Bolted joint is the most important connection method in aircraft composite/metal stacked connections due to its large load transfer capacity and high manufacturing reliability. Aircraft components are subjected to complex hybrid variable loads during service, and the mechanical properties of composite/metal bolted joint directly affect the overall safety of aircraft structures. Research on composite/metal bolted joint and their mechanical properties has also become a topic of general interests. This article reviews the current research status of aeronautical composite/metal bolted joint and its mechanical properties and looks forward to future research directions.

This article reviews the research progress on static strength failure and fatigue failure of composite/metal bolted joint, focusing on exploring failure analysis and prediction methods from the perspective of the theoretical models. At the same time, the influence and correlation mechanism of hole-making quality and assembly accuracy on the mechanical properties of their connections are summarized from the hole-making processes and damage of composite/metal stacked structures.

The progressive damage analysis method can accurately analyze and predict the static strength failure of composite/metal stacked bolted joint structures by establishing a stress analysis model combined with composite material performance degradation schemes and failure criteria. The use of mature metal material fatigue cumulative damage models and composite material fatigue progressive damage analysis methods can effectively predict the fatigue of composite/metal bolted joints. The geometric errors such as aperture accuracy and holes perpendicularity have the most significant impact on the connection performance, and their mechanical responses mainly include ultimate strength, bearing stiffness, secondary bending effect and fatigue life.

Current research on the theoretical prediction of the mechanical properties of composite/metal bolted joints is mainly based on ideal fits with no gaps or uniform gaps in the thickness direction, without considering the hole shape characteristics generated by stacked drilling. At the same time, the service performance evaluation of composite/metal stacked bolted joints structures is currently limited to static strength and fatigue failure tests of the sample-level components and needs to be improved and verified in higher complexity structures. At the same time, it also needs to be extended to the mechanical performance research under more complex forms of the external loads in more environments.

The mechanical performance of the connection structure directly affects the overall structural safety of the aircraft. Many scholars actively explore the theoretical prediction methods for static strength and fatigue failure of composite/metal bolted joints as well as the impact of hole-making accuracy on their mechanical properties. This article provides an original overview of the current research status of aeronautical composite/metal bolted joint and its mechanical properties, with a focus on exploring the failure analysis and prediction methods from the perspective of theoretical models for static strength and fatigue failure of composite/metal bolt joints and looks forward to future research directions.

Unconventional machining processes, particularly ultrasonic vibration cutting (UVC), can overcome such technical bottlenecks. However, the precise mechanism through which UVC affects the in-service functional performance of advanced aerospace materials remains obscure. This limits their industrial application and requires a deeper understanding.

The surface integrity and in-service functional performance of advanced aerospace materials are important guarantees for safety and stability in the aerospace industry. For advanced aerospace materials, which are difficult-to-machine, conventional machining processes cannot meet the requirements of high in-service functional performance owing to rapid tool wear, low processing efficiency and high cutting forces and temperatures in the cutting area during machining.

To address this literature gap, this study is focused on the quantitative evaluation of the in-service functional performance (fatigue performance, wear resistance and corrosion resistance) of advanced aerospace materials. First, the characteristics and usage background of advanced aerospace materials are elaborated in detail. Second, the improved effect of UVC on in-service functional performance is summarized. We have also explored the unique advantages of UVC during the processing of advanced aerospace materials. Finally, in response to some of the limitations of UVC, future development directions are proposed, including improvements in ultrasound systems, upgrades in ultrasound processing objects and theoretical breakthroughs in in-service functional performance.

This study provides insights into the optimization of machining processes to improve the in-service functional performance of advanced aviation materials, particularly the use of UVC and its unique process advantages.

The purpose of this study is to investigate a new and innovative sandwich material evaluating its capability for use in space habitat structural components in deployable and foldable configurations. The main habitat requirements were considered in the preliminary design of a typical space outpost, proposing a preliminary architecture.

The stiffness properties of the innovative sandwich (MAdFlex ®) were evaluated using numerical and experimental investigations. Four-point bending tests were performed for complete sandwich characterization. Numerical FE simulations were performed using typical material properties and performance. The application to a space habitat main structure as a basic material has also been discussed and presented.

MAdFlex basic stiffness performances have been determined considering its double behavior: sufficiently stiff if loaded in a specific direction, flexible if loaded in the opposite direction and enhanced folding performance. Successful application to a typical space habitat confirms the validity and convenience of such a material in designing alternative structures.

The innovative material demonstrates wide potential for structural application and design in demanding space situations under operating conditions and in stored ones at launch.

Several simple deployable structural components can be designed and optimized both for the space environment and for the more traditional terrestrial applications.

Simplification in structural design can be derived from deployable low-weight items.

Innovative customized material in sandwich configuration has been proposed and investigated with the aim to demonstrate its potentiality and validity in alternative design architecture.

There are over 40 million amputees globally with more than 185,000 Americans losing their limbs every year. For most of the world, prosthetic devices remain too expensive and uncomfortable. This paper aims to outline advancements made by a multidisciplinary research group, interested in advancing the restoration of human motion through accessible lower limb prostheses.

Customization, comfort and functionality are the most important metrics reported by prosthetists and patients. The work of this paper presents the design and manufacturing of a custom made, cost-effective and functional three-dimensional (3D) printed transtibial prosthesis monocoque design. The design of the prosthesis integrates 3D imaging, modelling and optimization techniques coupled with additive manufacturing.

The successful fabrication of a functional monocoque prosthesis through 3D printing indicates the workflow may be a solution to the worldwide accessibility crisis. The digital workflow developed in this work offers great potential for providing prosthetic devices to rural communities, which lack access to skilled prosthetic physicians. The authors found that using the workflow together with 3D printing, this study can create custom monocoque prostheses (Figure 16). These prostheses are comfortable, functional and properly aligned. In comparison with traditional prosthetic devices, the authors slowered the average cost, weight and time of production by 95%, 55% and 95%, respectively.

This novel digital design and manufacturing workflow has the potential to democratize and globally proliferate access to prosthetic devices, which restore the patient’s mobility, quality of life and health. LIMBER’s toolbox can reach places where proper prosthetic and orthotic care is not available. The digital workflow reduces the cost of making custom devices by an order of magnitude, enabling broader reach, faster access and improved comfort. This is particularly important for children who grow quickly and need new devices every few months or years, timely access is both physically and psychologically important.

In this manuscript, the authors show the application of digital design techniques for fabricating prosthetic devices. The proposed workflow implements several advantageous changes and, most importantly, digitally blends the three components of a transtibial prosthesis into a single, 3D printable monocoque device. The development of a novel unibody transtibial device that is properly aligned and adjusted digitally, greatly reduces the number of visits an amputee must make to a clinic to have a certified prosthetist adjust and modify their prosthesis. The authors believe this novel workflow has the potential to ease the worldwide accessibility crisis for prostheses.

Finite element (FE) analysis can be used for both design and verification of components. In the case of 3D-printed materials, a proper characterization of properties, accounting for anisotropy and raster angles, can help develop efficient material models. This study aims to use compression tests to characterize short carbon-reinforced PA12 made by fused filament fabrication (FFF) and to model its behaviour by the FE method.

In this work, the authors focus on compression tests, using post-processed specimens to overcome external defects introduced by the FFF process. The material’s elastoplastic mechanical behaviour is modelled by an elastic stiffness matrix, Hill’s anisotropic yield criterion and Voce’s isotropic hardening law, considering the stacking sequence of raster angles. A FE analysis is conducted to reproduce the material’s compressive behaviour through the LS-DYNA software.

The proposed model can capture stress values at different deformation levels and peculiar aspects of deformed shapes until the onset of damage mechanisms. Deformation and damage mechanisms are strictly correlated to orientation and raster angle.

The paper aims to contribute to the understanding of 3D-printed material’s behaviour through compression tests on bulk 3D-printed material. The methodology proposed, enriched with an anisotropic damage criterion, could be effectively used for design and verification purposes in the field of 3D-printed components through FE analysis.

Porous implant surface is shown to facilitate bone in-growth and cell attachment, improving overall osteointegration, while providing adequate mechanical integrity. Recently, biodegradable material possessing such superior properties has been the focus with an aim of revolutionizing implant’s design, material and performance. This paper aims to present a comprehensive investigation into the design and development of low elastic modulus porous biodegradable Mg-3Si-5HA composite by mechanical alloying and spark plasma sintering (MA-SPS) technique.

This paper presents a comprehensive investigation into the design and development of low elastic modulus porous biodegradable Mg-3Si-5HA composite by MA-SPS technique. As the key alloying elements, HA powders with an appropriate proportion weight 5 and 10 are mixed with the base elemental magnesium (Mg) particles to form the composites of potentially variable porosity and mechanical property. The aim is to investigate the performance of the synthesized composites of Mg-3Si together with HA in terms of mechanical integrity hardness and Young’s moduli corrosion resistance and in-vitro bioactivity.

Mechanical and surface characterization results indicate that alloying of Si leads to the formation of fine Mg2 Si eutectic dense structure, hence increasing hardness while reducing the ductility of the composite. On the other hand, the allying of HA in Mg-3Si matrix leads to the formation of structural porosity (5-13 per cent), thus resulting in low Young’s moduli. It is hypothesized that biocompatible phases formed within the composite enhanced the corrosion performance and bio-mechanical integrity of the composite. The degradation rate of Mg-3Si composite was reduced from 2.05 mm/year to 1.19 mm/year by the alloying of HA elements. Moreover, the fabricated composites showed an excellent bioactivity and offered a channel/interface to MG-63 cells for attachment, proliferation and differentiation.

Overall, the findings suggest that the Mg-3Si-HA composite fabricated by MA and plasma sintering may be considered as a potential biodegradable material for orthopedic application.

This paper aims to reduce waste management and generate wealth by investigating the novelty of combining chicken feather fiber and bamboo particles to produce hybrid biocomposites. This is part of responsible production and sustainability techniques for sustainable development goals. This study aims to broaden animal and plant fiber utilization in the sustainable production of epoxy resins for engineering applications.

This research used two reinforcing materials [chicken feather fiber (CFF) and bamboo particles (BP)] to reinforce epoxy resin. The BPs were kept constant at 6 Wt.%, while the CFF was varied within 3–15 Wt.% in the composites to make CFF-BP polymer-reinforced composite (CFF-BP PRC). The mechanical experiment showed a 21% reduction in densities, making the CFF-BP PRC an excellent choice for lightweight applications.

It was discovered that fabricated composites with 10 mm CFF length had improved properties compared with the 15 mm CFF length and pristine samples, which confirmed that short fibers are better at enhancing randomly dispersed fibers in the epoxy matrix. However, the ballistic properties of both samples matched. There is a 40% increase in tensile strength and a 54% increase in flexural strength of the CFF-BP PRC compared to the pristine sample.

According to the literature review, to the best of the authors’ knowledge, this is a novel study of chicken fiber and bamboo particles in reinforcing epoxy composite.

This paper comprehensively addresses the influence of chopped strand mat glass fiber-reinforced polymer (GFRP) patch configurations such as geometry, dimensions, position and the number of layers of patches, whether a single or double patch is used and how well debonding the area under the patch improves the strength of the cracked aluminum plates with different crack lengths.

Single-edge cracked aluminum specimens of 150 mm in length and 50 mm in width were tested using the tensile test. The cracked aluminum specimens were then repaired using GFRP patches with various configurations. A three-dimensional (3D) finite element method (FEM) was adopted to simulate the repaired cracked aluminum plates using composite patches to obtain the stress intensity factor (SIF). The numerical modeling and validation of ABAQUS software and the contour integral method for SIF calculations provide a valuable tool for further investigation and design optimization.

The width of the GFRP patches affected the efficiency of the rehabilitated cracked aluminum plate. Increasing patch width WP from 5 mm to 15 mm increases the peak load by 9.7 and 17.5%, respectively, if compared with the specimen without the patch. The efficiency of the GFRP patch in reducing the SIF increased as the number of layers increased, i.e. the maximum load was enhanced by 5%.

This study assessed repairing metallic structures using the chopped strand mat GFRP. Furthermore, it demonstrated the superiority of rectangular patches over semicircular ones, along with the benefit of using double patches for out-of-plane bending prevention and it emphasizes the detrimental effect of defects in the bonding area between the patch and the cracked component. This underlines the importance of proper surface preparation and bonding techniques for successful repair.

Utilizing electrical discharge machining (EDM) to process micro-holes in superalloys may lead to the formation of remelting layers and micro-cracks on the machined surface. This work proposes a method of composite processing of EDM and ultrasonic vibration drilling for machining precision micro-holes in complex positions of superalloys.

A six-axis computer numerical control (CNC) machine tool was developed, whose software control system adopted a real-time control architecture that integrates electrical discharge and ultrasonic vibration drilling. Among them, the CNC system software was developed based on Windows + RTX architecture, which could process the real-time processing state received by the hardware terminal and adjust the processing state. Based on the SoC (System on Chip) technology, an architecture for a pulse generator was developed. The circuit of the pulse generator was designed and implemented. Additionally, a composite mechanical system was engineered for both drilling and EDM. Two sets of control boards were designed for the hardware terminal. One set was the EDM discharge control board, which detected the discharge state and provided the pulse waveform for turning on the transistor. The other was a relay control card based on STM32, which could meet the switch between EDM and ultrasonic vibration, and used the Modbus protocol to communicate with the machining control software.

The mechanical structure of the designed composite machine tool can effectively avoid interference between the EDM spindle and the drilling spindle. The removal rate of the remelting layer on 1.5 mm single crystal superalloys after composite processing can reach over 90%. The average processing time per millimeter was 55 s, and the measured inner surface roughness of the hole was less than 1.6 µm, which realized the  micro-hole machining without remelting layer, heat affected zone and micro-cracks in the single crystal superalloy.

The test results proved that the key techniques developed in this paper were suite for micro-hole machining of special materials.

This study aims to understand how the facesheet size, orientation and core size influence the analytical failure mechanism mode of glass fibre reinforced polymer (GFRP)/polyvinyl chloride (PVC) sandwich structures subjected to three-point bending. The purpose of this study was to develop failure-mode map of GFRP/PVC sandwich structures. Sandwich structures with different facesheet and core thicknesses were used to develop the failure map.

The sandwich structure and facesheet were fabricated using a vacuum-assisted resin infusion method with core sizes of 10, 15 and 20 mm and facesheet thicknesses of 1.5 and 3 mm and were arranged in three different orientations: angle-ply, cross-ply and quasi-isotropic. The key failure modes that occur in sandwich structures were used to predict possible failures in the developed material. Analytical equations were used in MATLAB for each observed failure mode. The probable failure modes, namely, face yielding, core shear and indentation equations, were used to construct the failure maps and were compared with the experimental data.

The boundary of the two failure modes shifts with changes in the facesheet and core thicknesses. The theoretical stiffness of sandwich panels was higher than the experimental stiffness. Based on strength-to-weight ratio, specimens E10-4, A15-8 and E20-8 exhibited the best optimum values owing to their shorter distance to the boundary lines.

In this study, a failure map was used to predict the possible failure modes for different GFRP facesheet orientations and thicknesses and PVC core thickness sandwich structures. Little is known about the prediction of the failure modes of unidirectional GFRP arranged in different orientations and thicknesses and PVC core thicknesses for sandwich structures. Few studies have used failure mode maps with unidirectional GFRP oriented in angle-ply, cross-ply and quasi-isotropic directions as a facesheet for sandwich structures compared to bidirectional mats. This study can serve as a guide for the correct selection of materials during the design process of sandwich structures.