This paper aims to solve the problems molybdenum disulfide (MoS₂) nanosheets suffer from inadequate dispersion stability and form a weak lubricating film on the friction surface, which severely limits their application as lubricant additives.

MoS₂/C₆₀ nanocomposites were prepared by synthesizing molybdenum disulfide (MoS₂) nanosheets on the surface of hydrochloric acid-activated fullerenes (C₆₀) by in situ hydrothermal method. The composition, structure and morphology of MoS₂/C₆₀ nanocomposites were characterized. Through the high-frequency reciprocating tribology test, its potential as a lubricant additive was evaluated.

MoS₂/C₆₀ nanocomposites that were prepared showed good dispersion in dioctyl sebacate (DOS). When 0.5 Wt.% MoS₂/C₆₀ was added, the friction reduction performance and wear resistance improved by 54.5% and 62.7%, respectively.

MoS₂/C₆₀ composite nanoparticles were prepared by in-situ formation of MoS₂ nanosheets on the surface of C₆₀ activated by HCl through hydrothermal method and were used as potential lubricating oil additives.

The peer review history for this article is available at: https://publons.com/publon/10.1108/ILT-10-2023-0321/

Aluminum alloy is considered an ideal material in aerospace, automobile and other fields because of its lightweight, high specific strength and easy processing. However, low hardness and strength of the surface of aluminum alloys are the main factors that limit their applications. The purpose of this study is to obtain a composite coating with high hardness and lubricating properties by applying GO–PVA over MAO coating.

A pulsed bipolar power supply was used as power supply to prepare the micro-arc oxidation (MAO) coating on 6061 aluminum sample. Then a graphene oxide-polyvinyl alcohol (GO–PVA) composite coating was prepared on MAO coating for subsequent experiments. Samples were characterized by Fourier infrared spectroscopy, X-ray diffraction, Raman spectroscopy and thermogravimetric analysis. The friction test is carried out by the relative movement of the copper ball and the aluminum disk on the friction tester.

Results showed that the friction coefficient of MAO samples was reduced by 80% after treated with GO–PVA composite film.

This research has made a certain contribution to the surface hardness and tribological issues involved in the lightweight design of aluminum alloys.