This study aims to investigate the influence mechanism of brazing and aging on the strengthening and corrosion behavior of novel multilayer sheets (AA4045/AA7072/AA3003M/AA4045).

Polarization curve tests, immersion experiments and transmission electron microscopy analysis were used to study the corrosion behavior and tensile properties of the sheets before and after brazing and aging.

The strength of the sheet is weakened after brazing due to brittle eutectic phases, and recovered after aging due to enhanced precipitation strengthening in the AA7072 interlayer. The core of nonbrazed sheets cannot be protected due to the significant galvanic coupling effect between the intermetallic particles and the substrate. Brazing and aging treatments promote the redissolved of second phased and limit corrosion along the eutectic region in the clad, allowing the core to be protected.

AA7xxx alloy was added to conventional brazed sheets to form a novel Al alloy composite sheet with AA4xxx/AA7xxx/AA3xxx structure. The strengthening and corrosion mechanism of the sheet was proposed. The added interlayer can sacrificially protect the core from corrosion and improves strength after aging treatment.

The purpose of this paper is to reveal the effect of microstructure on the corrosion behavior of CoCrNi alloy in 3.5 Wt.% NaCl solution.

The as-cast CoCrNi alloy was prepared by arc melting, and the cold-rolled and annealed alloys were prepared by processing the as-cast alloy.

The experimental results showed that a protective passivation film was formed on the surfaces of these CoCrNi MEA, and the stability and compactness of alloys increased in the sequence of cold-rolled, as-cast and annealed CoCrNi alloys. The annealed CoCrNi alloys had the best pitting resistance.

This study proposes the effect of the microstructure of CoCrNi alloy on corrosion resistance.

The purpose of this study is to assess the influence of Al and Ag addition on thermal, mechanical and shape memory properties of Cu-Al-Ag alloy.

The material is synthesized in a controlled atmosphere to minimize the reaction of alloying elements with the atmosphere. Cast samples were homogenized, then subjected to hot rolling and further betatized, followed by step quenching. Eight samples were chosen for study among which first four samples varied in Al content, and the next set of four samples varied in Ag composition.

The testing yielded a result that the increase in binary alloying element decreased transformation temperature range but increased entropy and elastic energy values. It also improved the shape memory effect and mechanical properties (UTS and hardness). An increase in ternary alloying element increased transformation temperature range, entropy and elastic energy values. The shape memory effect and mechanical properties are enhanced by the increase in ternary alloying element. The study revealed that compositional variation of Al should be limited to a range of 8 to 14 Wt.% and Ag from 2 to 8 Wt.%. Microstructural and diffraction studies identified the ß’1 martensite as a desirable phase for enhancing shape memory properties.

Numerous studies have been made in exploring the transformation temperature and phase formation for similar Cu-Al-Ag shape memory alloys, but their influence on shape memory effect was not extensively studied. In the present work, the influence of Al and Ag content on shape memory characteristics is carried out to increase the design choice for engineering applications of shape memory alloy. These materials exhibit mechanical and shape memory properties within operating ranges similar to other copper-based shape memory alloys.

This article aims to focus on implementing Lean Six Sigma (LSS) in steel manufacturing to enhance productivity and quality in the galvanizing process line. In recent trends, manufacturing organizations have expressed strong interest in the LSS since they attempt to enhance its overall operations without imposing significant financial burdens.

This article used lean tools and Six Sigma's DMAIC (Define, Measure, Analyze, Improve and Control) with Yin's case study approach. This study tried to implement the LSS for the steel galvanizing process in order to reduce the number of defects using various LSS tools, including 5S, Value stream map (VSM), Pareto chart, cause and effect diagram, Design of experiments (DoE).

Results revealed a significant reduction in nonvalue-added time in the process, which led to improved productivity and Process cycle efficiency (PCE) attributed to applying lean-Kaizen techniques. By deploying the LSS, the overall PCE improved from 22% to 62%, and lead time was reduced from 1,347 min to 501 min. DoE results showed that the optimum process parameter levels decreased defects per unit steel sheet.

This research demonstrated how successful LSS implementation eliminates waste, improves process performance and accomplishes operational distinction in steel manufacturing.

Since low-cost/high-effect improvement initiatives have not been adequately presented, further research studies on adopting LSS in manufacturing sectors are needed. The cost-effective method of process improvement can be considered as an innovation.

An experimental investigation for developing structure-property correlations of hot-rolled E410 steels with different carbon contents, i.e. 0.04wt.%C and 0.17wt.%C metal active gas (MAG) and cold metal transfer (CMT)-MAG weldments was undertaken.

Mechanical properties and microstructure of MAG and CMT-MAG weldments of two E410 steels with varying content of carbon were compared using standardized mechanical testing procedures, and conventional microscopy.

0.04wt.%C steel had strained ferritic and cementite sub-structures in blocky shape and large dislocation density, while 0.17wt.%C steel consisted of pearlite and polygonal ductile ferrite. This effected yield strength (YS), and microhardness being larger in 0.04wt.%C steel, %elongation being larger in 0.17wt.%C steel. Weldments of both E410 steels obtained with CMT-MAG performed better than MAG in terms of YS, ultimate tensile strength (UTS), %elongation, and toughness. It was due to low heat input of CMT-MAG that resulted in refinement of weld metal, and subzones of heat affected zone (HAZ).

A substantial improvement in YS (∼9%), %elongation (∼38%), and room temperature impact toughness (∼29%) of 0.04wt.%C E410 steel is achieved with CMT-MAG over MAG welding. Almost ∼10, ∼12.5, and ∼16% increment in YS, %elongation, and toughness of 0.17wt.%C E410 steel is observed with CMT-MAG. Relatively low heat input of CMT-MAG leads to development of fine Widmanstätten and acicular ferrite in weld metal and microstructural refinement in HAZ subzones with nearly similar characteristics of base metal.

International outbreak of the SARS-CoV-2 infection has fostered the Italian government to impose the FFP2 protective facial masks in closed environments, including bar, restaurants and, more in general, in the food sector. Protective facial masks are rocketing, both in mass and in costs, in the food sector imposing efforts in fostering reuse strategies and in the achievement of sustainable development goals. The scope of the present paper is to depict possible strategies in manufacturing and reuse strategies that can reduce the carbon footprint (CF) of such devices.

To implement circular economy strategies in the protective facial masks supply chain, it was considered significant to move towards a study of the environmental impact of such devices, and therefore a CF study has been performed on an FFP2 facial mask used in the food sector. Different materials besides the mostly used polypropylene (PP) (polyethylene (PE), polycarbonate (PC), poly (lactic acid) (PLA), cotton, polyurethane (PUR), polystyrene (PS) and nylon 6,6) and different sanitisation alternatives as reuse strategies (both laboratory and homemade static oven, ultraviolet germicidal irradiation) readily implemented have been modelled to calculate the CF of a single use of an FFP2 mask.

The production of textiles in PP, followed by disposal was the main contributor to CF of the single-use FFP2 mask, followed by packaging and transportations. PP and PE were the least impacting, PC, cotton and Nylon 6-6 of the same weight results the worst. PLA has an impact greater than PP and PE obtained from crude oil, followed by PUR and PS. Static laboratory oven obtained an 80.4% reduction of CF with respect to single use PP-made FFP2 mask, whereas homemade oven obtained a similar 82.2% reduction; UV cabinet is the best option, showing an 89.9% reduction.

The key strategies to reduce the environmental impacts of the masks (research for new materials and reuse with sanitisation) should ensure both the retention of filtering capacities and the sanitary sterility of the reused ones. Future developments should include evaluations of textile recycling impacts, using new materials and the evaluation of the life cycle costs of the reused masks.

This paper intends to provide to stakeholders (producers, consumers and policy makers) the tools to choose the best option for producing and reuse environmentally friendly protective facial masks to be used in the food sector, by using both different materials and easily implemented reuse strategies.

The reduction of the CF of protective facial masks in the food sector surely will have relevant positive effects on climate change contributing to reach the goals of reducing CO₂ emissions. The food sector may promote sustainable practices and attract a niche piece of clients particularly sensible to such themes.

The paper has two major novelties. The first one is the assessment of the CF of a single use of an FFP2 mask made with different materials of the non-woven filtering layers; as the major contribution to the CF of FFP2 masks is related to the non-woven textiles manufacturing, the authors test some other different materials, including PLA. The second is the assessment of the CF of one single use of a sanitised FFP2 mask, using different sanitation technologies as those allowed in bars or restaurants.

The purpose of this study is to investigate the effect of nano ZrC particles on the mechanical and electrochemical corrosion properties of FeCrAl alloys, providing a beneficial reference basis for the development of high-performance carbide reinforced FeCrAl alloys with good mechanical and corrosion properties in the future.

Nano ZrC reinforced FeCrAl alloys were prepared by mechanical alloying and spark plasma sintering. Phases composition, tensile fractography, corrosion morphology and chemical composition of nano ZrC reinforced FeCrAl alloys were analyzed by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy, respectively. Microhardness and tensile properties of nano ZrC reinforced FeCrAl alloys were investigated by mechanical testing machine and Vickers hardness tester. Electrochemical corrosion properties of nano ZrC reinforced FeCrAl alloys were investigated by electrochemical workstation in 3.5 wt.% NaCl solution.

The results showed that addition of nano ZrC can effectively improve the mechanical and corrosion properties. However, excessive nano ZrC could decrease the mechanical properties and reduce the corrosion resistance. In all the FeCrAl alloys, FeCrAl–0.6 wt.% ZrC alloy exhibits the optimum mechanical properties with an ultimate tensile strength, elongation and hardness of 990.7 MPa, 24.1% and 335.8 HV1, respectively, and FeCrAl–0.2 wt.% ZrC alloy has a lower corrosion potential (−0.179 V) and corrosion current density (2.099 µA/cm2) and larger pitting potential (0.497 V) than other FeCrAl–ZrC alloys, showing a better corrosion resistance.

Adding proper nano ZrC particles can effectively improve the mechanical and corrosion properties, while the excessive nano ZrC is harmful to the mechanical and corrosion properties of FeCrAl alloys, which provides an instruction to develop high-performance FeCrAl cladding materials.

Stainless-clad bimetallic steels (SCBS) are widely investigated in some extremely environmental applications areas, such as polar sailing area and tropical oil and gas platforms areas, because of their excellent anticorrosion performance and relatively lower production costs. However, the properties of SCBS, including the mechanical strength, weldability and the anticorrosion behavior, have a direct relation with the manufacturing process and can affect their practical applications. This paper aims to review the application and the properties requirements of SCBS in marine environments to promote the application of this new material in more fields.

In this paper, the manufacturing process, welding and corrosion-resistant properties of SCBS were introduced systematically by reviewing the related literatures, and some results of the authors’ research group were also introduced briefly.

Different preparation methods, such as rolling composite, casting rolling composite, explosive composite, laser cladding and plasma arc cladding, as well as the process parameters, including the vacuum degree, rolling temperature, rolling reduction ratio, volume ratios of liquid to solid, explosive ratio and the heat treatment, influenced a lot on the properties of the SCBS through changing the interface microstructures. Otherwise, the variations in rolling temperature, pass, reduction and the grain size of clad steel also brought the dissimilarities of the mechanical properties, microhardness, bonding strength and toughness. Another two new processes, clad teeming method and interlayer explosive welding, deserve more attention because of their excellent microstructure control ability. The superior corrosion resistance of SCBS can alleviate the corrosion problem in the marine environment and prolong the service life of the equipment, but the phenomenon of galvanic corrosion should be noted as much as possible. The high dilution rate, welding process specifications and heat treatment can weaken the intergranular corrosion resistance in the weld area.

This paper summarizes the application of SCBS in marine environments and provides an overview and reference for the research of stainless-clad bimetallic steel.

The impact of rolling on the performance of micro arc oxidation (MAO) coatings on ZM5 alloy has been underreported. The purpose of this study is to explore the correlation between rolling and the failure mechanism of MAO coatings in greater depth.

The influence of rolling on the corrosion and wear properties of MAO coating was investigated by phase structure, bond strength test (initial bond strength and wet adhesion), electrochemical impedance spectroscopy and wear test. The change of the surface electrochemical properties was studied by first principles analysis.

The results showed that the MAO coating on rolled alloy had better corrosion and wear resistance compared to cast alloy, although the structure and component content of two kinds of MAO coating are nearly identical. The difference in interface bonding between MAO coating and Mg substrate is the primary factor contributing to the disparity in performance between the two types of samples. Finally, the impact of the rolling process on MAO coating properties is explained through first-principle calculation.

A comprehensive explanation of the impact of the rolling process on MAO coating properties will provide substantial support for enhancing the application of Mg alloy anticorrosion.

This study aims to identify the significant factors of the multi-dimpling process, determine the most influential parameters of multi-dimpling to increase the dimple sheet strength and make a low-cost model of the multi-dimpling for sheet metal industries. To create an empirical expression linking process performance to different input factors, the percentage contribution of these elements is also calculated.

Taguchi grey relational analysis is used to apply a new effective strategy to experimental data in order to optimize the dimpling process parameters while taking into account several performance factors and low-cost model. In addition, a statistical method called ANOVA is used to ensure that the results are adequate. The optimal process parameters that generate improved mechanical properties are determined via grey relational analysis (GRA). Every level of the process variables, a response table and a grey relational grade (GRG) has been established.

The factors created for experiment number 2 with 0.5 mm as the sheet thickness, 2 mm dimple diameter, 0.5 mm dimple depth, 8 mm dimples spacing and the material of SS 304 were allotted rank one, which belonged to the optimal parameter values giving the greatest value of GRG.

The study demonstrates that the process parameters of any dimple sheet manufacturing industry can be optimized, and the effect of process parameters can be identified.

The proposed low-cost model is relatively economical and readily implementable to small- and large-scale industries using newly developed multi-dimpling multi-punch and die.