1 – 10 of 216Mohammad Saleh Afsharkohan, Saman Dehrooyeh, Majid Sohrabian and Majid Vaseghi
Fabrication settings such as printing speed and nozzle temperature in fused deposition modeling undeniably influence the quality and strength of fabricated parts. As available…
Abstract
Purpose
Fabrication settings such as printing speed and nozzle temperature in fused deposition modeling undeniably influence the quality and strength of fabricated parts. As available market filaments do not contain any exact information report for printing settings, manufacturers are incapable of achieving desirable predefined print accuracy and mechanical properties for the final parts. The purpose of this study is to determine the importance of selecting suitable print parameters by understanding the intrinsic behavior of the material to achieve high-performance parts.
Design/methodology/approach
Two common commercial polylactic acid filaments were selected as the investigated samples. To study the specimens’ printing quality, an appropriate scaffold geometry as a delicate printing sample was printed according to a variety of speeds and nozzle temperatures, selected in the filament manufacturer’s proposed temperature range. Dimensional accuracy and qualitative surface roughness of the specimens made by one of the filaments were evaluated and the best processing parameters were selected. The scaffolds were fabricated again by both filaments according to the selected proper processing parameters. Material characterization tests were accomplished to study the reason for different filament behaviors in the printing process. Moreover, the correlations between the polymer structure, thermo-rheological behavior and printing parameters were denoted.
Findings
Compression tests revealed that precise printing of the characterized filament results in more accurate structure and subsequent improvement of the final printed sample elastic modulus.
Originality/value
The importance of material characterization to achieve desired properties for any purpose was emphasized. Obtained results from the rheological characterizations would help other users to benefit from the highest performance of their specific filament.
Details
Keywords
Fatima Barrarat, Karim Rayane, Bachir Helifa, Samir Bensaid and Iben Khaldoun Lefkaier
Detecting the orientation of cracks is a major challenge in the development of eddy current nondestructive testing probes. Eddy current-based techniques are limited in their…
Abstract
Purpose
Detecting the orientation of cracks is a major challenge in the development of eddy current nondestructive testing probes. Eddy current-based techniques are limited in their ability to detect cracks that are not perpendicular to induced current flows. This study aims to investigate the application of the rotating electromagnetic field method to detect arbitrary orientation defects in conductive nonferrous parts. This method significantly improves the detection of cracks of any orientation.
Design/methodology/approach
A new rotating uniform eddy current (RUEC) probe is presented. Two exciting pairs consisting of similar square-shaped coils are arranged orthogonally at the same lifting point, thus avoiding further adjustment of the excitation system to generate a rotating electromagnetic field, eliminating any need for mechanical rotation and focusing this field with high density. A circular detection coil serving as a receiver is mounted in the middle of the excitation system.
Findings
A simulation model of the rotating electromagnetic field system is performed to determine the rules and characteristics of the electromagnetic signal distribution in the defect area. Referring to the experimental results aimed to detect artificial cracks at arbitrary angles in underwater structures using the rotating alternating current field measurement (RACFM) system in Li et al. (2016), the model proposed in this paper is validated.
Originality/value
CEDRAT FLUX 3D simulation results showed that the proposed probe can detect cracks with any orientation, maintaining the same sensitivity, which demonstrates its effectiveness. Furthermore, the proposed RUEC probe, associated with the exploitation procedure, allows us to provide a full characterization of the crack, namely, its length, depth and orientation in a one-pass scan, by analyzing the magnetic induction signal.
Details
Keywords
Ali Hashemi Baghi and Jasmin Mansour
Fused Filament Fabrication (FFF) is one of the growing technologies in additive manufacturing, that can be used in a number of applications. In this method, process parameters can…
Abstract
Purpose
Fused Filament Fabrication (FFF) is one of the growing technologies in additive manufacturing, that can be used in a number of applications. In this method, process parameters can be customized and their simultaneous variation has conflicting impacts on various properties of printed parts such as dimensional accuracy (DA) and surface finish. These properties could be improved by optimizing the values of these parameters.
Design/methodology/approach
In this paper, four process parameters, namely, print speed, build orientation, raster width, and layer height which are referred to as “input variables” were investigated. The conflicting influence of their simultaneous variations on the DA of printed parts was investigated and predicated. To achieve this goal, a hybrid Genetic Algorithm – Artificial Neural Network (GA-ANN) model, was developed in C#.net, and three geometries, namely, U-shape, cube and cylinder were selected. To investigate the DA of printed parts, samples were printed with a central through hole. Design of Experiments (DoE), specifically the Rotational Central Composite Design method was adopted to establish the number of parts to be printed (30 for each selected geometry) and also the value of each input process parameter. The dimensions of printed parts were accurately measured by a shadowgraph and were used as an input data set for the training phase of the developed ANN to predict the behavior of process parameters. Then the predicted values were used as input to the Desirability Function tool which resulted in a mathematical model that optimizes the input process variables for selected geometries. The mean square error of 0.0528 was achieved, which is indicative of the accuracy of the developed model.
Findings
The results showed that print speed is the most dominant input variable compared to others, and by increasing its value, considerable variations resulted in DA. The inaccuracy increased, especially with parts of circular cross section. In addition, if there is no need to print parts in vertical position, the build orientation should be set at 0° to achieve the highest DA. Finally, optimized values of raster width and layer height improved the DA especially when the print speed was set at a high value.
Originality/value
By using ANN, it is possible to investigate the impact of simultaneous variations of FFF machines’ input process parameters on the DA of printed parts. By their optimization, parts of highly accurate dimensions could be printed. These findings will be of significant value to those industries that need to produce parts of high DA on FFF machines.
Details
Keywords
Mohammad A. Gharaibeh and Faris M. Al-Oqla
There are several lead-free solder alloys available in the industry. Over the years, the most favorable solder composition of tin-silver-copper (Sn-Ag-Cu [SAC]) has been vastly…
Abstract
Purpose
There are several lead-free solder alloys available in the industry. Over the years, the most favorable solder composition of tin-silver-copper (Sn-Ag-Cu [SAC]) has been vastly used and accepted for joining the electronic components. It is strongly believed that the silver (Ag) content has a significant impact on the solder mechanical behavior and thus solder thermal reliability performance. This paper aims to assess the mechanical response, i.e. creep response, of the SAC solder alloys with various Ag contents.
Design/methodology/approach
A three-dimensional nonlinear finite element simulation is used to investigate the thermal cyclic behavior of several SAC solder alloys with various silver percentages, including 1%, 2%, 3% and 4%. The mechanical properties of the unleaded interconnects with various Ag amounts are collected from reliable literature resources and used in the analysis accordingly. Furthermore, the solder creep behavior is examined using the two famous creep laws, namely, Garofalo’s and Anand’s models.
Findings
The nonlinear computational analysis results showed that the silver content has a great influence on the solder behavior as well as on thermal fatigue life expectancy. Specifically, solders with relatively high Ag content are expected to have lower plastic deformations and strains and thus better fatigue performance due to their higher strengths and failure resistance characteristics. However, such solders would have contrary fatigue performance in drop and shock environments and the low-Ag content solders are presumed to perform significantly better because of their higher ductility.
Originality/value
Generally, this research recommends the use of SAC solder interconnects of high silver contents, e.g. 3% and 4%, for designing electronic assemblies continuously exposed to thermal loadings and solders with relatively low Ag-content, i.e. 1% and 2%, for electronic packages under impact and shock loadings.
Details
Keywords
Saloni Purandare and Chunhui Xiang
Firefighter Personal Protective Equipment (PPE) is the only barrier between the firefighter and hazardous environment. Gloves are a crucial component of the multi-component PPE…
Abstract
Purpose
Firefighter Personal Protective Equipment (PPE) is the only barrier between the firefighter and hazardous environment. Gloves are a crucial component of the multi-component PPE. Over time the gloves have reduced the intensity of hand injuries, yet further improvement in terms of material selection and glove design is required to strike the balance between protection and comfort. Focusing on the material aspect, the purpose of this study is to present literature analysis on material selection and testing for firefighter gloves.
Design/methodology/approach
The study conducted a literature analysis on material selection and characterization of firefighter PPE. The review summarizes and evaluates past work addressing the characterization of firefighter gloves in accordance with NFPA 1971 requirements and points out found research gaps to aid with foundation of future research.
Findings
The study summarizes several research works to inform readers about the material selection and characterization of firefighter gloves. Based on the analyzed literature, the study resulted in material specification sheets for firefighter gloves. The developed material specification sheets provide information in terms of crucial material properties to be incorporated for accurate functioning of firefighter gloves, testing methods to validate those material properties and materials from analyzed literature exhibiting desired properties.
Originality/value
With large research addressing firefighter PPE, only limited studies focus specifically on gloves. Thus, this study provides a literature analysis covering material selection and testing for gloves. A consolidated firefighter gloves material specification document, which does not appear to be available in the literature, will provide a foundation for the development and characterization of firefighter gloves to better serve the functions along with ensuring user comfort.
Details
Keywords
Carlos A. Gonzalez Lugo, Dylan Scott Caputo, Michael J. Hutchinson, Kamran Fouladi and Babak Eslami
The purpose of this study is to design and develop an environmentally controlled enclosure for commercial three-dimensional (3D) printers.
Abstract
Purpose
The purpose of this study is to design and develop an environmentally controlled enclosure for commercial three-dimensional (3D) printers.
Design/methodology/approach
Computational fluid dynamics (CFD) simulations and experimental testing investigated various designs for environmentally controlled enclosures. CFD simulations provided the necessary information to select the optimal and feasible design, whereas experimental testing validated the CFD simulation results. An environmentally controlled environment allowed test samples to be printed at several relative humidity (RH) settings (20% RH, 50% RH and 80% RH). The test samples were characterized at both the macro and micro scales. The macroscale characterization was conducted using the static tensile testing procedure, while the microscale polymer material properties were determined using atomic force microscopy.
Findings
An environmentally controlled enclosure was designed and built to produce airflow in the print region with an average RH uniformity of over 0.70. Three batches of ASTM D638 standard test samples were printed at 20% RH (low RH), 50% RH (mid RH) and 80% RH (high RH). Macroscale characterization showed that the samples printed at lower humidity had statistically significantly higher tangent modulus, ultimate tensile strength and rupture strength. atomic force microscopy studies have also verified these results at the microscale and nanoscale. These studies also showed that a high humidity environment interacts with melted polylactic acid, causing additional surface roughness that reduces the strength of 3D-printed parts.
Originality/value
There is a need for stronger and higher-quality 3D-printed parts in the additive manufacturing (AM) market. This study fulfills that need by designing and developing an environmentally controlled add-on enclosure for the AM market.
Details
Keywords
James Elgy, Paul D. Ledger, John L. Davidson, Toykan Özdeğer and Anthony J. Peyton
The ability to characterise highly conducting objects, that may also be highly magnetic, by the complex symmetric rank–2 magnetic polarizability tensor (MPT) is important for…
Abstract
Purpose
The ability to characterise highly conducting objects, that may also be highly magnetic, by the complex symmetric rank–2 magnetic polarizability tensor (MPT) is important for metal detection applications including discriminating between threat and non-threat objects in security screening, identifying unexploded anti-personnel landmines and ordnance and identifying metals of high commercial value in scrap sorting. Many everyday non-threat items have both a large electrical conductivity and a magnetic behaviour, which, for sufficiently weak fields and the frequencies of interest, can be modelled by a high relative magnetic permeability. This paper aims to discuss the aforementioned idea.
Design/methodology/approach
The numerical simulation of the MPT for everyday non-threat highly conducting magnetic objects over a broad range of frequencies is challenging due to the resulting thin skin depths. The authors address this by employing higher order edge finite element discretisations based on unstructured meshes of tetrahedral elements with the addition of thin layers of prismatic elements. Furthermore, computer aided design (CAD) geometrical models of the non-threat and threat object are often not available and, instead, the authors extract the geometrical features of an object from an imaging procedure.
Findings
The authors obtain accurate numerical MPT characterisations that are in close agreement with experimental measurements for realistic physical objects. The assessment of uncertainty shows the impact of geometrical and material parameter uncertainties on the computational results.
Originality/value
The authors present novel computations and measurements of MPT characterisations of realistic objects made of magnetic materials. A novel assessment of uncertainty in the numerical predictions of MPT characterisations for uncertain geometry and material parameters is included.
Details
Keywords
Chiara Bedon and Christian Louter
Glass material is largely used for load-bearing components in buildings. For this reason, standardized calculation methods can be used in support of safe structural design in…
Abstract
Purpose
Glass material is largely used for load-bearing components in buildings. For this reason, standardized calculation methods can be used in support of safe structural design in common loading and boundary conditions. Differing from earlier literature efforts, the present study elaborates on the load-bearing capacity, failure time and fire endurance of ordinary glass elements under fire exposure and sustained mechanical loads, with evidence of major trends in terms of loading condition and cross-sectional layout. Traditional verification approaches for glass in cold conditions (i.e. stress peak check) and fire endurance of load-bearing members (i.e. deflection and deflection rate limits) are assessed based on parametric numerical simulations.
Design/methodology/approach
The mechanical performance of structural glass elements in fire still represents an open challenge for design and vulnerability assessment. Often, special fire-resisting glass solutions are used for limited practical applications only, and ordinary soda-lime silica glass prevails in design applications for load-bearing members. Moreover, conventional recommendations and testing protocols in use for load-bearing members composed of traditional constructional materials are not already addressed for glass members. This paper elaborates on the fire endurance and failure detection methods for structural glass beams that are subjected to standard ISO time–temperature for fire exposure and in-plane bending mechanical loads. Fire endurance assessment methods are discussed with the support of Finite Element (FE) numerical analyses.
Findings
Based on extended parametric FE analyses, multiple loading, geometrical and thermo-mechanical configurations are taken into account for the analysis of simple glass elements under in-plane bending setup and fire exposure. The comparative results show that – in most of cases – thermal effects due to fire exposure have major effects on the actual load-bearing capacity of these members. Moreover, the conventional stress peak verification approach needs specific elaborations, compared to traditional calculations carried out in cold conditions.
Originality/value
The presented numerical results confirm that the fire endurance analysis of ordinary structural glass elements is a rather complex issue, due to combination of multiple aspects and influencing parameters. Besides, FE simulations can provide useful support for a local and global analysis of major degradation and damage phenomena, and thus support the definition of simple and realistic verification procedures for fire exposed glass members.
Details
Keywords
Andrea Lucherini and Donatella de Silva
Intumescent coatings are nowadays a dominant passive system used to protect structural materials in case of fire. Due to their reactive swelling behaviour, intumescent coatings…
Abstract
Purpose
Intumescent coatings are nowadays a dominant passive system used to protect structural materials in case of fire. Due to their reactive swelling behaviour, intumescent coatings are particularly complex materials to be modelled and predicted, which can be extremely useful especially for performance-based fire safety designs. In addition, many parameters influence their performance, and this challenges the definition and quantification of their material properties. Several approaches and models of various complexities are proposed in the literature, and they are reviewed and analysed in a critical literature review.
Design/methodology/approach
Analytical, finite-difference and finite-element methods for modelling intumescent coatings are compared, followed by the definition and quantification of the main physical, thermal, and optical properties of intumescent coatings: swelled thickness, thermal conductivity and resistance, density, specific heat capacity, and emissivity/absorptivity.
Findings
The study highlights the scarce consideration of key influencing factors on the material properties, and the tendency to simplify the problem into effective thermo-physical properties, such as effective thermal conductivity. As a conclusion, the literature review underlines the lack of homogenisation of modelling approaches and material properties, as well as the need for a universal modelling method that can generally simulate the performance of intumescent coatings, combine the large amount of published experimental data, and reliably produce fire-safe performance-based designs.
Research limitations/implications
Due to their limited applicability, high complexity and little comparability, the presented literature review does not focus on analysing and comparing different multi-component models, constituted of many model-specific input parameters. On the contrary, the presented literature review compares various approaches, models and thermo-physical properties which primarily focusses on solving the heat transfer problem through swelling intumescent systems.
Originality/value
The presented literature review analyses and discusses the various modelling approaches to describe and predict the behaviour of swelling intumescent coatings as fire protection for structural materials. Due to the vast variety of available commercial products and potential testing conditions, these data are rarely compared and combined to achieve an overall understanding on the response of intumescent coatings as fire protection measure. The study highlights the lack of information and homogenisation of various modelling approaches, and it underlines the research needs about several aspects related to the intumescent coating behaviour modelling, also providing some useful suggestions for future studies.
Details
Keywords
Giacomo Frulla, Enrico Cestino, Federico Cumino, Alessio Piccolo, Nicola Giulietti, Eugenio Fossat and Ehsan Kharrazi
The purpose of this study is to investigate a new and innovative sandwich material evaluating its capability for use in space habitat structural components in deployable and…
Abstract
Purpose
The purpose of this study is to investigate a new and innovative sandwich material evaluating its capability for use in space habitat structural components in deployable and foldable configurations. The main habitat requirements were considered in the preliminary design of a typical space outpost, proposing a preliminary architecture.
Design/methodology/approach
The stiffness properties of the innovative sandwich (MAdFlex ®) were evaluated using numerical and experimental investigations. Four-point bending tests were performed for complete sandwich characterization. Numerical FE simulations were performed using typical material properties and performance. The application to a space habitat main structure as a basic material has also been discussed and presented.
Findings
MAdFlex basic stiffness performances have been determined considering its double behavior: sufficiently stiff if loaded in a specific direction, flexible if loaded in the opposite direction and enhanced folding performance. Successful application to a typical space habitat confirms the validity and convenience of such a material in designing alternative structures.
Research limitations/implications
The innovative material demonstrates wide potential for structural application and design in demanding space situations under operating conditions and in stored ones at launch.
Practical implications
Several simple deployable structural components can be designed and optimized both for the space environment and for the more traditional terrestrial applications.
Social implications
Simplification in structural design can be derived from deployable low-weight items.
Originality/value
Innovative customized material in sandwich configuration has been proposed and investigated with the aim to demonstrate its potentiality and validity in alternative design architecture.