Differentiated SnSb grain size distribution for improved tribological properties of Babbitt alloy

Abstract

Purpose

The grain size and grain distribution mode have a significant impact on the tribological properties of Babbitt alloy. The purpose of this paper is to study the effect of differentiated SnSb grain size distribution on the improvement of tribological properties of Babbitt alloy.

Design/methodology/approach

Babbitt (marked by babbitt-cr), with a differentiated SnSb grain size distribution, was fabricated using a selective zone laser surface treatment. Bare Babbitt with coarse SnSb grain was marked as babbitt-c, and Babbitt with refined SnSb grain was marked as babbitt-r. The microstructure, microhardness and wettability of specimens were tested. The tribological properties of babbitt-c, babbitt-r and babbitt-cr were evaluated under dry and lubricated conditions.

Findings

The microstructure transforms from single coarse SnSb grain distribution or single refined SnSb grain distribution to differentiated SnSb grain size distribution, as a result of selective zone laser surface treatment. Among three specimens of microhardness, babbitt-cr showed the highest microhardness. The lipophilicity property of babbitt-cr was better compared to babbitt-c. A mixture of coarse and refined grain is beneficial to improve the tribological properties of Babbitt alloy under dry condition. Furthermore, compared with babbitt-c, the wear resistance of babbitt-cr was enhanced under lubricated condition. However, the anti-wear property of babbitt-cr was not significantly improved relative to babbitt-r with an increase in the loads.

Originality/value

The study demonstrates that modulated different grain size alternating distribution modes can improve the tribological properties of Babbitt alloy.