This study aims to research the influence mechanism of microtextured geometric parameters of dry gas seal end face on the tribological behavior under dry frictional conditions.

The microtexture was processed using laser processing, while the diamond-like carbon (DLC) film was applied through magnetron sputtering; the experimental platform of friction vibration was established, the frictional and vibrational properties of different geometric parameters were tested; the data signals of vibrational acceleration and frictional torque were collected and processed using data acquisition instrument. The entropy characteristic parameters of 3D vibrational acceleration were extracted based on wavelet packet decomposition method. The end-face topography was measured with ST400 three-dimensional noncontact surface topography instrument.

The geometry of pits plays a key role in influencing friction performance; the permutation entropy and fuzzy entropy of the vibration acceleration signal changed with variations in microtextured parameters. A textured surface with appropriately size parameters can trap debris, enhance the dynamic pressure effect, reduce impact between the friction interfaces and improve the frictional vibrational performance. In this research, microtextured surface with Φ150 µm-10% and Φ200 µm-5% can effectively reduce friction and vibration between the end faces of a dry gas seal.

DLC film improves the hardness of seal ring end face, and microtexture improves the dynamic effect; the tribological behavior monitoring can be realized by analyzing the characteristics of vibration acceleration sensitive parameter with friction state. The findings will provide a basis for further research in the field of tribology and the microtexture optimization of dry gas seal ring end face.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-12-2023-0389/

With the rapid advancement in the automotive industry, the friction coefficient (FC), wear rate (WR) and weight loss (WL) have emerged as crucial parameters to measure the performance of automotive braking systems, so the FC, WR and WL of friction material are predicted and analyzed in this work, with an aim of achieving accurate prediction of friction material properties.

Genetic algorithm support vector machine (GA-SVM) model is obtained by applying GA to optimize the SVM in this work, thus establishing a prediction model for friction material properties and achieving the predictive and comparative analysis of friction material properties. The process parameters are analyzed by using response surface methodology (RSM) and GA-RSM to determine them for optimal friction performance.

The results indicate that the GA-SVM prediction model has the smallest error for FC, WR and WL, showing that it owns excellent prediction accuracy. The predicted values obtained by response surface analysis are closed to those of GA-SVM model, providing further evidence of the validity and the rationality of the established prediction model.

The relevant results can serve as a valuable theoretical foundation for the preparation of friction material in engineering practice.

To authenticate the existence and principles of the adhesion recovery phenomenon under water pollution conditions, an innovative circumferential rail–wheel adhesion test rig was used. The study conducted extensive tests on the adhesion characteristics under large sliding conditions.

Experiments were conducted to investigate the influence of speed, axle load and slip on adhesion recovery. Based on the experimental results, the adhesion recovery transition function was re-fitted.

The study reveals that the adhesion recovery phenomenon truly exists under water conditions. The adhesion coefficient shows an increasing trend with the growth of the slip ratio. Moreover, at the current speed and axle load levels, the adhesion recovery is directly proportional to the square of the slip ratio and inversely proportional to the axle load.

The phenomenon of adhesion recovery and the formulated equations in this study can serve as an experimental and theoretical foundation for the design of braking and anti-skid control algorithms for trains.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-11-2023-0379/

This paper aims to solve the problems molybdenum disulfide (MoS₂) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.

MoS₂/C₆₀ nanocomposites were prepared by synthesizing molybdenum disulfide (MoS₂) nanosheets on the surface of hydrochloric acid-activated fullerenes (C₆₀) by in situ hydrothermal method. The composition, structure and morphology of MoS₂/C₆₀ nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.

MoS₂/C₆₀ nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS₂/C₆₀ was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.

MoS₂/C₆₀ composite nanoparticles were prepared by in-situ formation of MoS₂ nanosheets on the surface of C₆₀ activated by HCl through hydrothermal method and were used as potential lubricating oil additives.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-10-2023-0321/

This study aims to enhance the lubrication performance of thrust bearings. The influence of columnar convex–concave compound microtexture on bearing performance is investigated

Based on the compound microtexture model of thrust bearings, considering surface roughness and turbulent effect, the variation of lubrication characteristics with the change in the compound microtexture parameters is studied.

The results indicate that, compared with circular microtexture, the maximum pressure of compound microtexture of thrust bearings increases by 7.42%. Optimal bearing performance is achieved when the internal microtexture depth is 0.02 mm. Turbulent flow states and surface roughness lead to a reduction in the optimal depth. The maximum pressure and load-carrying capacity of the bearing decrease as the initial angle increases, whereas the friction coefficient increases with the increase in the initial angle. The lubrication performance is best for bearings with a circumferential parallel arrangement of microtexture.

The novel composite microtexture with columnar convex-concave is proposed, and the computational model of thrust bearings is set. The influence of surface roughness and turbulent flow on the bearing performance should be considered for better conforming with engineering practice. The effect of microtexture depth, arrangement method and distribution position on the lubrication performance of the compound microtexture thrust bearing is investigated, which is of great significance for improving tribology, thrust bearings and surface microtexture theory.

This paper aims to compare the wear behavior, surface roughness, friction coefficient and volume loss of high-velocity oxy-fuel (HVOF) sprayed WC–Co and WC–Cr₃C₂–Ni coatings on AISI 1095 steel with spraying times of 10 and 15 s.

In this study, the pin-on-disc testing technique was used to evaluate the wear characteristics at a speed of 0.24 m/s, load of 40 N and test time of 60 min under dry conditions at room temperature. The wear characteristics were examined and analyzed by scanning electron microscopy and energy dispersive X-ray spectroscopy. The surface roughness of a coated surface was measured, and microhardness measurements were performed on the cross-sectioned and polished surfaces of the coating.

Spraying time and powder material affected the hardness of HVOF coatings due to differences in the porosity of the coated layers. The average hardness of the WC–Cr₃C₂–Ni coating with a spaying time of 15 s was approximately 14% higher than that of the WC–Cr₃C₂–Ni coating with a spraying time of 10 s. Under an applied load of 40 N, the WC–Co coating with a spraying time of 15 s had the lowest variation in the friction coefficient compared with the other coatings. The WC–Co coating with a spraying time of 10 s had the lowest average and variation in volume loss compared to the other coatings. The WC–Cr₃C₂–Ni coating with a spraying time of 10 s exhibited the highest average volume loss. The wear features changed slightly with the spraying time owing to variations in the hardness and friction coefficient.

This study investigated tribological performance of WC–Co; WC-Cr₃C₂-Ni coatings with spraying times of 10 and 15 s using pin-on-disc tribometer by rotating the relatively soft pin (C45 steel) against hard coated substrate (disc).

The purpose of this study is to design and process the optimal V-shaped microstructure for 7075 aluminum alloy and reveal its wear resistance mechanism and performance.

The hydrodynamic pressure lubrication models of the nontextured, V-shaped, circular and square microtextures are established. The corresponding oil film pressure distributions are explored. The friction and wear experiments are conducted on a rotating device. The effects of the microstructure shapes and sizes on the wear mechanisms are investigated via the friction coefficients and surface morphologies.

In comparison, the V-shaped microtexture has the largest oil film carrying capacity and the lowest friction coefficient. The wear mechanism of the V-shaped microtexture is dominated by abrasive and adhesive wear. The V-shaped microtexture has excellent wear resistance under a side length of 300 µm, an interval of 300 µm and a depth of 20 µm.

This study is conductive to the design of wear-resistant surfaces for friction components.

The long-span continuous rigid-frame bridges are commonly constructed by the section-by-section symmetrical balance suspension casting method. The deflection of these bridges is increasing over time. Wet joints are a typical construction feature of continuous rigid-frame bridges and will affect their integrity. To investigate the sensitivity of shear surface quality on the mechanical properties of long-span prestressed continuous rigid-frame bridges, a large serviced bridge is selected for analysis.

Its shear surface is examined and classified using the damage measuring method, and four levels are determined statistically based on the core sample integrity, cracking length and cracking depth. Based on the shear-friction theory of the shear surface, a 3D solid element-based finite element model of the selected bridge is established, taking into account factors such as damage location, damage number and damage of the shear surface. The simulated results on the stress distribution of the local segment, the shear surface opening and the beam deflection are extracted and analyzed.

The findings indicate that the main factors affecting the ultimate shear stress and shear strength of the shear surface are size, shear reinforcements, normal stress and friction performance of the shear surface. The connection strength of a single or a few shear surfaces decreases but with little effect on the local stress. Cracking and opening mainly occur at the 1/4 span. Compared with the rigid “Tie” connection, the mid-span deflection of the main span increases by 25.03% and the relative deflection of the section near the shear surface increases by 99.89%. However, when there are penetrating cracks and openings in the shear surface at the 1/2 span, compared with the 1/4 span position, the mid-span deflection of the main span and the relative deflection of the cross-section increase by 4.50%. The deflection of the main span increases with the failure of the shear surface.

These conclusions can guide the analysis of deflection development in long-span prestressed continuous rigid-frame bridges.

The purpose of this study is to solve the issues of time-consuming and complicated computation of traditional measures, as well as the underutilization of two-dimensional (2D) phase-trajectory projection matrix, so a new set of features were proposed based on the projection of attractors trajectory to characterize the friction-induced attractors and to reveal the tribological behavior during the running-in process.

The frictional running-in experiments were conducted by sliding a ball against a static disk, and the friction coefficient was collected to reconstruct the friction-induced attractors. The projection of the attractors in 2D subspace was then mapped and the distribution of phase points was adapted to conduct the feature extraction.

The evolution of the proposed moment measures could be described as “initial rapid decrease/increase- midterm gradual decrease/increase- finally stable,” which could effectively reveal the convergence degree of the friction-induced attractors. Moreover, the measures could also describe the relative position of the attractors in phase–space domain, which reveal the amplitude evolution of signals to some extent.

The proposed measures could reveal the evolution of tribological behaviors during the running-in process and meet the more precise real-time running-in status identification.

This paper aims to study the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ to improve the tribological properties of M50 bearing steel with microporous channels.

M50 matrix self-lubricating composites (MMSC) were designed and prepared by filling Sn–Ag–Cu and MXene–Ti₃C₂ in the microporous channels of M50 bearing steel. The tribology performance testing of as-prepared samples was executed with a multifunction tribometer. The optimum hole size and lubricant content, as well as self-lubricating mechanism of MMSC, were studied.

The tribological properties of MMSC are strongly dependent on the synergistic lubrication effect of MXene–Ti₃C₂ and Sn–Ag–Cu. When the hole size of microchannel is 1 mm and the content of MXene–Ti₃C₂ in mixed lubricant is 4 wt.%, MMSC shows the lowest friction coefficient and wear rate. The Sn–Ag–Cu and MXene–Ti₃C₂ are extruded from the microporous channels and spread to the friction interface, and a relatively complete lubricating film is formed at the friction interface. Meanwhile, the synergistic lubrication of Sn–Ag–Cu and MXene–Ti₃C₂ can improve the stability of the lubricating film, thus the excellent tribological property of MMSC is obtained.

The results help in deep understanding of the synergistic lubrication effects of Sn–Ag–Cu and MXene–Ti₃C₂ on the tribological properties of M50 bearing steel. This work also provides a useful reference for the tribological design of mechanical components by combining surface texture with solid lubrication.