Purpose – This purpose of the research is to investigate the process of manufacturing LDPE recycle thermoplastic composites with reinforcement oil palm empty fruit bunch (OPEFB) biomass microfillers.

Design/Methodology/Approach – Methods of physical and chemical modification of OPEFB fibers into the LDPE matrix and the addition of some compatibilizer such as MAPE and xylene process through melt blending can improve mechanical properties, electrical properties, biodegradability, and improve the morphology of composites.

Research Limitations/Implications – These composites are prepared by the following matrix ratio: filler (70:30)% and filler size (63, 75, 90, and 106) μm. The LDPE plastic is crushed to a size of 0.5–1 cm, then pressed with hot press free heating for 5 min and with a pressure of 10 min at 145 °C. Based on the characterization obtained, the tensile strength and the high impact on the use of 106 μm filler is 13.86 MPa and 3,542.6 J/m², and thermal stability indicates the degradation temperature (T₀) 497.83 °C. FT-IR analysis shows the presence of functional groups of cellulose and lignin molecules derived from TKKS collected in the composite.

Practical Implications – Based on the characterization obtained, this composite can be applied as furniture material and vehicle dashboard.

Originality/Value – Composites obtained from recycle of LDPPE plastics waste has some advantages such as good compatibility and high tensile strength. This composite used the OPEFB filler whose size is in micrometer, and so this product is different from other products.

The population of internationally forcibly displaced people, which includes refugees and asylum seekers, is large and heterogeneous. To determine the varying reasons for and experiences during the migration journey, including exposure to violence and health- and integration-related needs, there is an urgent need to involve children with refugee backgrounds in research and development activities. This chapter describes a model for the child participatory approach developed at Barnafrid, a national competence centre on violence against children at Linköping University in Sweden. The model has been tested in the Long Journey to Shelter study, which investigated exposure to violence and its consequences on mental health and functional ability among forcibly displaced children and young adults. As part of this project, we conducted workshops with children (n = 36, aged 13–18 years) to design a questionnaire on exposure to community violence in the country of resettlement. Experiences recounted during the child participatory workshops indicated no problems involving newly arrived children with refugee backgrounds and Swedish-born adolescents in research activities. However, attention should be paid to proper preparatory work and the need for adjustments. We discuss the results in light of other studies on refugee child participation, the United Nations Convention on the Rights of a Child and diversity considerations.

Purpose – The purpose of this research is to synthesize modified thermoplastic sago starch (TPS) through in-situ mechanism by reacting sago starch with diphenylmethanediisocyanate (MDI) and castor oil simultaneously, resulting in a more homogenous and finer-sized polyurethane prepolymer (PUP).

Design/Methodology/Approach – The methods used were Thermal Gravimetric Analysis (TGA) and Differential Scanning Calorimetry (DSC) for thermal characterization and stability of PUP, modified TPS non-extracted and extracted with toluene and water.

Findings – TGA test results presented shows that PUP begins to decompose thermally at a temperature of 300–500 °C. Weight loss occurs rapidly between these temperatures and is completely discharged at a temperature of 500°C, which is called weight loss transition.

Research Limitations/Implications – When extracted with toluene and a water solvent, the melting point and latent heat of fusion slightly decreased; however, it is still higher than the original value of sago. In terms of thermal stability, modified TPS decomposes and loses weight at 150–200 °C in small quantities, continues with weight loss rapidly, and is completely discharged at 500°C. The thermal stability is considered high; thus, modified TPS application can be varied.

Practical Implications – DSC analysis and TGA shows that modified TPS has good thermal characteristics and thermal stability. Modified TPS has a melting point of 104.69°C, and the latent heat of fusion (ΔH) is 234.27 J/g. This value is close to the PUP melting point and latent heat of fusion, which reveals the formation of cross-link between the starch and PUP.

The modern family constitution is a written declaration summarizing a process of agreement and decision-making within an entrepreneurial family regarding the motives, guidelines, and regulations for the family members’ cooperation within the family and the family business association. This chapter exposes facets of family constitutions from a historical and a practical point of view. In order to do so, it begins with a review of the predecessors and origins of family constitutions. Subsequently, focusing especially on the interplay between a family constitution and the family business’ binding legal agreements, it describes four forms of family constitutions that have evolved from different consulting approaches in practice. The chapter concludes with some legal implications.

This chapter provides an introduction to the world of family companies and family constitutions from a legal perspective. It first studies the legal types of business organizations that family firms have chosen across time and jurisdictions. It then illustrates how early predecessors of family constitutions evolved in the late Middle Ages and what modern family constitutions look like in different countries today. Further considerations are devoted to the governance framework of family firms. The chapter concludes by exploring the potential legal effects of family constitutions under German company and contract law.