This study aims to deal with both the development and mechanical investigations of unsaturated polyester matrix (UPR) composites containing recycled polyethylene terephthalate (PET) fibers as new fillers.

UPR/PET fibers composites have been developed as mats by incorporating 5, 8, 13 and 18 parts per hundred of rubber (phr) of 6-, 10- and 15-mm length PET fibers from the recycling of postconsumer bottles. The mechanical and physical properties of the composites were investigated as a function of fiber content and length. A significant increase in stress at break and in ultimate stress (sr) were observed for composites reinforced with 5 and 8 phr of 15-mm length PET fibers. The Izod impact strength of UPR/mat PET fiber composites as a function of fiber rate and length showed that the 5 and 8 phr composites for the 15-mm length PET fiber have the optimal mechanical properties 13.55 and 10.50 Kj/m², respectively. The morphological study showed that the strong adhesion resulting from the affinity of the PET fiber for the UPR matrix. The ductile fracture of materials reinforced with 5 and 8 phr is confirmed by the fiber deformation and fracture surface roughness.

This study concluded that the PET fiber enhances the properties of composites, a good correlation was observed between the results of the mechanical tests and the structural analysis revealing that for the lower concentrations, the PET fibers are well dispersed into the resin, but entanglements are evidenced when the fiber content increases.

It can be shown from scanning electron microscopy micrographs that the fabrication technique produced composites with good interfacial adhesion between PET fibers and UPR matrix.

Snap fits are crucial in automotive applications for rapid assembly and disassembly of mating components, eliminating the need for fasteners. This study aims to focus on designing and analyzing serviceable cantilever fit snap connections used in automobile plastic components. Snap fits are classified into permanent and semi-permanent fittings, with permanent fittings having a snap clipping angle between 0° and 5° and semi-permanent fittings having a clipping angle between 15° and 45°. Polypropylene random copolymer is chosen for its exceptional fatigue resistance and elasticity.

The design process includes determining dimensions, computing assembly, disassembly pressures and creating three-dimensional computer-aided design models. Finite element analysis (FEA) is used to evaluate the snap-fit mechanism’s stress, deformation and general functionality in operational scenarios.

The study develops a modified snap-fit mechanism with decreased bending stress and enhanced mating force optimization. The maximum bending stress during assembly is 16.80 MPa, requiring a mating force of 7.58 N, while during disassembly, it is 37.3 MPa, requiring a mating force of 16.85 N. The optimized parameters significantly improve the performance and dependability of the snap-fit mechanism. The results emphasize the need of taking into account both the assembly and disassembly processes in snap-fit design, because the research demonstrates greater forces during disassembly. The approach developed integrates FEA and design for assembly (DFA) concepts to provide a solution for improving the efficiency and reliability of snap-fit connectors in automotive applications.

The research paper’s distinctiveness comes from the fact that it presents a thorough and realistic viewpoint on snap-fit design, emphasizes material selection, incorporates DFA principles and emphasizes the specific requirements of both assembly and disassembly operations. These discoveries may enhance the efficiency, reliability and sustainability of snap-fit connections in plastic automobile parts and beyond. In conclusion, the idea that disassembly needs to be done with a lot more force than installation in a snap-fit design can have a good effect on buzz, squeak and rattle and noise, vibration and harshness characteristics in automobiles.

This study aims to evaluate the development of composites made of epoxy (E) resin with different weight percentages of polypropylene (PP) and graphene oxide (Go) to form nanocomposite plates.

A hand lay-up process was used to develop 21 different composites, with varying concentrations of PP (5%–35%) and Go (5%–35%). A ternary composite of E matrix was produced by combining binary fillers PP and Go (5%–35%) in a 1:1 ratio to a (95%–5%) solution. With the help of adopting the melt condensation deal to extract Go, the modified Hummers method was used to make Go platelets.

Through field emission scanning electron microscopy (FESEM) and X-ray diffraction investigations, the particulate’s size and structural characteristics were identified. Based on the FESEM analysis of the collapsed zones of the composites, a warp-and-weft-like structure is evident, which endorses the growth yield strength, flexural modulus and impact strength of the composites.

The developed nanocomposites have exceptional mechanical capabilities compared to plain E resin, with E resin exhibiting better tensile strength, modulus and flexural strength when combined with 10% PP and 10% Go. When compared to neat E resin, materials formed from composites have exceptional mechanical properties. When mixed with 10% PP and 10% Go, E resin in particular displays improved tensile strength (23 MPa), tensile modulus (4.15 GPa), flexural strength (75.6 MPa) and other attributes. Engineering implications include automobile side door panels, spacecraft applications, brake pads and flexible battery guards.

The purpose of this review paper is to provide a review of the most recent advances in the field of manufacturing composite sandwich panels along with their advantages and limitations. The other purpose of this paper is to familiarize the researchers with the available developments in manufacturing sandwich structures.

The most recent research articles in the field of manufacturing various composite sandwich structures were reviewed. The review process started by categorizing the available sandwich manufacturing techniques into nine main categories according to the method of production and the equipment used. The review is followed by outlining some automatic production concepts toward composite sandwich automated manufacturing. A brief summary of the sandwich manufacturing techniques is given at the end of this article, with recommendations for future work.

It has been found that several composite sandwich manufacturing techniques were proposed in the literature. The diversity of the manufacturing techniques arises from the variety of the materials as well as the configurations of the final product. Additive manufacturing techniques represent the most recent trend in composite sandwich manufacturing.

This work is valuable for all researchers in the field of composite sandwich structures to keep up with the most recent advancements in this field. Furthermore, this review paper can be considered as a guideline for researchers who are intended to perform further research on composite sandwich structures.

This study aims to prepare a low-formaldehyde and environmentally friendly glucose-lignin-based phenolic resin.

The authors directly used lignin to substitute formaldehyde to prepare lignin-based phenolic resin (LPF) with urea as formaldehyde absorbent. To improve the performance of the adhesive, the biobased glucose was introduced and the modified glucose-LPF (GLPF) was obtained.

The results showed that when the replacing amount of lignin to formaldehyde reached 15 Wt.%, the physical properties of the prepared LPF met the Chinese national standard, and the bonding strength increased by 21.9%, from 0.75 to 0.96 MPa, compared with PF. The addition of glucose boost the performance of wood adhesive, for example, the free phenol content of the obtained GLPF was significantly reduced by 79.11%, from 5.60% to 1.17%, the bonding strength (1.19 MPa) of GLPF increased by 19.3% in comparison to LPF and the curing temperature of GLPF decreased by 13.08%.

The low-formaldehyde and environmentally friendly GLPF has higher bonding strength and lower curing temperature, which is profitable to industrial application.

The prepared GLPF has lower free formaldehyde and formaldehyde emission, which is cost-effective and beneficial to human health.

The joint work of lignin and glucose provides the wood adhesive with increased bonding strength, decreased free phenol content and reduced curing temperature.