Search results

The purpose of this paper is to investigate the effects of electric current stressing on damping properties of Sn5Sb solder.

Uniformly shaped Sn5Sb solders were prepared as samples. The length, width and thickness of the samples were 60.0, 5.0 and 0.5 mm, respectively. The damping properties of the samples were tested by dynamic mechanical analyzer with a cooling system to control the test temperature in the range of −100 to 100°C. Simultaneously, electric current was imposed to the tested samples using a direct current supply. After tests, the samples were characterized using scanning electron microscope, electron backscatter diffraction and transmission electron microscope, which was aimed to figure out the damping mechanism in terms of electric current stressing induced microstructure evolution.

It is confirmed experimentally that the increase in damping properties is due to Joule heating and athermal effects of current stressing, in which Joule heating should make a higher contribution. G–L theory can be used to explain the damping properties of strain amplitude under current stressing by quantitative description of geometrically necessary dislocation density. While the critical strain amplitude and high temperature activation energy decrease with increasing electric current.

These results provide a new method for vibration reliability evaluation of high-temperature lead-free solders in serving electronics. Notably, this method should be also inspiring for the mechanical performance evaluation and reliability assessment of conductive materials and structures serving under electric current stressing.

This study aims to explore the feasibility of adding Si₃N₄ nanoparticles to Sn58Bi and provides a theoretical basis for designing and applying new lead-free solder materials for the electronic packaging industry.

In this paper, Sn58Bi-xSi₃N₄ (x = 0, 0.2, 0.4, 0.6, 0.8, 1.0 Wt.%) was prepared for bonding Cu substrate, and the changes in thermal properties, wettability, microstructure, interfacial intermetallic compound and mechanical properties of the composite solder were systematically studied.

The experiment results demonstrate that including Si₃N₄ nanoparticles does not significantly impact the melting point of Sn58Bi solder, and the undercooling degree of solder only fluctuates slightly. The molten solder spreading area reached a maximum of 96.17 mm², raised by 19.41% relative to those without Si₃N₄, and the wetting angle was the smallest at 0.6 Wt.% of Si₃N₄, with a minimum value of 8.35°. When the Si₃N₄ nanoparticles reach 0.6 Wt.%, the solder joint microstructure is significantly refined. Appropriately adding Si₃N₄ nanoparticles will slightly increase the solder alloy hardness. When the concentration of Si₃N₄ reaches 0.6 Wt.%, the joints shear strength reached 45.30 MPa, representing a 49.85% increase compared to those without additives. A thorough examination indicates that legitimately incorporating Si₃N₄ nanoparticles into Sn58Bi solder can enhance its synthetical performance, and 0.6 Wt.% is the best addition amount in our test setting.

In this paper, Si₃N₄ nanoparticles were incorporated into Sn58Bi solder, and the effects of different contents of Si₃N₄ nanoparticles on Sn58Bi solder were investigated from various aspects.

This study aims to investigate the thermal fracture mechanism of moisture-preconditioned SAC305 ball grid array (BGA) solder joints subjected to multiple reflow and thermal cycling.

The BGA package samples are subjected to JEDEC Level 1 accelerated moisture treatment (85 °C/85%RH/168 h) with five times reflow at 270 °C. This is followed by multiple thermal cycling from 0 °C to 100 °C for 40 min per cycle, per IPC-7351B standards. For fracture investigation, the cross-sections of the samples are examined and analysed using the dye-and-pry technique and backscattered scanning electron microscopy. The packages' microstructures are characterized using an energy-dispersive X-ray spectroscopy approach. Also, the package assembly is investigated using the Darveaux numerical simulation method.

The study found that critical strain density is exhibited at the component pad/solder interface of the solder joint located at the most distant point from the axes of symmetry of the package assembly. The fracture mechanism is a crack fracture formed at the solder's exterior edges and grows across the joint's transverse section. It was established that Au content in the formed intermetallic compound greatly impacts fracture growth in the solder joint interface, with a composition above 5 Wt.% Au regarded as an unsafe level for reliability. The elongation of the crack is aided by the brittle nature of the Au-Sn interface through which the crack propagates. It is inferred that refining the solder matrix elemental compound can strengthen and improve the reliability of solder joints.

Inspection lead time and additional manufacturing expenses spent on investigating reliability issues in BGA solder joints can be reduced using the study's findings on understanding the solder joint fracture mechanism.

Limited studies exist on the thermal fracture mechanism of moisture-preconditioned BGA solder joints exposed to both multiple reflow and thermal cycling. This study applied both numerical and experimental techniques to examine the reliability issue.