Wire-arc-based additive manufacturing (WAAM) is a promising technology for the efficient and economical fabrication of medium-large components. However, the anisotropic behavior of the multilayered WAAM-fabricated components remains a challenging problem.

The purpose of this paper is to conduct a comprehensive study of the grain morphology, crystallographic orientation and texture in three regions of the WAAM printed component. Furthermore, the interdependence of the grain morphology in different regions of the fabricated component with their mechanical and tribological properties was established.

The electron back-scattered diffraction analysis of the top and bottom regions revealed fine recrystallized grains, whereas the middle regions acquired columnar grains with an average size of approximately 8.980 µm. The analysis revealed a higher misorientation angle and an intense crystallographic texture in the upper and lower regions. The investigations found a higher microhardness value of 168.93 ± 1.71 HV with superior wear resistance in the bottom region. The quantitative evaluation of the residual stress detected higher compressive stress in the upper regions. Evidence for comparable ultimate tensile strength and greater elongation (%) compared to its wrought counterpart has been observed.

The study found a good correlation between the grain morphology in different regions of the WAAM-fabricated component and their mechanical and wear properties. The Hall–Petch relationship also established good agreement between the grain morphology and tensile test results. Improved ductility compared to its wrought counterpart was observed. The anisotropy exists with improved mechanical properties along the longitudinal direction. Moreover, cylindrical components have superior tribological properties compared with cuboidal components.

This study aims to investigate the corrosion behavior of cold-rolled Fe₃₅Ni₂₀C_r12Mn_(28-x)Al_x high-entropy alloys (HEAs) using the potentiodynamic polarization technique in 1 M H₂SO₄ acid. Additionally, the influence of molybdenum (Mo) additions as inhibitors and the effect of variations in cold rolling reduction ratios and Al content on corrosion behavior are examined.

Two cold rolling reduction ratios, namely, 50% (R50) and 90% (R90), were examined for the cold-rolled Fe₃₅Ni₂₀Cr₁₂Mn₂₈Al₅ (Al₅) and Fe₃₅Ni₂₀Cr₁₂Mn₂₃Al₁₀ (Al₁₀) HEAs. Mo inhibitor additions were introduced at varying concentrations of 0.3, 0.6 and 0.9 Wt.%. The potentiodynamic polarization technique was used to evaluate the corrosion rates (CRs) under different experimental conditions.

The results indicate that the addition of 0.3 Wt.% Mo in 1 M H₂SO₄ yielded the lowest CR for both R50 and R90, irrespective of the Al content in the HEAs. However, the highest CR was observed at 0.6 Wt.% Mo addition. Furthermore, increasing the concentration of Al resulted in a corresponding rise in the CR. Comparatively, the CR decreased significantly when the cold rolling reduction ratio increased from R50 to R90.

This research provides valuable insights into the intricate relationship between Mo inhibitors, cold rolling reduction ratio, Al content and the resulting corrosion behavior of Fe₃₅Ni₂₀Cr₁₂Mn_(28-x)Al_x HEAs. The comprehensive analysis of corroded HEAs, including surface morphology, compositions and elemental distribution mapping, contributes to the understanding of the corrosion mechanisms and offers potential strategies for enhancing the corrosion behavior of HEAs.

The purpose of this paper is to study the correlation between different topographies and the reaction of Ulva Linza fouling species.

In this research, topographies with a different method, such as hot embossing and hot pulling, were achieved, and biological analyses were done with macroalgae Ulva Linza cells. The effect of topography via local binding geometry (honeycomb size gradients) and Wenzel roughness on the settling of Ulva microorganisms was tested.

As a result, Ulva spores confirmed different reactions to a similar set of tapered microstructures that was in agreement with the results on distinct honeycombs. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.

The reaction of an organism at the interface of vehicles’ substrate is powerfully affected by surface topographies.

The best embedment occurred on structures with bigger sizes than Ulva Linza’s spores. The density of settled spores was proportional to Wenzel roughness and the spores favour to attach to “kink sites” positions.

Unfortunately, unpleasant aggregation of marine biofouling on marine vehicles’ surfaces, generate terrific difficulties in the relevant industry.

There was a sharp relationship between Wenzel roughness and settle of Ulva Linza spores. The local binding geometry and the Wenzel roughness factor “r” were dominant on settling of Ulva Linza spores.

This study aims to enhance merging of additive manufacturing (AM) techniques with powder injection molding (PIM). In this way, the prototypes could be 3D-printed and mass production implemented using PIM. Thus, the surface properties and mechanical performance of parts produced using powder/polymer binder feedstocks [material extrusion (MEX) and PIM] were investigated and compared with powder manufacturing based on direct metal laser sintering (DMLS).

PIM parts were manufactured from 17-4PH stainless steel PIM-quality powder and powder intended for powder bed fusion compounded with a recently developed environmentally benign binder. Rheological data obtained at the relevant temperatures were used to set up the process parameters of injection molding. The tensile and yield strengths as well as the strain at break were determined for PIM sintered parts and compared to those produced using MEX and DMLS. Surface properties were evaluated through a 3D scanner and analyzed with advanced statistical tools.

Advanced statistical analyses of the surface properties showed the proximity between the surfaces created via PIM and MEX. The tensile and yield strengths, as well as the strain at break, suggested that DMLS provides sintered samples with the highest strength and ductility; however, PIM parts made from environmentally benign feedstock may successfully compete with this manufacturing route.

This study addresses the issues connected to the merging of two environmentally efficient processing routes. The literature survey included has shown that there is so far no study comparing AM and PIM techniques systematically on the fixed part shape and dimensions using advanced statistical tools to derive the proximity of the investigated processing routes.