Shaping ceramics through indirect selective laser sintering
Abstract
Purpose
The purpose of this paper is to compare different powder metallurgy (PM) processes to produce ceramic parts through additive manufacturing (AM). This creates the potential to rapidly shape ceramic parts with an almost unlimited shape freedom. In this paper, alumina (Al2O3) parts are produced, as Al2O3 is currently the most commonly used ceramic material for technical applications.
Design/methodology/approach
Variants of the following PM route, with indirect selective laser sintering (indirect SLS) as the AM shaping step, are explored to produce ceramic parts: powder synthesis, indirect SLS, binder removal and furnace sintering and alternative densification steps.
Findings
Freeform-shaped Al2O3 parts with densities up to approximately 90 per cent are obtained.
Research limitations/implications
The resulting Al2O3 parts contain inter-agglomerate pores. To produce higher-quality ceramic parts through indirect SLS, these pores should be avoided or eliminated.
Originality/value
The research is innovative in many ways. First, composite powders are produced using different powder production methods, such as temperature-induced phase separation and dispersion polymerization. Second, four different binder materials are investigated: polyamide (nylon-12), polystyrene, polypropylene and a carnauba wax – low-density polyethylene combination. Further, to produce ceramic parts with increased density, the following densification techniques are investigated as additional steps of the PM process: laser remelting, isostatic pressing and infiltration.
Keywords
Acknowledgements
This work has been financially supported by the research fund of KU Leuven under projects GOA/2010/12 and GOA/15/012-SUMMA, by the Fund for Scientific Research Flanders (FWO) under project G.0956.14N and by the Institute for Innovation through Science and Technology in Flanders (IWT) under project 60,827.
Citation
Deckers, J.P., Shahzad, K., Cardon, L., Rombouts, M., Vleugels, J. and Kruth, J.-P. (2016), "Shaping ceramics through indirect selective laser sintering", Rapid Prototyping Journal, Vol. 22 No. 3, pp. 544-558. https://doi.org/10.1108/RPJ-10-2014-0143