1 – 2 of 2Yi Xin, Zijiang Jiang, Wenwen Li, Zonghao Huang and Cheng Wang
This paper aimed to prepare a kind of ZnS nanoparticles/poly(phenylene vinylene) (PPV) nanofibre and investigate its properties. Because the ZnS nanoparticles are important…
Abstract
Purpose
This paper aimed to prepare a kind of ZnS nanoparticles/poly(phenylene vinylene) (PPV) nanofibre and investigate its properties. Because the ZnS nanoparticles are important optoelectronic materials, their incorporation into one-dimensional (1D) nanoscale polymer matrices should be a meaningful subject for electrospinning.
Design/methodology/approach
ZnS/PPV composite nanofibres with an average diameter of 600 nm were successfully prepared by a combination of the in situ method and electrospinning technique. The nanofibres were electrospun from Zn(CH3COO)2·2H2O and PPV precursor composite solution, and the ZnS/PPV fibres were obtained by exposure of the electrospun fibres to H2S gas to prepare ZnS nanoparticles in situ. Such fibres were characterised using X-ray Diffraction (XRD), Fourier transform infrared, transmission electron microscope (TEM), scanning electron microscope and photoluminescence (PL). The photoelectric properties of the fibres obtained were also investigated.
Findings
XRD patterns proved that ZnS nanocrystals generated in the composite nanofibres. The TEM image showed that the nanocrystals were homogeneously dispersed in the nanofibres. The PL spectrum of ZnS/PPV composite nanofibres exhibited a blue shift relative to the PPV nanofibres. I-V curve of the single nanofibre device under 5.76 mW/cm2 light illumination showed that the composite nanofibres have good photoelectric properties.
Research limitations/implications
The comparisons of advantages between ZnS/PPV nanofibres with similar nanofibres will be further expanded in a later research.
Practical implications
Results demonstrate the promise of these novel nanostructures as ultraminiature photodetectors with the potential for integration into future hybrid nanophotonic devices and systems.
Originality/value
The integration of inorganic semiconductor nanoparticles into organic conjugated polymers leads to composite materials with unique physical properties and important application potential. In this work, ZnS nanoparticles were introduced into PPV by an in situ method, so as to obtain a kind of novel 1D nanomaterials with good photoelectric properties.
Details
Keywords
Haoyue Zhang, Luqi Chang, Hongwei Zhang, Junyan Li, Zijiang Yang, Bingxuan Qiao, Zhenjiang Zhao, Chaofang Dong and Kai Zhang
The purpose of this paper is to study the mechanical and corrosion behaviors of selective laser melting (SLM) 30CrMnSiA steel.
Abstract
Purpose
The purpose of this paper is to study the mechanical and corrosion behaviors of selective laser melting (SLM) 30CrMnSiA steel.
Design/methodology/approach
The microstructure, mechanical behavior and corrosion resistance of SLM 30CrMnSiA steel were studied by electrochemical test and immersion experiment.
Findings
The results showed that the microstructure of SLM 30CrMnSiA steel contained equiaxed fine (25.0 µm) ferrite and lamellar pearlite. The tensile strength of SLM 30CrMnSiA steel under the process parameters is 1,447 MPa and the elongation is 7.5%. As the immersion/salt spray test time increased to 15 days/48 h, corrosion mainly occurred in the local position of the sample and corrosion resistance decreased. When the immersion/salt spray test time increased to 30 days/168 h, the corrosion production covered the surface of the samples and the corrosion resistance increased.
Originality/value
The paper can guide the application and in situ repair for low-alloy steel by additive manufacturing.