1 – 10 of over 1000Thomas Pinger, Mirabela Firan and Martin Mensinger
Based on the known positive effects of conventional hot-dip galvanizing under fire exposure and indicative results on zinc–aluminum coatings from smallscale tests, a series of…
Abstract
Purpose
Based on the known positive effects of conventional hot-dip galvanizing under fire exposure and indicative results on zinc–aluminum coatings from smallscale tests, a series of tests were conducted on zinc-5% aluminum galvanized test specimens under fire loads to verify the previous positive findings under largescale boundary conditions.
Design/methodology/approach
The emissivity of zinc-5% aluminum galvanized surfaces applied to steel specimens was determined experimentally under real fire loads and laboratory thermal loads in accordance with the normative specifications of the standard fire curve. Both large and smallscale specimens were used in this study. The steel grade and surface conditions of the specimens were varied for both test scenarios.
Findings
Largescale tests on specimens with typical steel construction dimensions under fire loads showed that the surface emissivity of zinc-5% aluminum galvanized steel was significantly lower than that of the conventionally galvanized steel. Only minor influences from the weathering of the specimens and steel chemistry were observed. These results agree well with those obtained from smallscale tests. The design values of zinc-5% aluminum melt (Zn5Al) required for the structural fire design were proposed based on the obtained results.
Originality/value
The novel tests presented in this study are the first ones to study the behavior of zinc-5% aluminum galvanized largescale steel construction components under the influence of real fire exposure and their positive effect on the emissivity of steel components galvanized by this method. The results provide valuable insights and information on the behavior in the case of fire and the associated savings potential for steel construction.
Details
Keywords
Aminuddin Suhaimi, Izni Syahrizal Ibrahim and Mariyana Aida Ab Kadir
This review paper seeks to enhance knowledge of how pre-loading affects reinforced concrete (RC) beams under fire. It investigates key factors like deflection and load capacity to…
Abstract
Purpose
This review paper seeks to enhance knowledge of how pre-loading affects reinforced concrete (RC) beams under fire. It investigates key factors like deflection and load capacity to understand pre-loading's role in replicating RC beams' actual responses to fire, aiming to improve fire testing protocols and structural fire engineering design.
Design/methodology/approach
This review systematically aggregates data from existing literature on the fire response of RC beams, comparing scenarios with (WP) and without pre-loading (WOP). Through statistical tools like the two-tailed t-test and Mann–Whitney U-test, it assesses deflection extremes. The study further examines structural responses, including flexural and shear behavior, ultimate load capacity, post-yield behavior, stiffness degradation and failure modes. The approach concludes with a statistical forecast of ideal pre-load levels to elevate experimental precision and enhance fire safety standards.
Findings
The review concludes that pre-loading profoundly affects the fire response of RC beams, suggesting a 35%–65% structural capacity range for realistic simulations. The review also recommended the initial crack load as an alternative metric for determining the pre-loading impact. Crucially, it highlights that pre-loading not only influences the fire response but also significantly alters the overall structural behavior of the RC beams.
Originality/value
The review advances structural fire engineering with an in-depth analysis of pre-loading's impact on RC beams during fire exposure, establishing a validated pre-load range through thorough statistical analysis and examination of previous research. It refines experimental methodologies and structural design accuracy, ultimately bolstering fire safety protocols.
Details
Keywords
Takumi Yamaguchi and Fuminobu Ozaki
The main purpose of this study was to evaluate the tensile strengths of JIS G3549 super high-strength steel strand wire ropes (1,570 MPa-class high-carbon steels) and wire rope…
Abstract
Purpose
The main purpose of this study was to evaluate the tensile strengths of JIS G3549 super high-strength steel strand wire ropes (1,570 MPa-class high-carbon steels) and wire rope open swaged socket connections at fire and post fire.
Design/methodology/approach
Steady-state tests from ambient temperature (20 °C) to 800 °C, transient-state tests under the allowable design tensile force and tensile tests in an ambient temperature environment after heating (heating temperatures of 200–800 °C) were conducted.
Findings
The tensile strengths of the wire rope and end-connection specimens at both fire and post fire were obtained. The steel wire rope specimens possessed larger reduction factors than general hot-rolled mild steels (JIS SS400) and high-strength steel bolts (JIS F10T). The end-connection specimens with sufficient socket lengths exhibited ductile fracture of the wire rope part at both fire and post fire; however, those with short socket lengths experienced a pull-out fracture at the socket.
Originality/value
The fundamental and important tensile test results of the super high-strength steel strand wire ropes (1,570 MPa-class high-carbon steels) and wire rope open swaged socket connections were accumulated at fire and post fire, and the fracture modes were clarified. The obtained test results contribute to fire resistance performance-based design of cable steel structures at fire and fire-damage investigations to consider their reusability post fire.
Details
Keywords
Milad Shabanian and Nicole Leo Braxtan
Thermomechanical behavior of intermediate-size beam-to-wall assemblies including Glulam-beams connected to cross-laminated timber (CLT) walls with T-shape steel doweled…
Abstract
Purpose
Thermomechanical behavior of intermediate-size beam-to-wall assemblies including Glulam-beams connected to cross-laminated timber (CLT) walls with T-shape steel doweled connections was investigated at ambient temperature (AT) and after and during non-standard fire exposure.
Design/methodology/approach
Three AT tests were conducted to evaluate the load-carrying capacity and failure modes of the assembly at room temperature. Two post-fire performance (PFP) tests were performed to study the impact of 30-min (PFP30) and 60-min (PFP60) partial exposure to a non-standard fire on the residual strength of the assemblies. The assemblies were exposed to fire in a custom-designed frame, then cooled and loaded to failure. A fire performance (FP) test was conducted to study the fire resistance (FR) during non-standard fire exposure by simultaneously applying fire and a mechanical load equal to 65% of the AT load carrying capacity.
Findings
At AT, embedment failure of the dowels followed by splitting failure at the Glulam-beam and tensile failure of the epoxy between the layers of CLT-walls were the dominant failure modes. In both PFP tests, the plastic bending of the dowels was the only observed failure mode. The residual strength of the assembly was reduced 14% after 30 min and 37% after 60 min of fire exposure. During the FP test, embedment failure of timber in contact with the dowels was the only major failure mode, with the maximum rate of displacement at 51 min into the fire exposure.
Originality/value
This is the first time that the thermomechanical performance of such an assembly with a full-contact connection is presented.
Details
Keywords
Milad Shabanian and Nicole Leo Braxtan
3-ply cross-laminated timber (CLT) is used to investigate the thermo-mechanical performance of intermediate-size assemblies comprised of T-shaped welded slotted-in steel doweled…
Abstract
Purpose
3-ply cross-laminated timber (CLT) is used to investigate the thermo-mechanical performance of intermediate-size assemblies comprised of T-shaped welded slotted-in steel doweled connections and CLT beams at ambient temperature (AT), after and during non-standard fire exposure.
Design/methodology/approach
The first set of experiments was performed as a benchmark to find the load-carrying capacity of the assembly and investigate the failure modes at AT. The post-fire performance (PFP) test was performed to investigate the residual strength of the assembly after 30-min exposure to a non-standard fire. The fire-performance (FP) test was conducted to investigate the thermo-mechanical behavior of the loaded assembly during non-standard fire exposure. In this case, the assembly was loaded to 67% of AT load-carrying capacity and partially exposed to a non-standard fire for 75 min.
Findings
Embedment failure and plastic deformation of the dowels in the beam were the dominant failure modes at AT. The load-carrying capacity of the assembly was reduced to 45% of the ambient capacity after 30 min of fire exposure. Plastic bending of the dowels was the principal failure mode, with row shear in the mid-layer of the CLT beam and tear-out failure of the header sides also observed. During the FP test, ductile embedment failure of the timber in contact with the dowels was the major failure mode at elevated temperature.
Originality/value
This paper presents for the first time the thermo-mechanical performance of CLT beam-to-girder connections at three different thermal conditions. For this purpose, the outside layers of the CLT beams were aligned horizontally.
Highlights
Load-carrying capacity and failure modes of CLT beam-to-girder assembly with T-shaped steel doweled connections at ambient temperature presented.
Residual strength and failure modes of the assembly after 30-min partially exposure to the non-standard fire provided throughout the post-fire performance test.
Fire resistance of the assembly partially exposed to the non-standard fire highlighted.
Load-carrying capacity and failure modes of CLT beam-to-girder assembly with T-shaped steel doweled connections at ambient temperature presented.
Residual strength and failure modes of the assembly after 30-min partially exposure to the non-standard fire provided throughout the post-fire performance test.
Fire resistance of the assembly partially exposed to the non-standard fire highlighted.
Details
Keywords
Ali Nadjai, Naveed Alam, Marion Charlier, Olivier Vassart, Xu Dai, Jean-Marc Franssen and Johan Sjostrom
In the frame of the European RFCS TRAFIR project, three large compartment fire tests involving steel structure were conducted by Ulster University, aiming at understanding in…
Abstract
Purpose
In the frame of the European RFCS TRAFIR project, three large compartment fire tests involving steel structure were conducted by Ulster University, aiming at understanding in which conditions a travelling fire develops, as well as how it behaves and impacts the surrounding structure.
Design/methodology/approach
During the experimental programme, the path and geometry of the travelling fire was studied and temperatures, heat fluxes and spread rates were measured. Influence of the travelling fire on the structural elements was also monitored during the travelling fire tests.
Findings
This paper provides details related to the influence of travelling fires on a central structural steel column.
Originality/value
The experimental data are presented in terms of the gas temperatures recorded in the test compartment near the column, as well as the temperatures recorded in the steel column at different levels. Because of the large data, only fire test one results are discussed in this paper.
Details
Keywords
Irindu Upasiri, Chaminda Konthesingha, Anura Nanayakkara and Keerthan Poologanathan
Elevated temperature material properties are essential in predicting structural member's behavior in high-temperature exposures such as fire. Even though experimental…
Abstract
Purpose
Elevated temperature material properties are essential in predicting structural member's behavior in high-temperature exposures such as fire. Even though experimental methodologies are available to determine these properties, advanced equipment with high costs is required to perform those tests. Therefore, performing those experiments frequently is not feasible, and the development of numerical techniques is beneficial. A numerical technique is proposed in this study to determine the temperature-dependent thermal properties of the material using the fire test results based on the Artificial Neural Network (ANN)-based Finite Element (FE) model.
Design/methodology/approach
An ANN-based FE model was developed in the Matlab program to determine the elevated temperature thermal diffusivity, thermal conductivity and the product of specific heat and density of a material. The temperature distribution obtained from fire tests is fed to the ANN-based FE model and material properties are predicted to match the temperature distribution.
Findings
Elevated temperature thermal properties of normal-weight concrete (NWC), gypsum plasterboard and lightweight concrete were predicted using the developed model, and good agreement was observed with the actual material properties measured experimentally. The developed method could be utilized to determine any materials' elevated temperature material properties numerically with the adequate temperature distribution data obtained during a fire or heat transfer test.
Originality/value
Temperature-dependent material properties are important in predicting the behavior of structural elements exposed to fire. This research study developed a numerical technique utilizing ANN theories to determine elevated temperature thermal diffusivity, thermal conductivity and product of specific heat and density. Experimental methods are available to evaluate the material properties at high temperatures. However, these testing equipment are expensive and sophisticated; therefore, these equipment are not popular in laboratories causing a lack of high-temperature material properties for novel materials. However conducting a fire test to evaluate fire performance of any novel material is the common practice in the industry. ANN-based FE model developed in this study could utilize those fire testing results of the structural member (temperature distribution of the member throughout the fire tests) to predict the material's thermal properties.
Details
Keywords
Jakub Šejna, Stanislav Šulc, Vít Šmilauer, Pavel Reiterman and František Wald
The aim of this paper is to determine the thermal conductivity of a protective layer of alkali-activated cement and the possibility of performing fire protection with fireclay…
Abstract
Purpose
The aim of this paper is to determine the thermal conductivity of a protective layer of alkali-activated cement and the possibility of performing fire protection with fireclay sand and Lightweight mortar. Unprotected steel structures have generally low fire resistance and require surface protection. The design of passive protection of a steel element must consider the service life of the structure and the possible need to replace the fire protection layer. Currently, conventional passive protection options include intumescent coatings, which are subject to frequent inspection and renewal, gypsum and cement-based fire coatings and gypsum and cement board fire protection.
Design/methodology/approach
Alkali-activated cements provide an alternative to traditional Portland clinker-based materials for specific areas. This paper presents the properties of hybrid cement, its manufacturability for conventional mortars and the development of passive fire protection. Fire experiments were conducted with mortar with alkali-activated and fireclay sand and lightweight mortar with alkali-activated cement and expanded perlite. Fire experiment FE modelling.
Findings
The temperatures of the protected steel and the formation of cracks in the protective layer were investigated. Based on the experiments, the thermal conductivities of the two protective layers were determined. Conclusions are presented on the applicability of alkaline-activated cement mortars and the possibilities of applicability for the protection of steel structures. The functionality of the passive fire layer was confirmed and the strengths of the mortar used were determined. The use of alkali-activated cements was shown to be a suitable option for sustainable passive fire protection of steel structures.
Originality/value
Eco-friendly fire protection based on hybrid alkali-activated cement of steel members.
Details
Keywords
Ilias Thanasoulas, Dan Lauridsen, Bjarne Paulsen Husted and Luisa Giuliani
The purpose of this study is to contribute toward providing the main aspects of numerical modeling the fire behavior of steel structures with finite elements (FEs). The…
Abstract
Purpose
The purpose of this study is to contribute toward providing the main aspects of numerical modeling the fire behavior of steel structures with finite elements (FEs). The application of the method is presented for a characteristic case study comprising the series of large-scale fire door tests performed at the Danish Institute of Fire and Security Technology.
Design/methodology/approach
Following a general overview of current practices in structural fire engineering, the FE method is used to simulate the large-scale furnace tests on steel doors with thermal insulation exposed to standard fire.
Findings
The FE model is compared with the fire test results, achieving good agreement in terms of developed temperatures and deformations.
Originality/value
The numerical methodology and recommended practices for modeling the fire behavior of steel structures are presented, which can be used in support of performance-based fire design standards.
Details
Keywords
Steel-reinforced concrete-filled steel tubular (SRCFST) columns have been increasingly popular in engineering practice for the columns' excellent seismic and fire performance…
Abstract
Purpose
Steel-reinforced concrete-filled steel tubular (SRCFST) columns have been increasingly popular in engineering practice for the columns' excellent seismic and fire performance. Significant design progress guidance has been made through continuous numerical and experimental research in recent years. This paper tested and analysed the residual loading capacity of SRCFST columns under axial loading after experiencing non-uniform ISO-834 standard fire.
Design/methodology/approach
The experimental research covered the main parameter of heating conditions, 1-side and 2-side fire, through two specimens. Two specimens were heated and loaded simultaneously in the furnace for 240 min. After cooling, the columns were moved to the hydraulic loading system and loaded to failure to determine the columns' residual capacity.
Findings
The experimental results indicated that the non-uniform heating area plays an essential role in the overall performance of SRCFST columns, the increasing heating area of columns results in lower residual loading capacity and stiffness. The SRCFST columns still had a high loading capacity after heating and loading in the fire.
Originality/value
The comparison of experimental data against design results showed that the design method generated a 16% safety margin for S2H4 and a 39% safety margin for S1H4.
Details