This paper aims to fabricate a polymer-based polyethylene glycol (PEG) coating with acrylic resin as a binder that can show antiviral activity against the feline coronavirus (FCov) on the glass substrate.

The PEG/acrylic coating systems of different weight percentages were coated on the glass substrates using the spray-coating method and cured at room temperature for 24 h.

The coating system containing 20 Wt.% of PEG exhibits the highest antiviral activities as high as 99.9% against FCov compared with other samples.

Findings will be useful in the development of antiviral coating for PPE fabrics by using the simple synthesis method.

Application of PEG as an antiviral agent in the antiviral coating system with high antiviral activities about 99.9%.

There is a strong inducement to develop new inorganic materials to substitute the current industrial pigments, which are known for their poor ultraviolet absorbent and low photoluminescence (PL) properties. The purpose of this paper is to invent a better rare-earth-based pigment material as a spectral modifier with good luminescence properties to enhance the spectral response for photovoltaic panel application.

Different phosphor samples made of nano-calcium carbonate (CaCO₃) with varied wt.% of the dopant Dysprosium doped calcium borophosphate (CBP/Dy) as (W0 – 0%, W1 – 3,85%, W2 – 7.41%, W3 –10.71% and W4 –13.79%) were prepared via the solid-state diffusion method at 600 °C for 6 h using a muffle furnace. The structural, morphological and luminescence properties of the CaCO₃:CBP/Dy powder samples were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and PL test.

The XRD, SEM and FTIR results verified the crystalline formation, morphological behaviour and vibration bonds of synthesized CBP/Dy-doped CaCO₃ powder samples. XRD pattern revealed that the synthesized powder samples exhibit crystalline structured materials, and SEM results showed irregular shape and porous-like structured morphologies. FTIR spectrum shows prominent bands at 712, 874 and 1,404 cm⁻¹, corresponding to asymmetric stretching vibrations of CO3²⁻ groups and out-of-plane bending. PL characterization of CBP/Dy-doped CaCO₃ (sample W) shows emission at 427 nm (λmax) under the excitation of 358 nm. The intensity of PL emission spectra drops due to the concentration quenching effect, while the maximum PL intensity is observed in the W3 phosphor powder system.

This phosphor powder is expected to find out the potential application such as a spectral modifier which is applied to match the energy of photons with solar cell bandgap to improve spectral absorption and lead to better efficiency.

The introduction of a nano-CaCO₃:CBP/Dy hybrid powder system with good luminescence properties to be used as spectral modifiers for solar cell application has been synthesized in the lab, which is a novel attempt.

The purpose of this paper is to introduce the simple synthesis process of thermal-insulation coating by using three different nanoparticles, namely, nano-zinc oxide (ZnO), nano-tin dioxide (SnO₂) and nano-titanium dioxide (TiO₂), which can reduce the temperature of solar cells.

The thermal-insulation coating is designed using sol-gel process. The aminopropyltriethoxysilane/methyltrimethoxysilane binder system improves the cross-linking between the hydroxyl groups, -OH of nanoparticles. The isopropyl alcohol is used as a solvent medium. The fabrication method is a dip-coating method.

The prepared S1B1 coating (20 Wt.% of SnO₂) exhibits high transparency and great thermal insulation property where the surface temperature of solar cells has been reduced by 13°C under 1,000 W/m² irradiation after 1 h. Meanwhile, the Z1B2 coating (20 Wt.% of ZnO) reduced the temperature of solar cells by 7°C. On the other hand, the embedded nanoparticles have improved the fill factor of solar cells by 0.2 or 33.33%.

Findings provide a significant method for the development of thermal-insulation coating by a simple synthesis process and low-cost materials.

The thermal-insulation coating is proposed to prevent exterior heat energy to the inside solar panel glass. At the same time, it can prevent excessive heating on the solar cell’s surface, later improves the efficiency of solar cell.

This study presents a the novel method to develop and compare the thermal-insulation coating by using various nanoparticles, namely, nano-TiO₂, nano-SnO₂ and nano-ZnO at different weight percentage.