1 – 10 of 116Amin Barzegar, Mohammadreza Farahani and Amirreza Gomroki
Material extrusion-based additive manufacturing is a prominent manufacturing technique to fabricate complex geometrical three-dimensional (3D) parts. Despite the indisputable…
Abstract
Purpose
Material extrusion-based additive manufacturing is a prominent manufacturing technique to fabricate complex geometrical three-dimensional (3D) parts. Despite the indisputable advantages of material extrusion-based technique, the poor surface and subsurface integrity hinder the industrial application of this technology. The purpose of this study is introducing the hot air jet treatment (HAJ) technique for surface treatment of additive manufactured parts.
Design/methodology/approach
In the presented research, novel theoretical formulation and finite element models are developed to study and model the polishing mechanism of printed parts surface through the HAJ technique. The model correlates reflow material volume, layer width and layer height. The reflow material volume is a function of treatment temperature, treatment velocity and HAJ velocity. The values of reflow material volume are obtained through the finite element modeling model due to the complexity of the interactions between thermal and mechanical phenomena. The theoretical model presumptions are validated through experiments, and the results show that the treatment parameters have a significant impact on the surface characteristics, hardness and dimensional variations of the treated surface.
Findings
The results demonstrate that the average value of error between the calculated theoretical results and experimental results is 14.3%. Meanwhile, the 3D plots of Ra and Rq revealed that the maximum values of Ra and Rq reduction percentages at 255°C, 270°C, 285°C and 300°C treatment temperatures are (35.9%, 33.9%), (77.6%,76.4%), (94%, 93.8%) and (85.1%, 84%), respectively. The scanning electron microscope results illustrate three different treatment zones and the treatment-induced and manufacturing-induced entrapped air relief phenomenon. The measured results of hardness variation percentages and dimensional deviation percentages at different regimes are (8.33%, 0.19%), (10.55%, 0.31%) and (−0.27%, 0.34%), respectively.
Originality/value
While some studies have investigated the effect of the HAJ process on the structural integrity of manufactured items, there is a dearth of research on the underlying treatment mechanism, the integrity of the treated surface and the subsurface characteristics of the treated surface.
Details
Keywords
Ting Li, Junmiao Wu, Junhai Wang, Yunwu Yu, Xinran Li, Xiaoyi Wei and Lixiu Zhang
The purpose of this article is to prepare graphene/polyimide composite materials for use as bearing cage materials, improving the friction and wear performance of bearing cages.
Abstract
Purpose
The purpose of this article is to prepare graphene/polyimide composite materials for use as bearing cage materials, improving the friction and wear performance of bearing cages.
Design/methodology/approach
The oil absorption and discharge tests were conducted to evaluate the oil content properties of the materials, while the mechanical properties were analyzed through cross-sectional morphology examination. Investigation into the tribological behavior and wear mechanisms encompassed characterization and analysis of wear trace morphology in PPI-based materials. Consequently, the influence of varied graphene nanoplatelets (GN) concentrations on the oil content, mechanical and tribological properties of PPI-based materials was elucidated.
Findings
The composites exhibit excellent oil-containing properties due to the increased porosity of PPI-GN composites. The robust formation of covalent bonds between GN and PPI amplifies the adhesive potency of the PPI-GN composites, thereby inducing a substantial enhancement in impact strength. Notably, the PPI-GN composites showed enhanced lubrication properties compared to PPI, which was particularly evident at a GN content of 0.5 Wt.%, as evidenced by the minimization of the average coefficient of friction and the width of the abrasion marks.
Practical implications
This paper includes implications for elucidating the wear mechanism of the polyimide composites under frictional wear conditions and then to guide the optimization of oil content and tribological properties of polyimide bearing cage materials.
Originality/value
In this paper, homogeneously dispersed PPI-GN composites were effectively synthesized by introducing GN into a polyimide matrix through in situ polymerization, and the lubrication mechanism of the PPI composites was compared with that of the PPI-GN composites to illustrate the composites’ superiority.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0415
Details
Keywords
Martin Novák, Berenika Hausnerova, Vladimir Pata and Daniel Sanetrnik
This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass…
Abstract
Purpose
This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass production implemented using PIM. Thus, the surface properties and mechanical performance of parts produced using powder/polymer binder feedstocks [material extrusion (MEX) and PIM] were investigated and compared with powder manufacturing based on direct metal laser sintering (DMLS).
Design/methodology/approach
PIM parts were manufactured from 17-4PH stainless steel PIM-quality powder and powder intended for powder bed fusion compounded with a recently developed environmentally benign binder. Rheological data obtained at the relevant temperatures were used to set up the process parameters of injection molding. The tensile and yield strengths as well as the strain at break were determined for PIM sintered parts and compared to those produced using MEX and DMLS. Surface properties were evaluated through a 3D scanner and analyzed with advanced statistical tools.
Findings
Advanced statistical analyses of the surface properties showed the proximity between the surfaces created via PIM and MEX. The tensile and yield strengths, as well as the strain at break, suggested that DMLS provides sintered samples with the highest strength and ductility; however, PIM parts made from environmentally benign feedstock may successfully compete with this manufacturing route.
Originality/value
This study addresses the issues connected to the merging of two environmentally efficient processing routes. The literature survey included has shown that there is so far no study comparing AM and PIM techniques systematically on the fixed part shape and dimensions using advanced statistical tools to derive the proximity of the investigated processing routes.
Details
Keywords
Jie Wan, Biao Chen, Jianghua Shen, Katsuyoshi Kondoh, Shuiqing Liu and Jinshan Li
The metallic alloys and their components fabricated via laser powder bed fusion (LPBF) suffer from the microvoids formed inevitably due to the extreme solidification rate during…
Abstract
Purpose
The metallic alloys and their components fabricated via laser powder bed fusion (LPBF) suffer from the microvoids formed inevitably due to the extreme solidification rate during fabrication, which are impossible to be removed by heat treatment. This paper aims to remove those microvoids in as-built AlSi10Mg alloys by hot forging and enhance their mechanical properties.
Design/methodology/approach
AlSi10Mg samples were built using prealloyed powder with a set of optimized LPBF parameters, viz. 350 W of laser power, 1,170 mm/s of scan speed, 50 µm of layer thickness and 0.24 mm of hatch spacing. As-built samples were preheated to 430°C followed by immediate pressing with two different thickness reductions of 10% and 35%. The effect of hot forging on the microstructure was analyzed by means of X-ray diffraction, scanning electron microscopy, electron backscattered diffraction and transmission electron microscopy. Tensile tests were performed to reveal the effect of hot forging on the mechanical properties.
Findings
By using hot forging, the large number of microvoids in both as-built and post heat-treated samples were mostly healed. Moreover, the Si particles were finer in forged condition (∼150 nm) compared with those in heat-treated condition (∼300 nm). Tensile tests showed that compared with heat treatment, the hot forging process could noticeably increase tensile strength at no expense of ductility. Consequently, the toughness (integration of tensile stress and strain) of forged alloy increased by ∼86% and ∼24% compared with as-built and heat-treated alloys, respectively.
Originality/value
Hot forging can effectively remove the inevitable microvoids in metals fabricated via LPBF, which is beneficial to the mechanical properties. These findings are inspiring for the evolution of the LPBF technique to eliminate the microvoids and boost the mechanical properties of metals fabricated via LPBF.
Details
Keywords
Vishal Kumar and Amitava Mandal
Wire-arc-based additive manufacturing (WAAM) is a promising technology for the efficient and economical fabrication of medium-large components. However, the anisotropic behavior…
Abstract
Purpose
Wire-arc-based additive manufacturing (WAAM) is a promising technology for the efficient and economical fabrication of medium-large components. However, the anisotropic behavior of the multilayered WAAM-fabricated components remains a challenging problem.
Design/methodology/approach
The purpose of this paper is to conduct a comprehensive study of the grain morphology, crystallographic orientation and texture in three regions of the WAAM printed component. Furthermore, the interdependence of the grain morphology in different regions of the fabricated component with their mechanical and tribological properties was established.
Findings
The electron back-scattered diffraction analysis of the top and bottom regions revealed fine recrystallized grains, whereas the middle regions acquired columnar grains with an average size of approximately 8.980 µm. The analysis revealed a higher misorientation angle and an intense crystallographic texture in the upper and lower regions. The investigations found a higher microhardness value of 168.93 ± 1.71 HV with superior wear resistance in the bottom region. The quantitative evaluation of the residual stress detected higher compressive stress in the upper regions. Evidence for comparable ultimate tensile strength and greater elongation (%) compared to its wrought counterpart has been observed.
Originality/value
The study found a good correlation between the grain morphology in different regions of the WAAM-fabricated component and their mechanical and wear properties. The Hall–Petch relationship also established good agreement between the grain morphology and tensile test results. Improved ductility compared to its wrought counterpart was observed. The anisotropy exists with improved mechanical properties along the longitudinal direction. Moreover, cylindrical components have superior tribological properties compared with cuboidal components.
Details
Keywords
Yan Pan, Taiyu Jin, Xiaohui Peng, Pengli Zhu and Kyung W. Paik
The purpose of this paper was to investigate how variations in the geometry of silicon chips and the presence of surface defects affect their static bending properties. By…
Abstract
Purpose
The purpose of this paper was to investigate how variations in the geometry of silicon chips and the presence of surface defects affect their static bending properties. By comparing the bending radius and strength across differently sized and treated chips, the study sought to understand the underlying mechanics that contribute to the flexibility of silicon-based electronic devices. This understanding is crucial for the development of advanced, robust and adaptable electronic systems that can withstand the rigors of manufacturing and everyday use.
Design/methodology/approach
This study explores the impact of silicon chip geometry and surface defects on flexibility through a multifaceted experimental approach. The methodology included preparing silicon chips of three distinct dimensions and subjecting them to thinning processes to achieve a uniform thickness verified via scanning electron microscopy (SEM). Finite element method (FEM) simulations and a series of four-point bending tests were used to analyze the bending flexibility theoretically and experimentally. The approach was comprehensive, examining both the intrinsic geometric factors and the extrinsic influence of surface defects induced by manufacturing processes.
Findings
The findings revealed a significant deviation between the theoretical predictions from FEM simulations and the experimental outcomes from the four-point bending tests. Rectangular-shaped chips demonstrated superior flexibility, with smaller dimensions leading to an increased bending strength. Surface defects, identified as critical factors affecting flexibility, were analyzed through SEM and atomic force microscopy, showing that etching processes could reduce defect density and enhance flexibility. Notably, the study concluded that surface defects have a more pronounced impact on silicon chip flexibility than geometric factors, challenging initial assumptions and highlighting the need for defect minimization in chip manufacturing.
Originality/value
This research contributes valuable insights into the design and fabrication of flexible electronic devices, emphasizing the significant role of surface defects over geometric considerations in determining silicon chip flexibility. The originality of the work lies in its holistic approach to dissecting the factors influencing silicon chip flexibility, combining theoretical simulations with practical bending tests and surface defect analysis. The findings underscore the importance of optimizing manufacturing processes to reduce surface defects, thereby paving the way for the creation of more durable and flexible electronic devices for future technologies.
Details
Keywords
Abstract
Purpose
This study aims to study the formation mechanism of micro-arc oxidation (MAO) coating on AZ31 magnesium alloy and how the annealing process affects its corrosion resistance.
Design/methodology/approach
This study involved immersion experiments, electrochemical experiments and slow strain rate tensile experiments, along with scanning electron microscopy, optical microscopy observation and X-ray diffraction analysis.
Findings
The findings suggest that annealing treatment can refine the grain size of AZ31 magnesium alloy to an average of 6.9 µm at 300°C. The change in grain size leads to a change in conductivity, which affects the performance of MAO coatings. The MAO coating obtained by annealing the substrate at 300°C has smaller pores and porosity, resulting in better adhesion and wear resistance.
Originality/value
The coating acts as a barrier to prevent corrosive substances from entering the substrate. However, the smaller pores and porosity reduce the channels for the corrosive solution to pass through the coating. When the coating cracks or falls off, the corrosive medium and substrate come into direct contact. Smaller and uniform grains have better corrosion resistance.
Details
Keywords
Min Li, Hangxuan Liu, Xingquan Zhang, Hengji Yang, Lisheng Zuo, Ziyu Wang, Shiwei Duan and Song Shu
The purpose of this paper is to investigate the effect of laser peening (LP) on mechanical and wear properties of 304 stainless steel sheet.
Abstract
Purpose
The purpose of this paper is to investigate the effect of laser peening (LP) on mechanical and wear properties of 304 stainless steel sheet.
Design/methodology/approach
Three-dimensional morphology, micro-hardness and micro-structure of shocked samples were tested. The wear amount, wear track morphology and wear mechanism were also characterized under dry sliding wear using Al2O3 ceramics ball.
Findings
The LP treatment generates deformation twins that contribute to the grain refinement and hardness increase. The wear test displays that the wear mechanism of samples is mainly abrasive wear and oxidation wear at 10 N load. While at 30 N, the delamination and adhesion areas of treated sample are reduced visibly compared to untreated ones.
Originality/value
This study specifically investigates the mechanical and wear properties of 304 stainless steel after the direct action of LP on its surface, which shows an effective improvement on the wear resistance. For example, the wear loss of processed sample is reduced by 19% at 30 N, the friction coefficient decreases from 0.4714 to 0.4308 and the groove depth is reduced from 78.1 to 74.4 µm under same condition.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-01-2024-0007/
Details
Keywords
Mohammad Vahid Ehteshamfar, Amir Kiadarbandsari, Ali Ataee, Katayoun Ghozati and Mohammad Ali Bagherkhani
Stereolithography (SLA) additive manufacturing (AM) technique has enabled the production of inconspicuous and aesthetically pleasing orthodontics that are also hygienic. However…
Abstract
Purpose
Stereolithography (SLA) additive manufacturing (AM) technique has enabled the production of inconspicuous and aesthetically pleasing orthodontics that are also hygienic. However, the staircase effect poses a challenge to the application of invisible orthodontics in the dental industry. The purpose of this study is to implement chemical postprocessing technique by using isopropyl alcohol as a solvent to overcome this challenge.
Design/methodology/approach
Fifteen experiments were conducted using a D-optimal design to investigate the effect of different concentrations and postprocessing times on the surface roughness, material removal rate (MRR), hardness and cost of SLA dental parts required for creating a clear customized aligner, and a container was constructed for chemical treatment of these parts made from photocurable resin.
Findings
The study revealed that the chemical postprocessing technique can significantly improve the surface roughness of dental SLA parts, but improper selection of concentration and time can lead to poor surface roughness. The optimal surface roughness was achieved with a concentration of 90 and a time of 37.5. Moreover, the dental part with the lowest concentration and time (60% and 15 min, respectively) had the lowest MRR and the highest hardness. The part with the highest concentration and time required the greatest budget allocation. Finally, the results of the multiobjective optimization analysis aligned with the experimental data.
Originality/value
This paper sheds light on a previously underestimated aspect, which is the pivotal role of chemical postprocessing in mitigating the adverse impact of stair case effect. This nuanced perspective contributes to the broader discourse on AM methodologies, establishing a novel pathway for advancing the capabilities of SLA in dental application.