This study aims to investigate the ammonia-sensing performance of polyaniline/polyethylene oxide (PANI/PEO) and polyaniline/polyethylene oxide/zinc oxide (PANI/PEO-ZnO) composite nanofibers at room temperature.

Gas sensor structures were fabricated using microfabrication techniques. First, onto the SiO₂ wafer, gold electrodes were fabricated via thermal evaporation. PANI/PEO nanofibers were produced by the electrospinning method, and the ZnO layer was deposited by using radio frequency (RF) magnetron sputtering on the electrospun nanofibers as a sensing layer. Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and X-ray diffraction were performed to characterize the analysis of nanofibers. After all, gas sensing analysis of PANI/PEO and PANI/PEO/ZnO nanofibers was conducted using an experimental setup at room temperature conditions. Furthermore, the impact of humidity (17%–90% RH) on the sensor resistance was actively investigated.

FTIR analysis confirms the presence of functional groups of PANI, PEO and ZnO in nanofiber structure. SEM micrographs demonstrate beads-free, thinner and smooth nanofibers with ZnO contribution to electrospun PANI/PEO nanofibers. Moreover, according to the gas sensing results, the PANI/PEO nanofibers exhibit 115 s and 457 s response time and recovery time, respectively. However, the PANI/PEO/ZnO nanofibers exhibit 245 s and 153 s response time and recovery time, respectively. PANI/PEO/MOx composite nanofibers ensure stability to the NH₃ gas owing to the high surface/volume ratio and decrease in the humidity dependence of gas sensors, making gas sensors more stable to the environment.

In this study, ZnO was deposited via RF magnetron sputtering techniques on PANI/PEO nanofibers as a different approach instead of in situ polymerization to investigate and enhance the sensor response and recovery time of the PANI/PEO/ZnO and PANI/PEO composite nanofibers to ammonia. These results indicated that ZnO can enhance the sensing properties of conductive polymer-based resistive sensors.

Regular monitoring of bacteria, especially Escherichia coli, in wastewater is crucial to ensure the maintenance of public health. Amperometric detection proves to be a fast, sensitive and economically viable solution for E. coli enumeration. This paper reported a prototype amperometric sensor based on PANI-ZnO-NiO nanocomposite thin films prepared by sol–gel method and irradiated with gamma ray. The purpose of this study is to investigate the sensor performance of PANI-ZnO-NiO nanocomposite thin films to detect E. coli in water.

The films were varied with different compositions of ZnO and NiO by using the formula PANI-(ZnO)_1-x-(NiO)_x, with x = 0.2, 0.4, 0.6 and 0.8. PANI-ZnO-NiO nanocomposite thin films were characterized by using X-ray diffraction (XRD) and atomic force microscopy (AFM) to study the crystallinity and surface morphology of the films. The sensor performance was conducted using the current–voltage (I-V) measurement by testing the films in clean water and E. coli solution.

XRD diffractograms show the peaks of ZnO (1 0 0) and NiO (1 0 2). AFM analysis shows the surface roughness, and the grain size of PANI-ZnO-NiO thin films decreases when the concentration ratios of NiO increased. I-V curves show the difference in current flow, where the current in E. coli solution is higher than the clean water.

PANI-(ZnO)_1-x-(NiO)_x nanocomposite thin film with the highest concentration of ZnO performed the highest sensitivity among the other concentrations, which can be used to indicate the presence of E. coli bacteria in water.

The objective of this research is to evaluate the influence of mineral additions on the mechanical performances of polymer concrete. This study aims to propose a novel approach formulation of polymer concrete based on reduction in the quantity of the binder and disposal of large quantities of industrial by-products and household waste such as the marble, the brick and silica fume whose valuation in polymer concrete could be an interesting ecological and economical alternative. The incorporation of a rate of 10% brick powder affects the distribution of pores inside polymer concrete, that is, the pore diameters become thinner and decrease and the porosity becomes evenly distributed. The recycled mineral brick powder addition in polymer concrete mix improved the mechanical properties.

This polymer concrete was prepared by using polyester resin and two different types of sand, following a new formulation based on an empirical method. Furthermore, the optimal binder percentage was of 20% resin and a mixture of 52% dune sand and 48% quarry sand according to the Abrams method. To achieve our objective, five rates (from 2% to 10%) of brick powder, marble powder and silica fume were examined. Afterwards, its mechanical characteristics were evaluated via a three-point flexural with compressive resistance. The findings indicated that the addition of brick, marble and silica fume to polymer concrete increases the flexural strength with 21.84%, 12.76% and 9.07%, respectively.

Concerning the compressive strength, the best resistance is that of polymer concretes based on brick powder, and this economic formulation of polymer concrete serves the optimal cost/resistance ratio criteria. It allows an improvement in the mechanical resistance of concrete are obtained by adding brick powder that exceed that of the reference concrete.

In the past few decades, there has been several contribution concerning the subject of the reduction of the binder quantity in polymer concretes and adding the industrial and household wastes. However, previous studies revolving around the same area disregarded the effect of the brick powder, which appears scientifically of great importance for enriching the literature.

This paper aims to achieve an anti-corrosive coating via uniform dispersion of nanoclay particles (montmorillonite) and polypyrrole (PPy) as a conductive polymer as well as their effects on the anti-corrosion features in the presence of the eco-friendly ionic liquids (ILs).

In this research, PPy with different forms of nanoclay were used. Moreover, ILs additive is used to enhance the better dispersion process of clay and PPy nanoparticles in the resin.

As a result, the IL additive in the formulation of nano-composite coatings greatly improves the dispersion process of clay and PPy nanoparticles in the resin. Due to its high compatibility with polyurethane resin and clay and PPy nanoparticles, this additive contains a high dispersing power to disperse the investigated nanoparticles in the resin matrix.

High polarity of ILs as well as abilities to dissolve both mineral and organic materials, they can provide the better chemical processes compared to common solvents.

IL abilities have not been discovered to a large extent such as catalysts and detectors.

ILs have been emerging as promising green solvents to replace conventional solvents in recent years. They possess unique properties such as nonvolatility, low toxicity, ease of handling, nonflammability and high ionic conductivity. Thus, they have received much attention as green media for various chemistry processes.

The simultaneous existence of clay, PPy and IL additive in the nano-composite coating formulation is responsible for the high corrosion resistance of the coating.

Polyaniline (PANI) has garnered attention for its potential applications in anticorrosion fields because of its unique properties. Satisfactory outcomes have been achieved when using PANI as a functional filler in organic coatings. More recently, research has extensively explored PANI-based organic coatings with self-healing properties. The purpose of this paper is to provide a summary of the active agents, methods and mechanisms involved in the self-healing of organic coatings.

This study uses specific doped acids and metal corrosion inhibitors as active and self-healing agents to modify PANI using the methods of oxidation polymerization, template synthesis, nanosheet carrier and nanocontainer loading methods. The anticorrosion performance of the coatings is evaluated using EIS, LEIS and salt spray tests.

Specific doped acids and metal corrosion inhibitors are used as active agents to modify PANI and confer self-healing properties to the coatings. The coatings’ active protection mechanism encompasses PANI’s own passivation ability, the adsorption of active agents and the creation of insoluble compounds or complexes.

This paper summarizes the active agents used to modify PANI, the procedures used for modification and the self-healing mechanism of the composite coatings. It also proposes future directions for developing PANI organic coatings with self-healing capabilities. The summaries and proposals presented may facilitate large-scale production of the PANI organic coatings, which exhibit outstanding anticorrosion competence and self-healing properties.

The purpose of this study is to prepare thermal transfer ribbons with good alcohol resistance.

A variety of alcohol-resistant thermal transfer inks were prepared using different polyester resins. The printing temperature, printing effect, adhesion and alcohol resistance of the inks on the label were studied to determine the feasibility of using the ink for manufacturing thermal transfer ribbons. The ink formulations were prepared by a simple and stable grinding technology, and then use mature coating technology to make the ink into a thermal transfer ribbon.

The results show that the thermal transfer ink has good scratch resistance, good alcohol resistance and low printing temperature when the three resins coexist. Notably, the performance of the ribbon produced by 500 mesh anilox roller was better than that of other meshes. Specifically, the ink on the matte silver polyethylene terephthalate (PET) label surface was wiped with a cotton cloth soaked in isopropyl alcohol under 500 g of pressure. After 50 wiping cycles, the ink remained intact.

The proposed method not only ensures good alcohol resistance but also has lower printing temperature and wider label applicability. Therefore, it can effectively reduce the loss of printhead and reduce production costs, because of the low printing temperature.

The purpose of this study is to evaluate the effect of graphene, basalt flakes and their synergy on the corrosion resistance of zinc-rich coatings. As the important heavy-duty anticorrosion coatings, zinc-rich coatings provided cathodic protection for the substrate. However, to ensure cathodic protection, a large number of zinc powder made the penetration resistance known as the weakness of zinc-rich coatings. Therefore, graphene and basalt flakes were introduced into zinc-rich coatings to coordinate its cathodic protection and shielding performance.

Three kinds of coatings were prepared; they were graphene modified zinc-rich coatings, basalt flakes modified zinc-rich coatings and graphene-basalt flakes modified zinc-rich coatings. The anticorrosion behavior of painted steel was studied by using the electrochemical impedance spectroscopy (EIS) technique in chloride solutions. The equivalent circuit methods were used for EIS analysis to obtain the electrode process structure of the coated steel system. Simultaneously, the corrosion resistance of the three coatings was evaluated by water resistance test, salt water resistance test and salt spray test.

The study found that the addition of a small amount of graphene and basalt flakes significantly improved the anticorrosion performance of coatings by enhancing their shielding ability against corrosive media and increasing the resistance of the electrochemical reaction. The modified coatings exhibited higher water resistance, salt water resistance and salt spray resistance. The graphene-basalt flakes modified zinc-rich coatings demonstrated the best anticorrosion effect. The presence of basalt scales and graphene oxide in the coatings significantly reduced the water content and slowed down the water penetration rate in the coatings, thus prolonging the coating life and improving anticorrosion effects. The modification of zinc-rich coatings with graphene and basalt flakes improved the utilization rate of zinc powder and the shielding property of coatings against corrosive media, thus strengthening the protective effect on steel structures and prolonging the service life of anticorrosion coatings.

The significance of developing graphene-basalt flakes modified zinc-rich coatings lies in their potential to offer superior performance in corrosive environments, leading to prolonged service life of metallic structures, reduced maintenance costs and a safer working environment. Furthermore, such coatings can be used in various industrial applications, including bridges, pipelines and offshore structures, among others.

This study aims to identify research trends and technological evolution in the polymer three-dimensional (3D) printing process that can effectively identify the direction of technological advancement and progress of acceptance in both society and key manufacturing industries.

The Scopus database was used to collect data on polymer 3D printing papers. This study uses bibliometric approach along with network analytic techniques to identify and discuss the most important countries and their scientific collaboration, compares income groups and analyses keyword trends.

It was found that top research production results from heavy investments in research and development. The USA has the highest number of papers among the high-income countries. However, scientific production in the other two income groups is strongly dominated by China and India. Keyword analysis shows that countries with lower incomes in certain areas, such as composite and bioprinting, have fallen behind other groups over time. International collaborations were suggested as mechanisms for those countries to catch up with the current research trends. The evolution of the research field, which started with a focus on 3D printing processes and shifted to printed part designs and their applications, was discussed. The advancement of the research topic suggests that translational research on polymer 3D printing has been led mainly by research production from higher-income countries and countries with large research and development investments.

Previous studies have conducted performance analysis, science mapping and network analysis in the field of 3D printing, but none have focused on global research trends classified by country income. This study has conducted a bibliometric analysis and compared the outputs according to various income levels according to the World Bank classification.

The purpose of this study is to evaluate the effectiveness of nanocontainer solutions in removing deteriorated and aged polymers commonly used in coating and consolidating archaeological glass.

This study focused on characterizing glass surfaces coated with two commonly used polymeric materials in archaeological glass preservation. Furthermore, the study evaluates the elimination of these coatings from the surfaces by using innovative aqueous systems composed of micellar solutions (MS) and oil-in-water (O/W) Texapon-P microemulsions (TEX). Glass samples coated with selected polymers were subjected to thermal and photochemical aging to simulate natural degradation conditions. This study aimed to evaluate the effectiveness of nanocontainer aqueous systems compared to acetone (Ac), a conventional solvent commonly used for removal procedures. The characterization procedures involved transmission electron microscopy, USB digital microscopy, scanning electron microscopy, color alteration and gravimetric measurement.

The findings indicate that the effectiveness of novel techniques using aqueous nanocontainer systems is quite promising when considering a “green approach” to preserving cultural heritage. Microscopic examination demonstrated the efficacy of MS in effectively removing acrylic and vinyl polymers from the glass surface. Furthermore, TEX proved effective in removing polyvinyl acetate (PVA) over Paraloid B72 (B-72). In addition, the measurement of color alteration values revealed a decrease after using MS compared to the standard sample before applying the polymers, with values of ΔE = 1.48 and 1.82 for B-72 polymer and PVA, respectively.

This research provides nanocontainer solutions for removing aged polymers from the glass surface. This makes the current study a promising step for treating archaeological glass.

Toner is a crucial dry colorant composite used in printing based on the electrophotographic process. The quality of printed images is greatly influenced by the toner production method and material formulation. Chemically in situ polymerization methods are currently preferred. This paper aims to optimize the characteristics of a composite produced through emulsion polymerization using common raw materials for electrophotographic toner production.

Emulsion polymerization provides the possibility to optimize the physical and color properties of the final products. Response surface methodology (RSM) was used to optimize variables affecting particle size (PS), PS distribution (PSD), glass transition temperature (T_g°C), color properties (ΔE) and monomer conversion. Box–Behnken experimental design with three levels of styrene and butyl acrylate monomer ratios, carbon black pigment and sodium dodecyl sulfate surfactant was used for RSM optimization. Additionally, thermogravimetric analysis and surface morphology of composite particles were examined.

The results indicated that colorants with small PS, narrow PSDs, spherical shape morphology, acceptable thermal and color properties and a high percentage of conversion could be easily prepared by optimization of material parameters in this method. The anticipated outcome of the present inquiry holds promise as a guiding beacon toward the realization of electrographic toner of superior quality and exceptional efficacy, a vital factor for streamlined mass production.

To the best of the authors’ knowledge, for the first time, material parameters were evaluated to determine their impact on the characteristics of emulsion polymerized toner composites.