The purpose of this study is to modify the FDM 3D printer to print with polystyrene (PS) microspheres as the printing material, thus enabling bottom-up structural color printing and evaluating structural color printing.

This study chose a range of different heated bed temperatures to determine a suitable temperature for accelerating the self-assembly of photonic crystals and printing structural colors on various substrates. In addition, this study enhanced the structural color by doping PS microspheres with different contents of Acid Black 210 dye and evaluated the color-enhanced structural color by eye and spectrophotometer under different light sources.

The results show that the modified 3D printer can be used for structural color printing, and 50°C is determined as the heated bed temperature. There are significant differences in structural colors when printing under different color backgrounds and material substrates, and corresponding suitable substrates should be selected according to the application. The doping of PS microspheres with varying contents of dye results in different color levels of structural color. As with pigment colors, the visual perception of structural color varies when viewed under different light sources.

This paper proposes to print structural colors low-costly, analyze structural colors under substrate and light source conditions, and expand the structural color gamut by enhancing structural colors, which has positive implications for further research on structural colors as printing colors.

This study aims to fabricate a cool phthalocyanine green/TiO₂ composite pigment (PGT) with high near-infrared (NIR) reflectance, good color performance and good heat-shielding performance under sunlight and infrared irradiation.

With the help of anionic and cationic polyelectrolytes, the PGT composite pigment was prepared using a layer-by-layer assembly method under wet ball milling. Based on the light reflectance properties and color performance tested by ultraviolet-visible-NIR spectrophotometer and colorimeter, the preparation conditions were optimized and the properties of PGT pigment with different assembly layers (PGT-1, PGT-3, PGT-5 and PGT-7) were compared. In addition, their heat-shielding performance was evaluated and compared by temperature rise value for their coating under sunlight and infrared irradiation.

The PGT pigment had a core/shell structure, and the PG thickness increased with the self-assembly layers, which made the PGT-3 and PGT-7 pigment show higher color purity and saturation than PGT-1 pigment. In addition, the PGT-3 and PGT-7 pigment showed 11%–16% lower light reflectance in the visible region. However, their light reflectance in the NIR region was similar. Under infrared irradiation the PGT-5 and PGT-7 pigment coating showed 1.1°C–3.4°C and 1.3°C–4.7°C lower temperature rise value than PGT-1 pigment coating and physical mixture pigment coating, respectively. And under sunlight the PGT-3 pigment coating showed 1.5–2.6°C lower temperature rise value than the physical mixture pigment coating.

The layer-by-layer assembling makes the core/shell PGT composite pigment possess low visible light reflectance, high NIR reflectance and good heat-shielding performance.

This study aims to prepare an imprinted composite membrane with grafted temperature-sensitive blocks for the efficient adsorption and separation of rhenium(Re) from aqueous solutions.

PVDF resin membrane was used as the substrate, dopamine and chitosan (CS) were used to modify the membrane surface and temperature-sensitive block PDEA was grafted on the membrane surface. Then acrylic acid (AA) and N-methylol acrylamide (N-MAM) were used as the functional monomers, ethyleneglycol dimethacrylate (EGDMA) as the cross-linker and ascorbic acid-hydrogen peroxide (Vc-H₂O₂) as the initiator to obtain the temperature-sensitive ReO4⁻ imprinted composite membranes.

The effect of the preparation process on the performance of CS–Re–TIICM was investigated in detail, and the optimal preparation conditions were as follows: the molar ratios of AA–NH₄ReO₄, N-MAM and EGDMA were 0.13, 0.60 and 1.00, respectively. The optimal temperature and time of the reaction were 40 °C and 24 h. The maximum adsorption capacity of CS–Re–TIICM prepared under optimal conditions was 0.1071 mmol/g, and the separation was 3.90 when MnO4⁻ was used as the interfering ion. The quasi first-order kinetics model and Langmuir model were more suitable to describe the adsorption process.

With the increasing demand for Re, the recovery of Re from Re-containing secondary resources becomes important. This study demonstrated a new material that could be separated and recovered Re in a complex environment, which could effectively alleviate the conflict between the supply and demand of Re.

This contribution provided a new material for the selective separation and purification of ReO4⁻, and the adsorption capacity and separation of CS–Re–TIICM were increased with 1.673 times and 1.219 time compared with other Re adsorbents, respectively. In addition, when it was used for the purification of NH₄ReO₄ crude, the purity was increased from 91.950% to 99.999%.

This paper aims to focus on the research progress of intelligent self-healing anti-corrosion coatings in the aviation field in the past few years. The paper provides certain literature review supports and development direction suggestions for future research on intelligent self-healing coatings in aviation.

This mini-review uses a systematic literature review process to provide a comprehensive and up-to-date review of intelligent self-healing anti-corrosion coatings that have been researched and applied in the field of aviation in recent years. In total, 64 articles published in journals in this field in the last few years were analysed in this paper.

The authors conclude that the incorporation of multiple external stimulus-response mechanisms makes the coatings smarter in addition to their original self-healing corrosion protection function. In the future, further research is still needed in the research and development of new coating materials, the synergistic release of multiple self-healing mechanisms, coating preparation technology and corrosion monitoring technology.

To the best of the authors’ knowledge, this is one of the few systematic literature reviews on intelligent self-healing anti-corrosion coatings in aviation. The authors provide a comprehensive overview of the topical issues of such coatings and present their views and opinions by discussing the opportunities and challenges that self-healing coatings will face in future development.

The aim of this study is to present an overview of sustainable practices in the development of waterproof breathable fabrics for garments. It aims to provide insights into the current state of academic research in this domain and identify and analyze major sustainable trends in the field.

This study conducts a thorough examination of research publications sourced from the Scopus database spanning the years 2013–2023 by employing a systematic approach. The research utilizes both descriptive analysis and content analysis to identify trends, notable journals and leading countries in sustainable waterproof breathable fabric development.

The study reveals a notable increase in studies focusing on sustainable approaches in the development of waterproof breathable fabrics for garments. Descriptive analysis highlights the most prominent journal and leading country in terms of research volume. Content analysis identifies four key trends: minimizing chemical usage, developing easily degradable materials, creating fabrics promoting health and well-being and initiatives to reduce energy consumption.

The main limitation of this research lies in its exclusive reliance on the Scopus database.

The insights derived from this study offer practical guidance for prospective researchers interested in investigating sustainable approaches to developing waterproof breathable fabric for garments. The identified trends provide a foundation for aligning research endeavors with contemporary global perspectives, facilitating the integration of sustainable methodologies into the garment industry.

This systematic literature review contributes original insights by synthesizing current research trends and outlining evolving sustainable practices in the development of waterproof breathable fabrics. The identification of key focus areas adds a novel perspective to existing knowledge.

This study aims to develop multifunctional, namely, superhydrophobic, flame-retardant and antibacterial, coatings over cotton fabric, using casein as green-based flame-retardant and silver nanoparticles as antibacterial agent by solution immersion method.

The cotton fabric is first coated with casein to make it flame-retardant. AgNPs synthesized using Cinnamomum zeylanicum bark extract is coated over the casein layer. Finally, stearic acid is used to coat the cotton to make it superhydrophobic. X-ray diffraction, transmission electron microscopy analysis and ultraviolet-visible spectroscopy are used to investigate the produced AgNPs. The as-prepared multifunctional cotton is characterized by scanning electron microscopy, energy dispersive X-ray analysis and attenuated total reflection-infrared studies. Flame test, limiting oxygen index test and thermogravimetric analyzer studies have also been performed to study the flame-retardant ability and thermal stability of treated fabric, respectively. The antibacterial effect of the coatings is evaluated by disc-diffusion technique. Water contact angle is determined to confirm the superhydrophobic nature of cotton fabric.

The outcomes of this study showed that the prepared multifunctional cotton fabric had maximum contact angle of greater than 150° with good flame retardancy, high thermal stability, greater washing durability and high antibacterial activity against the growth of Pseudomonas aeruginosa and Acinetobacter indicus. Additionally, the as-prepared superhydrophobic cotton showed an excellent oil–water separation efficiency.

The trilayered multifunctional cotton fabric has limiting washing durability up to 20 washing cycles. Treated functional fabric can be used as an antibacterial, therapeutic, water repellent and experimental protective clothing for medical, health care, home curtains and industrial and laboratory purposes.

The study brings out the robustness of this method in the development of multifunctional cotton fabrics.

This study aims to investigate the morphology and physicochemical properties of BiOBr/Polyvinylidene fluoride (PVDF) composite membranes and the differences in the properties of BiOBr/PVDF composite membranes made by adding different precursor ratios during the casting process.

In this paper, sodium bromide and Bi(NO3)3 were used as precursors for the preparation of BiOBr photocatalysts, and PVDF membranes were modified by using the phase conversion method in conjunction with the in situ deposition method to produce BiOBr/PVDF hydrophilic composite membranes with both membrane separation and photocatalytic capabilities.

The characterization results confirmed that the composites were successfully and homogeneously co-mingled in the PVDF membranes. The related performance of the composite membrane was tested, and it was found that the composite membrane with the optimal precursor incorporation ratio had good photocatalytic efficiency and antipollution ability; the removal efficiencies of methyl orange, rhodamine B and methylene blue were 80.43%, 85.02% and 86.94%, respectively, in 2.5 h. The photocatalytic efficiency of composite membranes with different precursor ratios increased and then decreased with the increase of the precursor addition ratio.

The composite membrane is prepared by phase conversion method with in situ deposition method, and the BiOBr material has unique advantages for the degradation of organic dyes. The comprehensive experimental data can be known that the composite membrane prepared in this paper has high degradation efficiency and good durability for organic dyes.

The purpose of this research is as follows: DPP-BOH-PVA has been synthesized from 1,1′:3′,1″-terphenyl-5'-boronic acid (DPP-OH) and polyvinyl alcohol (PVA). The afterglow lifetime of DPP-BOH-PVA was studied by changing contents of DPP-OH (1, 2 and 4 Wt.%). These films were characterized with Fourier transform infrared, X-ray diffraction as structural analysis and DSC as thermal analysis. Afterglow lifetimes were evaluated as time-resolved emission decay profile analysis. Fiber films of DPP-BOH-PVA-2-E have been prepared by electrospinning method with the diameter of 5 μm and afterglow life time of 2.1 s (@ 535 nm) under ambient conditions. Stimulus responsive properties with afterglow emission for fiber film were investigated.

During the synthesis of the polymer, modification was carried out using DPP-OH/PVA with a molar ratio of 1/4, under an alkalinity medium with ammonium hydroxide and with a temperature of 80°C.

XRD results indicate that DPP-BOH-PVA film had high crystallinity, which is crucial for preparing organic room temperature phosphorescence (RTP) materials.

The reaction mixture must be stirred continuously. Temperature should be controlled to prevent the rapid evaporation of ammonium hydroxide.

This study provides technical information for the synthesis of multidimensional stimulation response RTP micron fiber thin film. The electrospinning technology may also promote the applications of the large areas of RTP films.

This resin will be used for the multidimensional stimulation response RTP fiber thin film.

The diameter of fiber film of PP-BOH-PVA-2-E by electrospinning method was in the range of 5 μm, and its afterglow lifetime decayed to be 2.1 s.

This paper aims to investigate the corrosion resistance of two types of coatings – one is ceria sol coating and the other is ceria sol coating modified by ZnO nanoparticles on 7075 aluminum alloy in 3.5% NaCl solution.

Aluminum alloys were dipped into ceria sol and ceria sol modified by ZnO nanoparticles separately and removed after 10 min from the solutions and dried at 110°C for 30 min and heated at 500 °C for 30 min to form the coatings. The coatings have been characterized by using field emission scanning electron microscopy (FE-SEM), electrochemical impedance spectroscopy (EIS), X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS). The EIS tests were performed in a corrosive solution of 3.5% NaCl.

The results showed that the coating of ceria sol modified by ZnO nanoparticles has higher corrosion resistance than the ceria sol coating and the bare sample. Also, the best efficiency is related to aluminum sample immersion after 1 h in NaCl corrosive solution for coating modified by ZnO nanoparticles.

In this research, the modification of ceria sol coating by ZnO nanoparticles had an effect on improving the corrosion behavior of aluminum alloy. It is also understood that modification of coatings is an effective parameter on corrosion resistance.