Preparation of polysulfone/sulfonated polysulfone-SiO₂ nanofiltration membrane and its performance characterization

Abstract

Purpose

This study aims to optimize the preparation conditions and modify the nanofiltration (NF) membranes to prepare high-performance polysulfone/sulfonated polysulfone composite nanofiltration (PSF/SPSF-NF) membranes through interfacial polymerization.

Design/methodology/approach

Investigating the impacts of anhydrous piperazine (PIP) concentration, trimesoyl chloride (TMC) concentration and basement membrane type on NF membrane performance, the optimal membrane was prepared. In addition, nano-SiO₂ was added to the active separation layer to modify the NF membranes.

Findings

The comprehensive performance of PSF/SPSF-NF membranes was optimized when the concentration of PIP was 0.75 Wt.% and the concentration of TMC was 0.15 Wt.%, at which time the water flux was 66.1 L·m⁻²·h⁻¹ and the retention rate of Na₂SO₄ was 98.1%. The comprehensive performance of polysulfone/sulfonated polysulfone-SiO₂ nanofiltration (PSF/SPSF-SiO₂-NF) membranes was optimized when the blending ratio of nano-SiO₂ to PIP was 2:3, with a pure water flux of 81.9 L·m⁻²·h⁻¹ and a Na₂SO₄ retention rate of 95.9%. Compared to polysulfone nanofiltration (PSF-NF) membranes and PSF/SPSF-NF membranes, NF membranes with nano-SiO₂ increased the flux recovery rate by 22.9% and 8.7%.

Practical implications

PSF/SPSF-SiO2-NF membrane exhibits excellent antifouling properties.

Originality/value

There is currently no literature available on the preparation of NF membranes using polysulfone/sulfonated polysulfone (PSF/SPFS) as a substrate. This provides a method for modifying NF membranes, starting with the modification of the basement membrane and then modifying the active separation layer.