This study aims to investigate the influence mechanism of brazing and aging on the strengthening and corrosion behavior of novel multilayer sheets (AA4045/AA7072/AA3003M/AA4045).

Polarization curve tests, immersion experiments and transmission electron microscopy analysis were used to study the corrosion behavior and tensile properties of the sheets before and after brazing and aging.

The strength of the sheet is weakened after brazing due to brittle eutectic phases, and recovered after aging due to enhanced precipitation strengthening in the AA7072 interlayer. The core of nonbrazed sheets cannot be protected due to the significant galvanic coupling effect between the intermetallic particles and the substrate. Brazing and aging treatments promote the redissolved of second phased and limit corrosion along the eutectic region in the clad, allowing the core to be protected.

AA7xxx alloy was added to conventional brazed sheets to form a novel Al alloy composite sheet with AA4xxx/AA7xxx/AA3xxx structure. The strengthening and corrosion mechanism of the sheet was proposed. The added interlayer can sacrificially protect the core from corrosion and improves strength after aging treatment.

This study aims to investigate the corrosion inhibitor effect of migrating corrosion inhibitor (MCI) on Q235 steel in high alkaline environment under cathodic polarization.

This study investigated the electrochemical characteristics of Q235 steel with and without MCI by polarization curve and electrochemical impedance spectroscopy. Besides, the surface composition of Q235 steel under different environments was analyzed by X-ray photoelectron spectroscopy. In addition, the migration characteristic of MCI and the adsorption behavior of MCI under cathodic polarization were studied using Raman spectroscopy.

Diethanolamine (DEA) and N, N-dimethylethanolamine (DMEA) can inhibit the increase of Fe(II) in the oxide film of Q235 steel under cathodic polarization. The adsorption stability of DMEA film was higher under cathodic polarization potential, showing a higher corrosion inhibition ability. The corrosion inhibition mechanism of DEA and DMEA under cathodic polarization potential was proposed.

The MCI has a broad application prospect in the repair of damaged reinforced concrete due to its unique migratory characteristics. The interaction between MCIs, rebar and concrete with different compositions has been studied, but the passivation behavior of the steel interface in the presence of both the migrating electric field and corrosion inhibitors has been neglected. And it was investigated in this paper.

The purpose of this paper is to prepare a multifunctional nanocomposite that is slow-release and resistant to seawater corrosion and biofouling corrosion and to explore the synergistic effect between the two corrosion inhibitors.

The morphology, structure and release properties of CAP@HNTs, BTA@HNTs and CAP/BTA@HNTs were investigated by scanning electron microscopy, transmission electron microscopy, Fourier transform infrared spectroscopy, specific surface area analysis and UV spectrophotometry. The corrosion resistance and antimicrobial properties were investigated by electrochemical measurements and bioinhibition rate tests, and the synergistic effect between the two corrosion inhibitors was explored by X-ray photoelectron spectroscopy.

The CAP/BTA@HNTs are responsive to acidic environments and have significantly improved antibacterial and corrosion resistance compared with CAP@HNTs and BTA@HNTs. CAP and BTA have a positive synergistic effect on anticorrosion and antifouling.

Two types of inhibitors, anticorrosion and antifouling, were loaded into the same nanocontainer to prepare a slow-releasable and multifunctional nanocomposite with higher resistance to seawater corrosion and biocorrosion and to explore the synergistic effect of CAP and BTA on corrosion resistance.