Wear comfort and thermal insulation of ceramic-imbedded fabrics with different yarn structures by thermal manikin experiment

Abstract

Purpose

This study examined the wear comfort and thermal insulation properties of Al₂O₃/graphite particle-imbedded sheath/core and dispersed fabrics via a thermal manikin experiment.

Design/methodology/approach

Al₂O₃/graphite sheath/core and dispersed polyethylene terephthalate (PET) yarn (POY 120d/24f) were spun using a pilot melt bi-component conjugated spinning machine, which was texturized as 75d/24f on the belt-type texturing machine. The woven fabric specimens were made using nylon 70d/34f in the warp with three types of weft yarn: Al₂O₃/graphite sheath/core, dispersed and regular PET yarns. Thermal insulation properties were measured and compared in terms of the heat retention rate (I) by KES-F7 apparatus and the maximum surface temperature by light heat emission equipment, as verified by the emissivity of various fabric specimens by far-infrared ray experiment. In addition, this study examined the thermal insulation (Clo value) characteristics of the clothes made of Al₂O₃/graphite sheath/core and dispersed fabrics using a thermal manikin apparatus, which were compared with the properties of regular PET clothing.

Findings

The thermal insulation of the dispersed fabric was superior to that of the sheath/core fabric, which was tentatively attributed to the higher emissivity of the dispersed yarn with Al₂O₃/graphite particles distributed over the whole yarn cross-section than that from the core of the sheath/core yarn. This result for the clothing measured using a thermal manikin was consistent with the higher heat retention rate (I) and the maximum surface temperature of the dispersed fabric than that of the sheath/core fabric. In addition, the thermal insulation of the dispersed and sheath/core fabrics was superior to that of the regular PET fabric, which revealed that the Al₂O₃/graphite particles imbedded in the dispersed and sheath/core yarns exerted a greater effect on the heat storage and release characteristics compared to that of the TiO₂ particles in regular PET yarn. The Clo values of the dispersed and sheath/core fabrics under the light-on condition were much higher than those under the light-off condition, and furthermore, the difference of the Clo value between the sheath/core and regular PET fabrics under light-on condition was approximately 1.7 times greater than that under the light-off condition. These results revealed that the far-infrared rays emitted from the Al₂O₃/graphite particles imbedded in the sheath/core and dispersed yarns enhance the heat storage and release characteristics from the fabric under the light-on condition, i.e. under the sunlight.

Originality/value

The previously examined thermal wear comfort properties of the various inorganic particle-imbedded fabrics were measured with the fabric state, not clothing, which could not provide objective data related to the actual wearing performance of clothing.

Citation

Kim, H. (2023), "Wear comfort and thermal insulation of ceramic-imbedded fabrics with different yarn structures by thermal manikin experiment", International Journal of Clothing Science and Technology, Vol. 35 No. 2, pp. 197-213. https://doi.org/10.1108/IJCST-06-2021-0081