The purpose of this paper is to investigate the effect of the replacement of natural coarse aggregate (NCA) with different percentages of recycled coarse aggregate (RCA) on properties of low calcium fly ash (FA)-based geopolymer concrete (GPC) cured at oven temperature. Further, this paper aims to study the effect of partial replacement of FA by ground granulated blast slag (GGBS) in GPC made with both NCA and RCA cured under ambient temperature curing.

M25 grade of ordinary Portland cement (OPC) concrete was designed according to IS: 10262-2019 with 100% NCA as control concrete. Since no standard guidelines are available in the literature for GPC, the same mix proportion was adopted for the GPC by replacing the OPC with 100% FA and W/C ratio by alkalinity/binder ratio. All FA-based GPC mixes were prepared with 12 M of sodium hydroxide (NaOH) and an alkalinity ratio, i.e. sodium hydroxide to sodium silicate (NaOH:Na₂SiO₃) of 1:1.5, subjected to 90^°C temperature for 48 h of curing. The NCA were replaced with 50% and 100% RCA in both OPC and GPC mixes. Further, FA was partially replaced with 15% GGBS in GPC made with the above percentages of NCA and RCA, and they were given ambient temperature curing with the same molarity of NaOH and alkalinity ratio.

The workability, compressive strength, split tensile strength, flexural strength, water absorption, density, volume of voids and rebound hammer value of all the mixes were studied. Further, the relationship between compressive strength and other mechanical properties of GPC mixes were established and compared with the well-established relationships available for conventional concrete. From the experimental results, it is found that the compressive strength of GPC under ambient curing condition at 28 days with 100% NCA, 50% RCA and 100% RCA were, respectively, 14.8%, 12.85% and 17.76% higher than those of OPC concrete. Further, it is found that 85% FA and 15% GGBS-based GPC with RCA under ambient curing shown superior performance than OPC concrete and FA-based GPC cured under oven curing.

The scope of the present paper is limited to replace the FA by 15% GGBS. Further, only 50% and 100% RCA are used in place of natural aggregate. However, in future study, the replacement of FA by different amounts of GGBS (20%, 25%, 30% and 35%) may be tried to decide the optimum utilisation of GGBS so that the applications of GPC can be widely used in cast in situ applications, i.e. under ambient curing condition. Further, in the present study, the natural aggregate is replaced with only 50% and 100% RCA in GPC. However, further investigations may be carried out by considering different percentages between 50 and 100 with the optimum compositions of FA and GGBS to enhance the use of RCA in GPC applications. The present study is further limited to only the mechanical properties and a few other properties of GPC. For wider use of GPC under ambient curing conditions, the structural performance of GPC needs to be understood. Therefore, the structural performance of GPC subjected to different loadings under ambient curing with RCA to be investigated in future study.

The replacement percentage of natural aggregate by RCA may be further enhanced to 50% in GPC under ambient curing condition without compromising on the mechanical properties of concrete. This may be a good alternative for OPC and natural aggregate to reduce pollution and leads sustainability in the construction.

The purpose of this research is to evaluate construction and industrial waste materials in concrete using different additives.

The experimental study investigated the effect of waste foundry sand (WFS), waste glass (GW) as partial substituent to natural sand and addition of waste glass fibers (GFs) and silica fume (SF) in natural/construction waste aggregate concrete on mechanical properties, durability and microstructure using.

The results reveal significant strength enhancement on using two admixtures, the maximum increase in compressive strength was obtained on using 20% WFS and 0.75% GF for both natural (75% increment) and construction waste (72% increment) coarse aggregates. Using three admixtures simultaneously, the maximum enhancement in compressive strength was found for (WFS(20%) + GW(10%) + GF(0.75%)) for both natural aggregates (122% increment) and construction waste (114% increment) coarse aggregates as compared to control mix. The 28 days split tensile and flexural strength of natural/construction waste aggregate concrete improve with age appreciably for optimal contents of single, two or three admixtures and the maximum tensile and flexural strength increment was 135 and 97% for mix (WFS(20%) + GW(10%) + GF(0.75%)) with natural aggregates as compared to control mix. The microstructural analysis results indicate improved microstructure upon partial substitution of sand with WFS, GW and SF along with addition of waste GFs.

The use of construction and industrial waste as a substituent to natural aggregate/sand will provide far reaching benefits for the green construction and the environment at large.

A study on the mechanical characteristics of cementitious mortar reinforced with basalt fibres at ambient and elevated temperatures was carried out. To investigate their effect, chopped basalt fibres with varying percentages were added to the cement mortar.

All the specimens were heated using a muffle furnace. Flexural strength and Compressive strength tests were performed, while monitoring the moisture loss to evaluate the performance of basalt fibre reinforced cementitious mortars at elevated temperatures.

From the study, it is clear that basalt fibres can be used to reinforce mortar as the fibres remain unaffected up to 500 °C. Minimal increases in flexural strengths and compressive strengths were measured with the addition of basalt fibres at both ambient and elevated temperatures. SEM pictures revealed fibre matrix interaction/degradation at different temperatures.

The current study shows the potential of basalt fibre addition in mortar as a reinforcement mechanism at elevated temperatures and provides experimental quantifiable mechanical performances of different fibre percentage addition.

Environmental issues caused by the production of Portland cement have led to it being replaced by waste materials such as fly ash, which is more economical and safer for the environment. Also, fly ash is a material with sustainable properties. Therefore, this paper aims to focus on the development of sustainable construction materials using 100% high-calcium fly ash and potassium hydroxide (KOH)-based alkaline solution and study the engineering properties of the resulting fly ash-based geopolymer concrete. Laboratory tests were conducted to determine the mechanical properties of the geopolymer concrete such as compressive strength, flexural strength, curing time and slump. In phase I of the study, carbon nanotubes (CNTs) were added to determine their effect on the strength of the geopolymer mortar. The results derived from the experiments indicate that mortar and concrete made with 100% fly ash C require an alkaline solution to produce similar (comparable) strength characteristics as Portland cement concrete. However, it was determined that increasing the amount of KOH generates a considerable amount of heat causing the concrete to cure too quickly; therefore, it is notable to forming a proper bond was unable to form a stronger bond. This study also determined that the addition of CNTs to the mix makes the geopolymer concrete tougher than the traditional concrete without CNT.

Tests were conducted to determine properties of the geopolymer concrete such as compressive strength, flexural strength, curing time and slump. In Phase I of the study, CNTs were studied to determine their effect on the strength of the geopolymer mortar.

The results derived from the experiments indicate that mortar and concrete made with 100% fly ash C require an alkaline solution to produce the same strength characteristics as Portland cement concrete. However, it was determined that increasing the amount of KOH generates too much heat causing the concrete to cure too quickly; therefore, it is notable to forming a proper bond. This study also determined that the addition of CNTs to the mix makes the concrete tougher than concrete without CNT.

This study was conducted at the construction engineering and management concrete laboratory at North Dakota State University in Fargo, North Dakota. All the experiments were conducted and analyzed by the authors.

The purpose of this paper is to develop an alternative new ternary geopolymer mortar (MKSP) to resolve a traditional mortar problem which exhibits several disadvantages, including poor strengths and surface microcracks and the CO₂ air pollution.

The MKSP ternary binder was produced using metakaolin (MK), slag (S), and palm oil fuel ash (POFA) activated with an alkaline mixture of sodium silicate (Na₂SiO₃) and 10 M NaOH in a mass ratio of 2.5. Seven different mix proportions of MK, slag, and POFA were used to fabricate MKSP mortars. The water-to-binder ratio was varied between 0.4 and 0.5. The mortars were heat cured for 2 h at 80°C and then aged in air. Flexural stress and strain, mortars flow and compressive strength were tested. Furthermore, the mortars were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) analyses.

The results showed that the sample MKSP6, which contained 40 percent MK, 40 percent slag, and 20 percent POFA, exhibited high compressive strength (52 MPa) without any cracks and flexural strength (6.9 MPa) at 28 days after being cured for 2 h at 80°C; however, the MKSP7 mortar with optimal strength of 55 MPa showed some surface cracks . Further, the results of the XRD, SEM, and FTIR analyses indicated that the MKSP mortars primarily consisted of a crystalline (Si+Al) phase (70 percent) and a smaller amorphous (Si+Ca) phase (30 percent).

The MKSP ternary geopolymer mix has three limitations as an importance of heat curing for development early strength, POFA content less than 20 percent to gain high normal strength and delaying the sitting time by controlling the slag content or the alkali activator type.

The use of geopolymer materials binder in a real building is limited and it still under research, Thus, the first model of real applied geopolymer cement in 2008 was the E-Crete model that formed by Zeobond company Australia to take the technology of geopolymer concrete to reality. Zeobond Pty Ltd was founded by Professor Jannie S.J. van (van Deventer et al., 2013), it was used to product precast concrete for the building structure. The second model was PYRAMENT model in 2002 by American cement manufacturer Lone Star Industries which was produced from the development carried out on inorganic alumino-silicate polymers called geopolymer (Palomo et al., 1999). In 2013 the third model was Queensland’s University GCI building with three suspended floors made from structural geopolymer concrete containing slag/fly ash-based geopolymer (Pathak, 2016). In Australia, 2014, the newly completed Brisbane West Wellcamp airport becomes the greenest airport in the world. Cement-free geopolymer concrete was used to save more than 6,600 tons of carbon emissions in the construction of the airport. Therefore, the next century will see cement companies developing alternative binders that are more environmentally friendly from a sustainable development point of view.

Production of new geopolymer binder of mortar as alternative to traditional cement binder with high early and normal strength from low cost waste materials, less potential of cracking, less energy consumption need and low carbon dioxide emission.

The cement-filled PA12 manufactured by selective laser sintering (SLS) offers desirable mechanical properties; however, these properties are dependent on several fabrication parameters. As a result, SLS prototypes may exhibit orthotropic mechanical properties unless properly oriented in build chamber. This paper aims to evaluate the effects of part build orientation, laser energy and cement content on mechanical properties of cement-filled PA12.

The test specimens were fabricated by SLS using the “DTM Sinterstation 2000” system at which the specimens were aligned along six different orientations. The scanning speed was 914mm/s, scan spacing was 0.15mm, layer thickness was 0.1mm and laser power was 4.5–8Watt. A total of 270 tensile specimens, 270 flexural specimens and 135 compression specimens were manufactured and the tensile, compression and flexural properties of fabricated specimens were evaluated.

The experiments revealed orientation-dependent (orthotropic) mechanical properties of SLS cement-filled PA12 and confirmed that the parts with shorter scan vectors have enhanced flexural strength as compared with longer scan vectors. The maximum deviations of ultimate tensile strength, compressive strength and flexural modulus along the six orientations were 32%, 26% and 36%, respectively.

Although part build orientation is a key fabrication parameter, very little was found in open literature with contradictory findings about its effect on mechanical properties of fabricated parts. In this work, the effects of build orientation when combined with other fabrication parameters on the properties of SLS parts were evaluated along six different orientations.

Cement can be replaced to reduce the energy consumption and the environmental impact of cement. Also, foamed concrete can be used structurally in residential buildings to reduce weight and improve thermal insulation. To achieve these two goals, this paper aims to investigate the effect of basalt powder as a partial replacement of either cement or sand.

This paper investigates the effect of basalt powder as a partial replacement of either cement or sand on the mechanical properties of foamed concrete used to cast slabs. First, mechanical properties of foamed concrete are tested with and without replacement of basalt. Then, six slabs of different thicknesses and mixes are investigated. The thicknesses considered are 150- and 200-mm slabs. The three mixes used to construct these slabs are foamed concrete with no basalt powder, foamed concrete with replacement of 20% of cement by basalt powder and foamed concrete with replacement of 20% of sand by basalt powder. The flexural behavior of these slabs is investigated.

All the slabs failed in the commonly intended flexural mode. The results show that the basalt powder acted as a strong filler material in the foamed concrete mix based on mechanical properties and flexural behavior. The proposed foamed concrete slabs can be used structurally in residential buildings.

A natural waste material that can be used to promote energy efficiency and reduce emission is basalt. In this paper, basalt powder is suggested to be used due to its chemical composition that is similar to cement. Also, basalt powder is low in cost as it is waste, while basalt aggregate is prepared, and it is only used as filler in paved roads. Accordingly, basalt is partially used instead of cement to reduce the emission of carbon dioxide that results from the cement manufacturing. Also, it is used as a partial alternative to sand which can be considered as a new stronger source as filling material used in the production of concrete.

This study aims to develop geopolymer concrete (GPC) using manufactured sand (M-sand) and recycled concrete aggregate (RCA) under different curing conditions. GPC is a sustainable construction material developed with industrial waste products such as fly ash to eliminate the use of cement in the production of concrete. GPC requires heat curing for the attainment of early age strength. The development of GPC under heat curing conditions is a hard process in practice. To overcome such circumstances, an attempt was made to develop the GPC under different curing conditions with the aid of coarse aggregate (CA) and RCA. The influence of different curing conditions on strength gain and microstructural characteristics of GPC is investigated. Mechanical properties of GPC such as compressive strength, tensile strength, flexural strength and elastic modulus are reported and discussed.

This study focuses on the assessment of mechanical and microstructure characterization of eco-efficient GPC developed with natural CA and RCAs. The required optimum quantity of binder, alkali activator, alkaline liquid to binder ratio and aggregates was determined by appropriate trials. Three types of curing methods, namely, ambient, oven and water, were used for the development of GPC mixes. Following the properties of RCA, it is realistic to substitute up to 40% of coarser aggregates as the resulting aggregate mix falls within the requirements of the analyzed mix.

Special attention is required for the mix with RCA because the mix’s consistency is affected by the high water absorption of the RCA mix. GPC specimens cured at ambient and water conditions exhibited marginal variation in the compressive strength for both CA and RCA. The compressive strength of GPC mixes prepared with RCA was marginally higher than that of the GPC made with CA under different curing regimes. RCA can be used as a sustainable material in lieu of CA in GPC.

The main significance of this research work is to develop the optimal mix design with appropriate mix proportion. The present study proposes a satisfactory methodology that enhances the mechanical strength of GPC as the guidelines are not available in the standards to address this problem. Effective use of waste materials such as fly ash and recycled aggregate for the development of GPC is another major research focus in the proposed investigation.

The purpose of this paper is to examine the use of phragmites australis ash (PAA) in cementitious systems to achieve sustainable construction.

In this paper, the properties of mortar containing PAA as partial cement replacement are determined. The PAA is produced through slow burning in a closed system to minimize the CO₂ emission. A total of four mortar mixes are prepared with PAA replacement levels ranging from 0% to 30% by weight. The water to binder and the proportions of binder to sand are 0.55 and 1:3 by weight, respectively. The properties tested are density, compressive strength, flexural strength, ultrasonic pulse velocity, water absorption by total immersion and capillary rise. Testing is conducted at 1, 7, 28 and 90 days.

While there is a decrease in strength as the amount of PAA increases, there is strong indication of pozzolanic reaction in the presence of PAA. This is in agreement with the results reported by Salvo et al. (2015), where they found noticeable pozzolanic activities in the presence of straw ash, which is rich in SiO₂ and relatively high K₂O content. At 90 days of curing, there is a decrease of 5% in compressive strength at 10% PAA replacement. However, at 20% and 30% replacement, the reduction in compressive strength is 23% and 32%, respectively. The trend in flexural strength and ultrasonic pulse velocity is similar to that in compressive strength. The water absorption by total immersion and capillary rise tends to increase with increasing amounts of PAA in the mix. There seems to be a linear relationship between water absorption and compressive strength at each curing age.

The Phragmites australis plant used in this investigation is obtained from one location and this present a limitation as the type of soil may change the properties. Also one method of slow burning is used. Different burning methods may alter the composition of the PAA.

This outcome of this research will contribute towards sustainable development as it will make use of the waste generated, reduce the amount of energy-intensive cement used in construction and help generate local employment in the area where the Phragmites australis plant grows.

To the best knowledge of the authors, the ash from the Phragmites australis plant has not been used in cementitious system and this research can be considered original as it examines the properties of mortar containing PAA. Also, the process of burning in a closed system using this material.

The purpose of this paper is to characterize mechanical properties (tensile, compressive and flexural) for the three-dimensional printing (3DP) process, using various common recommended infiltrate materials and post-processing conditions.

A literature review is conducted to assess the information available related to the mechanical properties, as well as the experimental methodologies which have been used when investigating the 3D printing process characteristics. Test samples are designed, and a methodology to measure infiltrate depths is presented. A full factorial experiment is conducted to collect the tensile, compressive and bending forces for a set of infiltrates and build orientations. The impact of the infiltrate type and depth with respect to the observed strength characteristics is evaluated.

For most brittle materials, the ultimate compression strength is much larger than the ultimate tensile strength, which is shown in this work. Unique stress–strain curves are generated from the infiltrate and build orientation conditions; however, the compressive strength trends are more consistent in behavior compared to the tensile and flexural results. This comprehensive study shows that infiltrates can significantly improve the mechanical characteristics, but performance degradation can also occur, which occurred with the Epsom salts infiltrates.

More experimental research needs to be performed to develop predictive models for design and fabrication optimization. The material-infiltrate performance characteristics vary per build orientation; hence, experimental testing should be performed on intermediate angles, and a double angle experiment set should also be conducted. By conducting multiple test scenarios, it is now understood that this base material-infiltrate combination does not react similar to other materials, and any performance characteristics cannot be easily predicted from just one study.

These results provide a foundation for a process design and post-processing configuration database, and downstream design and optimization models. This research illustrates that there is no “best” solution when considering material costs, processing options, safety issues and strength considerations. This research also shows that specific testing is required for new machine–material–infiltrate combinations to calibrate a performance model.

There is limited published data with respect to the strength characteristics that can be achieved using the 3DP process. No published data with respect to stress–strain curves are available. This research presents tensile, compressive and flexural strength and strain behaviors for a wide variety of infiltrates, and post-processing conditions. A simple, unique process is presented to measure infiltrate depths. The observed behaviors are non-linear and unpredictable.