Specific energy absorption during compression testing of ABS and FPU parts fabricated using LCD-SLA based 3D printer

Abstract

Purpose

Liquid crystal display (LCD)-based stereolithography (SLA) technique has been used in drug delivery and fabrication of microfluidic devices and piezoelectric materials. It is an additive manufacturing technique where an LCD source has been used as a mask to project the image onto the tank filled with photo curable resin. This resin, when interacted with light, becomes solid. However, critical information regarding the energy absorption during the compression analysis of different components three-dimensional (3D) printed by SLA process is still limited. Therefore, this study aims to investigate the effect of different process parameters on the compressive properties.

Design/methodology/approach

In the present study, the influence of layer thickness, infill density and build orientation on the compression properties is investigated. Four infill densities, that is, 20%, 40%, 60% and 80%; five-layer thicknesses, that is, 50 µm, 75 µm, 100 µm, 150 µm and 200 µm; and two different orientations, that is, YXZ and ZXY, have been selected for this study.

Findings

It is observed that the samples printed with acrylonitrile butadiene styrene (ABS) absorbed higher energy than the flexible polyurethane (FPU). Higher infill density and sample oriented on ZXY absorbed higher energy than sample printed on YXZ orientation, in both the ABS and FPU materials. Parts printed with 80% infill density and 200 µm layer thickness resulted into maximum energy for both the materials.

Originality/value

In this study, two different types of materials are used for the compression analysis using LCD-SLA-based 3D printer. Specific energy absorbed by the samples during compression testing is measured to compare the influence of parameters. The investigation of infill parameters particularly the infill density is very limited for the SLA-based 3D printing process. Also, the results of this study provide a database to select the print parameters to obtain the required properties. The results also compare the specific energy for hard and flexible material for the same combination of the process parameters.

Citation

Dave, H.K., Karumuri, R.T., Prajapati, A.R. and Rajpurohit, S.R. (2022), "Specific energy absorption during compression testing of ABS and FPU parts fabricated using LCD-SLA based 3D printer", Rapid Prototyping Journal, Vol. 28 No. 8, pp. 1530-1540. https://doi.org/10.1108/RPJ-04-2021-0075