1 – 10 of 30Zonglin Lei, Zunge Li and Yangyi Xiao
This study aims to investigate the surface modification on 20CrMnTi gear steel individually treated by diamond-like carbon films and nitride coatings.
Abstract
Purpose
This study aims to investigate the surface modification on 20CrMnTi gear steel individually treated by diamond-like carbon films and nitride coatings.
Design/methodology/approach
For this purpose, the mechanical properties of a-C:H, ta-C and AlCrSiN coatings are characterized by nano-indentation and scratch tests. The friction and wear behaviors of these three coatings are evaluated by ball-on-disc tribological experiments under dry contact conditions.
Findings
The results show that the a-C:H coating has the highest coating-substrate adhesion strength (495 mN) and the smoothest surface (Ra is about 0.045 µm) compared with the other two coatings. The AlCrSiN coating shows the highest mean coefficient of friction (COF), whereas the ta-C coating exhibits the lowest one (steady at about 0.16). The carbon-based coatings possess excellent self-lubricating properties compared with nitride ceramic ones, which effectively reduce the COF by about 64%. The major failure mode of carbon-based coatings in dry contact is slight abrasive wear. The damage of AlCrSiN coating is mainly adhesive wear and abrasive wear.
Originality/value
It is suggested that the carbon-based film can effectively improve the friction-reducing and wear resistance performance of the gear steel surface, which has a promising application prospect in the mechanical transmission field.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-05-2023-0129/
Details
Keywords
Kexin Ma, Jianxin Deng, Yichen Bao, Zhihui Zhang and Junyan Wang
Liquid-assisted laser surface texturing technology was used to create composite microtextures on triangular guide rail surfaces to enhance their tribological properties.
Abstract
Purpose
Liquid-assisted laser surface texturing technology was used to create composite microtextures on triangular guide rail surfaces to enhance their tribological properties.
Design/methodology/approach
Numerical simulations were used to investigate the impact of various microtextures on fluid dynamic lubrication. Reciprocating friction and wear tests, followed by mechanistic analysis, examined the combined tribological effects of microtextured surfaces and lubricants.
Findings
The numerical simulation outcomes reveal a significant augmentation in the influence of fluid dynamic pressure due to composite microtextures, consequently amplifying the load-bearing capacity of the oil film. The average friction coefficient of composite microtextured samples was approximately 0.136 in reciprocating pin-on-disk friction tests, representing approximately 17% decrease compared to polished samples. Triangular guide rails with composite microtextures demonstrated the lowest average coefficient under conditions of high-speed and heavy-loading in the reciprocating friction and wear tests. Additionally, the presence of composite microtextures was found to promote the formation of adsorbed and friction films during friction, potentially contributing to the enhancement of tribological properties.
Originality/value
Triangular guide rails face high friction and wear, limiting their stability in demanding applications like machine tool guideways. This paper proposes a novel approach for steel triangular guide rails, involving composite microtexturing, numerical fluid simulations, liquid-assisted laser surface texturing and friction-wear testing. By implementing composite microtextures, the method aims to reduce friction coefficients and extend guideway service life, thereby saving energy and reducing maintenance costs. Enhancing the antifriction and antiwear properties of machine tool guideways is crucial for improving performance and longevity.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-05-2024-0183/
Details
Keywords
Ronnarit Khuengpukheiw, Anurat Wisitsoraat and Charnnarong Saikaew
This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr3C2–Ni coatings on…
Abstract
Purpose
This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr3C2–Ni coatings on AISI 1095 steel with spraying times of 10 and 15 s.
Design/methodology/approach
In this study, the pin-on-disc testing technique was used to evaluate the wear characteristics at a speed of 0.24 m/s, load of 40 N and test time of 60 min under dry conditions at room temperature. The wear characteristics were examined and analyzed by scanning electron microscopy and energy dispersive X-ray spectroscopy. The surface roughness of a coated surface was measured, and microhardness measurements were performed on the cross-sectioned and polished surfaces of the coating.
Findings
Spraying time and powder material affected the hardness of HVOF coatings due to differences in the porosity of the coated layers. The average hardness of the WC–Cr3C2–Ni coating with a spaying time of 15 s was approximately 14% higher than that of the WC–Cr3C2–Ni coating with a spraying time of 10 s. Under an applied load of 40 N, the WC–Co coating with a spraying time of 15 s had the lowest variation in the friction coefficient compared with the other coatings. The WC–Co coating with a spraying time of 10 s had the lowest average and variation in volume loss compared to the other coatings. The WC–Cr3C2–Ni coating with a spraying time of 10 s exhibited the highest average volume loss. The wear features changed slightly with the spraying time owing to variations in the hardness and friction coefficient.
Originality/value
This study investigated tribological performance of WC–Co; WC-Cr3C2-Ni coatings with spraying times of 10 and 15 s using pin-on-disc tribometer by rotating the relatively soft pin (C45 steel) against hard coated substrate (disc).
Details
Keywords
Kiran G. Sirsath and Bhanudas D. Bachchhav
Low performance life and increased machine downtime due to wear of resistance welding copper electrode is of major concern in fin–tube resistance welding in waste heat recovery…
Abstract
Purpose
Low performance life and increased machine downtime due to wear of resistance welding copper electrode is of major concern in fin–tube resistance welding in waste heat recovery boilers. The purpose of this study is to investigate an alternative material with good wear resistance to replace the currently utilized C11000 electrolytic tough pitch (ETP) copper electrode.
Design/methodology/approach
In this study, a Cu-Cr-Zr ternary alloy was developed for fin-to-tube welding electrode by melting commercial grade electrolytic copper (99.9% purity) plates, chips of chromium, powder of zirconium at 1100°–1300°C, followed by hot forging and precipitation hardening at 450°–550°C to attain appropriate grain flow. Microstructures of Cu-Cr-Zr alloys were analysed using scanning electron microscopy coupled with energy-dispersive backscatter electron spectrometry.
Findings
Wear performance of Cu-Cr-Zr and C11000 ETP Cu was evaluated using pin-on-disc set-up with Taguchi’s L8 orthogonal array. Ranking of the parameters was done, and it was observed that the material and temperature play a very significant role in controlling the wear of an electrode.
Practical implications
Rate of fin–tube resistance welding was increased by 26% with Cu-Cr-Zr alloy. Further investigation on effect of plasma on the metallurgical characteristics of Cu-Cr-Zr is recommended.
Originality/value
Tribo-mechanical performance of newly developed Cu-Cr-Zr ternary alloy was compared with C11000 ETP copper.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-04-2023-0092/
Details
Keywords
Ravikantha Prabhu, Sharun Mendonca, Pavana Kumara Bellairu, Rudolf Charles DSouza and Thirumaleshwara Bhat
This paper aims to report the effect of titanium oxide (TiO2) particles on the physical, mechanical, tribological and water resistance properties of 5% NaOH-treated bamboo…
Abstract
Purpose
This paper aims to report the effect of titanium oxide (TiO2) particles on the physical, mechanical, tribological and water resistance properties of 5% NaOH-treated bamboo fiber–reinforced composites.
Design/methodology/approach
In this research, the epoxy/bamboo/TiO2 hybrid composite filled with 0–8 Wt.% TiO2 particles has been fabricated using simple hand layup techniques, and testing of the developed composite was done in accordance with the American Society for Testing and Materials (ASTM) standard.
Findings
The results of this study indicate that the addition of TiO2 particles improved the mechanical properties of the developed epoxy/bamboo composites. Tensile properties were found to be maximum for 6 Wt.%, and impact strength was found to be maximum for 8 Wt.% TiO2 particles-filled composite. The highest flexural properties were found at a lower TiO2 fraction of 2 Wt.%. Adding TiO2 filler helped to reduce the water absorption rate. The studies related to the wear and friction behavior of the composite under dry and abrasive wear conditions reveal that TiO2 filler was beneficial in improving the wear performance of the composite.
Originality/value
This research paper attempts to include both TiO2 filler and bamboo fibers to develop a novel composite material. TiO2 micro and nanoparticles are promising filler materials; it helps to enhance the mechanical and tribological properties of the epoxy composites and in literature, there is not much work reported, where TiO2 is used as a filler material with bamboo fiber–reinforced epoxy composites.
Details
Keywords
Ravikantha Prabhu, Sharun Mendonca, Pavana Kumara Bellairu, Rudolf Charles D’Souza and Thirumaleshwara Bhat
This paper aims to report the effect of titanium oxide (TiO2) particles on the specific wear rate (SWR) of alkaline treated bamboo and flax fiber-reinforced composites (FRCs…
Abstract
Purpose
This paper aims to report the effect of titanium oxide (TiO2) particles on the specific wear rate (SWR) of alkaline treated bamboo and flax fiber-reinforced composites (FRCs) under dry sliding condition by using a robust statistical method.
Design/methodology/approach
In this research, the epoxy/bamboo and epoxy/flax composites filled with 0–8 Wt.% TiO2 particles have been fabricated using simple hand layup techniques, and wear testing of the composite was done in accordance with the ASTM G99-05 standard. The Taguchi design of experiments (DOE) was used to conduct a statistical analysis of experimental wear results. An analysis of variance (ANOVA) was conducted to identify significant control factors affecting SWR under dry sliding conditions. Taguchi prediction model is also developed to verify the correlation between the test parameters and performance output.
Findings
The research study reveals that TiO2 filler particles in the epoxy/bamboo and epoxy/flax composite will improve the tribological properties of the developed composites. Statistical analysis of SWR concludes that normal load is the most influencing factor, followed by sliding distance, Wt.% TiO2 filler and sliding velocity. ANOVA concludes that normal load has the maximum effect of 31.92% and 35.77% and Wt.% of TiO2 filler has the effect of 17.33% and 16.98%, respectively, on the SWR of bamboo and flax FRCs. A fairly good agreement between the Taguchi predictive model and experimental results is obtained.
Originality/value
This research paper attempts to include both TiO2 filler and bamboo/flax fibers to develop a novel hybrid composite material. TiO2 micro and nanoparticles are promising filler materials, it helps to enhance the mechanical and tribological properties of the epoxy composites. Taguchi DOE and ANOVA used for statistical analysis serve as guidelines for academicians and practitioners on how to best optimize the control variable with particular reference to natural FRCs.
Details
Keywords
Zhi Li, YiYuan Du, Zhiming Xu, Xuqian Qiao and Hong Zhang
The purpose of this study is to investigate the influence of surface texture on the subsurface characteristics of contact interfaces under elastohydrodynamic lubrication…
Abstract
Purpose
The purpose of this study is to investigate the influence of surface texture on the subsurface characteristics of contact interfaces under elastohydrodynamic lubrication condition. As a typical contact form of gears and bearings, the optimization of friction characteristics at the elastohydrodynamic lubrication (EHL) interface has attracted the attention of scholars. Laser surface texturing is a feasible optimization solution, but there have been concerns about whether the surface texture of high-pair parts will affect their fatigue life.
Design/methodology/approach
To examine the impact of texture preparation on the subsurface characteristics of high-pair interfaces under EHL conditions, a point contact EHL model is developed that takes into account the effect of textured surface topography. The pressure and thickness of the oil film are calculated as input parameters under different loads and entrainment velocities. The finite element method is used to simulate the impact of textures with varying diameters, densities and depths on the subsurface characteristics of the elastohydrodynamic interface. According to ISO 25178, analyze the relationship between 3D topography parameters and subsurface characteristics and study the trend of friction characteristics and subsurface characteristics based on the results of the ball on disc friction tests.
Findings
The outcomes suggest that under different rotational velocity and load conditions, the textured surfaces exhibit improved friction reduction effects; however, the creation of textures can result in significant subsurface plastic deformation and local peeling. The existence of texture makes the larger stress zone in the subsurface layer closer to the surface, leading to fatigue failure near the surface. Reasonable design parameters can help enhance the attributes of the subsurface. A smaller Sa and a Str greater than 0.5 can achieve ideal subsurface properties on the textured surface.
Originality/value
This paper investigates the influence of surface texture on the friction and subsurface characteristics of EHL interfaces and analyzes the impact of surface texture on interface contact performance while achieving lubrication improvement functional characteristics. The results provide theoretical support for the optimization design and functional regulation of surface texture in EHL interfaces.
Peer review
The peer review history for this article is https://publons.com/publon/10.1108/ILT-10-2023-0324/
Details
Keywords
Mandeep Singh, Khushdeep Goyal and Deepak Bhandari
The purpose of this paper is to evaluate the effect of titanium oxide (TiO2) and yttrium oxide (Y2O3) nanoparticles-reinforced pure aluminium (Al) on the mechanical properties of…
Abstract
Purpose
The purpose of this paper is to evaluate the effect of titanium oxide (TiO2) and yttrium oxide (Y2O3) nanoparticles-reinforced pure aluminium (Al) on the mechanical properties of hybrid aluminium matrix nanocomposites (HAMNCs).
Design/methodology/approach
The HAMNCs were fabricated via a vacuum die-assisted stir casting route by a two-step feeding method. The varying weight percentages of TiO2 and Y2O3 nanoparticles were added as 2.5, 5, 7.5 and 10 Wt.%.
Findings
Scanning electron microscope images showed the homogenous dispersion of nanoparticles in Al matrix. The tensile strength by 28.97%, yield strength by 50.60%, compression strength by 104.6% and micro-hardness by 50.90% were improved in HAMNC1 when compared to the base matrix. The highest values impact strength of 36.3 J was observed for HAMNC1. The elongation % was decreased by increasing the weight percentage of the nanoparticles. HAMNC1 improved the wear resistance by 23.68%, while increasing the coefficient of friction by 14.18%. Field emission scanning electron microscope analysis of the fractured surfaces of tensile samples revealed microcracks and the debonding of nanoparticles.
Originality/value
The combined effect of TiO2 and Y2O3 nanoparticles with pure Al on mechanical properties has been studied. The composites were fabricated with two-step feeding vacuum-assisted stir casting.
Details
Keywords
Dongya Zhang, Yanping Gao, Pengju Wu, Yanchao Zhang and Liping Wang
This paper aims to enhance lubrication performance of the pitcher plant–like textured surface with various parameters.
Abstract
Purpose
This paper aims to enhance lubrication performance of the pitcher plant–like textured surface with various parameters.
Design/methodology/approach
A pitcher plant–like structure surface is fabricated on the copper alloy, and the lubrication performance of the pitcher plant–like structure with various parameters is evaluated. In addition, the pressure distribution and oil film load capacity of the pitcher plant–like surface are simulated based on Navier–Stokes equations.
Findings
When the direction of motion aligns with the pitcher plant–like structure, the friction coefficient remains lower than that of the nontextured surface, and it exhibits a decreasing trend with the increasing of the texture width and spacing distance; the lowest friction coefficient (0.04) is achieved with B = 0.3 mm, L = 1.0 mm and θ = 45°, marking a 75% reduction compared to the nontextured surface. Simulation results demonstrate that with the increase in texture width and spacing distance, the oil film load-bearing capacity demonstrates an increasing trend.
Originality/value
Bionic pitcher plants are prepared on the copper alloy to improve the lubrication performance and wear resistance.
Peer review
The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-04-2024-0119/
Details
Keywords
Ferhat Ceritbinmez, Yusuf Kanca, Ahmet Tuna and Erdoğan Kanca
FeNi36 (Invar-36) alloy is widely used in the fabrication of molding tools in aerospace industries but there remains a need to improve its wear and friction performance due to its…
Abstract
Purpose
FeNi36 (Invar-36) alloy is widely used in the fabrication of molding tools in aerospace industries but there remains a need to improve its wear and friction performance due to its relatively low hardness. The formation of a heat affected zone (HAZ) on the surface of Invar-36 cut by wire electric discharge machining (WEDM) is promising to enhance its tribological properties. This study aims to investigate the tribological performance of WEDM-treated Invar-36 via a ball-on-disk tribometer in dry-sliding conditions.
Design/methodology/approach
The untreated and WEDM-treated Invar-36 surfaces were reciprocated against an alumina ball at a sliding velocity of 40 mm/s, a stroke length of 10 mm and a sliding duration of 125 min under loads of 5, 10 and 20 N. The worn surfaces were characterized using a 2D profilometry and a scanning electron microscope equipped with energy-dispersive spectroscopy.
Findings
The results showed that the WEDM-treated surface had a superior friction coefficient and wear resistance in comparison to the untreated surface, due to the grown HAZ. There was found to be a 9.3%–11.4% decrease in the friction coefficient and a 47%–57% reduction in the wear volume after the WEDM treatment. Both the untreated and WEDM-treated Invar-36 surfaces found abrasion and plastic deformation as the dominant wear mechanisms.
Originality/value
Previous works have not focused on the tribological performance of the WEDM-treated Invar-36 extensively used for molding tools in aerospace industries. Our findings provide compelling evidence that the WEDM treatment improved the wear and friction performance of Invar-36 alloy because of the grown HAZ.
Details