Search results

A failed disc that was forged from S355J2 round bar was investigated in order to determine the failure route cause. The purpose of this paper is to determine the defects and route cause analysis regarding their origin.

Macroscopic evaluation, microstructure observation using light optical metallography and scanning electron microscopy with EDX analysis were the techniques used to analyse and characterize the defected areas.

Macro-inclusions (up to 850 µm) that correspond to high melting aluminium rich calcium-aluminate particles were detected. Their formation, possibly due to improper calcium treatment during ladle furnace steel refining process might be associated with clogging problems at casting. SEM-EDX analysis revealed whitish spots containing Zr that could be related to submerged entry nozzle (SEN) erosion/breakage. Characteristic is the large size and unusual shape of the traced particles, as well as the presence of low Si, Na, K. The findings indicated that nozzle clogging and/or breakage at casting was most possibly the root cause of the product’s quality degradation.

After extended root cause analysis, specific countermeasures are proposed to avoid clogging phenomena. The suggestions are based on the findings taking into account restrains of the steel-making process. Emphasis was laid in detecting the weaknesses that lead to product quality degradation and consequently in optimizing the steel-making process. Such incidents are often found during steelmaking a useful suggestion to steelmakers is to mark and remove cast parts after SEN problems are encountered. In this way quality issues in intermediate and/or final products will be avoided.

The improvements in quality of advanced aerospace steels have brought new challenges for the materials testing and inspection teams. Looks at the advances of this type of testing at British Steel Engineering Steels. Details non‐destructive testing of aerospace steels and the ultrasonic immersion tank. Finally looks at Engineering Steels’ recent investments in automation.

The purpose of this article is to numerically investigate the effect of casting speed on the fluid flow, solidification and inclusion motion under the influence of electromagnetic stirring (EMS) in the bloom caster mold with bifurcated submerged entry nozzle (SEN).

The electromagnetic field obtained by solving Maxwell’s equation is coupled with the fluid flow, solidification and discrete phase model using the in-house user-defined functions. An enthalpy porosity approach and Lagrangian approach are applied for the solidification analysis and non-metallic inclusions motion tracking, respectively.

Investigation shows that the casting speed and EMS significantly affect the steel flow, solidification and inclusion behavior inside the mold. Investigations are being conducted into the complex interplay between the induced flow and the SEN’s inertial impinging jet. In low and medium casting speeds, the application of EMS significantly increases the inclusion removal rate. Inclusion removal is studied for its different size and density and further effect of EMS is also reported on cluster formation and distribution of inclusion in the domain.

The model may be used to optimize the process parameter (casting speed and EMS) to improve the casting quality of steel by removing the impurities.

The effect of casting speed on the solidification and inclusion behavior under the influence of time-varying EMS in bloom caster mold with bifurcated nozzle has not been investigated yet. The findings may assist the steelmakers in improving the casting quality.