freeze-thaw damage of the base layer of asphalt pavements in cold regions and ensure the comfort and durability of asphalt pavements while having good economic and social benefits.

The purpose of this paper is to obtain a constitutive model of cement-based material in the rheological stage, which owns the different water-cement ratio (w/c) and temperature and have a significant impact on the workability of concrete materials.

It is introduced a modified Arrhenius equation into the Herschel–Bulkley model, which is widely applied in rheological analysis and constructed an ordinary differential equation (ODE) of w/c from the Navier–Stokes equation. By solving the ODE, an approximate constitutive relation of cement-based materials included w/c and temperature is derived. Compared with the experimental results, the present model is validated.

The shear stress and shear rate curves with different w/c and temperature are simulated by the present method, and the present model can be applied to analyze the changes of apparent viscosity in cement-based material slurry as the w/c and temperature varying.

This work gives a mathematical model, which can effectively approximate the shear stress–shear rate relation with different w/c and temperature in the rheological stage of cement-based material.

The purpose of this paper is to develop the efficiency of styrene-acrylate (SA) emulsions for polymer cement waterproof coatings with improved bacteria resistance and mechanical properties.

For effective bacteria resistance and excellent mechanical properties, various concentrations of methacryloxyethylhexadecyl dimethylammonium bromide (MHDB) were synthesised and incorporated into SA emulsions. The properties of SA emulsions modified with MHDB were characterised and compared with those of unmodified ones according to the formulations of polymer cement waterproof coatings.

The SA emulsions modified with MHDB exhibited significant enhancement of bacteria resistance and mechanical properties over the unmodified ones. The positive quaternary nitrogen and long-chain alkyl groups of MHDB in SA emulsions could attract phospholipid head groups of bacterial and insert them into the cell wall, which results in biomass leak and bactericidal effect. Moreover, MHDB as a softened monomer was beneficial to the synthesis of SA copolymer with low glass-transition temperature (T_g), then the copolymer and cement would form a more compact film which was the main reason for the enhancement of mechanical properties.

The modifier MHDB was synthesised from diethylaminoethyl methacrylate (DEAM) and 1-bromohexadecane. Besides, the congeners of MHDB could be synthesised from DEAM and 1-bromododecane, 1-tetradecyl dromide, 1-octadecyl bromide, etc. In addition, the efficiency of other modifications into SA emulsions for antibacterial polymer cement waterproof coatings could be studied as well.

The method provided a practical solution for the improvement of water-based antibacterial acrylate polymer cement waterproof coatings.

The method for enhancing bacteria resistance and mechanical properties of the waterproof coating was novel and valuable.