The purpose of this paper is to investigate the effects of electric current stressing on damping properties of Sn5Sb solder.

Uniformly shaped Sn5Sb solders were prepared as samples. The length, width and thickness of the samples were 60.0, 5.0 and 0.5 mm, respectively. The damping properties of the samples were tested by dynamic mechanical analyzer with a cooling system to control the test temperature in the range of −100 to 100°C. Simultaneously, electric current was imposed to the tested samples using a direct current supply. After tests, the samples were characterized using scanning electron microscope, electron backscatter diffraction and transmission electron microscope, which was aimed to figure out the damping mechanism in terms of electric current stressing induced microstructure evolution.

It is confirmed experimentally that the increase in damping properties is due to Joule heating and athermal effects of current stressing, in which Joule heating should make a higher contribution. G–L theory can be used to explain the damping properties of strain amplitude under current stressing by quantitative description of geometrically necessary dislocation density. While the critical strain amplitude and high temperature activation energy decrease with increasing electric current.

These results provide a new method for vibration reliability evaluation of high-temperature lead-free solders in serving electronics. Notably, this method should be also inspiring for the mechanical performance evaluation and reliability assessment of conductive materials and structures serving under electric current stressing.

This study aims to characterize the mechanical properties of sintered nano-silver under various sintering processes by nano-indentation tests.

Through microstructure observations and characterization, the influences of sintering process on the microstructure evolutions of sintered nano-silver were presented. And, the indentation load, indentation displacement curves of sintered silver under various sintering processes were measured by using nano-indentation test. Based on the nano-indentation test, a reverse analysis of the finite element calculation was used to determine the yielding stress and hardening exponent.

The porosity decreases with the increase of the sintering temperature, while the average particle size of sintered nano-silver increases with the increase of sintering temperature and sintering time. In addition, the porosity reduced from 34.88%, 30.52%, to 25.04% if the ramp rate was decreased from 25°C/min, 15°C/min, to 5°C/min, respectively. The particle size appears more frequently within 1 µm and 2 µm under the lower ramp rate. With reverse analysis, the strain hardening exponent gradually heightened with the increase of temperature, while the yielding stress value decreased significantly with the increase of temperature. When the sintering time increased, the strain hardening exponent increased slightly.

The mechanical properties of sintered nano-silver under different sintering processes are clearly understood.

This paper could provide a novel perspective on understanding the sintering process effects on the mechanical properties of sintered nano-silver.