Search results

There is recent emphasis on designing new materials and alloys specifically for metal additive manufacturing (AM) processes, in contrast to AM of existing alloys that were developed for other traditional manufacturing methods involving considerably different physics. Process optimization to determine processing recipes for newly developed materials is expensive and time-consuming. The purpose of the current work is to use a systematic printability assessment framework developed by the co-authors to determine windows of processing parameters to print defect-free parts from a binary nickel-niobium alloy (NiNb5) using laser powder bed fusion (LPBF) metal AM.

The printability assessment framework integrates analytical thermal modeling, uncertainty quantification and experimental characterization to determine processing windows for NiNb5 in an accelerated fashion. Test coupons and mechanical test samples were fabricated on a ProX 200 commercial LPBF system. A series of density, microstructure and mechanical property characterization was conducted to validate the proposed framework.

Near fully-dense parts with more than 99% density were successfully printed using the proposed framework. Furthermore, the mechanical properties of as-printed parts showed low variability, good tensile strength of up to 662 MPa and tensile ductility 51% higher than what has been reported in the literature.

Although many literature studies investigate process optimization for metal AM, there is a lack of a systematic printability assessment framework to determine manufacturing process parameters for newly designed AM materials in an accelerated fashion. Moreover, the majority of existing process optimization approaches involve either time- and cost-intensive experimental campaigns or require the use of proprietary computational materials codes. Through the use of a readily accessible analytical thermal model coupled with statistical calibration and uncertainty quantification techniques, the proposed framework achieves both efficiency and accessibility to the user. Furthermore, this study demonstrates that following this framework results in printed parts with low degrees of variability in their mechanical properties.

The purpose of this paper is to understand the effect of four different factors: building orientation, heat treatment (solution annealing and aging), thermal history and process parameters on the mechanical properties and microstructural features of 17-4 precipitation hardening (PH) stainless steel (SS) parts produced using selective laser melting (SLM).

Various sets of test samples were built on a ProX 100™ SLM system under argon environment. Characterization studies were conducted using mechanical tensile and compression test, microhardness test, optical microscopy, X-ray diffraction and scanning electron microscopy.

Results indicate that building orientation has a direct effect on the mechanical properties of SLM parts, as vertically built samples exhibit lower yield and tensile strengths and elongation to failure. Post-SLM heat treatment proved to have positive effects on part strength and hardness, but it resulted in reduced ductility. Longer inter-layer time intervals between the melting of successive layers allow for higher austenite content because of lower cooling rates, thus decreasing material hardness. On the other hand, tensile properties such as elongation to failure, yield strength and tensile strength were not significantly affected by the change in inter-layer time intervals. Similar to other AM processes, SLM process parameters were shown to be instrumental in achieving desirable part properties. It is shown that without careful setting of process parameters, parts with defects (porosity and unmelted powder particles) can be produced.

Although the manufacturing of 17-4 PH SS using SLM has been investigated in the literature, the paper provides the first comprehensive study on the effect of different factors on mechanical properties and microstructure of SLM 17-4 PH. Optimizing process parameters and using heat treatment are shown to improve the properties of the part.

Ti6Al4V alloy has received a great deal of attention in medical applications due to its biomechanical compatibility. However, the human bone stiffness is between 10 and 30 GPa while solid Ti6Al4V is several times stiffer, which would cause stress shielding with the surrounding bone, which can lead to implant and/or the surrounding bone’s failure.

In this work, the effect of selective laser melting (SLM) process parameters on the characteristics of Ti6Al4V samples, such as porosity level, surface roughness, elastic modulus and compressive strength (UCS), has been investigated using response surface method. The examined ranges of process parameters were 35-50 W for laser power, 100-400 mm/s for scan speed and 35-120 µm for hatch spacing. The process parameters have been optimized to obtain structures with properties very close to that in human bones.

The results showed that the porosity percentage of a SLM component could be increased by reducing the laser power and/or increasing the scan speed and hatch spacing. It was also shown that there was a reverse relationship between the porosity level and both the modulus of elasticity and UCS of the SLM part. In addition, the increased laser power was resulted into a substantial decrease of the surface roughness of SLM parts. Results from the optimization study revealed that the interaction between laser process parameters (i.e. laser power, laser speed, and the laser spacing) have the most significant influence on the mechanical properties of fabricated samples. The optimized values for the manufacturing of medical implants were 49 W, 400 mm/s and 99 µm for the laser power, laser speed and laser spacing, respectively. The corresponding porosity, surface roughness, modulus of elasticity and UCS were 23.62 per cent, 8.68 µm, 30 GPa and 522 MPa, respectively.

Previous investigations related to additive manufacturing of Ti alloys have focused on producing fully dense and high-integrity structures. There is a clear gap in literature regarding the simultaneous enhancement and adjustment of pore fraction, surface and mechanical properties of Ti6Al4V SLM components toward biomedical implants. This was the objective of the current study.