In recent years, fire accidents in engineering structures have often been reported worldwide, leading to a severe risk to life and property safety. The present study is carried out to evaluate the performance of Ground Granulated Blast Furnace Slag (GGBS) and fly ash–blended laterized mortars at elevated temperatures.

This test program includes the replacement of natural river sand with lateritic fine aggregates (lateritic FA) in terms of 0, 50 and 100%. Also, the ordinary Portland cement (OPC) was replaced with fly ash and GGBS in terms of 10, 20, 30% and 20, 40 and 60%, respectively, for producing blended mortars.

This paper presents results related to the determination of residual compressive strengths of lateritic fine aggregates-based cement mortars with part replacement of cement by fly ash and GGBS exposed to elevated temperatures. The effect of elevated temperatures on the physical and mechanical properties was evaluated with the help of microstructure studies and the quantification of hydration products.

A sustainable cement mortar was produced by replacing natural river sand with lateritic fine aggregates. The thermal strength deterioration features were assessed by exposing the control specimens and lateritic fine aggregates-based cement mortars to elevated temperatures. Changes in the mechanical properties were evaluated through a quantitative microstructure study using scanning electron microscopy (SEM) images. The phase change of hydration products after exposure to elevated temperatures was qualitatively analyzed by greyscale thresholding of SEM images using Image J software.

To reduce environmental impact caused by excessive use of ordinary Portland cement (OPC) and to mitigate scarcity of base materials such as natural coarse aggregate (NCA), industrial by-products can be carefully used as alternatives to OPC and NCA, in production of concrete. This paper aims to describe the performance of using ground granulated blast furnace slag (GGBS), fly ash (FA) as a complete replacement to OPC and ferrochrome slag (FCS) as replacement to NCA in production of novel FCS based alkali activated slag/fly ash concretes (AASFC) and evaluate their performance at elevated temperatures.

Two control factors with three levels each i.e. FA (0, 25 and 50 per cent by weight) and FCS (0, 50 and 100 per cent by volume) as a GGBS and NCA replacement, respectively, were adopted in AASFC mixtures. Further, AASFC mixture specimens were subjected to different levels of elevated temperature, i.e. 200°C, 400°C, 600°C and 800°C. Compressive strength and residual compressive strength were considered as responses. Three different optimization techniques i.e. gray relational analysis, technique for order preference by similarity to ideal solution and Desirability function approach were used to optimize AASFC mixtures subjected to elevated temperatures.

As FA replacement increases in FCS based AASFC mixtures, workability increases and compressive strength decreases. The introduction of FCS as replacement to NCA in AASFC mixture did not show any significant change in compressive strength under ambient condition. AASFC produced with 75 per cent GGBS, 25 per cent FA and 100 per cent FCS was found to have excellent elevated temperature enduring properties among all other AASFC mixtures studied.

Although several studies are available on using GGBS, FA and FCS in production of OPC-based concretes, present study reports the performance of novel FCS based AASFC mixtures subjected to elevated temperatures. Further, GGBS, FA and FCS used in the present investigation significantly reduces CO₂ emission and environmental degradation associated with OPC production and NCA extraction, respectively.

This study reports the performance of thermally deteriorated concrete with and without fibres. Attempts have been made to find the suitable performance of steel polypropylene (PP) hybrid fibre combination that could significantly enhance the performance of mechanical properties at elevated temperatures.

In this experimental investigation, concrete cubes of 100 mm in size of various compositions were cast and water-cured for 28 days, and later exposed to elevated temperatures of either 200 or 400°C or 600 and or 800°C with a retention period of 2 h. The properties like change in colour and percentage weight loss were evaluated. Ultrasonic Pulse Velocity test was used to obtain qualitative information of strength variation. Residual strength of thermally deteriorated concrete specimen was measured by destructive testing.

Steel fibre volume fraction of 1 per cent improves the compressive strength of concrete in the temperature range of 400 to 800°C. The addition of steel fibre and PP fibre (Mix 3) improves the splitting strength of the concrete at elevated temperature range of 400 to 600°C.

Performance enhancement is observed with hybrid fibres for temperature endurance of concrete.

This paper aims to study and assess residual strengths of concrete specimen exposed to elevated temperatures by core recovery tests.

The appraisal of concrete structures is typically carried out by means of partially destructive tests such as tests on concrete cores taken from the structure and non-destructive testing.

This paper presents results associated with determination of residual compressive strengths of plain and reinforced concrete elements exposed to elevated temperatures by core recovery test. Physical observations and results of compressive strengths of cores extracted from plain cement concrete, as well as from reinforced concrete beam elements exposed to elevated temperatures, have been presented.

The empirical relations have been proposed between standard cube and core extracted for compressive strength of concretes exposed to elevated temperatures are useful for damage diagnosis.

Concrete loses strength in the event of accidental fires. The residual strength of normal strength concrete is of vital importance for ascertaining serviceability of buildings after the event of fires. Strength loss in concrete is dependent on the temperature of exposure, its duration and the way it gets cooled. In this study concrete cubes of size 100 mm have been cast for M25 grade of concrete, 28 days water cured. The specimens were subjected to elevated temperatures of 150°C, 250°C, 350°C, 450°C and 550°C with a retention period of 1 hour. After 1 hour of exposure, specimens were allowed to cool under different cooling regimes to ambient temperature. Later their appearance, colour and cracks were observed and also weight losses were determined. Further, destructive tests were conducted to estimate residual compressive and split tensile strengths. Important performance changes have been presented and discussed. Split tensile strengths are related to compressive strengths for all the cases of cooling regimes.

Concrete in structures is likely to be exposed to high temperatures during fire. The probability of its exposure to elevated temperatures is high due to natural hazards, accidents and sabotages. Therefore, the performance of concrete during and after exposure to elevated temperature is a subject of great importance and interest to the designer. Popular normal strength grades of concrete produced by Ready Mix Concrete (RMC) India, Mangalore have been used in production of test specimens (150 mm cubes), cured and tested by destructive method for gathering data on strength characteristics. Later, these test samples were subjected to elevated temperatures ranging from 100°C to 800°C, in steps of 100°C with a retention period of 2 hours. After exposure, weight losses and the residual compressive strength retention characteristics are studied. Test results indicated that weight and strength significantly reduces with an increase in temperature. Residual compressive strength prediction equations are proposed for normal strength concretes subjected to elevated temperatures.

Concrete is found to undergo degradation when subjected to elevated temperatures during an accidental event, such as fire and lose substantial amount of its original strength. The loss of strength in concrete is mainly attributed to the decomposition of Calcium Silicate Hydrate (C-S-H) and release of chemically bound water, which begins when the exposure temperature exceeds 500°C. When such a concrete is supplied with water and allowed to recure, it is found to recover substantial amount of its lost strength. This work is carried out to investigate the effect of recuring on strength recovery of un-blended and blended concrete specimen (100 mm cubes) subjected to elevated temperatures from 400°C to 700°C, in steps of 100°C, for a retention period of two hours at the designated temperatures. The concrete cubes immediately after exposure were subjected to thermal shock by quenching them in water, and then temperature of thermally shocked concrete is allowed to cool to room temperature. The cooled specimen were then recured in water for 1, 3, 7, 14, 21, 28, 56 days and tested for compressive strength recovery. These studies were carried out for Portland Cement (PC) based concrete and Portland & Granulated Blast Furnace Slag (70% PC + 30% GGBS) based concrete (blended concrete), and some interesting results are presented and discussed in this paper.