The surface finish is an essential step in printed circuit boards design because it provides a solderable surface for electronic components. The purpose of this study to investigate the effects of different surface finishes during the soldering and ageing process.

The solder joints of Sn-4.0Ag-0.5Cu/Cu and Sn-4.0Ag-0.5Cu/electroless nickel/immersion silver (ENImAg) were investigated in terms of intermetallic (IMC) thickness, morphology and shear strength. The microstructure and compositions of solder joints are observed, and analyzed by using scanning electron microscopy (SEM-EDX) and optical microscope (OM).

Compounds of Cu₆Sn₅ and (Cu, Ni)₆Sn₅ IMC were formed in SAC405/Cu and SAC405/ENImAg, respectively, as-reflowed. When the sample was exposed to ageing, new layers of Cu₃Sn and (Ni, Cu)₃Sn₅ were observed at the interface. Analogous growth in the thickness of the IMC layer and increased grains size commensurate with ageing time. The results equally revealed an increase in shear strength of SAC405/ENImAg because of the thin layer of IMC and surface finish used compared to SAC405/Cu. Hence, a ductile fracture was observed at the bulk solder. Overall, the ENImAg surface finish showed excellent performance of solder joints than that of bare Cu.

The novel surface finish (ENImAg) has been developed and optimized. This alternative lead-free surface finish solved the challenges in electroless nickel/immersion gold and reduced cost without affecting the performance.

This paper presents the results of the investigations of LED modules soldered with the use of different soldering pastes.

The tested power LED modules are soldered using different solder pastes and soldering processes. Thermal parameters of the performed modules are tested using indirect electrical methods. The results of measurements obtained for different modules are compared and discussed.

It was shown that the soldering process visibly influences the results of measurements of optical and thermal parameters of LED modules. For example, values of thermal resistance of these modules and the efficiency of conversion of electrical energy into light differ between each other even by 15%.

The obtained results of investigations can be usable for designers of the assembly process of power LED modules.

This paper shows the investigations results in the area of effective assembly of power LEDs to the metal core printed circuit board (MCPCB) using different soldering pastes (REL22, REL61, LMPA-Q6, OM-5100, OM-338-PT, M8, OM-340, CVP-390). It was shown that the best thermal and optical properties of these modules are obtained for the OM5100 paste by Alpha Assembly.

The purpose of this paper is to investigate the effects of Sn-Ag-x leveling layers on the mechanical properties of SnBi solder joints. Four Sn-Ag-x (Sn-3.0Ag-0.5Cu, Sn-0.3Ag-0.7Cu, Sn-0.3Ag-0.7Cu-0.5 Bi-0.05Ni and Sn-3.0Ag-3.0 Bi-3.0In) leveling layers were coated on Cu pads to prepare SnBi/Sn-Ag-x/Cu solder joints. The microstructure, hardness, shear strength and fracture morphology of solder joints before and after aging were studied.

The interfacial brittleness of the SnBi low-temperature solder joint is a key problem affecting its reliability. The purpose of this study is to improve the mechanical properties of the SnBi solder joint.

Owing to the addition of the leveling layers, the grain size of the ß-Sn phase in the SnBi/Sn-Ag-x/Cu solder joint is significantly larger than that in the SnBi/Cu eutectic solder joint. Meanwhile, the hardness of the solder bulk in the SnBi/Cu solder joint shows a decrease trend because of the addition of the leveling layers. The SnBi/Cu solder joint shows obvious strength drop and interfacial brittle fracture after aging. Through the addition of the Sn-Ag-x layers, the brittle failure caused by aging is effectively suppressed. In addition, the Sn-Ag-x leveling layers improve the shear strength of the SnBi/Cu solder joint after aging. Among them, the SnBi/SACBN/Cu solder joint shows the highest shear strength.

This work suppresses the interfacial brittleness of the SnBi/Cu solder joint after isothermal aging by adding Sn-Ag-x leveling layers on the Cu pads. It provides a way to improve the mechanical performances of the SnBi solder joint.